• Composites Research
• /
• v.21 no.4
• /
• pp.1-6
• /
• 2008

This paper explains fire safety tests of a hybrid composite train carbody with carbon/epoxy sandwich bodyshell and stainless steel underframe. In this study, a large scale mock-up was used to evaluate the fire safety of the composite train carbody. The test was conducted to the bare composite carbody mock-up without interior facilities and the fully equipped one. Tile fire propagation and temperature distribution of the carbon/epoxy bodyshell and the glass phenol interior panels was evaluated under the real fire accident scenario. The test scenario was based on the DaeGu subway fire accident. From the tests, both the surface temperature of the interiors and the composite bodyshell wore lower than tile ignition temperature. In addition, the fire spread along the surface of the interiors and bodyshell was not occurred.

• Composites Research
• /
• v.18 no.3
• /
• pp.7-13
• /
• 2005

This paper presents a study on the low velocity impact response of the woven fabric laminates for the hybrid composite bodyshell of a tilting railway vehicle. In this study, the low velocity impact tests for the three laminates with size of $100mm\times100mm$ were conducted at three impact energy levels of 2.4J, 2.7J and 4.2J. Based on the tests, the impact force, the absorbed energy and the damaged area were investigated according to the different energy levels and the stacking sequences. The damage area was evaluated by the visual inspection and the C-scan device. The test results show that the absorbed energy of [fill]8 laminate is highest whereas (fill2/warp2)s is lowest. The [fill]8 laminate has the largest damage area because of the highest impact energy absorption.

• Proceedings of the KSME Conference
• /
• 2005.11a
• /
• pp.121.1-121.1
• /
• 2005

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.264-267
• /
• 2005

Impact damages are very important in the perspective of residual strength of composite structures such as aircrafts, ships, and trains because those damages are sometimes not visible on the surface of the point of impact and the impact resistance of laminated composites is usually not so high. Thus, the impact characteristics of laminated composites should he investigated for the safety of composite structures. This paper investigates the low-velocity impact and damage detection conducted on woven carbon/epoxy laminates. Experimental results show that the type of damage is dependent on the impact energy level and the delamination area becomes larger as the impact energy increases.

• Proceedings of the KSR Conference
• /
• 2005.05a
• /
• pp.251-256
• /
• 2005

This study was performed the heat transportation ratio of three types of the following sandwich panel by KS F 2278(2003) ; Type ${\sharp}1$ : Carbon/epoxy Aluminum Honeycomb and Balsa Core Sandwich Panel(Thickness : 37mm), Type ${\sharp}2$ : Carbon/epoxy Aluminum Honeycomb Core Sandwich Panel(Thickness : 57mm), and Type ${\sharp}3$ : Carbon/epoxy Aluminum Honeycomb Core Sandwich Panel(Thickness : 37mm). Also was performed the heat transportation of next three types of the following sandwich panel by KS F2277(2002) ; Type ${\sharp}4$ and ${\sharp}5$ : 27mm, and 35mm thick-Aluminum Honeycomb Sandwich Panels, and Type ${\sharp}6$ : 27mm thick-Foaming Aluminum Sandwich Panel. It is the larger area between the skin and core, the heat transportation ratio is the higher, and when it is composed of the hybrid composite structure, good insulation property was shown.