• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.379-384
• /
• 2005

Polyurethane foams (PUFs) were prepared from polymeric 4,4'-diphenylmethane diisocyanate (PMDI), seven polyols with different functionalities and OH values, silicone surfactant, two catalysts, and three blowing agents. Chlorofluorocarbon (CFC-11), hydrochlorofluorocarbon (HCFC-141b) and hydrofluorocarbon (HFC-365mfc) were used as blowing agents. The effect of gelling and blowing catalysts on basic properties and cell structure of PUF with HCFC-141b was investigated. The cell size of the PUF decreased with an increase in the amount of catalyst from 0 to 2 pph (parts per hundred polyol). In the case of gelling type catalyst, the compressive strength increased from 11.9 to $12.66kg_f/cm^2$ with an increase in the amount catalyst from 0 to 2 pph but the density did not change significantly. The gelling time, density, and compressive strength of the PUF with three different blowing agents were measured. There was no detectable change in their properties. However, the cell structure of PUF with HCFC-141b was not uniform as in the other systems.

• Polymer(Korea)
• /
• v.39 no.2
• /
• pp.210-218
• /
• 2015

The reaction behavior of rigid polyurethane foams were studied on the effects of gelling catalysts of amine type, such as; dimethylcyclohexyl amine (DMCHA) and of potassium type, such as; potassium octoate (PO). Rigid polyurethane foams were provided with polymeric 4,4'-diphenylmethane diisocyanate, polyester polyol, silicone surfactant, blowing agent and a few gelling catalysts. As the contents of catalyst, DMCHA increased from 0 to 2.0 g, the reaction time decreased from ca. 330 to ca. 35 sec and due to the exothermic reaction, the maximum temperature increased from ca. 217 to ca. $234^{\circ}C$, respectively. As the contents of PO increased from 0 to 2.5 g, the reaction time decreased from ca. 79 to ca. 38 sec and the maximum temperature increased from ca. 182 to ca. $271^{\circ}C$, respectively. The kinetic parameters were calculated and the conversions were based on the temperature rising method of adiabatic process. As the content of DMCHA increased, the rate constant $k_0$ increased. But in the case of PO catalyst, $k_0$ did hardly depend upon its amount, and showed us similar reaction rate constants.

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.367-374
• /
• 1994

Inorganic-organic composite was made through sol-gel process. Possible range for hosting organic dye was investigated with various composition. The transmittance of the composite was the most important condition for a host was increased to 90% with decreasing HCl as a catalyst. Clear absorbance peak was obtained by decreasing concentration of organic dye, fluorescent intensity was increased and transmittance was decreased with rising gelling temperature.

• Journal of the Korean Institute of Gas
• /
• v.16 no.6
• /
• pp.115-122
• /
• 2012

Polyurethane foams were synthesized with different contents and kinds of catalysts to know change of properties under various NCO index. UTM(universal testing machine), DSC(differential scanning calorimetry), SEM(scanning electron microscope) and FT-IR(Fourier transform spectroscopy) were used for studying the PUF's physical properties change. Compressive strength of PUF increased with increasing contents of catalyst. Glass transition temperature(Tg) and compressive strength of PUF using PC-8 and 33LV catalyst, increased with increasing NCO index at the aging. According to the results of Infrared spectral analysis, reduction of NCO peak was found in gelling catalyst, because unreacted NCO reacted with polyurethane. Although Tg and compressive strength of PUF using TMR-2, unchanged with increasing NCO index at the aging, because trimerization of isocyanate.

• Analytical Science and Technology
• /
• v.7 no.1
• /
• pp.17-23
• /
• 1994

Through sol-gel process, inorganic/organic composite as a dye host was made. It was observed that this composite has about 90% of trnasmittance by UV/VIS spectrophotometer. The transmittance is the most important requirement to decide whether the composite could apply or not as the dye host. The transmittance was increased with decreasing HCl as a catalyst, aging time, and amount of PDMS. Also, fluorescent and transmittant charateristics of Rhodamine 6G Perchlorate that was doped into ORMOSIL were measured. The fluorescent intensity was increased and the trnasmittance was decreased with rising gelling temperature.

• Polymer(Korea)
• /
• v.29 no.5
• /
• pp.457-462
• /
• 2005

Polyurethane foams (PUFs) were prepared from polymeric 4,4'-diphenylmethane diisocyanate (PMDI), mixed polyol with OH value of 480, silicone surfactant, three catalysts, and hydrofluorocarbon(HFC) as blowing agent. Balance (PC-8), gelling (33LV), and trimerization (TMR-2) catalysts were used. The effect of the catalysts on the physical properties of PUF with increase of isocyanate (NCO) index and aging time was investigated. The cell size of the PUF with PC-8 and 33LV slightly increased with an increase in NCO index from 100 to 170 but compressive strength did not change significantly. In case of trimerization catalyst, the compressive strength of PUF increased from 8.75 to 1$10.5 kg_f/cm^2$ and the cell size decreased with an increase in NCO index. The compressive strength of the PUF with 33LV increased from 9.21 to $10.15 kg_f/cm^2$ with an increase in aging time. However, there was no detectable change in the compressive strength of PUF with TMR-2. A possible interpretation of the results includes an additional cross-link reaction of non-reacted MDI and FTIR spectrum illustrated the change of NCO peak.