• Journal of the Korea institute for structural maintenance and inspection
• /
• v.10 no.6
• /
• pp.175-182
• /
• 2006

In the design of composite structures, shear connectors such as headed stud, channel, perforated plate, etc, are commonly used to transfer longitudinal shear forces across the steel-concrete interface. Many researches have been conducted to improve the characteristics of different types of shear connector. This paper presents the results of 11 push-out tests performed on the new perforated rib connectors with shearing bars embedded in concrete slab under static loads. The results obtained from these tests are as following : 1) The bearing plate welded on both sides of perforated rib plate improves the stiffness and strength. 2) The capacity of perforated connectors is influenced primarily by the transverse reinforcements and shearing bars.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.2
• /
• pp.131-138
• /
• 2008

Fiber-reinforced polymer (FRP) sheets have been successfully used to retrofit a number of existing concrete buildings and structures because of their excellent properties (high strength, light weight and high durability). Bond characteristics between FRP sheets and concrete should be investigated to ensure an effective retrofitting system. RC structures strengthened with FRP sheets are often subjected to cyclic load (traffic, seismic, temperature, etc.). This research addresses a local bond stress-slip relationship under cyclic loading conditions for the FRP-concrete interface. 18 specimens were prepared with three types of FRP sheets (aramid, carbon, and polyacetal) and two types of sheet layer(one or two). The characteristics of bond stress-slip were verified through experimental results on load-displacement relationship.

• Steel and Composite Structures
• /
• v.52 no.4
• /
• pp.419-434
• /
• 2024

A flat slab is a structural system where columns directly support it without the presence of beam elements. However, despite its wide advantages, this structural system undergoes a major deficiency where stresses are concentrated around the column perimeter, resulting in the progressive collapse of the entire structure as a result of losing the shear transfer mechanisms at the cracked interface. Predicting the punching shear capacity of RC flat slabs is a challenging problem where the factors contributing to the overall slab strength vary broadly in their significance and effect extent. This study proposed a new expression for predicting the slab's capacity in punching shear using a nonuniform concrete tensile stress distribution assumption to capture, as well as possible, the induced strain effect within a thick RC flat slab. Therefore, the overall punching shear capacity is composed of three parts: concrete, aggregate interlock, and dowel action contributions. The factor of the shear span-to-depth ratio (a_v/d) was introduced in the concrete contribution in addition to the aggregate interlock part using the maximum aggregate size. Other significant factors were considered, including the concrete type, concrete grade, size factor, and the flexural reinforcement dowel action. The efficiency of the proposed model was examined using 86 points of published experimental data from 19 studies and compared with five code standards (ACI318, EC2, MC2010, CSA A23.3, and JSCE). The obtained results revealed the efficiency and accuracy of the model prediction, where a covariance value of 4.95% was found, compared to (13.67, 14.05, 15.83, 19.67, and 20.45) % for the (ACI318, CSA A23.3, MC2010, EC2, and JSCE), respectively.

• The korean journal of orthodontics
• /
• v.25 no.1 s.48
• /
• pp.55-72
• /
• 1995

The purpose of this study is to evaluate the effects of mechanical and thermal fatigue on the shear bond strength(SBS) in orthodontic brackets bonded to human premolars with chemically cured adhesive(Mono-$Lok^2$, Rocky Mountain Orthodontics). Two types of metal brackets (Ormesh, Microloc) and three types of ceramic brackets (Fascination, Starfire, Transcend 2000) were used in this study. The $10^6$ loadcycles of $|7.4{\times}10{^2}sin2{\pi}ft|g{\cdot}cm$ and the 1,000 thermocycles of 15 second dwell time each in $5^{\circ}C\;and\;55^{\circ}C$ baths were acturated as mechanical and thermal fatigue stress, and SBS were measured after each fatigue test. The fracture sites were examined by stereoscope and scanning electron microscope. The results obtained were summarized as follows, 1. In static shear bond test, Fascination brackets showed the maximum SBS($20.78\pm3.45$ MPa) and Microloc brackets showed the minimum SBS($14.88\pm3.10$ MPa). Fascination and Starfire brackets showed significantly greater SBS than Microloc brackets(P<0.05). 2. In mechanical fatigue test, Fascination brackets showed the maximum SBS ($20.19\pm3.45$ MPa) and Starfire brackets showed the minimum SBS($9.10\pm8.33$ MPa). The SBS or Transcend 2000 brackets(P<0.01) and Starfire brackets(P<0.05) significantly decreased after $10^6$ loadcycles. 3. In thermocycling test, Ormesh brackets showed the maximum SBS ($19.36\pm2.76$ MPa) and Starfire brackets showed the minimum SBS($11.94\pm6.86$ MPa). The SBS of Transcend 2000(P<0.01), Microloc and Starfire brackets(P<0.05) significantly decreased after $10^3$ thermocycles. 4. Failure sites of thermocycling groups were similar to those of static groups but after mechanical fatigue test, Ormesh and Transcend 2000 brackets failed at the bracket/resin interface and Microloc brackets failed within adhesive. Facination brackets failed at the enamel/resin interface irrespective of experimental condition.

• Restorative Dentistry and Endodontics
• /
• v.32 no.3
• /
• pp.169-179
• /
• 2007

This study was to compare the microshear bond strength $({\mu}SBS)$ of light- and chemically cured composites to enamel coupled with four 2-step self-etch adhesives and also to evaluate the incompatibility between 2-step self-etch adhesives and chemically cured composite resin. Crown segments of extracted human molars were cut mesiodistally, and a 1 mm thickness of specimen was made. They were assigned to four groups by adhesives used: SE group (Clearfil SE Bond) AdheSE group (AdheSE), Tyrian group (Tyrian SPE/One-Step Plus), and Contax group (Contax) Each adhesive was applied to a cut enamel surface as per the manufacturer's instruction. Light-cured (Filtek Z250) or chemically cured composite (Luxacore Smartmix Dual) was bonded to the enamel of each specimen using a Tygon tube. After storage in distilled water for 24 hours, the bonded specimens were subjected to ${\mu}SBS$ testing with a crosshead speed of 1 mm/minute. The mean ${\mu}SBS$ (n=20 for each group) was statistically compared using two-way ANOVA, Tukey HSD, and t test at 95% level. Also the interface of enamel and composite was evaluated under FE-SEM. The results of this study were as follows ; 1. The ${\mu}SBS$ of the SE Bond group to the enamel was significantly higher than that of the AdheSE group, the Tyrian group, and the Contax group in both the light-cured and the chemically cured composite resin (p < 0.05). 2. There was not a significant difference among the hdheSE group, the Tyrian group, and the Contax group in both the light-cured and the chemically cured composite resin. 3. The ${\mu}SBS$ of the light-cured composite resin was significantly higher than that of the chemically cured composite resin when same adhesive was applied to the enamel (p < 0.05). 4. The interface of enamel and all 2-step self-etch adhesives showed close adaptation, and so the incompatibility of the chemically cured composite resin did not show.

• Korean Chemical Engineering Research
• /
• v.45 no.5
• /
• pp.466-472
• /
• 2007

A technology platform for wafer-level three-dimensional integration circuits (3D-ICs) is presented, and that uses wafer bonding with low-k polymeric adhesives and Cu damascene inter-wafer interconnects. In this work, one of such technical platforms is explained and characterized using a test vehicle of inter-wafer 3D via-chain structures. Electrical and mechanical characterizations of the structure are performed using continuously connected 3D via-chains. Evaluation results of the wafer bonding, which is a necessary process for stacking the wafers and uses low-k dielectrics as polymeric adhesive, are also presented through the wafer bonding between a glass wafer and a silicon wafer. After wafer bonding, three evaluations are conducted; (1) the fraction of bonded area is measured through the optical inspection, (2) the qualitative bond strength test to inspect the separation of the bonded wafers is taken by a razor blade, and (3) the quantitative bond strength is measured by a four point bending. To date, benzocyclobutene (BCB), $Flare^{TM}$, methylsilsesquioxane (MSSQ) and parylene-N were considered as bonding adhesives. Of the candidates, BCB and $Flare^{TM}$ were determined as adhesives after screening tests. By comparing BCB and $Flare^{TM}$, it was deduced that BCB is better as a baseline adhesive. It was because although wafer pairs bonded using $Flare^{TM}$ has a higher bond strength than those using BCB, wafer pairs bonded using BCB is still higher than that at the interface between Cu and porous low-k interlevel dielectrics (ILD), indicating almost 100% of bonded area routinely.

• Restorative Dentistry and Endodontics
• /
• v.34 no.1
• /
• pp.42-50
• /
• 2009

Deterioration of long-term dentin adhesion durability is thought to occur by hydrolytic degradation within hydrophilic domains of the adhesive and hybrid layers. This study investigated the hypothesis that priming the collagen network with an organic solvent displace water without collapse and thereby obtain good bond strength with an adhesive made of hydrophobic monomers and organic solvents. Three experimental adhesives were prepared by dissolving two hydrophobic monomers, bisphenol-A-glycidylmethacrylate (Bis-GMA) and triethyleneglycol dimethacrylate (TEGDMA), into acetone, ethanol or methanol. After an etching and rinsing procedure, the adhesives were applied onto either wet dentin surfaces (wet bonding) or dentin surfaces primed with the same solvent (solvent-primed bonding). Microtensile bond strength (MTBS) was measured at 48 hrs, 1 month and after 10,000 times of thermocycles. The bonded interfaces were evaluated using a scanning electron microscope (SEM). Regardless of bonding protocols, well-developed hybrid layers were observed at the bonded interface in most specimens. The highest mean MTBS was observed in the adhesive containing ethanol at 48 hrs. With solvent-primed bonding, increased MTBS tendencies were seen with thermo cycling in the adhesives containing ethanol or methanol. However, in the case of wet bonding, no increase in MTBS was observed with aging.

• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.4
• /
• pp.235-242
• /
• 2012

Purpose: The purpose of this study was to compare the fracture behavior of Zironia, glass infiltrated Alumina and PFM full crown system. Materials and methods: Fifteen crowns for each of 3 experimental groups (Zironia, glass infiltrated Alumina and PFM full crown) were made by the conventional method. The crowns mounted on the testing jig were inclined in 30 degrees to the long axis of the tooth and the universal testing machine was used to measure the fracture strength. Results: 1. The mean fracture strengths were $588.3{\pm}49.6MPa$ for zirconia system, $569.1{\pm}61.8MPa$ for PFM system and $551.0{\pm}76.5MPa$ for glass-infiltrated alumina system (P>.05). 2. The mean shear bond strengths were $25.5{\pm}5.6MPa$ for zirconia system, $38.9{\pm}5.0MPa$ for Ni-Cr alloy system and $39.4{\pm}5.1MPa$ for glass-infiltrated alumina system. 3. The chemical bonding was observed at interfaces between PFM or glass-infiltrated alumina and veneering porcelain, however, no chemical bonding was observed at interface between zirconia and veneering porcelain. Conclusion: With the study, the fracture strengths of PFM crown system had a higher fracture strength than conventional zirconia system crown and glass-infiltrated alumina crowns. and than the shear bond strengths glass-infiltrated alumina system had a higher shear bond strength than conventional PFM system and zirconia system.

• Progress in Medical Physics
• /
• v.23 no.4
• /
• pp.269-278
• /
• 2012

Aquaplast Thermoplastic (AT) is a tissue-equivalent oral compensator that has been developed to improve dose uniformity at the common boundary and around the treated area during radiotherapy in patients with head and neck cancer. In order to assess the usefulness of AT, the degree of improvement in dose distribution and physical properties were compared to those of oral compensators made using paraffin, alginate, and putty, which are materials conventionally used in dental imprinting. To assess the physical properties, strength evaluations (compression and drop evaluations) and natural deformation evaluations (volume change over time) were performed; a Gafchromic EBT2 film and a glass dosimeter inserted into a developed phantom for dose verification were used to measure the common boundary dose and the beam profile to assess the dose delivery. When the natural deformation of the oral compensators was assessed over a two-month period, alginate exhibited a maximum of 80% change in volume from moisture evaporation, while the remaining tissue-equivalent properties, including those of AT, showed a change in volume that was less than 3%. In a free-fall test at a height of 1.5 m (repeated 5 times as a strength evaluation), paraffin was easily damaged by the impact, but AT exhibited no damage from the fall. In compressive strength testing, AT was not destroyed even at 8 times the force needed for paraffin. In dose verification using a glass dosimeter, the results showed that in a single test, the tissue-equivalent (about 80 Hounsfield Units [HU]) AT delivered about 4.9% lower surface dose in terms of delivery of an output coefficient (monitor unit), which was 4% lower than putty and exhibited a value of about 1,000 HU or higher during a dose delivery of the same formulation. In addition, when the incident direction of the beam was used as a reference, the uniformity of the dose, as assessed from the beam profile at the boundary after passing through the oral compensators, was 11.41, 3.98, and 4.30 for air, AT, and putty, respectively. The AT oral compensator had a higher strength and lower probability of material transformation than the oral compensators conventionally used as a tissue-equivalent material, and a uniform dose distribution was successfully formed at the boundary and surrounding area including the mouth. It was also possible to deliver a uniformly formulated dose and reduce the skin dose delivery.

• Restorative Dentistry and Endodontics
• /
• v.18 no.1
• /
• pp.73-83
• /
• 1993

The purpose of this study was to evaluate the effect of various acid treatments on dentin bonding. Freshly extracted human teeth were uprightly embedded in self curing acrylic resin, and their occlusal surfaces were grinded to expose flat dentin surfaces. The specimens were divided into 4 groups. Specimens of one group were not treated so as to be a control and those of the other three groups were threated with 10% polyacrylic acid, 10% phosphoric acid, and 10-3 solution(10% citric acid/3% ferric chloride) respectively. Primer, bonding resin and composite resin were applied over the treated dentin surfaces sequentially. All specimens were stored in $37^{\circ}C$ distilled water for 24 hours, then the tensile bond strength was measured and the treated dentin surfaces and fracured dentin surfaces were examined under a scanning electron microscope. The results were as follows: Bond strengths of acid-treated groups were higher than those of the untreated group. In the acid-treated groups, bond strength was found to be the highest in the 10-3 solution group followed by the 10% phosphoric acid group and the 10% polyacrylic acid group(P<0.01). On SEM examination of dentin surfaces, the untreated dentin surface showed a remaining smear layer and closed dentinal tubules. Dentin surfaces treated with 10 % polyacrylic acid showed a clean dentin surface without the smear layer, but showed remaining smear plugs in dentinal tubules. A dentin surface treated with 10% phosphoric acid or 10-3 solution showed open dentinal tubules without the smear layer or smear plugs. On SEM observation of the fractured dentin-resin interface, the untreated group showed that failure occurred in the smear layer. The group treated with 10% polyacrylic acid showed no resin tag remained in the dentinal tubules, but resin tags in the dentinal tubules were observed in the group treated with the 10% phosphoric acid or the 10-3 solution. On the failure mode examination, the higher the bond strength of the group, the higher the frequency of cohesive failure. The coefficient between bond strength and cohesive failure rate was 0.71.