• Journal of the Korean Ceramic Society
• /
• v.28 no.6
• /
• pp.457-464
• /
• 1991

Aluminum nitride (AlN) has excellent properties such as high thermal conductivity and electrical resistivity, whereas it has some disadvantages such as low sinterability and tendency to be hydrolyzed by moisture at room temperature. In the present work, the relative density, modulus of rupture and microhardness were examined for pressure-less-sintered AlN (synthetic and commercial) bodies which were prepared under the conditions of various sintering temperatures, holding times and additions of CaCO3 which showed the best effect on sinterability among the various sintering aids. As a result, the AlN bodies with 1.0 wt% CaCO3 (0.56wt% CaO) which were sintered at 1800$^{\circ}C$ for 20 min showed good densification. In this case, the relative densities were 95.9% and 95.2%, and microhardnesses were 10.3 GPa and 9.8 GPa for synthetic and commercial AlN respectively. And as the holding time at 1800$^{\circ}C$ was increased from 10 min to 60 min, the relative density was increased from 91.9% to 96.5%. It was considered that impurities of metals and oxygen promoted the densification of AlN at low temperature (1600$^{\circ}C$).

• Journal of Welding and Joining
• /
• v.18 no.6
• /
• pp.48-54
• /
• 2000

The corrosion properties of Ni-Cr-W-Mo-B alloy sprayed by the high velocity oxy-fuel spraying (HVOF) was studied as a function of heat treatment by using both potentiodynamic polarization and immersion tests in the H₂SO₄ solution. The mechanical property was also evaluated by a microhardness tester. Microstructural characteristics of te as-sprayed and annealed coatings at 550, 750 and 950℃ have been analyzed by means of OM, XRD, SEM and TEM. The results showed that the corrosion resistance was improved by increasing the annealing temperature. As-sprayed coating had metastable and heterogeneous phases such as amorphous, nanocrystalline and very refined grain and precipitates, which induced a localized corrosion. The localized corrosion occurred preferentially at the unmelted particles which were composed of Ni matrix and Cr, W and Mo riched phase segregated in the boundaries. As annealing temperature was increased, the microstructure had shown some changes - reduction of porosity and s[plat boundary decomposition and crystallization of amorphous/nanocrystalline phases, grain coarsening,, formation and growth of precipitates such as {TEX}$M_{23}C_{6}${/TEX} and {TEX}$M_{7}C_{3}${/TEX}. In addition, the compositional difference between matrix and boundary phases gradually disappeared, which changed the corrosion type from localized corrosion to general corrosion and thus enhanced corrosion resistance.

• Journal of Korea Foundry Society
• /
• v.17 no.4
• /
• pp.338-346
• /
• 1997

Mechanical properties of ($10%Al_2O_3{\cdot}SiO_2+5%Ni$)/Al hybrid composites fabricated by the reaction squeeze casting were compared with those of ($15%Al_2O_3{\cdot}SiO_2$)/Ai composites. Al-Ni intermetallic compounds ($10{\sim}20 {\mu}m$) formed by the reaction between nickel powder and molten aluminum were uniformly distributed in the Al matrix. These intermetallic compounds were identified as $Al_3Ni$ using X-ray diffraction analysis and they resulted in beneficial effects on room and high temperature strength and wear resistance. Microhardness values of ($10%Al_2O_3{\cdot}SiO_2+5%Ni$)/Al hybrid composite were greater by about 100Hv than those of ($15%Al_2O_3{\cdot}SiO_2$)/Al composite. Wear resistance of ($10%Al_2O_3{\cdot}SiO_2+5%Ni$)/Al hybrid composites was superior to that of ($15%Al_2O_3{\cdot}SiO_2$)/Al composites regardless of the applied load. While tensile and yield strength of ($10%Al_2O_3{\cdot}SiO_2+5%Ni$)/Al hybrid composites were greater at room temperature and $300^{\circ}C$, strength drop at high temperature was much smaller in hybrid composites.

• Journal of the Korean Vacuum Society
• /
• v.4 no.S2
• /
• pp.100-105
• /
• 1995

Nitrogen implantation process has been applied for improvement of wear resistance of Zircaloy-4 fuel cladding materials. Nitrogen was implanted at 120keV to a total dose range of $1\times 10^{17}$ions/$\textrm{cm}^2$ to $1\times 10^{18}$ions/$\textrm{cm}^2$ at various temperatures between $270^{\circ}C$ and $671^{\circ}C$. The microstructure changes by nitrogen implantation were analyzed by XRD and AES and wear behavior was evaluated by performing ball-on-disc type wear testing at various loads and sliding velocities under unlubricated condition. Nitrogen implantation produced ZrNx nitride above $3\times 10^{17}$ions/$\textrm{cm}^2$ as well as heavy dislocations, which resluted in an increase in microhardness of the implanted surface of up to 1400 $H_k$ from 200 $H_k$ of unimplanted substrate. Hardness was also found to be increased with increasing implantation temperature up to 1760 $H_k$ at $620^{\circ}C$. The wear resistance was greatly improved as total ion dose and implantation temperature increased. The effective enhancement of wear resistance at high dose and temperature is believed to be due to the significant hardening associated with high degree of precipitation of Zr nitrides and generation of prismatic dislocation loops.

• Nuclear Engineering and Technology
• /
• v.53 no.8
• /
• pp.2582-2590
• /
• 2021

The high-energy milling is one of the most extended techniques to produce Oxide dispersion strengthened (ODS) powder steels for nuclear applications. The consequences of the high energy mill process on the final powders can be measured by means of deformation level, size, morphology and alloying degree. In this work, an ODS ferritic steel, Fe-14Cr-5Al-3W-0.4Ti-0.25Y₂O₃-0.6Zr, was fabricated using two different mechanical alloying (MA) conditions (M_std and M_act) and subsequently consolidated by Spark Plasma Sintering (SPS). Milling conditions were set to evidence the effectivity of milling by changing the revolutions per minute (rpm) and dwell milling time. Differences on the particle size distribution as well as on the stored plastic deformation were observed, determining the consolidation ability of the material and the achieved microstructure. Since recrystallization depends on the plastic deformation degree, the composition of each particle and the promoted oxide dispersion, a dual grain size distribution was attained after SPS consolidation. M_act showed the highest areas of ultrafine regions when the material is consolidated at 1100 ℃. Microhardness and small punch tests were used to evaluate the material under room temperature and up to 500 ℃. The produced materials have attained remarkable mechanical properties under high temperature conditions.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2000.05a
• /
• pp.1-1
• /
• 2000

The results of the modification of metal materials treated by high temperature pulst:d plasma fluxes (HTlPPF) with a specific power of incident flux changing in the $(3...100)10^5{]\;}W/cm^2$ range and a pulse duration lying from 15 to $50{\;}\mu\textrm{s}$ have been presented. The results of HTPPF action were studied on the stainless steels of 18Cr-l0Ni, 16Cr- 15Ni, 13Cr-2Mo types; on the structural carbon steels of (13...35)Cr, St. 3, St. 20, St. 45 types; on the tool steels of U8, 65G, ShHI5 types, and others; on nickel and high nickel alloy of 20Cr-45Ni type; on zirconium- and vanadium-base alloys and other materials. The microstructure and properties (mechanical, tribological, erosion, and other properties) of modified materials and surface alloying of metals exposed to HTPPF action have been investigated. It was found that the modification of materials by HTPPF resulted in a simultaneous increase of several properties of the treated articles: microhardness of the surface and layers of 40...60 $\mu\textrm{m}$ in depth, tribological characteristics (friction coefficient, wear resistance), mechanical properties ({\sigma_y}, {\;}{\sigma_{0.2}}.{\;}{\sigma_r}) on retention of the initial plasticity ($\delta$), corrosion resistance, radistanation erosion under ion irradiation, and others. The determining factor of the changes observed is the structural-phase modification of the near-surface layers, in particular, the formation of the fine cellular structure in the near-surface layers at a depth of $20{\;}{\mu\textrm{m}}$ with dimension of cells changing in the range from 0.1 to $1., 5{\;}\mu\textrm{m}$, depending on the kind of material, its preliminary treatment, and the parameters of plasma fluxes. The remits obtained have shown the possibility of purposeful surface alloying of metals exposed to HTPPF action over a depth up to 20...45 $\mu\textrm{m}$ and the concentration of alloying element (Ni, Cr, V) up to 20 wt.%. Possible industrial brunches for using the treatment have been also considered, as well as some results on modifying the serial industrial articles by HTPPF.

• Conservation and Restoration of Cultural Heritage
• /
• v.1 no.1
• /
• pp.9-22
• /
• 2012

The most widely excavated iron artifacts used as weapons or farm tools from central southern regions of Korea were subjects of non-metallic inclusion analysis through metallographic examination, microhardness measurement, and scanning electron microscopy with energy dispersive X-ray spectroscopy. Through metallographic interpretation and study of the analyzed results, the steel manufacturing and iron smelting using heat processing in the iron artifacts excavated from the central southern region of the ancient Korean peninsula was studied, and the analysis of the non-metallic inclusions mixed within the metallic structures was interpreted as the ternary phase diagram of the oxide to infer the type of iron ores for the iron products and the temperature of the furnace used to smelt them. Most of the ancient forged iron artifacts showed $Al_2O_3/SiO_2$ with high $SiO_2$ contents and relatively low $Al_2O_3$ contents for iron ore, indicating t hat for $Al_2O_3$ below 5%, it is presumed that magnetic iron ores were reduced to bloom iron (sponge iron) with direct-reduction process for production. The temperature for extraction of wustite for $Al_2O_3$ below 1% was found to be $1,020{\sim}1,050^{\circ}C$. Considering the oxide ternary constitutional diagram of glassy inclusions, the steel-manufacturing temperature was presumed to have been near $1,150{\sim}1,280^{\circ}C$ in most cases, and minimum melting temperature of casting iron part excavated in Daeseong-ri. Gyeonggi was near $1,400^{\circ}C$, and it is thought that hypoeutectic cast iron of about 2.3% carbon was casted and fragility of cast iron was improved by decarburizing in solid state.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.29-30
• /
• 2001

This paper presents some results of plasma nitriding on hard chromium deposit. The substrates were C45 steel and $30~50{\;}\mu\textrm{m}$ of chromium deposit by electroplating was formed. Plasma nitriding was carried out in a plasma nitriding system with $95NH_3{\;}+{\;}SCH_4$ atmosphere at the pressure about 600 Pa and different temperature from $450^{\circ}C{\;}to{\;}720^{\circ}C$ for various time. Optical microscopy and X-ray diffraction were used to evaluate the characteristics of surface nitride layer formed by nitrogen diffusion from plasma atmosphere inward iCr coating and interface carbide layer formed by carbon diffusion from substrate outward Cr coating. The microhardness was measured using microhareness tester at the load of 100 gf. Corrosion resistance was evaluated using the potentiodynamic measurement in 3.5% NaG solution. A saturated calomel electrode (SiCE) was used as the reference electrode. Fig.1 shows the typical microstructures of top surface and cross-section for nitrided and unnitrided samples. Aaer plasma nitriding a sandwich structure was formed consisting of surface nitride layer, center chromium layer and interface carbide layer. The thickness of nitride and carbide layers was increased with the increase of processing temperature and time. Hardness reached about 1000Hv after nitriding while 900Hv for unnitrided hard chromium deposit. X-ray diffraction indicated that surface nitrided layer was a mixture of $Cr_2N$ and CrN at low temperature and erN at high temperature (Fig.2). Anodic polarization curves showed that plasma nitriding can greatly improve the corrosion resistance of chromium e1ectrodeposit. After plasma nitriding, the corrosion potential moved to noble direction and passive current density was lower by 1 to 4 orders of magnitude compared with chromium deposit(Fig.3).

• Nuclear Engineering and Technology
• /
• v.52 no.3
• /
• pp.597-609
• /
• 2020

Accident Tolerant Fuels have been widely studied since the Fukushima-Daiichi accident in 2011 as one of the options on how to further enhance the safety of nuclear power plants. Deposition of protective coatings on nuclear fuel claddings has been considered as a near-term concept that will reduce the high-temperature oxidation rate and enhance accidental tolerance of the cladding while providing additional benefits during normal operation and transients. This study focuses on experimental testing of Zr-based alloys coated with Cr-based coatings using Physical Vapour Deposition. The results of long-term corrosion tests, as well as tests simulating postulated accidents, are presented. Zr-1%Nb alloy used as nuclear fuel cladding serves as a substrate and Cr, CrN, Cr_xN_y layers are deposited by unbalanced magnetron sputtering and reactive magnetron sputtering. The deposition procedures are optimized in order to improve coating properties. Coated as well as reference uncoated samples were experimentally tested. The presented results include standard long-term corrosion tests at 360℃ in WWER water chemistry, burst (creep) tests and mainly single and double-sided high-temperature steam oxidation tests between 1000 and 1400℃ related to postulated Loss-of-coolant accident and Design extension conditions. Coated and reference samples were characterized pre- and post-testing using mechanical testing (microhardness, ring compression test), Thermal Evolved Gas Analysis analysis (hydrogen, oxygen concentration), optical microscopy, scanning electron microscopy (EDS, WDS, EBSD) and X-ray diffraction.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.6
• /
• pp.207-211
• /
• 2005

In this work a multi-layered nanostructured TiAIN/CrN superlattice coatings was synthesized using closed-field unbalanced magnetron sputtering method and the relationships between their superlattice period (1), micro-structure, hardness and elastic modulus were investigated. In addition, wear test at $500^{\circ}C$ and oxidation resistance test at $900^{\circ}C$ were performed to investigate high temperature properties of these thin films. The coatings were characterized in terms of microstructure and mechanical properties by transmission electron microscopy (TEM) and nano-indentation test. Results from TEM analysis showed that superlattice periods was inversely proportional to the jig rotation speed. The maximum hardness and elastic modulus of 37 GPa and 375 GPa were observed at superalttice period of 6.1 nm and 4.4 nm, respectively. An higher value of microhardness from TiAIN/CrN thin films than either TiAIN (30 GPa) or CrN (26 GPa) was noted while the elastic modulus was approximately an average of TiAIN and CrN films. These enhancement effects in superlattice films could be attributed to the resistance to dislocation glide across interface between the CrN and TiAIN layers. Much improved plastic deformation resistance ($H^3/E^2$) of 0.36 from TiAIN/CrN coatings was observed, compared with 0.15 and 0.16 from TiAIN and CrN, respectively. Also the wear resistance at $500^{\circ}C$ was largely increased than those of single TiAIN and CrN coatings and TiAIN/CrN coatings showed much reduced weight gain after exposure at $900^{\circ}C$ for 20 hours.