• Proceedings of the Korea Concrete Institute Conference
• /
• 1991.04a
• /
• pp.111-116
• /
• 1991

In order to discuss the mechanical properties of carbon fiber reinforced polymer impregnated cement composties with silica powder, experimental studies on CFRC were carried out. The types of fiber used which are in CFRC are PAN-based carbon fiber and Pitch-based carbon fiber. To examine the effects of types, length, contents of carbon fibers and matrices, their properties of fresh and hardened CFRC were tested. According to the test results, compressive, tensile flexural strength of polymer impregnated CFRC were remarkably increased more than that of air cured and autoclaved CFRC. Also, polymer impregnated CFRC were considerably effective in improving thoughness, freezing-thaw resistance and loss of shrinkage compared with air cured and autoclaved CFRC.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.433-438
• /
• 2000

The purpose of this study is to examine the resistance of water-permeable concretes to freezing and thawing action. The water-permeable concretes with cement-aggregate ratio of 1:5.5(by weight) and two kinds of admixture content [SP : superplasticizer(0, 1.0%), HPAE : high performance air entraining agent(0.5, 1%)] used OPC(ordinary portland cement) as binder were prepared, and then tested for relative dynamic modulus of elasiticity, mass change, length change and durablity factor. It's been concluded from the test results that the superior relative dynamic modulus of elasiticity and durability factor of water-permeable concretes were obtained at superplaciticizer 1.0% after 300 cycles. The water-permeable concretes used superplasiticizer 1.0% having relative durability factor of 88% after 300 cycles.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.54-57
• /
• 2003

Scaling deterioration of port concrete structures due to the combined effects of chemical actions by seawater and the freeze-thaw action is also a problem which has not yet been fundamentally solved. Furthermore, deterioration of concrete surface was considered as accelerate factor of concrete durability tended to decrease. Therefore, we considered the scaling measuring method and decreasing influence of durability of concrete according to kind of binders, such as OPC, Slag, Slag+Fa, due to freeze and haw of sea water. As a results of this study, it was effective method of scaling deterioration of concrete, and confirmed the salt deterioration resistance effect to use slag binder against to sea water.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.30 no.3
• /
• pp.565-568
• /
• 2001

A study was conducted to investigate cryoprotectant effect of commercially produced oligosaccharides (IMO: isomalto-oligosaccharides, FO: fructo-oligosaccharides and GO: galacto-oligosaccharides) on beef protein and to compare their effectiveness to sucrose or a mixture of sucrose and sorbitol on freezing. The optimal addition level of cryoprotectants was determined by measuring $Ca^{2+}$-ATPase activity of sample treated with different concentration (0 to 12%) after freeze-thaw cycle. Since the stabilization effect was not dramatically increased above 8% sugar concentrations, the 8% was determined as an usage level. During frozen storage (at -18$^{\circ}C$ for 12 week), commercially produced oligosaccharides showed lower cryoprotection ability than sucrose but higher than sucrose+sorbitol as measured by protein solubilities and $Ca^{2+}$-ATPase activities.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1995.10a
• /
• pp.84-88
• /
• 1995

The results of an experimental study on manufacture and mechanical properties of concrete utilizing crushed sand and fly ash for construction materials are presented in theis paper. As the results show, the workability, compressive strength and freezing-thaw resistance were improved by proper contents of fly ash, replaced crushed sand, and air entraining agent. And the drying shinkage was decreased by proper contents of those. Also, the suitable weight contents of replacing ratio of crushed sand and weight ratio fly ash in concrete using crushed sand were in range of 30% and 15% respectively.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.04a
• /
• pp.1-6
• /
• 1996

Cellulose fiber reinforced cement composites manufactured by the slurry-dewatering process have found broad applications in thin cement products as replacement for asbestos cement. This paper focuses on the durability characteristics of these composites under different aging conditions. The effects of wetting-drying and freezing-thaw cycles, carbonation, and exposure to hot and humid environments on the structure and properties of cellulose fiber-cement composites were investigated. The predominant mechanisms of aging in the composites were identified through investigation of structure-property relationships. Measures to control these aging mechanisms were diversed and evaluated. Refined cellulose fiber-cement composites are shown to possess excellent durability characteristics under the effects of various aging processes.

• Reproductive and Developmental Biology
• /
• v.29 no.3
• /
• pp.155-162
• /
• 2005

The present study evaluated whether an exogenous antioxidants, taurine and $\alpha$-tocopherol, could, when added to the freezing extender, improve the post-thaw sperm characteristics, function, the level of reactive oxygen species (ROS) generation, and the level of lipid peroxidation (LPO) in frozen-thawed porcine semen. CASA (computer-aided sperm analysis), HOST (hypoos-motic swelling test), chemiluminescence using luminol and lucigenin and the detection of malondialdehyde for LPO was performed in frozen-thawed porcine sper-matozoa. The results obtained in these studies are as follows. While no beneficial effects of taurine and $\alpha$-tocopherol supplementation were visible in motility, viability, acrosome reaction, tail swelling patterns, and the generation of $O^{2-}$ of frozen-thawed porcine sper-matozoa, $H_{2}O_{2}$ was decreased by all treatments except taurine 50mM treatment. In conclusion the taurine and $\alpha$-tocopherol treatments during freezing reduced generation of reactive oxygen species and production of malondialdehyde in frozen-thawed porcine semen, and the ROS savangers may minimize various damages of spermatozoa during freezing.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.4
• /
• pp.153-161
• /
• 1998

Concrete structures has been deteriorated by and freezing the thawing due to temperature gap. This study was conducted to evaluate durability of concrete which are increasingly demanded recently. Therefore the research of durability must be executed for application of waste foundry sand concrete real structures. Concrete durability properties incorporating waste foundry sand was performed with the variable of W/C ratio. Sand/Waste foundry sand ratio and Air entrainment-Non air entrainment. Cylinder specimens were made and subjected to freezing and thawing cycle at -18$^{\circ}C$ and 4$^{\circ}C$. Dynamic modulus of elasticity were evaluated as F/T cycle increase. The results show that strength of concrete is increased the W/C ratio decrease, the Sand/Waste foundry sand ratio increases when the concrete contains AE agent and decreasing W/C ratio and AE concrete makes improved resistance of freezing and thawing improved. Especially, resistance of freezing and thawing is improved by Fine aggregate/Waste foundry sand ratio which is 50%, 25%, 0% in a row. Therefore it is turn out the waste foundry sand could be applied to concrete from the experiment.

• Journal of the Korean Geosynthetics Society
• /
• v.10 no.2
• /
• pp.73-79
• /
• 2011

Based on the results of Part 1 of our two-parts paper, the possibility on field applicability of CMDS(Coal Mine Drainage Sludge) mixed with bentonite and cement as a liner in landfill sites was investigated. The optimum moisture content that met the landfill liner condition was obtained when the ratio of CMDS: bentonite: cement was 1: 0.5: 0.3 in a lab-scale. The relative compaction was measured in 90.1%, which results for construction field have been generally acceptable. In this study, a large-scale Lysimeter($1.0m{\times}1.5m{\times}2.0m$) was used to simulate the effects of the layer on the freeze/thaw by -20 average temperature. The mixture after freezing/thawing showed compressive strength more than $5kg/cm^2$, which was satisfied with EPA standards. Initial permeability of CMDS was $7.10{\times}10^{-7}cm/s$ and permeability its mixture after freezing/thawing was increased to $9.80{\times}10^{-7}cm/s$. The change of temperature in the layers rises and falls with linear and temperature gradient keep maintain the present state. Moisture contents in the layers have not been radically changed. Through the leaching test determined by KSLT method, it was found that heavy metals excluding Zn and Ni were not leached out or leached out less than the standards during 7 cycles of freezing/thawing process. Since it shows the increased permeability about 1.5 times and slight change in moisture content, but it was satisfied with EPA standar through 7 cycles of freezing/thawing process, this mixture can be applied as a liner in landfill final cover system.

• Journal of The Geomorphological Association of Korea
• /
• v.20 no.3
• /
• pp.95-107
• /
• 2013

In order to examine the temperature regime responsible for periglacial processes, air and ground temperatures were monitored from October 2010 to May 2011 at a subalpine bare patch (1,710m asl) of Mt. Halla. Four thermistor sensor probes were installed at 55 cm above a ground surface and depths of 2 cm, 10 cm, and 20 cm, respectively. A mean air temperature is $-0.1^{\circ}C$, while mean ground temperatures are $1.8^{\circ}C$ at 2 cm, $2.6^{\circ}C$ at 10 cm and $3.2^{\circ}C$ at 20 cm deep. A mean monthly ground temperature at 2 cm deep demonstrates below $0^{\circ}C$ successively from January to March, while those at 10 cm and 20 cm deep show no sub-zero temperature. A total of 72 freeze-thaw cycle was observed in air temperature. However, the numbers in ground temperature reduced into 17 at 2 cm, 8 at 10 cm, and 3 at 20 cm deep. The cycles of air temperature and ground temperature at 2 cm deep mostly fluctuated diurnally, while those of ground temperature at 10 cm and 20 cm deep exhibited a several-daily oscillation. Snow cover over 55 cm high remained from January to early April, and it seemed to disappear completely on April 16. A seasonal frost of at least 2 cm thick was formed on late December and the isotherm of $0^{\circ}C$ descended slowly into 10 cm deep on late March to early April due to the insulating snow cover. It showed the maximum freezing depth of 20 cm on April 7 to 14 and then thawed rapidly so that the frozen ground did not longer after April 17. Periglacial processes are predominant during a freezing period than a thawing period when the ground surface is still covered with snow. The periglacial mass movement in the subalpine zone of Mt. Halla is mainly generated by frost creep in terms of the occurrence depth of diurnal freeze-thaw cycle and the maximum freezing depth of ground.