• Transactions of the Korean Society of Automotive Engineers
• /
• v.7 no.6
• /
• pp.214-221
• /
• 1999

Spot welding is very important and useful technology in fabriaction of the thin sheet structure such as the automobile, train and air craft, Because fatigue strength of the spot welding point is however considerably lower than base metal due to stress concentration at the nugget edge, reasonable fatigue strength evaluation of spot welded lap joint is very important to estimate the reliability and durability of th spot welded structure and to establish a criterion of ling life fatigue design. For reasonalbe fatigue strength evaluation, it is necessary to estimate the fatigue strength of spot welded lap joints, systematically. So far, many investigators have numerically and experimentally studied on the systematic fatigue strength estimation for various spot welded lap joints, and the methods suggested has been considerably accumulated. By the way, for applying them in practical fatigue design of the thin sheet structure fabricated by spot welding ,it is also necessary to verify their efficiency and reliability on the predicted results, Therefore, in this study, a statistical fatigue strength estimation method for spot welded lap joints was developed by using the Weibull probability distribution function. From the result, it was found that fatigue strength and fatigue life of the spot welded lap joints having various dimension were able to be statically predicted . And also, a reliable criterion for long life fatigue design of the spot welded lap joint could be established.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.3
• /
• pp.315-321
• /
• 2010

Co-cured single lap joints under cyclic tensile loads fail initially at the tip of the interface corner between the two adherents. The failure mechanism is complex because it is related to corrosion fatigue. Corrosion behavior at the interface affects the failure of the joints because corrosion deteriorates fatigue resistance. In this study, we clarified the cause of interfacial corrosion in co-cured single lap joints under cyclic tensile loads. The failure mechanism was also analyzed by observing the failed surfaces of specimens and the stress distribution along the interface. The surface roughness at the interface and the stacking sequence of the composite adherent were examined to investigate their effects on failure of the joint.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.05a
• /
• pp.5-8
• /
• 2002

The use of the co-cured joining method for composite structures is attractive due to several benefits. However, since the design stress level in cyclic loads is often smaller than the joint strength obtained from the static tensile load test, it is important to establish proper fatigue design criteria. Although some researchers have reported on co-cured joints, there are only a few papers published on the fatigue characteristics of co-cured joints. In this paper, the effect of bond parameters on the fatigue characteristics of a steel-composite co-cured double lap joint under cyclic tensile loads was experimentally investigated. We considered the surface roughness of the steel adherend and the stacking sequence of the composite adherend as bond parameters. A fatigue failure mechanism of the co-cured double lap joint was explained systematically by investigating the surfaces of failed specimens.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1997.10a
• /
• pp.127-131
• /
• 1997

In systematic and orderly estimation of fatigue strength of the spot welded lap joints, because the influence of residual stress of fatigue crach initiation and growth is not negligible, there need to estimate fatigue strength considered residual stress at near spot weld part of the lap joints. Therefore, in this thesis, peformed stress distribution and residual stress analysis at near the spot weld part by F.E.M and X-ray diffraction method, and obtained the maximum principal stress considered residual stress at nugget edge by superposing residual stress at nugget edge by superposing their results. From the results obtained above, we could find that fatigue strength of the IB-type spot welded lap joints was rearranged by the maximum principal stress considered residual stress at nugget edge and was entirely low about 13 percents compare with that neglected residual stress.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.04a
• /
• pp.232-236
• /
• 2004

The fracture characteristics of unidirectional composite single-lap bonded joints were investigated experimentally and numerically. The effects of bonding method, surface roughness, bondline thickness and the existence of fillet on the failure characteristics and strength of bonded single-lap joints were evaluated experimentally. The failure process, failure mode and the behavior of load-displacement curve was apparently different according to bonding method. The failure load of the specimen co-cured without adhesive was definitely superior to other types of specimens but the specimens co-cured with adhesive film had a less strength than secondary bonded specimens. In the secondary bonded specimens, the lower value of surface roughness and existence of fillet improved the strength of specimens. The strain energy release rates calculated by geometric nonlinear finite element analyses and Virtual Crack Closure Technique for the secondary bonded specimens considering the three types of initial cracks - comer crack, edge crack and delamination crack - were consistent with the test results.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.10
• /
• pp.983-989
• /
• 2017

This paper presents the bearing strength for laminates in advanced composite materials in bolted joints. Bolted single lap joint tests were experimentally investigated with respect to stabilized and unstabilized lap joints. Stabilized bolted single lap joints refer to joints with out-of-plane rotational constraints. Unstabilized bolted single lap joints refer to joints with absence of out-of-plane deflection constraints. The bearing strength values of laminates in the bolted joint showed that the percentages of ply angle for 0, 45, -45, and 90 degrees were not affected. The bearing strength value in the unstabilized bolted joint was smaller than the bearing strength value in the stabilized bolted joint because of the influence of the out-of-plane behavior. The composite material studied in this paper is a carbon/epoxy unidirectional (UD) tape prepreg cured at $177^{\circ}C(350^{\circ}F)$. In the laminate reference system, the standard angles of 0, 45, -45, and 90 degrees were used for ply orientation within the laminate. A total of 112 bolted single lap joint tests were conducted on specimens from eight distinct laminates. The ASTM-D-5961M standards were adhered to for the stabilized and unstabilized bolted single lap joint tests.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.250-255
• /
• 2008

This study utilized a high speed lap-shear test to evaluate the mechanical behavior of Sn-37Pb/Cu and Sn-37Pb/Electroless Nickel immersion Gold under bump metallization solder joints under high speed loading and hence the drop reliability. The samples were aged for 120 h at different temperatures ($120^{\circ}C,\;150^{\circ}C,\;170^{\circ}C$) and afterward tested at different displacement rates (0.01 mm/s to 500 mm/s) to examine the effects of aging on the drop life reliability. The combination of the stress-strain graphs captured from the shear tests and identifying a fracture mode dominant in the samples for different strain rates leads us to conclude that the drop reliability of solder joints degrades as the aging temperature increases, possibly due to the role of the IMC layer. This study successfully demonstrates that the analysis based on a high speed lap-shear test could be critically used to evaluate the drop reliability of solder joints.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1039-1044
• /
• 2003

Adhesive-bonded joints are widely used in the industry. Recently aircraft applications of adhesive bonding joints have been increased extensively in automobile and air industry. Because adhesives which are available for structural applications have been developed a lot and understanding of adhesive bonding has been improved so much. In this study, as the fundamental research of design of adhesive bonding joints, this study considers specimen shape are affect strength and durability of Al/Polymer lap joints. In this research, cross head speed difference were concerned to evaluate their effects on the adhesive strength. Cross head speed makes a change 0.05mm/min, 0.5mm/min, 5mm/min. The result is load-displacement diagram showed brittleness fracture tendency. Fracture tendency that is shown enough on stress distribution of trigonal single lap joint and trigonal edged single lap joint occur the inside of adhesive.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.10
• /
• pp.1841-1852
• /
• 1992

With the wide application of fiber-reinforced composite material in aircraft, space structures and robot arms, the design and manufacture of composite joints have become a very important research area because they are often the weakest areas in composite structures. In this study, the effects of the adhesive thickness, residual thermal stress on the torque capacity of the tubular single lap joints were studied. The torque capacity of the adhesive joints were experimentally determined and found to be inversely proprotional to the adhesive thickness. In order to match the experimental results to the theoretical analyses, the elastic-perfectly plastic material properties of the adhesive were used in the closed form solution. Also, the residual thermal stress of the joints were calculated by the finite element method and it was proved that the residual thermal stress could play an important role in the thick adhesive joints.

• Structural Engineering and Mechanics
• /
• v.44 no.1
• /
• pp.35-49
• /
• 2012

A series of fatigue test were carried out on scarfed lap joints (SLJ) using in airfoil siding to explore the effect of structural details, such as rows of rivets, lap angles, on its fatigue performance. Finite element (FE) analysis was employed to explore the effect of lap angle on load transfer and the stress evolution around the rivet hole. At last, the fatigue lives were predicted by nominal stress approach and critical plane approach. Both of the test results and predicted results showed that fatigue life of SLJ was remarkably increased after introducing lap angle into the faying surface. Specimen with the lap angle of $1.68^{\circ}$ exhibits the best fatigue performance in the present study.