• Journal of the Korean Wood Science and Technology
• /
• v.42 no.3
• /
• pp.282-289
• /
• 2014

After being laminated with a combination of glass fiber reinforced plastic and plywood, the GFRP laminated plate was densificated for 1 hour at $150^{\circ}C$ with pressure of $1.96N/mm^2$. A partial reinforced beam was produced by attaching the 5 GFRP laminated plates to the joint of glulam and the column. In addition, the column to beam joint was produced by using reinforced laminated wooden pin which was made of GFRP sheet and plywood, fiber glass reinforced cylindrical-LVL column. The joint was made of round log, glulam and drift pin as the reference specimen, and its moment resistance was evaluated. As a result, the strength performance of specimens with partial reinforced beams were 1.8 times stronger than the reference specimen on average. Furthermore, rupture was neither occurred on partial reinforced beam nor column. Toughness and stiffness of joints were also fine. The GFRP sheet reinforced laminated plate showed better reinforcement effect than GFRP textile reinforced one. GFRP sheet was inserted into each layer of laminate, and it showed good condition in rotation-angle and strength, therefore it is the most appropriate to reinforce the part of the beam.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.1
• /
• pp.60-67
• /
• 2015

In order to evaluate the bond performance of domestic larch glulam and the glass fiber reinforced plastic (GFRP) rod, the specimen with the GFRP rod bonded-in domestic larch glulam for pull-out test was produced. The test was carried out using various specimens with different gluing depth, width of glue-line and type of adhesive. The cantilever type rahmen structure specimen with bonded-in GFRP rods was produced based on the result of pull-out test, and its moment resistance performance was compared and examined with the moment resistance performance of slotted-in steel plate specimen. As a result of the pull-out test, the most excellent bond performance was found when the insertion depth of GFRP rods was 5 times larger than the diameter of GFRP rods. When the glue-line thickness was 1 mm, the bond performance improved by 17%~29% in comparison to the bond performance in the case of the glue-line thickness of 2 mm. Also, the bonded strength of the specimen used with poly-urethane adhesive was 2.9~4.0 times greater than the bonded strength of specimen used with resorcinol adhesive. The cantilever type rahmen structure specimen with bonded-in GFRP rods showed the moment resistance performance 0.82 times lower in comparison to the slotted-in steel plate specimen used with the drift pin, but the initial stiffness was similar as 0.93 times.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.4
• /
• pp.357-363
• /
• 2009

This study was carried out to investigate whether adhesive used in manufacturing glulam can be used to bond wood and GFRP, when considering working process and economical efficiency. The six different glulams were manufactured, changing the adhesives and the mixing ratios of the adhesives, and investigated by the block shear test and the delamination of the water soaking or boiling water soaking. The three glulams were manufactured, using the resocinol resin based adhesive, the PVAc resin based adhesive and the epoxy resin adhesive, and the other three glulams, using the adhesives mixing resocinol resin and PVAc resin. The block shear strength is higher than $7.1N/mm^2$ in all types, which is standard of KS F3021. However, in the wood failure the block shear strength was the highest as 65.9% in the PVAc. The delamination of glulams glued with PVAc adhesive, which was 1.08% in water soaking and 4.16% in boiling water soaking, was lower than 5.00% which is the standard of KS F 3021, and the adhesive strength is good. In glulams glued with only resocinol resin adhesive, the wood layers were good as 1.26% in the water soaking delamination and 0.00% in the boiling water soaking delamination. The GFRP layers were not good as 21.85% in the water soaking delamination but were good as 1.45% in the boiling water soaking delamination.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.1
• /
• pp.53-61
• /
• 2017

In this study, specimens were produced with a column member and a wooden gusset only by inserting an wooden gusset which is a substitute for steel plate into the center of a slit-processed column member. The moment resistance performance of the specimens was compared with that of control specimens that used a steel plate. The measured maximum moments of the specimens produced with GFRP-reinforced wooden laminated gussets and pins were lower by 24% on average compared to the steel plate-inserted specimens, but they showed good toughness. The fracture shape suggests that it was fractured along the annual rings between the pin and the end of the column member. The rigid specimen that integrated a laminated wood and a wooden laminated gusset with adhesive showed 2.8 times greater initial rigidity and 40% greater maximum moment on average compared to the control specimen. The rigid specimens mainly fractured on a glulam around glue line.