• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.50 no.4
• /
• pp.388-395
• /
• 2017

We investigated the toxicity of zinc and aluminum hot-dip galvanized sheet steel to abalone Haliotis discus hannai via changes in the gill and hepatopancreas using histological and transmission electron microscopy analysis. Experimental groups were composed of one control and four exposure conditions (direct or indirect exposure to zinc and aluminum hot-dip galvanized sheet steel). In the control group, aluminum exposure groups (direct and indirect), and indirect zinc exposure group, abalone mortality was not observed until the end of the experiment, and no histopathological changes were observed in the gill and hepatopancreas. However, the direct zinc exposure group exhibited 100% mortality. Ultrastructural analysis of the cytoplasm of ciliated and microvilli-bearing epithelial cells from gill filaments revealed electron-dense vesicles near the cell membrane and disruption of the nuclear membrane. We also observed swollen mitochondria and a loss of mitochondrial cristae. The hepatopancreas showed similar changes, and we detected highly electron-dense particles within the vesicles. These results suggest that abalone exposed directly to zinc hot-dip galvanized sheet steel experience acute toxicity, causing damage to cell organelles in the gill and hepatopancreas and, finally, inducing mortality.

• Corrosion Science and Technology
• /
• v.23 no.2
• /
• pp.121-130
• /
• 2024

In recent years, Zn-Al-Mg alloy galvanized steel sheets have been widely used as coated steel sheets to support social capital in the infrastructure field. A feature of Zn-Al-Mg alloy-coated steel sheets is that they provide a better corrosion protection period than Zn-coated steel sheets. In this study, the corrosion resistance of a new Zn-Al-Mg alloy-coated steel sheet was investigated and compared to that of conventional commercially available coated steel sheets. The investigation confirmed that increasing the Mg concentration in the Zn-Al-Mg-coated steel sheet improved corrosion resistance, which was more than 10 times that of the galvanized steel sheet specified in JIS G 3302. The study findings also confirmed that the corrosion resistance reached more than twice that of the coated steel sheet specified in JIS G 3323. If such galvanized steel sheets are applied to social infrastructures that are exposed to severely corrosive environments, the service life of the infrastructure might be extended.

• Corrosion Science and Technology
• /
• v.9 no.6
• /
• pp.254-258
• /
• 2010

Due to the global warming and economic crisis, automakers are currently focusing on the development of high fuel-efficiency vehicles. To accord with these requirements, steelmakers have been trying to develop advanced high-strength steels with improved automotive-related properties. In addition, galvanizing technologies have been developed to improve coating properties for AHSS (Advanced High Strength Steel) such as pre-oxidation and pre-coating, as well as roll dent prevention. In this paper, newly developed products and technologies for automotive galvanized steel sheet are reviewed.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.4
• /
• pp.253-260
• /
• 1996

Regular spangle hot dip galvanized steel sheets were made in the zinc bath containing a small amount of Al and with the addition of Pb, Sb, Sb-Mg, Sb-Cu and Bi respectively whose average glosses were measured. Zero-spangle hot dip galvanized steel sheets were also made by spraying a 2% $NH_4H_2PO_4$ solution on molten coating surfaces with exactly the same chemical compositions as above used for regular spangle and whose glosses and corrosion losses were also evaluated. For manufacturing zero- spangle hot dip galvanized steel sheets with high brightness, the zinc bath with 0.02%Sb and the spraying of a 2% $NH_4H_2PO_4$ solution were proposed and for better brightness and corrosion resistance, the zinc bath with 0.02% Sb-0.50%Mg and the spraying of a 2% $NH_4H_2PO_4$ solution were also proposed.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.6
• /
• pp.307-316
• /
• 1998

The effects of surface roughness on chromate conversion coating and the corrosion behavior of galvanized steel sheets were investigated. Surface roughness was differently given to the galvanized steel sheets tested and these were then chromated. Accelerated corrosion test was conducted under the condition of $30^{\circ}C$, 90%RH with flowing 200ppm $SO_2$ gas. The galvanized steels were also exposed to urban environment for 5 weeks. The corrosion rates were measured by weight gain method. The distribution of chromate film and corrosion product on the coating were examined which SEM/EDS. The chromate film formed preferentially at the convex sites rather than at the concave sites on the surface. The corrosion products were found at the concave sites where the chromate film formed rarely. The corrosion product on the coating were found at the concave sites where the chromate film formed rarely. The corrosion rates increased slightly with the surface roughness in accelerated corrosion test but significantly in field test.

• Journal of Welding and Joining
• /
• v.21 no.4
• /
• pp.56-62
• /
• 2003

MIG brazing is used for many parts without melting base metal because of high productivity. Pulsed MIG brazing can be used to further reduce heat input and to improve the process stability. However, a significant amount of zinc in galvanized sheet steel is burned off in the area of brazes. Therefore, the brazing method to reduce the heat input is needed. In the brazing for galvanized sheet steel, variable polarity AC pulse MIG arc brazing can be applied to more decrease the heat input by setting EN-ratio adequately. In this research, we studied for the variable polarity AC pulse MIG arc brazing to decrease the heat input by using ERCuSi-A wire. As the result of increasing EN-ratio, melting ratio of base metal and burning off of zinc were reduced in galvanized sheet steel.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.4
• /
• pp.547-554
• /
• 1999

The interfacial reaction, spangle and coating thickness of galvanized steel in Ni added Zn-0.18Al bath have been investigated. The size of spangle and thickness of reaction layer were observed under an optical microscope, SEM and EDS. Analysing the experimental results concerning spangle size of galvanized steel it was found that Ni addition in Zn-0.18Al bath tended to be minimized spangle size. For Zn-0.18Al bath, addition of 0.1Ni suppressed the formation of Fe-Zn intermetallic compounds but increased with Ni content above 0.1%. The coating thickness of galvanized steel was reduced with Ni addition in Zn-0.18Al bath, especially in Zn-0.18Al-0.05Ni bath. Addition of Al in Ni containing bath resulted in forming the Al-Ni intermetallic compounds such as $Al_3$Ni$_2$ and $Al_2$Ni which consist most of top precipitates.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.19 no.4
• /
• pp.4544-4554
• /
• 1977

The objective of this study was to measure and compare the radiation heat load generated through a few chosen shade-materials that would protect animals from the direct solar radiation heat in summer condition. The results obtained from this study are as follows; 1. when the materials were used in original state, the most effective material for radiation heat reduction was slate, followed by aluminum and galvanized steel successively. 2. The radiation heat load under the white top and black underside aluminum was 2.5 Cal. per hour per square cm less than that under the bare aluminum of their diurnal peak. 3. When the modified galvanized steel was used, the radiation heat load was reduced as much as 2.4 cal per hour per square cm by attaching plywood under the galvanized steel, 3.9 cal per hour per square cm by attaching plywood and coating white paint on the top of the galvanized steel. The galvanized steel covered by hay material showes similar result as that of the galvanized steel lined with plywood. 4. In case of slate, the radiation heat reduction value was increased by using bare slate, white top slate and white-top-black-underside slate in the descending order. 5. The calculated value of radiosity of inside surface of aluminum was about 20 percent of the radiation heat load, the reduced value of radiosity by coating paint was considered to be indirect indication of the effect of total radiation heat load reduction of painted surface. 6. About an hour of the time lag of radiation heat load peak on sept. 10 for slate materials should be investigated more comprehensively in future.

• Journal of Korean Society of Water and Wastewater
• /
• v.22 no.3
• /
• pp.379-387
• /
• 2008

The pH & alkalinity adjustment method by lime and carbon dioxide($CO_2$) for corrosion control in water distribution system was investigated to evaluate the corrosion characteristics of metal pipes, such as galvanized iron, copper, stainless steel, and carbon steel. When the pH in sand filtered and ozone+GAC treated water was increased with lime and $CO_2$ from 7.5 to 8.0, the concentration of residual chlorine decreased at higher pH and longer reaction time; the concentration of trihalomethane increased. The corrosion rate of coupons with corrosion control using lime and carbon dioxide was showed much smaller than those without corrosion control using pilot-scale simulated distribution system. The galvanized iron was corroded much faster than carbon steel, copper, and stainless steel. Especially, copper and stainless steel coupons were hardly corroded. The galvanized iron and carbon steel coupons with corrosion control were produced the corrosion products less than those without corrosion control by the results of environmental scanning electron microscope(ESEM) and energy dispersive x-ray spectroscopy(EDS) analyses. The galvanized iron coupon with pH and alkalinity adjustment by lime and carbon dioxide was detected about 30 percent of zinc, when the carbon steel was detected about 30 percent of calcium by calcium carbonate products formation. For the results of X-ray diffraction(XRD) analyses, the goethite(${\alpha}$-FeOOH) was identified as primary corrosion product of galvanized iron without corrosion control, while the Zinc oxide(ZnO) was found on corrosion products of galvanized iron coupon with corrosion control as the results of EDS analyses. However, the carbon steel corrosion products regardless of corrosion control were composed predominantly of maghemite(${\gamma}-Fe_2O_3$) and hematite(${\alpha}-Fe_2O_3$).

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.15 no.1
• /
• pp.110-115
• /
• 2016

The need for high-strength galvanized steel has recently increased because of the increased number of car consumers who want improved efficiency and exterior quality. High-strength galvanized steel with high corrosion resistance improves the durability of products and exterior quality. Furthermore, the gilt of zinc does not come off during machining because of the fine adhesive property of zinc. When these are welded, zinc has a lower melting temperature than iron, so zinc is more quickly vaporized than iron. Vaporized zinc can stick to electrodes, which increases spatter in welding transportation. Created spatter can enter the molten pool and develop into inner defects or blowholes and pits. Scattered spatter sticks to the product, which leads to the secondary cost of spatter removal. Therefore, in this study, comparisons of amounts of spatter generated are conducted according to the composition of shielding gas in the MIG and CMT processes to find optimal welding parameters.