• Computers and Concrete
• /
• v.22 no.5
• /
• pp.449-459
• /
• 2018

Concrete is one of the most widely used construction materials in the world. Producing economical and durable concrete is possible by employing pozzolanic materials. The aim of this study is to underline the possibility of the utilization of natural zeolite in producing concrete and investigate its effects basically on the strength and durability of concrete. In the production of concrete mixes, Portland cement was replaced by the natural zeolite at ratios of 0%, 10%, 15%, and 20% by weight. Concretes were produced with total binder contents of $300kg/m^3$ and $400kg/m^3$, but with a constant water to cement ratio of 0.60. In addition to compressive and flexural strength measurements, freeze-thaw and high temperature resistance measurements, rapid chloride permeability, and capillary water absorption tests were performed on the concrete mixes. Compared to the rest mixes, concrete mixes containing 10% zeolite yielded in with the highest compressive and flexural strengths. The rapid chloride permeability and the capillary measurements were decreased as the natural zeolite replacement was increased. Freeze-thaw resistance also improved significantly as the replacement ratio of zeolite was increased. Under the effect of elevated temperature, natural zeolite incorporated concretes with lower binder content yielded higher compressive strength. However, the compressive strengths of concretes with higher binder content after elevated temperature effect were found to be lower than the reference concrete.

• Geomechanics and Engineering
• /
• v.28 no.4
• /
• pp.375-384
• /
• 2022

The glacial tills and shales in Midwestern states of the USA often show strength degradation after construction. They are often in need of applying soil modification techniques to remediate their strength degradation with weathering process. This study investigated the weathering durability of these natural soils and biopolymer treated soils by comparing direct shear test results for wet-dry and wet-freeze-thaw-dry cycled specimens. The tests showed that untreated glacial tills maintained only 62% and 50% initial shear strength after eight wet-dry cycles and eight wet-freeze-thaw-dry cycles, respectively. These untreated soils could not withstand by themselves after 16 weathering cycles. The same soils treated with 1.5% (by dry weight) food-grade Xanthan gum maintained 140% and 88% initial shear strength of untreated soils after 16 weathering cycles for wet-dry cycles and wet-freeze-thaw-dry cycles, respectively. The same soils treated with 1.5% (by dry weight) Gellan gum maintained 82% and 60% initial shear strength of untreated ones after 16 weathering cycles, respectively. Similar results were obtained for crushed shales, manifesting that the biopolymerization method may be adopted as a new eco-friendly method to enhance the weathering durability of these problematic soils of glacial tills and shales.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.4
• /
• pp.128-135
• /
• 2016

In the current concrete structure of the highway is still the major problem most of concrete deterioration caused by the freeze-thaw and deicing salt, which is of issues that are not completely resolved. In particular, a single freezing event does not cause much harm, durability of concrete under multi-deterioration environment by repeated freeze-thaw and deicing salt is rapidly degraded and reduce its service life. In this study, the exposure environmental condition according the regional highway points were established. The damage condition and chloride content of the concrete at general and severe environmental exposure condition were also investigated. In addition, the experimental test of chloride ion permeability, scaling resistant and freeze-thaw resistance were carried out to improve the durability of the mechanical placing concrete of subsidiary structure. According to the results of this study, in observation of concrete surface condition, the concrete exposed by severe environmental condition showed broad ranges of damage with high chloride contents. Meanwhile, the water-binder(W/B) ratio and the less water content, and fly ash concrete than the specified existing mix proportion is significantly improved the durability. Also, the optimal mix proportion derived for test is satisfied the strength and air contents, water-binder ratio, and durability criteria of concrete specifications, as well as service life seems greatly improved.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.6
• /
• pp.144-151
• /
• 2023

In this study, a database was established by collecting experimental results on various concrete mixtures subjected to freeze-thaw cycles, based on which an artificial neural network-based prediction model was developed to estimate durability resistance of concrete. A regression analysis was also conducted to derive an equation for estimating relative dynamic modulus of elasticity subjected to freeze-thaw loads. The error rate and coefficient of determination of the proposed artificial neural network model were approximately 11% and 0.72, respectively, and the regression equation also provided very similar accuracy. Thus, it is considered that the proposed artificial neural network model and regression equation can be used for estimating relative dynamic modulus of elasticity for various concrete mixtures subjected to freeze-thaw loads.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.23-30
• /
• 2011

In this study, deterioration degrees of concrete were investigated at laboratory under seawater attack and cycling freeze-thaw, which are major durability performance deterioration factors of concrete. Deteriorations of mixed concrete using Portland & blended cement were examined by instrumental analysis of changes in relative dynamic modulus of elasticity and compressive strength. After 520 cycles of freeze-thaw, relative dynamic modulus of elasticity and compressive strength of concrete mixed with normal Portland and LHC over 75% showed relatively low resistance of approximately 44% of those values of SRC. Concrete replaced with 50% fine powder of blast furnace slag showed the most excellent freeze-thaw resistance among the tested blended cement concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.6
• /
• pp.148-156
• /
• 2022

Although most domestic concrete structures are simultaneously exposed to freeze-thaw and chloride environments, concrete durability in the field is evaluated by each single action, and the evaluation of chloride-caused damage of concrete requires additional indoor experimental analysis of chloride contents by coring samples from structures in the field. However, in Korea, policies to strengthen facility maintenance, such as 「Special Act on the Safety Control and Maintenance of Establishments」 and 「Framework Act on Sustainable Infrastructure Management」, have been established and implemented since 2018 and facilities subject to safety inspection management by the government and local governments increases, the effective simplification technology for the inspection and diagnosis of concrete structure is needed. Therefore, this study attempted to evaluate the possibility of determining the acceleration chloride penetration of freeze-thaw damaged concrete by using the surface rebound value. For this purpose, concrete specimens already having freeze-thaw damage by exposure to the freeze-thaw acceleration environment were immersed in chloride water. After that, the acceleration relationship of chloride penetration according to freeze-thaw damage was analyzed using the amount of chloride contents in concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.5
• /
• pp.161-168
• /
• 2008

The freeze-thaw deterioration and chloride attack, which are the typical degradation factors for durability of marine concrete, are significantly affected by pore structures in terms of penetration and diffusion. These pore structures of concrete are closely related to the types and amount of AE agent, used to guarantee the resistance of freeze-thaw deterioration, and the elapsed time before concrete pouring. This paper evaluates the durability of concrete based on the results of tests on cylinder specimens and core specimens from mock-up members with different air content of 4~6% and 8~10%, respectively. According to the test results, the air content of hardened concrete is 2.5~5.2% at 7 days and 2.4~5.1% at 28 days. These air contents are about half of the initial values just after the concrete mixing. Judging from the amount of scale after the freeze-thaw test completed, air content of 8~10% is slightly more beneficial against the deterioration of concrete than air content of 4~6%. Meanwhile, the core specimens from mock-up members exhibit somewhat unfavorable freeze-thaw deterioration and chloride migration characteristic compared with the cylinder specimens tested in the laboratory under the same mixing condition, as to show 106% in freeze-thaw test and 160% in chloride diffusion coefficient test, respectively.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.1
• /
• pp.49-58
• /
• 2017

The phenomena that we experience in everyday life such as snow, rain, wind, and temperature are referred to as weather, and the average state of atmospheric phenomena that occur over a long period of time in a specific region is referred to as climate. In addition, significant variation of climate compared to the average state is referred to as climate change. Concrete structures can have various problems when exposed to elements. Among the problems, the freeze-thaw problem due to extreme climatic factors such as heavy rain and snowfall has become a particularly significant issue recently. The concrete that has been subjected to repeated freeze-thaw rather than too high or low temperature shows serious degradation of durability, and the performance of structures with degraded performance is difficult to recover. Therefore, in this study, concrete durability performance with respect to freeze-thaw from curing conditions change due to wind speed and sunshine exposure time. Concrete freeze-thaw experiment are performed. using wind speed and sunlight exposure time. Also, performance based evaluation through the satisfaction curve based on the freeze-thaw test results are performed.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.05a
• /
• pp.259-260
• /
• 2018

This study evaluated the compressive strength, freeze-thaw and sulfate resistance characteristics of concrete using CFBC-Ash. The CFBC-Ash was adjusted to a particle size of 75 ㎛ or less and using by increasing the fineness of powder through milling. As a result, it was confirmed that the concrete using CFBC-Ash shows a high compressive strength, durability. Also, it is confirmed that CFBC-ash can be used as a concrete binder.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.765-770
• /
• 2001

Concrete curbing blocks have been widely used in construction of roadways because they are easy too manufacture and cheap. But recently stone curbs are taking away the role from concrete curbs, because the durability of concrete curbs is inferior to stone curbs. Especially freeze-thaw effect on concrete is the most important cause that damages concrete curbs. The aim of this study is to increase the durability of concrete curbs. The concrete curbs that have been manufactured are extremely damaged below 60 cycles of freeze-thaw, but the ones that was manufactured with admixtures that entrains air are maintaining over 87% of relative dynamic modulus.