• Membrane Journal
• /
• v.22 no.1
• /
• pp.16-22
• /
• 2012

The influence of co-existing gases on the hydrogen permeation without sweep gas was studied through a Pd-coated $V_{99.8}B_{0.2}$ alloy membrane. Membranes have been investigated in the pressure range 1.5-8.0 bar under pure hydrogen, hydrogen-carbon dioxide and hydrogen-carbon monoxide gas mixture without sweep gas at $400^{\circ}C$. Preliminary hydrogen permeation experiments without sweep gas have been confirmed that hydrogen flux was $40.7mL/min/cm^2$ for a Pd-coated $V_{99.8}B_{0.2}$ alloy membrane (thick : 0.5 mm) using pure hydrogen as the feed gas. In addition, hydrogen flux was $21.4mL/min/cm^2$ for $V_{99.8}B_{0.2}$ alloy membrane using $H_2/CO_2$ as the feed gas. The hydrogen permeation flux decreased with decrease of hydrogen partial pressure irrespective of pressure when $H_2/CO_2$and $H_2/CO$mixture applied as feed gas respectively and permeation fluxes were satisfied with Sievert's law in different feed conditions. It was found from XRD, SEM/EDX results after permeation test that the Pd-coated $V_{99.8}B_{0.2}$ alloy membrane had good stability and durability for various mixtures feeding condition.

• Korean Membrane Journal
• /
• v.2 no.1
• /
• pp.36-47
• /
• 2000

This paper deals with the separation of MTBE-methanol mixtures using crosslinked Poly(vinyl alcohol)(PVA) membranes with sulfur-succinic acid(SSA) as a crosslinking agent by pervaporation and vapor permeation technique. The operating temperatures, methanol concentration in feed mixtures, and SSA concentrations in PVA membranes were varied to investigate the separation performance of PVA/SSA membranes and the optimum separation characteristics by pervaporation and vapor permeation. And also, for PVA/SSA membranes, the swelling measurements were carried out to study the transport phenomena. The swelling measurements were carried out for pure MTBE and methanol, and MTBE/methanol=90/10, 80/20 mixtures using PVA/SSA membranes with varying SSA compositions. There are two factors of the membrane network and the hydrogen bonding. In pervaporation separation was also carried out for MTBE/methanol=90/10, 80/20 mixtures at various temperatures. The sulfuric acid group in SSA took an important role in the membrane performance. The crosslinking effect might be over the hydrogen bonding effect due to the sulfuric acid group at 3 and 5% SSA membranes, and this two factors act vice versa on 7% SSA membrane. In this case, the 5% SSA membrane shows the highest separation factor of 2,095 with the flux of 12.79g/㎡$.$hr for MTBE/methanol=80/20 mixtures at 30$^{\circ}C$ which this mixtures show near the azeotopic composition. Compared to pervaporation, vapor permeation showed less flux and similar separation factor. In this case, the flux decreased significantly because of compact structure and the effect of hydrogen bonding. In vapor permeation, density or concentration of methanol in vaporous feed is lower than that of methanol in liquid feed, as a result, the hydrogen bonding portion between the solvent and the hydroxyl group in PVA is reduced in vapor permeation. In this case, the 7% SSA membranes shows the highest separation factor of 2,187 with the flux of 4.84g/㎡$.$hr for MTBE/methanol=80/20 mixtures at 30$^{\circ}C$.

• Membrane Journal
• /
• v.2 no.1
• /
• pp.36-36
• /
• 1992

This paper deals with the separation of MTBE-methanol mixtures using crosslinked Poly(vinyl alcohol)(PVA) membranes with sulfur-succinic acid(SSA) as a crosslinking agent by pervaporation and vapor permeation technique. The operating temperatures, methanol concentration in feed mixtures, and SSA concentrations in PVA membranes were varied to investigate the separation performance of PVA/SSA membranes and the optimum separation characteristics by pervaporation and vapor permeation. And also, for PVA/SSA membranes, the swelling measurements were carried out to study the transport phenomena. The swelling measurements were carried out for pure MTBE and methanol, and MTBE/methanol=90/10, 80/20 mixtures using PVA/SSA membranes with varying SSA compositions. There are two factors of the membrane network and the hydrogen bonding. In pervaporation separation was also carried out for MTBE/methanol=90/10, 80/20 mixtures at various temperatures. The sulfuric acid group in SSA took an important role in the membrane performance. The crosslinking effect might be over the hydrogen bonding effect due to the sulfuric acid group at 3 and 5% SSA membranes, and this two factors act vice versa on 7% SSA membrane. In this case, the 5% SSA membrane shows the highest separation factor of 2,095 with the flux of 12.79g/㎡·hr for MTBE/methanol=80/20 mixtures at 30℃ which this mixtures show near the azeotopic composition. Compared to pervaporation, vapor permeation showed less flux and similar separation factor. In this case, the flux decreased significantly because of compact structure and the effect of hydrogen bonding. In vapor permeation, density or concentration of methanol in vaporous feed is lower than that of methanol in liquid feed, as a result, the hydrogen bonding portion between the solvent and the hydroxyl group in PVA is reduced in vapor permeation. In this case, the 7% SSA membranes shows the highest separation factor of 2,187 with the flux of 4.84g/㎡·hr for MTBE/methanol=80/20 mixtures at 30℃.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.06a
• /
• pp.9-12
• /
• 2007

The transport mechanisms of the MTES (methyltriethoxysilane) templating silica/a-alumina composite membrane were evaluated by using four binary and one quaternary hydrogen mixtures through permeation experiments at unsteady- and steady-states. Since the permeation flux in the MTES membrane, through the experimental and theoretical studies, was affected by molecular sieving effects as well as surface diffusion properties, the kinetic and equilibrium separation should be considered simultaneously according to molecular properties. In order to depict the transient multi-component permeation on the templating silica membrane, the GMS (generalized Maxwell-Stefan) and DGM (dust gas model) were adapted to unsteady-state material balance.

• Journal of the Korean Ceramic Society
• /
• v.51 no.6
• /
• pp.566-569
• /
• 2014

ZnO and SiC powders were fabricated to make crack-free composite membranes. Parts of some membranes were re-treated with an encapsulation process. These membranes were characterized by XRD, BET, and FE-SEM analyzes. The hydrogen permeation fluxes of the encapsulated and heat-treated membranes after encapsulation were observed using Sievert's type equipment. Values were measured at 1 bar with increasing temperatures. The obtained values of encapsulated and further heat-treated membrane at 298 K were $4.20{\times}10^{-6}$ and $8.64{\times}10^{-5}mol/m^2sPa$, respectively.

• Membrane Journal
• /
• v.34 no.2
• /
• pp.140-145
• /
• 2024

In modern times, when a change in the energy paradigm is required, hydrogen is an attractive energy source. Among these hydrogen purification technologies, technology using a membrane is attracted attention as a technology that can purify high purity hydrogen at low cost. However, palladium(Pd), which is mostly used because of its excellent hydrogen separation performance, is very expensive, so a replacement material is needed. In this study, a alloy membrane was manufactured from an alloy of niobium (Nb), which has high hydrogen permeability but is weak to hydrogen embrittlement, and nickel (Ni) and zirconium (Zr), which have low hydrogen permeability but are highly durable. Hydrogen permeation characteristics were confirmed under conditions of 350~450 ℃ at 1 to 4 bar. The maximum hydrogen permeation flux was 0.69 ml/cm²/min for the Ni₄₈Nb₃₂Zr₂₀ alloy membrane without Pd coating, and 13.05 ml/cm²/min for the Pd coated alloy membrane.

• Membrane Journal
• /
• v.10 no.3
• /
• pp.148-154
• /
• 2000

Poly(vinyl alcohol)(PVA)/sulfur-siccinic acid(SSA) membrane performances have been studied for the vapor permeation separation of methyl tort-butyl ether(MTBE)/methanol mixtures with varying operation temperatures, amount of cross-linking agents, and feed compositions. 1'here are two factors, the membrane network and the hydrogen bonding, in the swelling measurements of PVA/SSA membranes. These two factors act interdependently on the membrane swelling. The sulfuric acid group in SSA took an important role in the membrane performance. The cross-linking effect might be more dominant than the hydrogen bonding effect due to the sulfuric acid group at 7% SSA membrane. Hydrogen bonding effect was more important for 5% SSA membrane. In vapor permeation, density or concentration of methanol in vapor feed is lower than that of methanol in liquid feed, as a result, the hydrogen bonding portion between the solvent and the hydroxyl group in PVA is reduced in vapor permeation. In this case, the 7% SSA membrane shows the highest separation factor of 2187 with the flux of 4.84g/$m^2$hr for MTBE/methanol=80/20 mixtures at 3$0^{\circ}C$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.18 no.2
• /
• pp.182-188
• /
• 2007

[ $Zr_{50}-Ni_{27}-Nb_{18}-Co_5$ ] amorphous alloys ribbon was prepared by a single-roller melt-spinning technique. In order to improve the hydrogen kinetics Pd-coating were carried out on each side of the amorphous ribbon. Pd prevents oxidation of Zr and catalyses the dissociation of molecular hydrogen to atomic hydrogen. In this work, the hydrogen embrittlement and surface properties on Zr-based amorphous alloys were investigated. The Zr-based amorphous alloys were characterized by X-ray diffractometry(XRD) and differential scanning calorimetry(DSC). The morphology of surface and roughness was observed by using scanning electron microscopy(SEM) and atomic force microscopy (AFM). A lattice parameter of both Pd and Zr-based amorphous alloy was increased after hydrogen permeation at 473 K. After hydrogen permeation at 473 K, some cracks were observed on the surface of Pd, which was the cause for the hydrogen embrittlement. The crystallization temperature of Zr-based amorphous alloy was decreased due to the permeated hydrogen.

• Corrosion Science and Technology
• /
• v.2 no.3
• /
• pp.109-116
• /
• 2003

It is well known that SSCC (sulfide stress corrosion cracking) is caused by drastic ingression of hydrogen during the service and accumulation of hydrogen near the potential crack initiation site in the material. It is important to characterize the hydrogen trapping behavior to evaluate the service performance of the high strength pipeline steels. In this study. the relationship between the hydrogen trapping behavior and SSCC susceptibility is evaluated in terms of alloy composition, microstructure and carbide behavior. The hydrogen trapping behavior was measured by electrochemical hydrogen permeation test cell (Devanathan cell). The SSCC susceptibility is evaluated by constant extension rate test and constant strain lest method. The hydrogen trapping behavior is affected greatly by microstructure and nature of carbide particles. The fine TiC, and NbC in the matrix of ferritic structure acts as strong irreversible trap sites whereas the bainitic structure acts as reversible trap site. The SSCC susceptibility is closely related to not only the hydrogen trapping behavior but also the loading condition. As the activity of reversible trap site increases, SSCC susceptibility decreases under static loading condition below yield strength, whereas SSCC susceptibility increases under dynamic loading condition or above yield strength. As the activity of irreversible trap site increases. SSCC susceptibility increases regardless of loading condition. It is cased by the mixed effect of dislocation on hydrogen diffusion and trapping behavior.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.477-480
• /
• 2014

An $Al_2O_3$-CuO-ZnO (ACZ) precursor powder was synthesized by a facial sol-gel process using a nonionic surfactant span 80 as the chelating agent to improve the surface area and morphology. When creating a hydrogen membrane, several kinds of properties are required, such as easy dissociation of hydrogen molecules, fast hydrogen diffusion, high hydrogen solubility, and resistance to hydrogen embrittlement. ACZ-Ni composite membranes (cermet) were prepared with this precursor and pure Ni powder via the hot press sintering (HPS) method. The ACZ powder was characterized by XRD, BET, and FE-SEM. Hydrogen permeation experiments were performed by Sievert's type of hydrogen permeation membrane equipment. The hydrogen permeability of ACZ/Ni 10 wt% and ACZ/Ni 20 wt% was obtained as 7.2 and $10molm^{-2}s^{-1}$ at RT, respectively. These values of the corresponding membranes were slightly increased with increasing pressures.