• Corrosion Science and Technology
• /
• 제9권3호
• /
• pp.109-115
• /
• 2010

Interstitial-free (IF) steels are widely used for car body material. However, a few types of streaky mark defect are commonly found on hot dip galvannealed (GA) IF steel sheets. In the present study, both the phase structure of a streaky mark defect and the microstructure of the substrate just below it were characterized by optical microscopy (OM) and scanning electron microscopy (SEM). It was found that the bright streaky mark area was composed of ${\delta}$ phase while the dark normal area was full of craters. More than half of the grains at the uppermost surface of the substrate just below the streaky mark defect are unrecrystallized grains which could result from lower finish rolling temperature during hot rolling and be kept stable during the annealing process, while almost all the grains in the normal area are equiaxed grains. In order to confirm the effect of the unrecrystallized grains on the coating morphology, hot dip galvannealing simulation experiments were carried out in IWATANI HDPS. It is proved that the unrecrystallized grains accelerate the Fe-Zn reaction rate during galvannealing and result in a flatter coating surface and an even coating thickness. Finally, a formation mechanism of the streaky mark defect on the hot dip galvannealed IF steel sheet was discussed.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2007년도 추계학술대회 논문집
• /
• pp.215-222
• /
• 2007

Coating of Hot-dip galvannealed steel consists of various Fe-Zn intermetallic compounds. Since the coating is hard and there for is very brittle, the surface of steel sheet is easy to be ruptured during second manufacturing processing. This is called as powdering. In addition, forming equipment might be polluted with debris by powdering. Therefore, various research have been carried out to prohibit powdering fur improving the quality of GA steel. This paper carried out finite element analysis combined with damage model which simulate the failure of local layer of hot-dip galvannealed steel surface during v-bending test. Since the mechanical property of intermetallic compound was unknown exactly, we used the properties calculated from measurements. The specimen was divided into substrate, coating layer and interface layer. Local failure at coating layer or interface layer was simulated when elemental strain reached a prescribed strain.

• 한국자동차공학회논문집
• /
• 제16권6호
• /
• pp.141-147
• /
• 2008

Hot-dip galvannealed sheet (GA) with high strength of 590MPa grade in tensile strength, has developed for automotive applications. However, for a successful application, the microstructure and galvannealing behavior of galvannealed TRIP steel sheets must be strictly controlled. High silicon contents steel has problems with weld-ability, zinc coating and reduction of retained austenite volume fraction after galvannealing process. The main purpose of this study is to solve the problem as indicated above.

• 대한금속재료학회지
• /
• 제46권2호
• /
• pp.58-64
• /
• 2008

Surface-void defects observed on the galvannealed(GA) steel sheets in Interstitial-free high-strengthened steels containing Si and Mn have been investigated using the combination of the FIB(Focused Ion Beam) and FE-TEM(Field Emission-Transmission Electron Microscope) techniques. The scanning ion micrographs of cross-section microstructure of defects showed that these defects were identified as craters which were formed on the projecting part of the substrate surface. Also, those craters were formed on the Si or Mn-Si oxides film through the whole interface between galvannealed coating and steel substrate. Interface enrichments and oxidations of the active alloying elements such as Si and Mn during reduction annealing process for galvanizing were found to interrupt Zn and Fe interdiffusion during galvannealing process. During galvannealing, Zn and Fe interdiffusion is preferentially started on the clean substrate surface which have no oxide layer on. And then, during galvannealing, crater is developed with consumption of molten zinc on the oxide layer.

• 한국표면공학회지
• /
• 제36권6호
• /
• pp.466-474
• /
• 2003

To develop a method of detecting dross in coating layer on hot-dip galvanizing steel, chemical etching behavior of the artificial coating layers with top and bottom dross were investigated. After chemical etching with the mixture of picric acid and sodium thiosulfate, each of the top and bottom dross take its distinct color, and alloy layer in coating is also observed. Defects in the coating layers of HGI(hot rolled galvanized iron), CGI(continuous galvanized steel sheet) and GA(galvannealed steel) were analysed, and methods of dross detection which can be applied to inspection process in manufacture were suggested.

• 한국표면공학회지
• /
• 제33권2호
• /
• pp.135-144
• /
• 2000

Hot-dip galvannealed sheet (GA) with high strength of $45kg/mm^2$ in tensile strength, has developed for automotive applications. However, for a successful application, the powdering behaviour of GA must be minimized. The powdering of galvannealed coatings was reduced as the silicon content in the steel increased. Rapid heating and rapid cooling rate during the galvannealing process improved the powdering resistance due to the suppression of not only the ξ phase, but also the $ \Gamma _1$, phase. An analysis of the Fe-Zn alloy phases and its relation to the powdering behaviour are discussed with SEM micrographs.

• 한국표면공학회지
• /
• 제31권6호
• /
• pp.371-378
• /
• 1998

The zind bate contaminated in the hot dip galvannealed operation was successfully by appling the dross formation mechanism ; the Fe content was lowered from 0.028% to 0.011% and the dress size was decreased from 15~20$\mu\textrm{m}$ to under 3$\mu\textrm{m}$. The cooled metal from CGL zinc bath during operation of the galvannealed steel strip was remelted in graphite crucible at the lab and agitated after increasing Al content from 0.14% to 0.16% with decreasing the molten metal temperature from $470^{\circ}C$to $445^{\circ}C$. The agitating was done by agitator and nitrogen. The molten was analyed by SEM and EDS. It was considered that the Fe and the bottom dross($FeZN_7$) could react with aluminium to from the float dress($Fe_2Al_5$) according to the molten metal temperature down and the float dress rise to the surface of the zine bath. So the Fe and dross in the bath could be romoved out of the bath. It was confirmed that the proper purication conditions of GA zine bath is 0.02% of Al increasing, bath temperature down from $460^{\circ}C$ to $450^{\circ}C$and agitator and nitrogen.

• 대한금속재료학회지
• /
• 제46권5호
• /
• pp.289-295
• /
• 2008

The effect of the alloy elements(Si/Mn) ratio on the coating quality including wettabilty with molten zinc, galvannealing kinetics and crater has been investigated in interstitial-free high strength steel(IFHSS) containing Si and Mn. When the Si/Mn ratio was below 0.75, IF-HSS exhibited a good wettability leading to a good galvannealed coating quality after annealing at $800^{\circ}C$ for 40s in $15%H_2-N_2$ mixed gas with dew point $-60^{\circ}C$. In contrast, the wettability and galvannealed coating quality were deteriorated in the Si/ Mn ratio above 0.75. It is shown that they have relevance to oxides forms by selective oxidation on the steel surface. The oxide particles dispersed on the steel surface with a surface coverage of below 40% resulted in good wettability and galvannealed coating quality. The oxide particle is mainly consisted of $Mn_2SiO_4$ with low contact angle in molten zinc. On the other hand, the continuous oxide layer on the steel surface, such as network- and film-type,caused to poor wettability and galvannealed coating quality. The coverage of oxide layer was above 80%, and its chemical species was $SiO_2$ with high contact angle in molten zinc. Consequently, the Si/Mn alloy ratio played an importance role in galvannealed coating quality of IF-HSS.

• 대한기계학회논문집A
• /
• 제32권12호
• /
• pp.1107-1114
• /
• 2008

This paper is aimed to understand the effect of different galvannealing temperatures on the frictional properties and Fe-Zn intermetallic phases of the galvannealed (GA) coatings on steel sheets. Their galvannealing treatments were conducted at 465, 505, 515 and $540^{\circ}C$ for about 10s in the additional heating furnace of an industrial continuous hot-dip galvanizing line. The mechanical and the frictional properties of the coatings were estimated using nanoindentation, nanoscratch, micro vickers hardness tests and flat friction tests, which were performed at contact pressures of 4, 20 and 80MPa. Also, the correlation between the microstructure and the frictional properties of the GA coatings were investigated by SEM observation for the cross-section of the GA coating after and before flat friction tests. The results showed that the mechanical and the frictional properties of the coatings are strongly dependent on their phase distributions and microstructure. Especially, in low contact pressure of 4MPa the frictional properties of the coatings were dependent on the surface phases and morphology, while in high contact pressure of 80MPa it was influenced by their mechanical properties based on the dominant phase distributions.

• 한국표면공학회지
• /
• 제34권4호
• /
• pp.297-302
• /
• 2001

As GA (Hot dip galvannealed steel sheet) has good corrosion resistance, weldability and paintability as well as excellent formability, it's demand is rapidly increasing for automotive panels. The GA coated layers are composed of several kinds of brittle Fe-Zn Metallic compounds which are susceptible to powdering during the press forming, however, very careful controls of manufacturing conditions such as galvannealing heat-treatment or bath composition are essential to meet with the required quality of automotive use. In this study the required characteristics of automotive panel are practically surveyed in detail and the appropriate manufacturing conditions of galvannealing or bath composition have experimentally investigated by using the various analyzing and simulating equipments. The result in this study indicated that the corrosion resistance at the cut edges was improved by increasing of coating weight and decreasing of thickness of sheet steels.