• Geomechanics and Engineering
• /
• v.34 no.1
• /
• pp.51-67
• /
• 2023

In this research, the degradation rate of physical properties of the Angouran pit bedrock (calc-schist) is first investigated under the specific numbers of freeze-thaw (F-T) cycles. Then, the durability of calc-schist specimens against the F-T cycle number (N) is examined considering the mechanical parameters, and using the decay function and half-time techniques. For this purpose, point load strength (I_S(50)), second durability index (I_d2), Brazilian tensile strength (BTS), and compressive (V_P) and shear (V_S) wave velocities of calc-schist specimens are measured after 0, 7, 15, 40, and 75 N. For comparing the degradation rate of mechanical properties of available rock types on the Angouran mine walls, these tests are also carried out on the limestone and amphibolite schist specimens beside the calc-schist. According to test results, the exponential regression models are developed between the mechanical parameters of rock specimen's and N variable. Also, the long-term durability of each rock type versus N is studied using the decay function and half-time techniques. Results indicated that the degradation rate differs for the above rock types in which amphibolite schist and calc-schist specimens have the highest and least resistance against the N, respectively. The obtained results from this study can play a key role in the optimal design of the mine's final walls.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.991-996
• /
• 2001

The long-term durability characteristics of high-early-strength concrete were assessed. The effect of long-term durability characteristics of high-early-strength concrete were investigated. In experiment, two different types of fiber were adopted for improvement of durability. High-early-strength fiber reinforced concretes using regulated-set cements are compared with high-early-strength concrete without fiber. The durability performance of the laboratory-cured high-early-strength concrete specimens was determined by conducting an accelerated chloride permeability, abrasion resistance, freeze-thaw, surface deicer salt scaling and wet-dry repetition test. The results indicated that incorporation of fibers enhance durability performance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.537-540
• /
• 2003

The effects of substituting cement with fly ash(10%, 15%, 20%) and different fiber addition(polypropylene, cellulose, poly vinyl alcohol), on the control of microcrack and enhanced durability performance of face slab concrete in CFRD was studied experimentally It was conducted experiments of plastic shrinkage of mortar and concrete, and drying shrinkage of concrete. Also, durability test were carried out the chloride permeability, abrasion resistance and freeze-thaw repetition. Through the experimental results, it was concluded that ploy vinyl alcohol fiber containing concrete was the most effective mixture in control of cracking and durability.

• Computers and Concrete
• /
• v.21 no.2
• /
• pp.149-156
• /
• 2018

This paper investigated the influence of binary and ternary blends of mineral admixtures in self-compacted mortar (SCM) on the fresh, mechanical and durability properties. For this purpose, 25 mortar mixtures were prepared having a total binder content of $640kg/cm^3$ and water/binder ratio between 0.41 and 0.50. All the mixtures consisted of Portland cement (PC), fly ash (FA) and silica fume (SF) as binary and ternary blends and air-entrained admixture wasn't used while control mixture contained only PC. The compressive and tensile strength tests were conducted for 28 and 91 days as well as slump-flow and V-funnel time tests whilst freeze-thaw (F-T) resistance and capillary water absorption tests were made for 91-day. Finally, in general, the use of SF with FA as ternary blends improved the tensile strength of mortars at 28- and 91-day while the use of SF15 with FA increased the compressive strength of the mortars compared to binary blends of FA. SCM mixtures with ternary blends had lower the sorptivity values than that of the mortars with binary blends of FA and the control mixture due to the beneficial properties of SF while the use of FA with SF as ternary blends induced the F-T resistance enhancement.

• Advances in concrete construction
• /
• v.16 no.5
• /
• pp.269-276
• /
• 2023

In order to study the effect of rubber particle size and admixture on the frost resistance of self-compacting concrete, three self-compacting concrete specimens with equal volume replacement of fine aggregate by rubber particles of different particle sizes were prepared, while conventional self-compacting concrete was made as a comparison specimen. The degradation law of rubber aggregate self-compacted concrete under freeze-thaw cycles was investigated by fast-freezing method test. The results show that the rubber aggregate has some influence on the mechanical properties and freeze-thaw durability of the self-compacting concrete. With the increase of rubber aggregate, the compressive strength of self-compacting concrete gradually decreases, and the smaller the rubber aggregate particle size is, the smaller the effect on the compressive strength of the matrix; rubber aggregate can improve the frost resistance of self-compacting concrete, and the smaller the rubber particle size is, the more obvious the effect on the improvement of the frost resistance of the matrix under the same dosage. Through the research of this paper, it is recommended to use 60~80 purpose rubber aggregate and the substitution rate of 10% is chosen as the best effect.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04a
• /
• pp.293-298
• /
• 1998

The result of an experimental study on the mechanical properties and durability of polypropylene fiber reinforced concrete are presented in this paper. This study has been performed to obtain the properties of PFRC such as strength, toughness and durability. The test variables are fiber content, fiber types, W/C ratio. PFRC shows the highest strength when the polypropylene fiber contents were increased to 2.0 vol.%. Also, freeze-thaw resistance and carbonation were somewhat more improved than plain concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1995.10a
• /
• pp.80-83
• /
• 1995

In order to develope and apply high-performance steel fiber reinforced concrete (SFRC), the effects of steel fibers on durability and long-term deformation of SFRC due to various mixing conditions have been studied. As the test result show, the manufacturing process technology of industrial SFRC is developed And the durability of SFRC such as freeze-thaw, resisteance abrasion resistance are significantly improved, the drying shrinkage of SFRC, is remarkably decreased by increasing the steel fiber contents than plain concrete

• Proceedings of the Korean Geotechical Society Conference
• /
• 2005.03a
• /
• pp.1412-1419
• /
• 2005

Preventing the infiltration of rainwater into the landfill site is the main purpose of the final cover in landfill sites. Compacted clay layer or geomembrain have been used as a conventional landfill final cover. But they have several disadvantages when damages might occur due to puncturing, differential settlement and desiccation or freeze and thaw. For this reason, as an alternative method SRSL(Self Recovering Sustainable Liner) has been developed. Adopting the precipitation reaction of two chemical material, by forming precipitates that fill the pores, and lower the overall permeability of the liner. The advantage of this method is that when fracture of the liner occurs the remaining reactants of the two layers form precipitates that fill the fracture and recover the low permeability of the liner. In this study, the recovering ability of the SRSL with a crack due to the seasonal variation or differential settlements was investigated by permeability tests. And in order to estimate the durability of the SRSL after freeze/thaw and desiccation, uniaxial compression strength tests were performed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.261-262
• /
• 2009

The prevent methods of Alkali-Silica Reaction (ASR) are studying after the failure cases by ASR were reported in Korea. In this study, the freeze-thaw test and scaling test for premixed fly ash cement were performed. The ratio of fly ash and cement is 20 percent and 80 percent by weight of total cementious material. The results show that the dynamic modulus after 300 cycles the freeze-thaw test for most of specimen except the specimen have less 3% air was more than 90 % and the loss of weigh the specimen after 50 cycles scaling test was less than 1kg/$m^3$.

• International Journal of Highway Engineering
• /
• v.19 no.6
• /
• pp.129-137
• /
• 2017

PURPOSES : The purpose of this study is to develop bridge deck concrete materials based on ordinary Portland cement concrete, and to evaluate the applicability of the developed materials through material properties tests. METHODS : For field implementation, raw material (cement, fine aggregate, and coarse aggregate) properties, fresh concrete properties (slump and air content), strength (compressive, flexural and bond strength) gain, and durability (freeze-thaw resistance, scaling resistance, and rapid chloride penetrating resistance) performance were evaluated in the laboratory. RESULTS : For the selected binder content of $410kg/m^3$, W/B = 0.42, and S/a = 0.48, the following material performance results were obtained. Considering the capacity of the deck finisher, a minimum slump of 150 mm was required. At least 6 % of air content was obtained to resist freeze-thaw damage. In terms of strength, 51.28 MPa of compressive strength, 7.41 MPa of flexural strength, and 2.56 MPa of bond strength at 28 days after construction were obtained. A total of 94.9 % of the relative dynamic modulus of elasticity after 300 cycles of freeze-thaw resistance testing and $0.0056kg/m^2$ of weight loss in a scaling resistance test were measured. However, in a chloride ion penetration resistance test, the result of 3,356 Coulomb, which exceeds the threshold value of the standard specification (1000 Coulomb at 56 days) was observed. CONCLUSIONS : Instead of using high-performance modified bridge deck materials such as latex or silica fume, we developed an optimum mix design based on ordinary Portland cement concrete. A test construction was carried out at ramp bridge B (bridge length = 111 m) in Gim Jai City. Immediately after the concrete was poured, the curing compound was applied, and then wet mat curing was applied for 28 days. Considering the fact that cracks did not occur during the monitoring period, the applicability of the developed material is considered to be high.