• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.118-119
• /
• 2016

γ-C₂S is known as a kind of substance that it does not react with water at room temperature. However it could react with the CO₂ producing CaCO₃ and silica gel as the carbonation products. Thus γ-C₂S can be used as a mineral addition to improve the compressive strength and durability of concrete. On the other hand, the manufacture of γ-C₂S can give an effective utilization of industrial by-product with low energy consumption and low CO₂ emission. This paper aims to summarize the development situation on this field.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.177-184
• /
• 2015

In order to use the high-volume slag cement as a construction materials, a proper activator which can improve the latent hydraulic reactivity is required. The dissolved aluminum silicon ions from ground granulated blast furnace slag (GGBFS) react with sulfate ions to form ettringite. The proper formation of ettringite can increase the early-age strength of high-volume GGBFS (80%) cement. The aim of this study is to investigate the hydration properties with sulfate activators (sodium sulfate, anhydrite). In this paper, the effects of $Na_2SO_4$ and $CaSO_4$ on setting, compressive strength, hydration, micro-structure were investigated in high-volume GGBFS cement and compared with those of without activator. Test results indicate that equivalent $SO_3$ content of 3~5% improve the early-age hydration properties such as compressive strength, heat evolution rate, micro-pore structure in high-volume GGBFS cement.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.115-125
• /
• 2015

This study investigated the fluidity, heat of hydration, setting time, strength development, and characteristics of hydration and pozzolanic reactions of high-strength high-volume ground granulated blast-furnace slag(GGBFS) blended cement pasts with the water-to-binder ratio of 20% by experiments, and analyzed the effects of the replacement ratio and fineness of GGBFS on the hydration and pozzolanic reaction. The results show that, in the high-strength mixtures with low water-to-binder ratio, the initial hydration is accelerated due to the "dilution effect" which means that the free water to react with cement increases by the replacement of cement by GGBFS, and thus, strengths at from 3 to 28 days were higher than those of plain mixtures with ordinary Portland cement only. Whereas it was found that the long term strength development is limited because the hydration reaction rates rapidly decreases with ages and the degree of pozzolanic reaction is lowered due to insufficient supply of calcium hydroxide according to large replacement of cement by GGBFS. Also, the GGBFS with higher fineness absorbs more free water, and thus it decreases the fluidity, the degree of hydration, and strength. These results are different with those of normal strength concrete, and therefore, should be verified for concrete mixtures. Also, to develop the high-strength concrete with high-volume of GGBFS, the future research to enhance the long-term strength development is needed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.64-69
• /
• 1999

Slags are by-products of the metallurgical industry. The most important slag from the standpoint of the quantity used as building material is iron blastfurnace slag. Slags are either crystalline stable solid used as aggregates or glassy material used as hydraulic binder. Slag cements are low heat of hydration cements. Slags react more slowly with than portland cement but they can be activated chemically. Activatiors can be either alkaline activators such as soda, lime, sodium carbonate, sodium silicate or sulphate activators such as calcium sulphate or phosphogypsum. So, in this study slaked lime was used as an activator that the compressive strength of this modified cement(M1 type) is high range in early age. And initial setting time of M1 type cement was shorter than conventional cements.

• Bulletin of the Korean Chemical Society
• /
• v.5 no.3
• /
• pp.126-129
• /
• 1984

The reaction of aryl halides with phenoxides and alkoxides were investigated under phase transfer catalytic conditions. 2,4-Dinitro- and 4-nitrohalobenzenes reacted readily with phenoxides in NaOH(aq)-benzene in the presence of Bu4N+Br, affording the products quantitatively. Although the aryl halides did not react with alkoxides under the same condition, the reactions were completed within 2 hours at room temperature when conducted under solid-liquid phase transfenr catalytic condition. The reactivity of aryl halides was in the order, Ar = 2,4-dinitrophenyl > 4-nitrophenyl, and X = F > Cl, consistent with the SNAr mechanism. The reactivity of oxyanions increased with the change of reaction condition from liquid-liquid to solid-liquid phase transfer catalysis. The results were explained with the concentration and the degree of hydration of the anion in benzene.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.11a
• /
• pp.207-208
• /
• 2023

Concrete bricks and hollow concrete block products manufactured using ordinary portland cement react with salt and carbon dioxide absorbed from the soil and atmosphere in the use environment, causing contamination such as efflorescence. This is due to the reaction between calcium hydroxide, a cement hydration product, and carbon dioxide, producing and eluting calcium carbonate. This study was a preliminary study to compare and evaluate the reduction of efflorescence in concrete bricks and hollow concrete block products manufactured using carbon dioxide reaction hardening cement. The purpose was to evaluate the efflorescence occurrence in products using ordinary Portland cement.

• Proceedings of the Korean Geotechical Society Conference
• /
• 2005.10a
• /
• pp.453-460
• /
• 2005

Sodium silicate - the usual portland cement which accomplishes a cement pouring reconsideration main stream and sodium silicate(No.3) after reacting sodium silicate(No.3) with the reaction sodium silicate where oxidation natrium which is included does not react with the cement receiving stiffening water it will burn together on underwater and to become the durability lacks pouring it is recognized. From the hazard which improves an advantage it used the additive which relates in congealing and stiffening of the portland cement and sodium tripolyphosphate(STPP) addition hour initial material age(72 hours at once) which does to be revealed the at high-in-tensity is discovered while accomplishing. The effect of additives on the reactions of sodium silicate solution and cement suspesion was investigated by various physical and chemical tests, such as Si-NMR, XRD, SEM uniaxial compression test. The additives were STPP(sodium tripolyphosphate), EDTA, SUGAR. The compressive strength of sodium silicate(No.3) - cement grout with additives was about $1.5{\sim}10$ times higher than that without additive in early age(72 hours).

• Journal of the Korea Concrete Institute
• /
• v.18 no.2 s.92
• /
• pp.267-274
• /
• 2006

Greenhouse gas reduction will be highlighted as the most pending question in the cement industry in future because the production of Portland cement not only consumes limestone, clay, coal, and electricity, but also release waste gases such as $CO_2,\;SO_3$, and NOX, which can contribute to the greenhouse effect and acid rain. To meet the increase of cement demand and simultaneously comply with the Kyoto Protocol, cement that gives less $CO_2$ discharge should be urgently developed. This study aims to manufacture non-sintering cement(NSC) by adding phosphogypsum(PG) and waste lime(WL) to granulated blast furnace slag(GBFS) as sulfate and alkali activators. This study also Investigates the hydration reaction of NSC through analysis of scanning electron microscopy(SEM), X-ray diffraction(XRD), differential thermal analysis(DTA), and pH. Results obtained from analysis of the hydrate have shown that the glassy films of GBFS are destroyed by the activation of alkali and sulfate, ions eluted from the inside of GBFS react with PG and produce ettringite, and consequently the remaining component in GBFS slowly produced C-5-H(I) gel. Here, PG is considered not only to play the role of simple activator, but also to work as a binder reacting with GBFS.

• Journal of the Korean Geosynthetics Society
• /
• v.20 no.4
• /
• pp.1-7
• /
• 2021

In response to the carbon emission reduction trends and the depletion of natural sand caused by the use of cement in construction works, graphene oxide and porous feldspar were applied as countermeasures in this study. By using (3-aminopropyl)trimethoxysilane-functionalized graphene oxide with enhanced bond characteristics, a concrete specimen was prepared with 5% less cement content than that in a standard mortar mix, and the compressive strengths of the specimens were examined. The compressive strengths of the specimen with (3-aminopropyl)trimethoxysilane-functionalized graphene oxide and porous feldspar and the specimen with standard mixing were 26MPa and 28MPa, respectively, showing only a small difference. In addition, both specimens met the compressive strength of cement mortar required for geotechnical structures. It is believed that a reasonable level of compressive strength was maintained in spite of the lower cement content because the high content of pozzolans, namely SiO₂ and Al₂O₃, in the porous feldspar enhanced the reactions with Ca(OH)₂ during hydration, the nano-sized graphene surface acted as a reactive surface for the hydration products to react actively, and the strong covalent bonding of the carboxyl functional group increased the bonding strength of the hydration products.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.3
• /
• pp.204-210
• /
• 2022

Cement is pointed out as the main cause of carbon dioxide emission in the construction industry. Many researchs are underway to use blast furnace slag, an industrial by-product, as a substitute for cement to reduce carbon dioxide emitted during the manufacturing the cement. When blast furnace slag is used as a substitute for cement, it has advantages such as long-term strength and chemical resistance improvement. However, blast furnace slag has a problem that makes initial strength low. This is due to the impermeable film on the surface created during the production of blast furnace slag. The created film is known to be destroyed in an alkaline environment, and based on this, previous studies have suggested a solution using various alkali activators. But, alkali activator is dangerous product since it is a strong alkaline material. And it has the disadvantage in price competitiveness. In this study, an experiment was conducted to improve the initial hydration reactivity of the blast furnace slag to secure the initial strength of the mortar substituted with the blast furnace slag and to check whether the carbonation resistance was increased. As a result of the experiment, it was confirmed that the mortar using alkaline water showed higher strength than the mortar using tap water, and there were more hydration products generated inside. In addition, it was confirmed that the mortar using alkaline water as a compounding water had high carbonation resistance.