• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2008년도 추계 학술논문 발표대회
• /
• pp.57-60
• /
• 2008

According to the recent tendency that the buildings in the downtown concerning rising land prices and efficient use of building are gradually Manhattanized mainly the grand scaled residential buildings, structure of the buildings relates to safety and so the very thick mat concrete is selected as the foundation of architectures. Because mat concretes can not be simultaneously pour in a great quantity due to the circumstance at the field, not only the questions on the unification between the concretes pour on the upper layer and the lower layer are presented but also the cracks by the internal force from the difference of hydration exothermic period are occurred because of the time lag. Thus, this study checked the efficiency to apply "The hydration heat controlling method of mass concrete for horizontal partition pouring construction" to the skyscraper sites under construction at Haiundai in Busan. After applying this method, the result of observation that the cracks by hydration heat in all over the placement surface did never be founded. Also, in case of the economic analysis that the hydration heat reduction method using super retarding agent by difference of setting time is approximately 80% cheaper than the hydration heat reduction method by pipe cooling in the construction expenses.

• 콘크리트학회논문집
• /
• 제14권1호
• /
• pp.118-125
• /
• 2002

콘크리트는 수화과정을 통하여 재료가 성숙되고, 경화된다. 수화의 진행은 엄밀한 의미에서 재령에 의하지 않고 수화도에 의해 제어되므로, 경화가 진행되는 콘크리트의 모든 재료특성과 미세구조 형성과정은 수화도에 의해 정식화되는 것이 바람직하다. 기존 연구는 주로 양생온도가 수화발열속도에 미치는 영향을 고려한 반응함수 개념을 주로 사용하였고, 또한 내부 수분상태의 영향을 습도함수의 형태로 고려한 연구결과는 실제 수화기구를 반영하지 못하고 단지 각 연구자의 실험조건과 배합조건에만 부합하는 결과를 보인다. 따라서 본 연구는 기존 제안식의 단점을 보완하기 위하여 수화기구와 미세구조 형성 과정에 기초하여 반응속도함수를 모델링하였다. 수화반응속도는 온도 및 수분상태에 따라 변화하므로, 본 연구에서는 수화발열 속도에 영향을 미치는 인자로, 시멘트 종류, 물-시멘트비 등의 배합특성과 양생온도 빛 세공조직의 내부수분상태를 고려하였다. 똔 연구에서 제시한 콘크리트의 수화도 예측모델은 기존의 온도영향만을 주로 고려하는 반응속도함수를 콘크리트내부의 수분분포 상태를 고려하여 모델을 개선하였으며, 이는 실제 측정한 수화도에 매우 근접하여 그 유용성을 검증하였다. 또한 수화도의 정의와 제시한 모델을 이용하여 콘크리트 요소내의 온도, 습도 덴 수화도를 수치적으로 결정하여 단열온도상승곡선을 정확히 모사 할 수 있었다. 제안된 모델은 수화가 진행되는 콘크리트의 여러 역학적 특성 및 미세구조 형성과정을 적절히 표현하고, 수화과정이 온도 및 습도상태를 결정하는 초기재령 콘크리트의 단면 내 온 습도상태를 추정하여 궁극적으로 초기재령 콘크리트의 균열 위험성을 평가하는데 유용하게 이용될 수 있을 것으로 사료된다.

• 콘크리트학회논문집
• /
• 제21권4호
• /
• pp.481-488
• /
• 2009

시멘트페이스트, 모르타르 및 콘크리트의 자기수축의 크기 및 발현율은 초기재령 내부온도의 이력과 크기에 의해 영향을 받는다고 보고된 바 있으나, 초기재령 수화열과 자기수축에 대한 구체적인 관계분석은 아직 미흡한 실정 이다. 이 연구에서는 초기재령 수화온도 및 자기수축의 이력특성에 대한 분석방법을 제시한 선행연구를 기초로, 시험체 크기 및 수화지연 효과에 따른 고강도콘크리트의 초기재령 수화열과 자기수축의 거동특성 및 상관관계를 분석하였다. 또한 자기수축에 의한 균열평가시 유효자기수축의 기준이 되는 응결시간과 수화온도 및 자기수축의 이력과의 관계도 검토하였다. 그 결과, 시험체가 매스화될수록 초기재령 수화발열 상승구간의 수화온도 상승량 및 수화발열 상승속도, 자 기수축 증가구간의 자기수축 증가량 및 자기수축 속도는 증가하는 것으로 나타났으며, 지연제를 사용할 경우 그 값은 감소하는 것으로 나타났다. 초기재령 콘크리트의 수화발열 상승속도가 증가하면 자기수축 속도는 증가하며, 이와 더불 어 재령 91일 자기수축도 증가하는 것으로 나타나, 종국 자기수축은 초기재령 수화발열상승 속도에 의해 영향을 받을 수 있을 것으로 사료된다. 한편, 콘크리트 균열평가시 유효자기수축의 기준이 되는 응결시간과 변곡점 및 수화온도 상 승시점은 시멘트의 수화반응 과정에 있어 서로 밀접한 관계가 있음을 확인할 수 있었다.

• 자원리싸이클링
• /
• 제24권1호
• /
• pp.12-20
• /
• 2015

본 연구에서는 고로 수쇄 슬래그 및 석고를 혼합한 3성분계 천연 수경성 석회 페이스트에서 석고종류 및 혼합량에 따른 수화특성 변화를 확인하고자 하였다. 고로 수쇄 슬래그 20 %를 혼합한 천연 수경성 석회에 무수석고, 반수석고, 이수석고를 각각 3 %, 10%를 혼합하여 석고의 용해도 및 반응성에 따라 수화초기 생성되는 수화물의 종류와 생성량을 분석하였으며, 이에 따른 물리적 특성 변화거동에 대하여 조사하였다. 페이스트를 활용한 수화특성 결과 모든 샘플에서 수화초기 ettringite, C-S-H와 같은 수화물이 생성되었으며, 재령이 길어짐에 따라 수화물의 생성량이 증가하였다. 압축강도 측정결과, 석고 혼합량이 3 %일 때 더 높은 강도를 보였으며 재령 28일에서 무수석고 및 반수석고가 이수석고를 혼입할 경우 보다 높은 특성을 나타내었다.

• 한국건축시공학회지
• /
• 제20권4호
• /
• pp.321-330
• /
• 2020

지오폴리머의 반응성은 원재료의 구성성분 및 Si/Al비, Na/Al비, 물-결합재비, 비정질 요소 등을 고려하여 명확한 메커니즘을 규명하는 것은 매우 중요하다. 따라서 원재료 및 알칼리 활성화제의 구성성분을 고려한 %Na₂O, M_s는 반응성을 결정하는 중요한 요소가 된다. 하지만 다수의 연구에서는 알칼리 활성화제의 농도와 양생 조건 등의 기본적인 요소만을 고려하는 한계점을 나타내고 있다. 따라서 본 연구에서는 %Na₂O, Ms 및 고로슬래그 미분말의 혼입량에 따른 지오폴리머 페이스트의 강도특성, 반응열, 길이변화, 미세구조 분석을 실시하였다.

• Computers and Concrete
• /
• 제20권5호
• /
• pp.529-537
• /
• 2017

Excessively elevated temperature can lead to cracks in prestressed concrete (PC) continuous bridge with box girder on the pier top at cement hydration age. This paper presents a case study for evaluating the behavior of PC box girder during the early hydration age using a two-stage computational model, in the form of computer program ANSYS, namely, 3-D temperature evaluation and determination of mechanical response in PC box girders. A numerical model considering time-dependent wind speed and ambient temperature in ANSYS for tracing the thermal and mechanical response of box girder is developed. The predicted results were compared to show good agreement with the measured data from the PC box girder of the Zhaoshi Bridge in China. Then, based on the validated numerical model three parameters were incorporated to analyze the evolution of the temperature and stress within box girder caused by cement hydration heat. The results of case study indicate that the wind speed can change the degradation history of temperature and stress and reduce peak value of them. The initial casting temperature of concrete is the most significant parameter which controls cracking of PC box girder on pier top at cement hydration age. Increasing the curing temperature is detrimental to prevent cracking.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.501-504
• /
• 2004

This paper proposes degree of hydration based shrinkage prediction model of 40MPa HPC. This model shows degree of hydration which is defined as the ratio between the hydrated cement mass and the initial mass of cement is very closely related to shrinkage deformation. In this study, degree of hydration was determined by CEMHYD-3D program of NIST. Verification of the predicted degree of hydration is performed by comparison between test results of compressive strength and estimated one by CEMHYD-3D. Proposed model is determined by statistical nonlinear analysis using the program Origin of Origin Lab. Co. To get coefficients of the model, drying shrinkage tests of four specimen series were followed with basic material tests. Testes were performed in constant temperature /humidity chamber, with difference moisture curing ages to know initial curing time effect. Verification with another specimen, collected construction field of FCM bridge, was given in the same condition as pre-tested specimens. Finally, all test results were compared to propose degree of hydration based model and other code models; AASHTO, ACI, CEB-FIP, JSCE, etc.

• 한국세라믹학회지
• /
• 제47권5호
• /
• pp.394-400
• /
• 2010

This study examined the effects of particle size on characteristics of cement by controlling the particle size of commercial cement. Through a size adjustment, the cement has increasing more of particles that are less than $10{\mu}m$ in size so the initial reaction time has been shortened as a result of improvement in the early hydration reaction. Additionally, it showed a great characteristics of strength from the early age and the initial hydration heat has been increased as well. In the upper and middle parts cements, the initial hydration reaction rate contribution is high with the $10{\mu}m$ compared to original cement. So the initial hydration reaction rate is improved and as a result, it also showed relatively high hydration heat as well. Additionally, adiabatic temperature also showed an increase rate in the results.

• 한국세라믹학회지
• /
• 제24권3호
• /
• pp.289-295
• /
• 1987

The changes of physical properties of portland cement pastes and mortars were investigated by addition of sodium gluconate. Flow table experiment and viscosity measurement were took in order to find dispersing effect, and time-dependent changesof viscosity and rates of hydration heat evolution were carried out for the sake of finding retardation effect of hydration. And changes of physical properties of cement pastes and mortars were discussed by setting time, compressive strength and porosity.

• 한국세라믹학회지
• /
• 제39권10호
• /
• pp.943-947
• /
• 2002

Chlorine을 다량으로 함유하고 있는 산업 폐부산물의 시멘트 키른을 이용한 소각 가능성을 검토하고자 OPC에 KCl을 함량별로 첨가하여 수화발열, 응결시간, 유동성, 길이변화 및 몰탈 압축강도를 측정하였다. 실험결과 KCl를 첨가함에 따라 수화가 촉진되어 유도기가 짧아짐으로써 응결시간이 짧아지고 유동성이 하락하며 초기수축이 커지고 3일 이전의 초기 압축강도는 상승하나 7일 이후의 후기 압축강도는 크게 하락하였다.