• Corrosion Science and Technology
• /
• v.10 no.2
• /
• pp.52-59
• /
• 2011

Corrosion of metallic materials occurs by the reaction with corrosive environment such as atmosphere, marine, soil, urban, high temperature etc. In general, reduction of thickness and cracking and degradation are resulted from corrosion. Corrosion in all industrial facilities and infrastructure causes large economic losses as well as a large number of accidents. Economic loss by corrosion has been reported to be nearly 1-6% of GNP or GDP. In order to reduce corrosion damage of industrial facilities, corrosion map as well as a systematic investigation of the loss of corrosion in each industrial sector is needed. The Corrosion Science Society of Korea in collaboration with 15 universities and institutes has started to survey on the cost of corrosion and corrosion map of Korea since 2005. This work presents the results of the survey on cost of corrosion by Uhlig, Hoar, and input-output methods, and the evaluation of atmospheric corrosion rate of carbon steel, weathering steel, galvanized steel, copper, and aluminum in Korea. The total corrosion cost was estimated in terms of the percentage of the GDP of industry sectors and the total GDP of Korea. According to the result of Input/output method, corrosion cost of Korea was calculated as 2.9% to GDP (2005). Time of wetness was shown to be categories 3 to 4 in all exposure areas. A definite seasonal difference was observed in Korea. In summer and fall, time of wetness was higher than in other seasons. Because of short exposure period (12 months), significant corrosion trends depending upon materials and exposure corrosion environments were not revealed even though increased mass loss and decreased corrosion rate by exposure time.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.19 no.3
• /
• pp.285-289
• /
• 2013

The coastal area of Republic of Korea is very clean compared to other countries. In this reason, west coastal area of our country is a good place for breeding up a fish such as shrimp. In winter season, the heating system is required for preventing shrimp death caused by freezing in the farm. The heater in the heating system for fishery's farm is operated very severe combating corrosion due to high accumulation by feeding material and high temperature in heated sea water. Almost all manufactured heaters of STS 316L and Ti material are scrapped every year due to heavy corrosion such a general and crevice corrosion. For comparing the general and galvanic corrosion in new heater material, the test material of Zirconium (Zr), Titanium (Ti) and STS 316L are tested by potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), current density-time methods and microscopic examination in a 3.5% NaCl solution. The corrosion potential (Ecor) measured by potentiodynamic polarization for Zr, Ti and STS 316L reveals -198, -250 and -450mV, corrosion current density 0.5, 2.5 and $6.5{\mu}A/cm^2$ respectively. The film resistance measured by EIS are Zr 63,000, Ti 39,700 and 316L $3,150{\Omega}$, and the current of Zr-Ti couple is $0.03{\mu}A$, whereas Zr-316L SS is $0.1{\mu}A$. According to the result of this experiment in 3.5% NaCl solution, Zr is excellent corrosion resistance material than Ti and STS 316L.

• Corrosion Science and Technology
• /
• v.8 no.3
• /
• pp.119-125
• /
• 2009

Corrosion assessment has a number of uses but the use considered here is as a precursor to Risk-Based Inspection (RBI) planning. Systematic methods consisting of technical modules of RBI program were used to assess the effect of specific corrosion mechanism on the probability of failure in equipments of petrochemical plants. Especially in part of the damage and corrosion assessment, screening step involved evaluating the combinations of process conditions and construction materials for each equipment item in order to determine which damage mechanisms are potentially active. For general internal corrosion, either API 510 or API 570 was applied as the damage rate in the calculation to determine the remaining life and inspection frequency. In some cases, a measured rate of corrosion may not be available. The technical modules of RBI program employ default values for corrosion, typically derived from published data or from experience with similar processes, for use until inspection results are available. This paper describes the case study of corrosion and damage assessment by using RBI methodology in petrochemical plant. Specifically, this paper reports the methodology and the results of its application to the petrochemical units using the $KGS-RBI^{TM}$ program, developed by the Korea Gas Safety Corporation to suit Korean situation in conformity with API 581 Codes.

• Journal of Ocean Engineering and Technology
• /
• v.18 no.5
• /
• pp.50-56
• /
• 2004

This study is on the constant-current stress corrosion test, related to the load stress, in both the welded and non-welded zones of high tensile strength steel that is used for natural gas transmission. The surface corrosion pattern of the welded zone of API 5L-X65 specimens for natural gas transmission showed general corrosion and narrow pitting, and the pitting was increased with load stress. Initially, the average relative electrode potential and the average relative current of the high tensile strength steel, used for natural gas transmission specimens, were decreased rapidly, and the average relative electrode potential was higher and the average relative current was lower in welded zone, compared to base metal. The average relative electrode potential was decreased with load stress, and the average relative current was somewhat increased by increasing the load stress. The corrosion rate was less in welded zone, compared to base metal, and the corrosion rate was decreased by increasing the load stress.

• Nuclear Engineering and Technology
• /
• v.49 no.4
• /
• pp.769-775
• /
• 2017

The corrosion behavior of stainless steel (304 and 316 type) and copper induced by LiCl-KCl at low temperatures in the presence of sufficient oxygen and moisture was investigated through a series of experiments (at $30^{\circ}C$, $40^{\circ}C$, $60^{\circ}C$, and $80^{\circ}C$ for 24 hours, 48 hours, 72 hours, and 96 hours). The specimens not coated on one side with an aqueous solution saturated with LiCl-KCl experienced no corrosion at any temperature, not even when the test duration exceeded 96 hours. Stainless steel exposed to LiCl-KCl experienced almost no corrosion below $40^{\circ}C$, but pitting corrosion was observed at temperatures above $60^{\circ}C$. As the duration of the experiment was increased, the rate of corrosion accelerated in proportion to the temperature. The 316 type stainless steel exhibited better corrosion resistance than did the 304 type. In the case of copper, the rate of corrosion accelerated in proportion to the duration and temperature but, unlike the case of stainless steel, the corrosion was more general. As a result, the extent of copper corrosion was about three times that of stainless steel.

• Corrosion Science and Technology
• /
• v.17 no.1
• /
• pp.6-11
• /
• 2018

Outdoor exposure tests using of 7B04 aluminium alloy samples including plate, tensile and various SCC samples were carried out in Tuandao station, Shandong province (East of China) and Wanning station, Hainan province (South of China). Corrosion characteristics including weight loss, microstructure, tensile strength and SCC susceptibility were investigated. The corrosion rates in Tuandao and Wanning showed high to low and the corrosion rates changed to the following equation of $w=at^b$ (b<1). The corrosion of 7B04 aluminium alloy in Wanning was more serious than that in Tuandao. Pitting appeared at early stage of expose test, and it can be changed to general corrosion with test time extension. The 7B04 aluminium alloy of which specimen shapes are forging and thick plate also showed SCC (Stress corrosion cracking) in the marine atmosphere. The higher SCC sensitivity was observed in Wanning station than in Tuandao station. The 7B04 aluminium alloy with a high stress level was more sensitive to SCC. Intergranular and transgranular or a mixed mode of cracking can be observed in different marine exposure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.755-758
• /
• 1999

Reinforced concrete is in general known as high durability construction material under normal environments due to strong alkalinity of cement. Marine and harbour concrete in the tidal and the splash zone at seashore are exposed to cyclic wet and dry saltwaters which cause to accelerate corrosion of reinforcing steel in concrete. If corrosion resistance of concrete gets to weaken due to carbonations and cracks in cover concrete, furthermore, concrete durability rapidly decreases by corrosion of reinforcement steel embedded in concrete. The objective of this study is to develop appropriate corrosion protection systems so as to enhance the durability of concrete by controlling the cover depth of concrete and by using corrosion inhibitors as concrete admixtures.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.345-350
• /
• 2001

Reinforced concrete is, in general, known as a high durability material due to a strong alkalinity of cement. Probable concrete cracks could incur steel corrosion of RC structures and then could easily deteriorate the concrete durability, which can be fully secured by a systematic quality control for the construction of concrete structures. For the corrosion protection of reinforcing steels in concrete, however, current design specifications of concrete cover depth do not in-depth consider the effect of the cracks as well as the chloride content of RC structures. Therefore, appropriate provisions for concrete cover depth should be coded by considering the influence of concrete cracks on the corrosion of reinforcing steels. The objective of this research is to investigate pertinent cover depth, which can prohibit rebar corrosion, on the basis of experimental corrosion measurements of reinforcing steels on crack characteristics such as the width, depth and frequency of concrete cracks.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.12
• /
• pp.157-162
• /
• 2000

The object of this work is to develop an assessment system for pipeline integrity. the system consists of four module applications for internal algorithm; the effect of corrosion in pipeline, crack, stress corrosion crack (SCC) and fatigue modules. Presently, the module of the external corrosion has been developed and the internal algorithm for the effect of corrosion in pipeline and the database of the system are described in this paper. The database of the system is separated to mainly four parts; geometry of pipeline, material properties, boundary conditions and general properties. Each components of the system are designed by user-friendly concept. This system may give a guideline for maintenance and modifications for the pipeline at the industrial sight. Furthermore, a procedure to evaluate an inspection interval is also provided.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.821-826
• /
• 2000

Reinforced concrete is in general known as high durability construction material under normal environments due to strong alkalinity of cement. Marine concrete specimens in the tidal and the splash zone at seashore have been exposed to cyclic wet and dry saltwaters which cause to accelerate corrosion of reinforcing steel in concrete. If corrosion resistance of concrete gets to weaken de to carbonations and cracks in cover concrete, furthermore, concrete durability rapidly decreases by the corrosion of reinforcement steel embeded in concrete. The objective of this study is to develop appropriate corrosion protection systems of marine concrete so as to enhance the durability of concrete by establishing pertinent cover depth of concrete and by using corrosion inhibitors as concrete admixtures.