• 한국세라믹학회지
• /
• 제43권5호
• /
• pp.277-283
• /
• 2006

A porous material with a surface layer was fabricated from glass abrasive sludge and expanding agents. The glass abrasive sludges were mixed with expanding agents and compacted into precursors. These precursors were sintered in the range of $700-900^{\circ}C$ for 20 min. The sintered porous materials had a surface layer with smaller pores and inner parts with larger pores. The surface layer and closed pores controlled water absorption. As the expanding agent fraction and the sintering temperature increased, the porosity and pore size increased. The porous materials with $Fe_2O_3$ and graphite as the expanding agents had a low absorption ratio of about 3% or lower while the porous material with $CaCO_3$ as the expanding agent had a higher absorption ratio and more open pores.

• 한국전기전자재료학회논문지
• /
• 제17권2호
• /
• pp.184-189
• /
• 2004

The effects of $Y_2$ $O_3$-substitution on the piezoelectric properties of Pb[(N $i_{1}$3/N $b_{2}$3/)$_{0.15}$(Z $r_{1}$2/ $Ti_{1}$2/)$_{0.85}$] $O_3$ceramics were investigated. It was found that $Y^{3+}$ ions incorporate into Pb-sites of the ceramics, resulting in a increased lattice anisotropy and formation of Pb-vacancies. As a result, an orthorhombic-tetragonal phase transition was induced when $\chi$>0.005. At the morphotropic phase boundary of x=0.005, piezoelectric constants( $k_{p}$, $k_{33}$, and $d_{33}$) showed maximum values of 0.53, 0.58, and 350pC/N, respectively. A 30-layer actuator fabricated with the above material showed a maximum strain of 0.12％ under 100V DC bias.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.533-536
• /
• 2006

A light-weight aggregate with a surface layer was fabricated using glass abrasive sludge and expanding agents. The glass abrasive sludges were mixed with expanding agents ($Fe_2O_3,\;graphite,\;CaCO_3$) and formed into precursors. These precursors were sintered in the range of $700-900^{\circ}C$ for 20min. The sintered light-weight aggregate had a surface layer with smaller pores and an inner region with larger pores. The surface layer and pores controlled the water absorption ratio and physical properties. As the expanding agent fraction and the sintering temperature increased, the porosity and pore size increased. The light-weight aggregate with $Fe_2O_3$ and graphite as the expanding agents had a low water absorption ratio while the porous material with $CaCO_3$ as the expanding agent had a higher water absorption ratio and more open pores.

• 한국세라믹학회지
• /
• 제35권10호
• /
• pp.1055-1060
• /
• 1998

고주파 저손실 재질로 사용되는 Mn-Zn ferrites의 제조공정 중 입도분포제어가 전자기적 물성에 미치는 효과에 관하여 연구하였다. 입도분포는 분쇄시간을 변화시켜 제어하였으며 철의 유입을 막기위하여 지르코니아볼을 사용하였다. 분쇄시간이 증가함에 따라 입자크기는 2.1 $\mu\textrm{m}$에서 1.0$\mu\textrm{m}$로 감소하였으며, 비표면적은 0.55에서 3.21m2/g으로 증가하였다. 비표면적 값이 증가할수록 소결체의 밀도는 증가하였으며, 높은 비표면적을 가진 분말의 경우 1300$^{\circ}C$ 이 상의 고온에서 소결할 때 불균일한 미세구조와 과대입성장이 발생하였으며, 전자기적 물성감소가 나타났다.

• 한국산학기술학회:학술대회논문집
• /
• 한국산학기술학회 2001년도 춘계학술대회 발표논문집
• /
• pp.40-46
• /
• 2001

A1₂TiO/sub 5/ 세라믹스의 열적 안정성은 MgO와 고온 arc용융노에서 MgAl₂O₄ spinel과 같은 고용체를 이루고, SiO₂, ZrO₂와 α-Al₂O₃등의 첨가제로 입자크기와 미세 균열을 감소시킴으로서 증가시킨다. A1₂TiO/sub 5/ 세라믹스의 낮은 열팽창 특성은 상이한 열팽창으로 hysteresis 곡선을 나타내며 이 현상은 미세균열의 opening과 closing으로 설명된다. 이들의 열팽창 곡선, 소성온도에 EK른 관계를 dilatometer로 연구하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.240-244
• /
• 2003

후막 리소그라피 기술은 기판 위에 감광성 페이스트를 도포한 후 자외선과 패턴마스크를 사용하는 광식각(photolithography) 방법을 이용하여 세부 패턴을 형성시키는 기술이다, 이 기술은 후막기술로서는 높은 해상도인 선폭 $30{\mu}m$ 이하의 미세도선을 구현할 수 있어, 후막기술을 이용한 고주파 모듈의 제조에 있어서 새로운 대안으로 주목받고 있다. 본 연구에서는 알루미나 기판 상에 수십 ${\mu}m$ 이하의 마이크로 비아를 가지는 유전체 층을 형성시킬 수 있는 저온소결용 감광성 유전체 페이스트를 개발하였다. 저온소결용 유전체 파우더와 폴리머, 모노머, 광개시제 등의 양을 조절하여 마이크로 비아를 형성할 수 있는 최적 페이스트 조성을 연구하였으며, 노광량 및 현상시간과 같은 공정변수가 마이크로 비아의 해상도에 미치는 영향을 평가하였다. 알루미나 기판에 전면 프린팅 한 후 건조, 노광, 현상, 소성 과정을 거쳐 소결전 $37{\mu}m$, 소결후 $49{\mu}m$의 해상도를 가지는 마이크로 비아를 형성할 수 있었다.

• 한국분말재료학회지
• /
• 제10권4호
• /
• pp.241-248
• /
• 2003

Biaxially textured Ni tapes were fabricated by a cold working and recrystallization heat treatment processes from powder compact rods. The processing parameters associated with the cube texture formation in Ni tapes were systematically investigated by using X-ray diffraction and pole-figure analysis. The Ni powder used in this study was 5 $\mu$m in size and 99.99% in purity. To find the optimum sintering temperature, tensile tests were performed for Ni rods sintered at various temperatures. The Ni rods sintered at 100$0^{\circ}C$ showed poor elongation and low fracture strength, while the Wi rods sintered above 100$0^{\circ}C$ revealed good mechanical properties. The higher elongation and fracture strength of the Ni rods sintered at higher temperatures than 100$0^{\circ}C$ are attributed to the full densification of the sintered rods. The sintered Ni rods were cold-rolled with 5% reduction to the final thickness of 100 $\mu$m and then annealed for development of rube texture in rolled Ni tapes. The annealed Ni tapes depicted strong cube texture with FWHM(full-width at half-maximum) of in-plane and out-of-plane in the range of 8$^{\circ}$ to 10$^{\circ}$. The NiO deposited on the Ni tapes by MOCVD process showed good epitaxy with FWHM=10$^{\circ}$, which indicates that the Ni tapes can be used as a substrate for YBCO coated conductors.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.323-324
• /
• 2006

저온동시 소결용 세라믹스, LTCC를 사용한 RF/MW용 고유전율 세라믹을 개발하기 위하여 300이상의 고유전율과 낮은 손실 계수를 가지는 것으로 알려진 $Ag(Nb_{1/4}Ta_{3/4})O_3$ 고용체와 $CaTiO_3$, $TiO_2$를 각각 혼합하여 공진주파수의 온도 계수가 0에 가까운 안정된 유전체 특성을 얻고자 하였다. 유전율의 온도 안정성을 도모하기 위해 음의 온도 계수를 갖는 $CaTiO_3$, $TiO_2$와 양의 온도계수를 갖는 $CaTiO_3$ 및 $TiO_2$를 일정 분율로 혼합한 복합체 구조의 시편을 제작하였다. LTCC 소자로의 적용을 위해 3wt.%의 CuO를 첨가하여 소결 온도를 낮추었으며, 소결 시편의 상 분석, 미세구조 및 전기적 특성을 조사하였다.

• 한국전기전자재료학회논문지
• /
• 제23권7호
• /
• pp.521-524
• /
• 2010

Low loss perovskite niobates and tantalates have been placed on a short list of functional materials for future technologies. In this study, we fabricated Ag(Ta,Nb)$O_3$ thick films on the $Al_2O_3$ substrates by the screen printing method. The Ag(Ta,Nb)$O_3$ powders were fabricated by the mixed oxide method. The sintering temperature and time were $1150^{\circ}C$ and 2 hrs, respectively. The results of XRD analysis showed that the specimens employed in this study had the pesudo cubic structure. The dielectric permittivity and loss tangent of the films have been characterized from 1 kHz to 1 MHz. Also the dielectric permittivity and loss tangent were measured from 303 K to 393 K. The electrical properties of the film are also discussed.

• 한국분말재료학회지
• /
• 제26권5호
• /
• pp.369-374
• /
• 2019

The properties of powder metallurgy products are related to their densities. In the present work, we demonstrate a method to apply artificial neural networks (ANNs) trained on experimental data to predict the bulk density of barium titanates. The density is modeled as a function of pressure, press rate, heating rate, sintering temperature, and soaking time using the ANN method. The model predictions with the training and testing data result in a high coefficient of correlation (R2 = 0.95 and Pearson's r = 0.97) and low average error. Moreover, a graphical user interface for the model is developed on the basis of the transformed weights of the optimally trained model. It facilitates the prediction of an infinite combination of process parameters with reasonable accuracy. Sensitivity analysis performed on the ANN model aids the identification of the impact of process parameters on the density of barium titanates.