• Journal of the Korean Wood Science and Technology
• /
• v.44 no.5
• /
• pp.677-684
• /
• 2016

This study was carried out to confirm the effects of the knife-incising and longitudinal kerfing treatment on high-temperature drying characteristics of red pine square timber with dimensions of thickness 15 cm. The range of final moisture content was investigated 5.6% to 7.5% after drying. The differences did not exist in the moisture content and distribution according to the pretreatment condition. In the case of longitudinal kerfing treatment, the surface check occurrence was reduced than the control. In addition, the twist had a tendency to decrease due to the longitudinal kerfing treatment. The knife-incising and longitudinal kerfing treatment were investigated to be ineffective on internal checks and drying shrinkage.

• Journal of the Korean Wood Science and Technology
• /
• v.40 no.5
• /
• pp.343-351
• /
• 2012

A large diameter roundwood is an important element of Korean traditional buildings, Hanok, and is hard to be dried without surface cracks. Four different pretreatments, such as pre-cracking, oil heating, kerfing-oil heating and PEG impregnation, were investigated for reducing the surface cracks of large-diameter roundwood specimens during heat treatment. The roundwood specimens of pre-cracking, oil heating and kerfing-oil heating showed surface cracks during pretreatment, but that of PEG impregnation did not. It was confirmed that kerfing reduced the total crack width. Among the four pretreatments and control only the PEG impregnation roundwood specimen had no crack on both outer and inner surfaces after heat treatment. The PEG impregnation specimen shrank only 1.6% in the tangential direction while the pre-cracking did 8.0%.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.3
• /
• pp.345-363
• /
• 2020

This study was conducted to identify the effect of kerfing and incising pretreatments on high-temperature drying characteristics of cedar and larch boxed-heart timbers with a cross section of less than 150 mm. The result showed that the pretreatments have made a significant difference regarding surface check and shrinkage. Although the kerfing was suitable as a pretreatment to reduce the occurrence of surface check, the incising was not suitable as a pretreatment since the knives of timber joined together, causing the conversion to the surface checks. The shrinkage showed a significant result that the final moisture content was reduced in the order of incising, kerfing, and kerfing-incising after the drying process based on the pretreatment condition. Twist was more affected by the grain angle than the anisotropy of the juvenile wood, and there was no effect of pretreatments.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.3
• /
• pp.302-314
• /
• 2016

This study was carried out to confirm the effects of the knife-incising and kerfing pretreatment on the moisture content and surface check occurrence of Douglas-fir heavy timber. In the case of moisture content, the moisture gradient that formed in the inner part of the specimen was observed in all specimens. In addition, the moisture gradient was formed differently from the surface layer to 72 mm depending on the pretreatment conditions, and it was formed gradually in the kerfing than the knife-incising. In addition, it was found that the solid volume should be considered when measuring the average moisture content. In the case of surface check, the surface check occurrence was reduced in the knife-incising, kerfing, and the combination of knife-incising and kerfing than the control. In particular, the kerfing treatment was shown that the expansion of surface check width was effectively suppressed. In the case of knife-incising treatment, although the surface check was less than the control, the preventive effect on the surface check occurrence did not reach the level of the kerfing treatment.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.5
• /
• pp.726-735
• /
• 2016

This study was carried out to evaluate the high-temperature drying characteristics of douglas-fir, hemlock, and radiata pine square timber with dimensions of thickness 15 cm and 18 cm. As a result, radiata pine showed the lowest final moisture content followed by douglas-fir and hemlock without reference to the timber size. Moreover, when the longitudinal kerfing is processed, the final moisture content was lower than control. The kerfing treatment was effective to decreasing the twist of radiata pine and hemlock. When douglas-fir is processed to the shape like the edge-grained timber that does not include the pith, the decrease of drying defect was possible.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.4
• /
• pp.51-60
• /
• 1997

We investigated the characteristics of air-and vacuum-drying heated by hot plates for 8~14cm-diameter logs or 6~12cm-thick pillars of Pinus koraiensis. And we evaluated the effects of longitudinal kerf and vacuum drying heated by hot plates. The vacuum drying times from green to 10.9~18.6% MC were 15 days, and these times were one-fifth compared to the air-drying times. The longitudinal kerfing had no significant, effect on drying rates during both air-drying and vacuum drying. But drying defects such as surface checks and V-shaped cracks were effectively prevented during air-drying and vacuum drying by longitudinal kerfing. The vacuum drying was more advantageous than air-drying for preventing of surface checks, end checks and V-shaped cracks, and especially, the vacuum dried pillars with longitudinal kerf were almost free from drying defects. In accelerated weathering conditions the resin did not exude for all specimens.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.1
• /
• pp.107-115
• /
• 2017

In this study, the surface check reduction effect of preservative-treated Korean larch round-wood was investigated by applying three physical treatments, such as incising, kerfing, and kiln-drying. Moreover, the possibility of long-term service life was also checked by comparing the depth of surface check and the penetration depth of preservative. A rapid gradient of wood moisture content between surface and center causes a surface check. Thus, the effect of reducing surface check was carried out at the lowest equilibrium moisture content (EMC) condition, temperature ($2^{\circ}C$), humidity (44.6%), in outdoor locations in Korea until the test specimens reach to the 8.6% EMC. As a result, the preservative-treated specimens without incising, kerfing, kiln-drying (Type C) could not ensure the long-term service life due to a large surface check. Because the surface check depth of all specimens was deeper than the penetration depth of preservative. In case of the incising treated specimens (Type I), 80% of them, the depth of surface check was not deeper than the penetration depth of preservative. However, when a kerfing was additionally treated (Type B), a possibility of happening deeper surface check than penetration depth of preservative was increased rather than Type I.

• Explosives and Blasting
• /
• v.19 no.3
• /
• pp.105-113
• /
• 2001

채석, 굴착, 가공과 같은 워터젯 응용분야에서 대상재료에 깊은 홈(kerf)을 절단할 수 있는 실험실용 회전식 슬로터(slotter)를 제작하여 암석을 대상으로 워터젯 시스템의 절단효율을 시험하였다. 고압펌프는 유율 7.5 l/min, 압력 379 MPa, 용량 75 kW급의 JETPAC을 주로 사용하였고, 암석시료는 화강석인 제천석, 거창석을 사용하였다. 시험과정에서는 물과 연마재 투입에 의한 절단 및 진동식 슬로터에 의한 슬롯절단 기초시험을 먼저 수행하고, 그 결과를 토대로 회전식 슬로터에 의한 절단시험을 실시하였다. 순수한 물에 의한 시험의 결과 고압수류의 토출압력은 절단심도에 정비례하였고, 노즐의 이송속도는 이차함수 형태의 반비례 관계를 보였다. 연마재 투입시험에서는 순수한 물에 의한 경우에 비해 연마재로 인한 충격력의 증가로 절단심도가 크게 증가하였는데, 유사한 조건하에서 3~5배 이상의 절단심도의 증가를 보였다. 진동식 슬로터에 의한 슬롯절삭에서는 생성된 슬롯의 내벽면이 바닥으로 갈수록 좁아짐으로써 넓은 폭의 슬롯형성은 가능하나 절삭심도가 제한되었다. 회전식 슬로터에 의한 시험에서 생성된 슬롯들은 평균 22 mm의 폭으로 내벽면이 바닥까지 서로 평행하여 깊은 심도까지 비트진입이 가능하였다. 절단율은 16~32 mm/sec의 속도범위에서 $40~160{\;}\textrm{mm}^2/sec$로 나타났다. 한편, 최대유율 24 l/min의 HUSKY S-200 펌프에 의한 시험결과 JETPAC 펌프에 비해 1.13~3.47 배의 절단심도를 보였다

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.2
• /
• pp.132-139
• /
• 2011

This study examined the characteristics of radio-frequency/vacuum dried Korean red pine ($Pinus$ $densoflora$) heavy timbers with 250 ${\times}$ 250 mm (S), 300 ${\times}$ 300 mm (L) in cross section and 300 mm in diameter, and 3,600 mm in length, which were subjected to compressive loading after a kerf pretreatment. The following results were obtained : The drying time was short and the drying rate was high in spite of the large cross section of specimens. The moisture gradient inall specimens was gentle in both longitudinal and transverse directions owing to dielectric heating. The shrinkage of the width in the direction perpendicular to was 21 percent ~ 76 percent of that of the thickness of square timbers in the direction parallel to the mechanical pressure. The casehardening for all specimens was very slight because of significantly reduced ratio of the tangential to radial shrinkage of specimens and kerfing. The surface checks somewhat severely occurred although the occurrence extent of the surface checks on the kerfed specimens was slight compared withthat on the control specimen.

• Journal of the Korean Wood Science and Technology
• /
• v.51 no.6
• /
• pp.493-508
• /
• 2023

Round timber materials of 600 mm length, cut from large-cross-section round timber of red pine (Pinus densiflora S. et Z.) of 450 mm width and 4.2 m length, were prepared as the target of kiln drying in this study. After treating the target materials through end sealing (ES), end sealing - kerfing (ES-K), lateral sealing - end sealing - boring (LS-ES-B), or lateral sealing - partial end sealing (LS-PES), the effects of the treatment on the incidence of drying defects were determined. The target materials with exposed lateral surface and sealed cross surface were steamed at the initial temperature of 65℃ above the official pest control temperature of 56℃, followed by kiln drying toward the final temperature of 75℃. The target materials with sealed lateral surfaces, on the other hand, were dried at the initial temperature of 90℃ at almost the maximum temperature of conventional kiln drying, as there is no risk of early check formation caused by surface moisture evaporation. The final temperature was set at approximately 100℃. The drying time, taken for the target materials with initial moisture content of 70%-80% to reach the target moisture content of 19%, varied across treatment conditions. The measured drying time was 1,146 hours (approximately 48 days) for the timber with sealed cross surface and 745 hours (approximately 31 days) for the timber with sealed lateral surface, until the moisture content reached the target level. The formation of surface checks could not be prevented in the control and ES groups, but a definite preventive effect was obtained for the LS-ES-B and LS-PES groups.