• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.203-204
• /
• 2016

In this research, it used cement power and reduction slag, which generates high hydration heat in hydration reation without heat cure below -5℃ degree. Purpose of final research is preventing freezing and thawing by making the compressive strength 5MPa in 3days below zero temperature due to own heat of concrete. and it is the result of physical characteristic and thermal property evaluation of reduction slag. Because reduction sag generates high hydration heat, compressive strength development is excellent. By generating highly Hydration heat by C₁₂A₇ and C₃A in reduction slag, compressive strength is developed in low temperature. In case of displacing only reduction slag without SO₃, it is indicated that quick-setting occurs by shortage of SO₃. For preventing quick-setting, gypsum is used essentially. According to this research result, in case of using reduction slag and gypsum as a ternary system, Compressive strength developed 5MPa in 3days below zero temperature. It is identified to prevent early frost damage of concrete below zero temperature.

• Journal of the Korean Ceramic Society
• /
• v.36 no.1
• /
• pp.77-81
• /
• 1999

In order to investigate the effect of fineness on the properties of Portland cement, we prepared five kinds of portland cements with different Blaine values(2300, 2500, 3000, 3500, 45oo $\textrm{cm}^2$/g) and measured Ca(OH)2 analysis, hydration heat, the fluidity and the physical properties of them. According to the results, as the Blain value of cement is lower, the rate of hydration is delayed, and the hydration heat and the compressive strength are decreased. But the fluidity of cement paste is improved. Especially, the hydration heat of the cement with 2500$\textrm{cm}^2$/g of Blaine value is decreased about 15% compared with 3500 $\textrm{cm}^2$/g cement.

• International Journal of Concrete Structures and Materials
• /
• v.5 no.1
• /
• pp.3-10
• /
• 2011

Theoretical models for prediction of the mechanical properties of cement mortar are developed based on the morphology and interactions of cement hydration products, capillary pores and microcracks. The models account for intermolecular interactions involving the nano-scale calcium silicate hydrate (C-S-H) constituents of hydration products, and consider the effects of capillary pores as well as the microcracks within the hydrated cement paste and at the interfacial transition zone (ITZ). Cement mortar was modeled as a three-phase material composed of hydrated cement paste, fine aggregates and ITZ. The Hashin's bound model was used to predict the elastic modulus of mortar as a three-phase composite. Theoretical evaluation of fracture toughness indicated that the frictional pullout of fine aggregates makes major contribution to the fracture energy of cement mortar. Linear fracture mechanics principles were used to model the tensile strength of mortar. The predictions of theoretical models compared reasonably with empirical values.

• Archives of Pharmacal Research
• /
• v.27 no.11
• /
• pp.1177-1182
• /
• 2004

The effect of poly[2-methacryloyloxyethyl phosphorylcholine] (pMPC) on the skin permeation property was investigated by performing in vitro skin permeation study of a model drug, nicotinic acid (NA). Effect of pMPC polymer in donor solution on skin permeation rates was evaluated using side-by-side diffusion cells. Also, the structural alterations in the stratum corneum (SC), inter-lamellar bilayer (ILB) and dermis layers in pMPC-treated and -untreated skin sections were investigated with transmission electron microscopy (TEM). The permeation profile of NA without pMPC in donor solution showed biphasic mode: initial $1^{st} phase and 2^{nd}$ hydration phase. The sudden, more than 10-fold increase in flux from the initial steady state (43.5 $\mu g/cm^2$/hr) to the $2^{nd}$ hydration phase (457.3 $\mu g/cm^2$/hr) suggests the disruption of skin barrier function due to extensive hydration. The permeation profile of NA with 3% pMPC in the donor solution showed monophasic pattern: the steady state flux (10.9 $\mu g/cm^2$/hr) without abrupt increase of the flux. The degree of NA permeation rate decreased in a concentration-dependent manner of pMPC. TEM of skin equilibrated with water or 2% pMPC for 12 h showed that corneocytes are still cohesive and epidermis is tightly bound to dermis in 2% pMPC-treated skin, while wider separation between corneocytes and focal dilations in inter-cellular spaces were observed in water-treated skin. This result suggests that pMPC could protect the barrier property of the stratum corneum by preventing the disruption of ILB structure caused by extensive skin hydration during skin permeation study.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2011.10a
• /
• pp.39-41
• /
• 2011

The recycling rate of recovered paper in Korea is the highest in the world, 92%, but remanufacturing yield is low due to the extremely poor quality of the paper. The poor quality, in turn, influences to the reject amount in deinking process. To increase the yield of old newspaper recycling process, hydrophobic degree of inorganic pigments of deinking stock must be reduced. To determine the hydrophobicity, Pitch Potential Deposit Tester (PDT) was newly designed and applied with respect to the SB latex property of various quality used in Korea; its hydrophobic degree according to Tg, gel content, charge and particle size of latex and optimum designing condition of SB latex. And below are the conclusions: 1. The reason of excessive reject from old newspaper deinking process for total amount of printed ink is loss of inorganic pigments. When lipase, a biochemical catalyst, was applied with the purpose of preventing inorganic pigments loss about more than 70% of total reject weight and promoting hydration of pulp for deinking, deinking process yield of pre flotation secondary stage increased remarkably without any changes of deinking efficiency. 2. Lipase improved deinking stock by cutting ester linkage on surface of hydrophobic materials to promote its hydration. From this, it reached the conclusion that hydration degree of stock exercises significant effect on flotation deinking process yield. 3. Inorganic alkali promotes hydration of deinking stock. But there have been needs for more fundamental measures other than inorganic alkali of promoting hydration for yield improvement. For this, this study intended to find out reasons of chemical properties change on surface of hydrophobic material by change of pH. 4. Pitch Deposit Test (PDT) was performed for understanding principle of why surface of coating flake from OMG is hydrophobic and why it becomes hydrophilic when pH of stock is alkaline. As a result of this test, it is determined that swelling property by change of pH of latex film, which were used as coating adhesive is the reason for hydrophobic change. 5. Hydrophilicity of coating flake increased with hydrophilic pigments. And as more of SB Latex adhesive was used and higher of calcium hardness of stock became, its hydrophilicity decreased. SB Latex adhesive film is reformed by mechanical friction. For having hydrophilicity under neutral pH, strong bruising action such as kneading is required. 6. Because swelling of adhesive film decreases as Tg of SB latex gets lower and mean diameter gets smaller, it shows hydrophobicity under neutral pH. This lowers hydrophilicity of coating flake, which leads to easy elimination with flotation reject on DIP process. Therefore, for improving future flotation yield, it is necessary to develop to use eco-friendly clean SB latex by raising Tg and increasing mean diameter for recycling, and as a result, to reduce excessive loss of coating flake as a reject from deinking process.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10c
• /
• pp.151-156
• /
• 1998

Concrete structures is appeared the shrinkage after being harden of the hydration effect of cement. To overcome this disadvantage, expansive additives are used. In our country, the most popular expansive additives are hauyne(CSA) or free lime(free-CaO) systems. These expansive additives are used to expansive cement mortar or concrete materials. In this study, we analyzed the expansive property mechanism about the hydration reaction of the free lime systems and in particular we convinced size distributions of the free lime size affect the expansion ratio with expansion ratio with experiments. We carried out the experiment for the expansive properties by using the soundness molds and with various the humidity and dry setting conditions. The hydration reactions of the free lime affect the reaction properties according to the relative humidity by laboratory experiments.

• Journal of the Korean Ceramic Society
• /
• v.34 no.4
• /
• pp.399-405
• /
• 1997

With the increase of ZnO content, heat of hydration decreased. For specimens containing ZnO more than 0.6 wt.%, the compressive stength of cement cured for 28 days could not be measured because setting was not occurred. With the increase of ZnO content, Blaine specific surface area of cement was decreased and the residue of 45 ${\mu}{\textrm}{m}$ and 90 ${\mu}{\textrm}{m}$ was increased when cement was ground. That is, grindability became worse as ZnO increased in clinker. The difference of color as a function of ZnO content could not be observed, but in the excess of amount of ZnO added, color became more white and reddish yellow.

• Journal of the Korean Ceramic Society
• /
• v.17 no.3
• /
• pp.158-162
• /
• 1980

The experiments of suspension hydration were performed in the mixtures of slag and water or NaOH solutions which were made up with a liquid/solid ratio of 10. The liquid phase of the suspension was chemically analysed and discussed. When slag was in contact with water, CaO component was released from slag grains into the solution. The amounts of $SiO_2$ and $Al_2O_3$ liberated in the solution were very low as compared with CaO, for the impermeable coating of $SiO_2$, $Al_2O_3$-rich gel was formed on the surface of slag grains. The hydration was considered to be inhibited by this impermeable coating. The weak hydraulic property of slag was based on slowly released CaO and dissolved Na, K components which increased pH in the solution.

• Journal of the Korean Wood Science and Technology
• /
• v.28 no.4
• /
• pp.41-50
• /
• 2000

Cement-bonded particleboard is being used as outdoor siding material all over the world, because this composite particularly bears a light weight, high resistance against fire, decay, and crack by cyclic freezing and thawing, anti-shock property, and strength enhancement. Construction systems are currently changing into a frame-building style and wooden houses are being constructed with prefabrication type. Therefore, they require a more durability at outdoor-exposed sides. In this study, the cement hydration property for Korean pine particle, Japanese larch particle and face- and middle layer particles (designated as PB particle below) used in Korean particleboard-manufacturing company was investigated, and the rapid manufacturing characteristics of cement-bonded particleboard by supercritical $CO_2$ curing was evaluated. Korean pine flour showed a good hydration property, however, larch flour showed a bad one. PB particle had a better hydration property than larch flour. The addition of $Na_2SiO_3$ indicated a negative effect on hydration, however, $MgCl_2$ had a positive one. Curing by supercritical $CO_2$ fluid gave a conspicuous enhancement in the performances of cement-bonded particleboards compared to conventional curing. $MgCl_2$ 3%-added PB particle had the highest properties, and $MgCl_2$ 1%-added Korean pine particle had the second class with the conditions of cement/wood ratio of 2.7, a small fraction-screened particle and supercritical curing. On the contrary, the composition of non-hammermilled or large fraction-screened particle at cement/wood ratio of 2.2 was poorer. Also, the feasibility for actual use of 3%-added, small PB particle-screened fraction was greatest of all the conventional curing treatments. Relative superiority of supercritical curing vs. conventional curing at dimensional stability was not so apparent as in strength properties. Through the thermogravimetric analysis, it was ascertained that the peak of a component $CaCO_3$ was highest, and the two weak peaks of calcium silicate hydrate and ettringite and $Ca(OH)_2$ were present in supercritical treatment. Accordingly, it was inferred that the increased formation of carbonates in board contributes to strength enhancement.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.943-947
• /
• 2002

In order to examine the possibility of incineration of inderstrial by-product and wastes which contains a large percentage of chlorine by the cement kiln, measured heat of hydration, setting time, flow, change of length, compressive strength of OPC by the amount of KCl. The result was that a shorter setting time, a lower flow, a increasing the degree of initial shrinkage, a increasing of compressive strength before 3 days and decrease after 7 days by the induction period is shorter as promote the hydration with KCl.