• Journal of the Korean Magnetics Society
• /
• v.13 no.6
• /
• pp.231-236
• /
• 2003

The $Al_{0.2}$CoF $e_{1.8}$ $O_4$ferrite powders have been prepared by the sol-gel method. The crystallographic and magnetic properties of the sample depending on annealing temperature have been investigated by means of x-ray diffraction, FE SEM, Mossbauer spetroscopy and vibrating sample magnetometry. The x-ray diffractions of all samples annealing temperature above 873 K clearly indicate the presence of spinel structure, the lattice constant decrease from 8.425 $\AA$ at 873 K to 8.321 $\AA$ at 1073 K, whereas the particle size rapidly increase from about 39 nm at 673 K to about 108 nm at 1073 K. The Mossbauer spectra annealed above 873 K could be fitted as the superposition of two sextets due to F $e^{3+}$ at A-site and B-site. The isomer shift (IS) and quadruple splitting (QS) values nearly constant with annealing temperature, whereas magnetic hyperfine field ( $H_{hf}$) of A-site slowly in crease and that of B-site fastly increases with increasing annealing temperature. The magnetic behaviour of powders shows that the saturation magnetization increase from 0.7 emu/g at 473 K to 72.1 emu/g at 1073 K while the coercivity decrease from 0.951 kOe at 673 K to 0.374 kOe at 1073 K with increasing annealing temperature.

• Journal of the Korean Magnetics Society
• /
• v.16 no.6
• /
• pp.287-292
• /
• 2006

Al substituted $CoAl_{0.5}Fe_{1.5}O_{4}$ has been studied with x-ray and neutron diffraction, $M\"{o}ssbauer$ spectroscopy and magnetization measurements. $CoAl_{0.5}Fe_{1.5}O_{4}$ revealed a cubic spinel structure of ferrinmagnetic long range ordering at room temperature, with magnetic moments of $Fe^{3+}(A)(-2.29{\mu}_{B}),\;Fe^{3+}(B)(3.81\;{\mu}_{B}),\;Co^{2+}(B)(2.66{\mu}_{B})$, respectively. The temperature dependence of the magnetic hyperfine field in $^{57}Fe$ nuclei at the tetrahedral (A) and octahedral (B) sites was analyzed based on the $N\'{e}el$ theory of magnetism. In the sample of $CoAl_{0.5}Fe_{1.5}O_{4}$, the interaction A-B interaction and intrasublattice A-A superexchange interaction were antiferromagnetic with strengths of $J_{A-B}=-19.3{\pm}0.2k_{B}\;and\;J_{A-A}=-21.6{\pm}0.2k_{B}$, respectively, while the intrasublattice B-B superexchange interaction was found to be ferromagnetic with a strength of $J_{B-B}=3.8{\pm}0.2k_{B}$.

• Journal of the Korean Magnetics Society
• /
• v.18 no.1
• /
• pp.24-27
• /
• 2008

We have prepared $MnFe_2O_4$ nanoparticles with polyol method. The crystallographic and magnetic properties were measured by using X-ray diffraction(XRD), vibrating sample magnetometer(VSM) and $M\"{o}ssbauer$ spectroscopy. The high resolution transmission electron microscope(HRTEM) shows uniform nanoparticle-sizes with $6{\sim}8$ nm. The crystal structure is found to be single-phase cubic spinel with space group of Fd3m. The lattice constant of $MnFe_2O_4$ nanparticles is determined to be $8.418{\pm}0.001{\AA}$. $M\"{o}ssbauer$ spectrum of $MnFe_2O_4$ nanparticles at room temperature(RT) shows a superparamagnetic behavior. In VSM analysis, the diagnosis of the superparamagnetic behavior is also shown in hysteresis loop at RT. $M\"{o}ssbauer$ spectrum at 4.2K shows that the well developed two sextets are with different hyperfine field $H_{hfA}=498$(A-site) and $H_{hfB}=521$(B-site) kOe.

• Journal of the Korean Magnetics Society
• /
• v.16 no.2
• /
• pp.144-148
• /
• 2006

$CoGa_{0.1}Fe_{1.9}O_4$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by XRD, SEM, VSM and $M\ddot{o}ssbauer$ spectroscopy. $CoGa_{0.1}Fe_{1.9}O_4$ powder that was annealed at $250^{\circ}C$ has spinel structure and behaved superparamagnetically. The estimated size of superparammagnetic $CoGa_{0.1}Fe_{1.9}O_4$ nanoparticle is around 10 nm. The hyperfine fields at 4.2 K f3r the A and B patterns were found to be 518 and 486 kOe, respectively. The blocking temperature $(T_B)$ of superparammagnetic $CoGa_{0.1}Fe_{1.9}O_4$ nanoparticle is about 250 K. The magnetic anisotropy constant of $CoGa_{0.1}Fe_{1.9}O_4$ nanoparticle was calculated to be $3.0X10^5\;ergs/cm^3$. $CoGa_{0.1}Fe_{1.9}O_4$ nanoparticle was annealed at $250^{\circ}C$ will be used to candidate for biomedicine applications as magnetic carriers.

• Journal of the Korean Magnetics Society
• /
• v.8 no.6
• /
• pp.335-340
• /
• 1998

Colossal magnetoresistance $La_{0.67}Ca_{0.33}Mn_{0.99}^{57}Fe_{0.01}O_3$ material has been produced by a metal-salt routed sol-gel process method. Magnetic properties of $La_{0.67}Ca_{0.33}Mn_{0.99}^{57}Fe_{0.01}O_3$ have been studied with x-ray diffraction, Rutherford back-scattering spectroscopy(RBS), vibrating sample magnetometer, and Mossbauer spectroscopy. Crystalline $La_{0.67}Ca_{0.33}Mn_{0.99}^{57}Fe_{0.01}O_3$ was perovskite cubic structure with a lattice parameter $a_0=3.868$\AA$$. And there was no appreciable change in the value of the lattice parameter when a small amount (x=0.01) of iron was added. However, Mossbauer and VSM data indicate the Curie temperature of the $La_{0.67}Ca_{0.33}Mn_{0.99}^{57}Fe_{0.01}O_3$ decreased from 282 to 270 k and also the saturation magnetization from 84 to 81 emu/g at 77 K. Mossbauer spectra of $La_{0.67}Ca_{0.33}Mn_{0.99}^{57}Fe_{0.01}O_3$ have been taken at various temperatures ranging form 4.2 K to room temperature. Analysis of $^{57}Fe$ Mossbauer data in terms of the local configurations of Mn atoms has permitted the influence of the magnetic hyperfine interactions to be monitored. The isomer shifts show that the charge state of all Fe ions are ferric. The magnetoresistance of $La_{0.67}Ca_{0.33}Mn_{0.99}^{57}Fe_{0.01}O_3$ was about 33 % at semiconductor-metal transition temperature $T_{SC-M}=250K$.

• Journal of the Korean Magnetics Society
• /
• v.14 no.1
• /
• pp.46-50
• /
• 2004

Compounds of $Y_{3-x}Ce_{x}Fe{5}O_{12}$(x=0.0, 0.1, 0.2, and 0.3) were prepared using the sol-gel method. The XRD measurements show that these samples have only a single phase of the garnet structure regardless of the amount of Ce substitution. The lattice constants of x = 0.0 and x = 0.3 were found to be a$_0$ = 12.3758 ${\pm}$0.0005 ${\AA}$ and 12.4062 ${\pm}$0.0005 ${\AA}$, respectively. The lattice constant increases linearly with increasing Ce concentration. The saturation magnetization was not changed flirty, with increasing Ce concentration, but coercivity decreased form 18.3 Oe to 5.8 Oe as x increased form x = 0.0 to x = 0.1. Mossbauer spectra of $Y_{3-x}Ce_{x}Fe{5}O_{12}$ were measured at various absorber temperatures from 13 K to Neel temperature. The Mossbauer spectra were fitted by least-squares technique with two subpatterns of Fe sites in the structure and corresponding to the 16a and 24d site. The temperature dependence of the magnetic hyperfine field in $^{57}$/Fe nuclei at the tetrahedral 240 and octahedral 16a sites were analyzed based on the Neel theory of ferrirnagnetism. The result of the Debye temperatures indicated that the inter-atomic binding force for the 24d site was larger than that for the 16a site.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.100-105
• /
• 2005

$Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by DTA/TGA, XRD, SEM, and $M\ddot{o}ssbauer$ spectroscopy, VSM. $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ has spinel structure and behaved superparamagnetically. The estimated size of superparammagnetic Ni-Zn ferrite nanoparticle is around 10 nm. The hyperfine fields at 13 K for the A and B patterns were found to be 533 and 507 kOe, respectively. The blocking temperature ($T_B$) of superparammagnetic $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle is about 250 K. The magnetic anisotropy constant and relaxation time constant of $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle were calculated to be $1.6\times10^6\;ergs/cm^3$ and ${\tau}_0=5.0{\times}10^{-13}$ s, respectively. Also, Temperature increased up to $43^{\circ}C$ within 10 minutes under AC magnetic field of 7 MHz. It is considered that $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ is available for biomedicine application such as hyperthermia, drug delivery system and contrast agents in MRI.