• Corrosion Science and Technology
• /
• v.18 no.4
• /
• pp.121-128
• /
• 2019

Electrochemical Impedance Spectroscopy (EIS) was used to predict corrosion behaviour of metallic Cultural Heritage assets in two monitoring campaigns: 1) an iron bar chain exposed indoor from over 500 years in the Notre Dame Cathedral in Amiens (France); and 2) a large weathering steel sculpture exposed outdoor from tens of years in Ferrara (Italy). The EIS portable instrument employed was battery operated. In situ EIS measurements on the iron chain could be used to investigate the phenomena involved in the electrochemical interfaces among various corrosion products and assess and predict their corrosion behaviour in different areas of the Cathedral. Meanwhile, the sculpture of weathering steel, like most outdoor artefacts, showed rust layers of different chemical composition and colour depending on the orientation of metal plates. The EIS monitoring campaign was carried out on different areas of the artefact surface, allowing assessment of their protective effectiveness. Results of EIS measurements evidenced how employing a simple test that could be performed in situ without damaging the artefacts surface is possible to quickly gain knowledge of the conservation state of an artefact and highlight potential danger conditions.

• Corrosion Science and Technology
• /
• v.14 no.3
• /
• pp.113-119
• /
• 2015

Alloy 82/182 weld metals had been extensively used in joining the components of the PWR primary system. Unfortunately, there have been a number of incidents of cracking caused by PWSCC in Alloy 82/182 welds during the operation of PWR worldwide. To mitigate PWSCC, optimization of water-chemistry conditions, especially dissolved hydrogen (DH) and Zn contents, is considered as the most promising and effective remedial method. In this study, the PWSCC behaviours of Alloy 182 weld were investigated in simulated PWR environments with various DH content. Both in-situ and ex-situ oxide characterizations as well as PWSCC initiation tests were performed. The results showed that PWSCC crack initiation time was shortest in PWR water (DH: 30cc/kg). Also, high stress reduced crack initiation time. Oxide layer showed multi-layered structures consisted of the outer needle-like Ni-rich oxide layer, Fe-rich crystalline oxide, and inner Cr-rich inner oxide layers, which was not altered by the level of applied stress. To analyse the multi-layer structure of oxides, EIS measurement were fitted into an equivalent circuit model. Further analyses including TEM and EDS are underway to verify appropriateness of the equivalent circuit model.

• Journal of Power Electronics
• /
• v.16 no.2
• /
• pp.695-703
• /
• 2016

A fuel cell power conditioning system for online diagnosis and load leveling under the condition of varying load is developed in this study. The proposed system comprises a unidirectional boost converter and a bidirectional buck-boost converter with a battery. The system operates in two different modes. In normal mode, the bidirectional converter is utilized for load leveling; in diagnostic mode, it is utilized to control load voltage while the boost converter generates perturbation current to implement the online diagnosis function through in-situ electrochemical impedance spectroscopy (EIS). The proposed method can perform EIS for a fuel cell under varying-load conditions with no influence on the load. The validity and feasibility of the proposed system are verified by experiments, and the design procedure of the proposed system is detailed.

• Journal of Environmental Impact Assessment
• /
• v.6 no.2
• /
• pp.153-164
• /
• 1997

This study was conducted to develop the new Environmental Impact Assessment techniques for the grading of rareness in plant. 17 EISs which were submitted in 1996 were analyzed to know the problems in existent EIA techniques for the conservation of rare plants. Category of rare plant was reevaluated and evaluation technique for the grading of rareness in plant was developed. The results obtained from this study were as follows: 1. The evaluation technique of rareness in plant was not reflected in the current preparation provision for EIS. And t his fact also appeared in most of the EIS which were reexamined in this study. 2. The category of rare species which have been considered as the subject of protection in EIA have to be enlarged to more than legally protected species designated by MOE. 3. The taxonomic characteristics and status of species, characteristics of population, geographical characters, extent of threat and its possibility by man resulted from the habitat loss were investigated. Each item was endowed scores from 1 to 5 and all the scores were summed, and then this value was used to evaluate the order of conservation. 4. Conservation measures for the rare plants have to be applied according to the levels of rareness grade, and they are absolute conservation, in situ conservation, transplanting and ex situ conservation, post observation and none by the levels from A to E. 5. Considering the phenology of rare plants, investigation for the rare plants have to be made a1 least three times. 6. Size of the MVP(Minimum Viable Population), pollination ecology also have to be considered for the conservation of rare plants. And in the case of adopting ex situ conservation measure, the site and methods for the conservation of rare plants have to be proposed in detail.

• International Journal of Korean Welding Society
• /
• v.3 no.2
• /
• pp.29-39
• /
• 2003

The durability and reliability of thermal barrier coatings (TBCs) play an important role in the service reliability, availability and maintainability (RAM) of hot­section components in advanced turbine engines for aero and utility applications. Photostimulated luminescence spectroscopy (PSLS) and electrochemical impedance spectroscopy (EIS) are being concurrently developed as complimentary non­destructive evaluation (NDE) techniques for quality control and life­remain assessment of TBCs. This paper overviews the governing principles and applications of the luminescence and the impedance examined in the light of residual stress, phase constituents and resistance (or capacitance) in TBC constituents including the thermally grown oxide (TGO) scale. Results from NDE by PSLS and EIS are discussed and related to the microstructural development during high temperature thermal cycling, examined by using a variety of microscopic techniques including focused ion beam (FIB) in­situ lift­out (INLO), transmission and scanning transmission electron microscopy (TEM and STEM).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.402.1-402.1
• /
• 2016

The performance of solid oxide fuel cells (SOFCs) is directly related to the electrocatalytic activity of composite electrodes in which triple phase boundaries (TPBs) of metallic catalyst, oxygen ion conducting support, and gas should be three-dimensionally maximized. The distribution morphology of catalytic nanoparticle dispersed on external surfaces is of key importance for maximized TPBs. Herein in situ grown nickel nanoparticle onto the surface of fluorite oxide is demonstrated employing gadolium-nickel co-doped ceria ($Gd0.2-xNixCe0.8O2-{\delta}$, GNDC) by reductive annealing. GNDC powders were synthesized via a Pechini-type sol-gel process while maximum doping ratio of Ni into the cerium oxide was defined by X-ray diffraction. Subsequently, NiO-GNDC composite were screen printed on the both sides of yttrium-stabilized zirconia (YSZ) pellet to fabricate the symmetrical half cells. Electrochemical impedance spectroscopy (EIS) showed that the polarization resistance was decreased when it was compared to conventional Ni-GDC anode and this effect became greater at lower temperature. Ex situ microstructural analysis using scanning electron microscopy after the reductive annealing exhibited the exsolution of Ni nanoparticles on the fluorite phases. The influence of Ni contents in GNDC on polarization characteristics of anodes were examined by EIS under H2/H2O atmosphere. Finally, the addition of optimized GNDC into the anode functional layer (AFL) dramatically enhanced cell performance of anode-supported coin cells.

• Corrosion Science and Technology
• /
• v.4 no.6
• /
• pp.217-221
• /
• 2005

In the present investigation, holographic interferometry was utilized for the first time to monitor in situ the thickness of the oxide film of aluminium samples during anodization processes in boric acid solutions. The anodization process (oxidation) of the aluminium samples was carried out by the technique of the electrochemical impedance spectroscopy(EIS), in different concentrations of boric acid (0.5-5.0% $H_3BO_3$) at room temperature. In the mean time, the real-time holographic interferometry was used to measure the thickness of anodized (oxide) film of the aluminium samples in solutions. Consequently, holographic interferometry is found very useful for surface finish industries especially for monitoring the early stage of anodization processes of metals, in which the thickness of the anodized film of the aluminium samples can be determined without any physical contact. In addition, measurements of electrochemical values such as the alternating current (A.C) impedance(Z), the double layer capacitance($C_{dl}$), and the polarization resistance(Rp) of anodized films of aluminium samples in boric acid solutions were made by the electrochemical impedance spectroscopy(EIS). Attempts to measure electrochemical values of Z, Cdl, and Rp were not possible by holographic interferometry in boric acid especially in low concentrations of the acid. This is because of the high rate of evolutions of interferometric fringes during the anodization process of the aluminium samples in boric acid, which made measurements of Z, Cdl, and Rp are difficult.

• Corrosion Science and Technology
• /
• v.22 no.2
• /
• pp.99-107
• /
• 2023

Layered silicate clay montmorillonite (MMT) has been used in nanocomposite coating to improve corrosion protection by reinforcing the barrier property. The better dispersion of MMT in the coating produces a higher barrier effect. Pretreatment with MMT could favor the delamination of clay platelets, facilitating MMT dispersion in the coating. In the present work, a montmorillonite/silica (MMT/Si) composite was prepared by the in situ sol-gel method. x-ray diffraction measurements and field-emission scanning electron microscopy observations showed silica crystal formation and increased basal spacing between the MMT platelets. Composite MMT/Si particles were introduced in an epoxy resin to reinforce the corrosion protection of the coating applied on the AA2024 surface. Electrochemical impedance spectroscopy (EIS) was performed to characterize the protective property of the coating. The results demonstrated the high barrier effect of the coating containing 5 wt% of MMT/Si. Adhesion evaluation after a salt spray test exhibited a high adherence to the epoxy coating containing MMT/Si.

• Journal of Environmental Impact Assessment
• /
• v.22 no.3
• /
• pp.265-276
• /
• 2013

This study assessed documentation status of each environmental assessment items by analyzing the 243 case of marine EIS on the Consultation System of Sea Area Utilization. Observed rate of tidal elevation, current, temperature, salinity in maine environment were below 20%. The EFDC tool is applied substantially in hydrodynamic modeling. The verification process, however, is very insufficient using the recent observed data. Also, in-situ assessment rate of pelagic organism such as phytoplankton was below 50%, and assessment for Chlorophyll a was not accomplished. Ecological index evaluation for zooplankton and benthic ecosystem were not considered in statements. Especially, the rational assessment on the fisheries resources and protected species were very limited. It was necessary that the core assessment items (checklists) were established for environmental scoping. Furthermore, suggestion of information related to development, regional coastal management plan, aquaculture farms, and facilities were enhanced. The redundancy problem of proceedings between Environmental Impact Assessment and Sea Area Utilization Assessment System was improved.

• Nuclear Engineering and Technology
• /
• v.55 no.4
• /
• pp.1518-1527
• /
• 2023

A method was proposed for in-situ evaluating the thickness and resistivity of the oxide/hydroxide film formed on the surface of aluminum alloy exposed to sump water formed in the containment after a loss-of-coolant accident. The evaluation entailed fitting a model for the film impedance, which has film thickness and other variables describing the resistivity profile of the film along its thickness direction as fitting parameters, to the practically measured electrochemical impedance data. The obtained resistivity profiles implied that the films formed at pHs_25℃ 7, 8, 9, 10, and 11 all had a duplex structure; compared to the outer layer in contact with the solution, the inner layer of the film had a much higher resistivity and was inferred to be denser and provide most of the protectiveness of the film. Both the thickness and the total resistance of the film decreased with the increasing solution pH_25℃, suggesting that the films formed in more alkaline solutions had less protectiveness against corrosion, consistent with the increasing aluminum alloy corrosion rates previously identified.