Abstract
The changes of magnetic properties in neutron irradiated F $e_{81}$ $B_{13.5}$S $i_{3.5}$ $C_2$ amorphous ribbon were studied by X-ray diffraction, hysteresis loop, temperature dependence of magnetization and complex permeability. The fluences of thermal ( $n_{th}$) and fast ( $n_{f}$) neutron were 6.95$\times$10$^{18}$ $n_{th}$ c $m^{-2}$ and 4.56$\times$10$^{16}$ $n_{f}$c $m^{-2}$ , respectively. The changes of XRD Profiles were not observable at the neutron irradiated sample. The complex permeability spectra showed that the permeability from domain wall motion decreased due to the increase of pinning force against domain motion by the neutron irradiation, and the relaxation frequency of rotational magnetization moved to higher frequency region. The measurement of hysteresis loop showed the increase of magnetic softness, related to rotational magnetization, but saturation magnetization was decreased in neutron irradiation sample. The Curie temperature was decreased in the neutron irradiated sample.e.e.e.
비정질 F $e_{81}$ $B_{13.5}$S $i_{3.5}$ $C_2$리본에서 중성자 조사 후 X-선 회절, 상온에서의 자기이력곡선, 자화의 온도의존성 그리고 복소 투자율 측정하고, 결함에 의한 자기 특성과 관련하여 분석하였다. 중성자 조사량은 열 중성자( $n_{th}$)와 고속 중성자( $n_{f}$)가 각각 6.95$\times$$10^{18}$ $n_{th}$$cm^{-2}$ 과 4.56$\times$$10^{16}$ $n_{f}$$cm^{-2}$ 이었다. 중성자 조사된 시료의 X-선 회절상의 변화는 보이지 않았다. 중성자 조사 후, 복소 투자율의 자기이완특성에서 자벽운동에 의한 부분은 감소하였고, 자화회전에 의한 자기이완 주파수는 좀더 높은 주파수 영역으로 이동하였는데 , 이는 pinning력이 증가된 것을 반영한다. 자기이력곡선에서는 중성자 조사 후의 시료의 softness는 좋아지는 한편 포화자화값은 감소되는 것을 볼 수 있었으며, Curie 온도가 감소하는 결과가 나왔다. 자기 softness 향상은 자화회전에 의한 것이라 여겨진다.다.다.다.