• Journal of the Korea Concrete Institute
• /
• v.18 no.1 s.91
• /
• pp.57-64
• /
• 2006

The crack presented in concrete structures causes a structural defect, the durability decrease, and external damages etc. Therefore, it is necessary to improve durability through the effort to control the crack. Fluosilicic acid($H_2SiF_6$) is recovered as aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded $H_3PO_4$ or HF. Generally, fluosilicates prepared by the reaction between $H_2SiF_6$ and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. Mix proportions for experiment were modulated at 0.45 of water to cement ratio and $0.0{\sim}2.0%$ of adding ratio of fluosilicate salt based inorganic compound. To evaluate correlation of concrete strength and adding ratio of fluosilicate salt based inorganic compound, the tests were performed about design strength(21, 24, 27 MPa) with 0.5% of adding ratio of fluosilicate salt based inorganic compound. Applications of fluosilicate salt based inorganic compound to reduce cracks resulted from plastic and drying shrinkage, to improve durability are presented in this paper. Durability was evaluated as neutralization, chloride ion penetration depth, freezing thawing resistant tests and weight loss according reinforcement corrosion. It is ascertained that the concrete added fluosilicate salt based inorganic compound showed m ability to reduce the total area and maximum crack width significantly as compared non-added concrete. In addition, the durability of concrete improved because of resistance to crack and watertightness by packing role of fluosilicate salt based inorganic compound obtained and pozzolanic reaction of soluble $SiO_2$ than non-added concrete.

• Journal of the Korean GEO-environmental Society
• /
• v.8 no.6
• /
• pp.53-60
• /
• 2007

L/EPS, manufactured in the shape of block and used for civil engineering, is a lightweight material with an excellent resistance to compression, and provides a superb self-sufficient stability. EPS is a suitable material capable of resolving the problem of settlement and lateral flow if it is applied as the soil on soft ground. The Korean Standards (KS) has not yet proposed any testing method for use of EPS as an engineering banking material. Only its testing and quality ordinance as a heat insulation material has been standardized. The design criteria for EPS has been established and applied through the trial construction of KHC (Korea Highway Corporation) and quality test of manufacturer, but most studies on them have been confined to factory products. This study is focused on comparing and analyzing long-term durability by conducting cyclic load test, freezing and thawing test, absorption rate test and others. EPS used in the test was chosen from construction sites and factory products, focusing on the long-term durability of EPS depending on the passage of time. Unconfined compression test results indicated that the strength of collected samples was lower than factory products. While the triaxial compression test results indicated that the shear strength increased in proportion to the increase of confining pressure, and factory products had declining shear strength as the confining pressure rose.

• Journal of the Korea Concrete Institute
• /
• v.20 no.5
• /
• pp.661-668
• /
• 2008

It is necessary to develop a new technology for effectively reducing hydration heat and controlling thermal cracking caused increasing construction of large size massive concrete structures such as mat foundation of high-rise building, grandiose bridge, and LNG tank. Therefor, to develop a new technology for reducing hydration heat of large size massive concrete in this study, after developing the latent heat binder for controling hydration heat of concrete by application of latent heat material, it was investigated basic properties and durability such as slump, air content and compressive strength, shrinkage properties, permeability, freezing and thawing resistance, corrosion, and hydration heat generation properties of concrete using latent heat binder. As a test result, it was confirmed that latent heat binder was not affected adversely the basic property and durability of concrete, and was advanced on the reduction of hydration heat and control of thermal crack. It is expected to be applied as the excellent technology on the management of hydration heat and thermal crack in large size mass concrete structures.

• Journal of the Korean Wood Science and Technology
• /
• v.28 no.4
• /
• pp.41-50
• /
• 2000

Cement-bonded particleboard is being used as outdoor siding material all over the world, because this composite particularly bears a light weight, high resistance against fire, decay, and crack by cyclic freezing and thawing, anti-shock property, and strength enhancement. Construction systems are currently changing into a frame-building style and wooden houses are being constructed with prefabrication type. Therefore, they require a more durability at outdoor-exposed sides. In this study, the cement hydration property for Korean pine particle, Japanese larch particle and face- and middle layer particles (designated as PB particle below) used in Korean particleboard-manufacturing company was investigated, and the rapid manufacturing characteristics of cement-bonded particleboard by supercritical $CO_2$ curing was evaluated. Korean pine flour showed a good hydration property, however, larch flour showed a bad one. PB particle had a better hydration property than larch flour. The addition of $Na_2SiO_3$ indicated a negative effect on hydration, however, $MgCl_2$ had a positive one. Curing by supercritical $CO_2$ fluid gave a conspicuous enhancement in the performances of cement-bonded particleboards compared to conventional curing. $MgCl_2$ 3%-added PB particle had the highest properties, and $MgCl_2$ 1%-added Korean pine particle had the second class with the conditions of cement/wood ratio of 2.7, a small fraction-screened particle and supercritical curing. On the contrary, the composition of non-hammermilled or large fraction-screened particle at cement/wood ratio of 2.2 was poorer. Also, the feasibility for actual use of 3%-added, small PB particle-screened fraction was greatest of all the conventional curing treatments. Relative superiority of supercritical curing vs. conventional curing at dimensional stability was not so apparent as in strength properties. Through the thermogravimetric analysis, it was ascertained that the peak of a component $CaCO_3$ was highest, and the two weak peaks of calcium silicate hydrate and ettringite and $Ca(OH)_2$ were present in supercritical treatment. Accordingly, it was inferred that the increased formation of carbonates in board contributes to strength enhancement.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.3
• /
• pp.265-271
• /
• 2015

This study is intended to produce a PC (Precast Concrete) member without a steam curing process in developing the high early strength concrete satisfying the condition of 10MPa in compressive strength at the age of 6 hours, and is intended to ensure economic feasibility by increasing the turnover rate of concrete form. Hence, high early strength cement with high $C_3S$ content and the hardening accelerator of powder type accelerating the hydration of $C_3S$ was used. And the properties of concrete were evaluated according to the hardening accelerator mixing ratio (0, 1.2, 1.6, 2.0). No big difference was found from the tests of both slump and air content. When 1.6 % or higher amounts of the hardening accelerator were mixed, the compressive strength of 10MPa was achieved at the age of 6 hours. From the test results of autogenous (drying) shrinkage and plastic shrinkage, it can be seen that there was a difference according to hydration reaction rate due to the addition of the hardening accelerator. However, it was shown that no problem arose with crack and durability. And it was shown that resistance to freezing-thawing, carbonation, and penetration were excellent.

• Journal of the Korea Concrete Institute
• /
• v.17 no.4 s.88
• /
• pp.489-498
• /
• 2005

Recently, the deterioration of concrete structures have been increased by the damage from salt, carbonization, freezing & thawing and the others. Therefore, the measures for the deterioration of concretes have been taken. Among them, it has been often used that surface treatment which cut off the deterioration factors of durability by protecting the surface of concrete. The water proof and repair materials for concrete mainly use organic materials such as epoxy, these materials excel in intial bonding force and resistance to chemical agents. But they cause difference in the modulus of elasticity and the rate of shrinkage and expansion of concrete, and thus result in such problems as scaling and spatting in the progress of time. Therefore in this study it develop the performance Improving agent of concrete surface that can block a deterioration cause such as $CO_2$ gas, chloride ion and water from the outside and enhance waterproofing ability by reinforcing the concrete surface when applying it to concrete structures.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.4
• /
• pp.96-102
• /
• 2019

When GGBFS(Ground Granulated Blast Furnace Slag) with high blaine is incorporated in concrete, compressive strength in the initial period is improved, but several engineering problems arise such as heat of hydration and quality control. In this paper, compressive strength and durability performance of concrete with 3,000 Grade-low fineness slag are evaluated. Three conditions of concrete mixtures are considered considering workability, and the related durability tests are performed. Although the strength of concrete with 3,000 Grade slag is slightly lower than the OPC(Ordinary Portland Cement) concrete at the age of 28 days, but insignificant difference is observed in long-term compressive strength due to latent hydration activity. The durability performances in concrete with low fineness slag show that the resistances to carbonation and freezing/thawing action are slightly higher than those of concrete with high fineness slag, since reduced unit water content is considered in 3,000 Grade slag mixture. For the long-term age, the chloride diffusion coefficient of the 3000-grade slag mixture is reduced to 20% compared to the OPC mixture, and the excellent chloride resistance are evaluated. Compared with concrete with OPC and high fineness GGBFS, concrete with lower fineness GGBFS can keep reasonable workability and durability performance with reduced water content.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.22 no.3
• /
• pp.611-619
• /
• 2021

Porous asphalt pavement (PAP) has many functions, such as reducing accidents and decreasing noise. On the other hand, vulnerability is inevitable because PAP contains approximately 20% porosity. This study evaluated the effects of the maximum aggregate size (MAS), temperature, and porosity on the PAP durability. The indirect tensile strength measures durability. This study tested the samples that stayed dry and were moisturized by freezing and thawing for mixtures having the same porosity of 20% and MAS of 13mm, 10mm, and 8mm. The same test was performed on a mixture of 20% and 22% voids made of the same material with a MAS of 10mm. As a result, for 20% porosity, significant differences in the changes in MAS and temperature were found. A clear difference was observed between 8mm and 13mm under dry conditions, but there were no other significant differences in the MAS change. Furthermore, there was a clear difference in temperature for the change in porosity and temperature, but the gap in 2% porosity at 20% did not show a clear difference. Therefore, it is necessary to develop a more durable PAP through quantitative evaluations of the factors affecting the PAP durability.