• Restorative Dentistry and Endodontics
• /
• 제25권1호
• /
• pp.56-62
• /
• 2000

The purpose of this study was to assess the effects of restorative materials on the marginal leakage of wedge-shaped class V cavity. The study was performed in vitro in 25 defect-free permanent, extracted teeth. Wedge-shaped class V cavities were prepared and then the teeth were randomly selected and restored according to the following. Group A : restoration with Tetric Ceram(composite resin) Group B : restoration with Tetric flow(flowable resin) Group C : restoration with Compoglass after acid etching(compomer) Group D : restoration with Compoglass(compomer) Group E : restoration with Fuji II LC improved(resin-modified GIC) After thermocycling, the specimens were immersed in 5% basic fuchsin solution for 6 hours and sectioned longitudinally through the center of the restoration. The degree of marginal leakage was measured as the extent of dye penetration under the stereomicroscope. The data were analysed using one-way ANOVA. When significant differences found, multiple comparisons were made using Duncan's Multiple Range Test. The results were as follows: 1. The occlusal margins of all groups except for Fuji II LC improved showed lesser leakage than gingival margins and there was statistically significant difference(p<0.05). 2. At the occlusal margins, group A, B showed same marginal leakage scores, and others were decreased as group C, D, E in that order. There were statistically significant difference between group A, Band group D, E, group C and group E(p<0.05). 3. At the gingival margins, group B, C showed same marginal leakage scores, and others were decreased as group A, D, E in that order. But there was statistically significant difference between group B, C and group E(p<0.05). 4. In the Compoglass restoration, acid-etching technique was beneficial for marginal sealing ability at all of margins. But there was no statistically significant difference (p>0.05). In the restorations for wedge-shaped class V cavities, resin restoration with acid etching technique is recommended.

• Restorative Dentistry and Endodontics
• /
• 제48권3호
• /
• pp.30.1-30.11
• /
• 2023

Objectives: This study verified the possibility of cementing fiberglass-reinforced posts using a flowable bulk-fill composite (BF), comparing its push-out bond strength and microhardness with these properties of 3 luting materials. Materials and Methods: Sixty endodontically treated bovine roots were used. Posts were cemented using conventional dual-cured cement (CC); self-adhesive cement (SA); dual-cured composite (RC); and BF. Push-out bond strength (n = 10) and microhardness (n = 5) tests were performed after 1 week and 4 months of storage. Two-way repeated measures analysis of variance (ANOVA), 1-way ANOVA, t-test, and Tukey post-hoc tests were applied for the push-out bond strength and microhardness results; and Pearson correlation test was applied to verify the correlation between push-out bond strength and microhardness results (α = 0.05). Results: BF presented higher push-out bond strength than CC and SA in the cervical third before aging (p < 0.01). No differences were found between push-out bond strength before and after aging for all the luting materials (p = 0.84). Regarding hardness, only SA presented higher values measured before than after aging (p < 0.01). RC and BF did not present 80% of the maximum hardness at the apical regions. A strong positive correlation was found between the luting materials' push-out bond strength and microhardness (p < 0.01, R² = 0.7912). Conclusions: The BF presented comparable or higher push-out bond strength and microhardness than the luting materials, which indicates that it could be used for cementing resin posts in situations where adequate light curing is possible.

• 구강회복응용과학지
• /
• 제34권2호
• /
• pp.89-96
• /
• 2018

목적: 본 연구의 목적은 비스 아크릴 복합 레진의 수리 시 지연시간, 표면처리, 수리재료가 미치는 영향을 전단 결합강도 비교를 통해 알아보고, 폴리메틸 메타크릴레이트 레진을 이용한 비스 아크릴 복합 레진 수리의 효용성을 평가하고자 하는 것이다. 연구 재료 및 방법: 총 90개의 비스 아크릴 복합 레진 시편을 제작하였고, 지연시간, 표면처리, 수리재료에 따라 10개씩 9개의 실험군으로 분류하였다. 각각의 시편들은 제작 직후 만능시험기를 사용하여 전단 결합강도를 측정하였고, 통계분석 프로그램(IBM SPSS statistics 20)을 이용하여 분석하였다. 전단 결합강도 측정 후 시편의 파절 단면을 관찰하였다. 결과: 시편 제작 직후, 접착제(bonding agent)를 이용하여 광중합형 유동성 복합 레진을 접착한 실험군에서 가장 높은 전단 결합강도를 보였다($17.54{\pm}3.14MPa$). 결론: 비스 아크릴 복합 레진을 수리할 때 경과시간에 따라 재제작 여부를 고려해야 하며, 효과적인 수리를 위해 사용부위나 목적에 따라 알맞은 재료와 표면처리 방법을 고려하는 것이 바람직할 것이다.

• 대한소아치과학회지
• /
• 제33권2호
• /
• pp.221-232
• /
• 2006

본 연구는 단계별 광중합 방법이 복합레진의 중합 및 수축 응력에 미치는 효과를 비교, 평가하고자 자연치를 대상으로 와동을 형성하고 할로겐 광중합기와 LED 광중합기의 통법에 의한 연속 조사 및 단계별 조사법으로 각각 복합레진을 중합시킨 후 수축 응력을 측정하고 주사전자현미경을 통해 수복물과 와동의 계면부에서 접착 상태를 관찰하여 다음과 같은 결과를 얻었다. 1. 모든 군에서 광중합 직후에는 일시적으로 팽창되었다가 초기에는 급격한 수축 응력의 증가를 보였고 시간이 경과될수록 수축 응력의 증가가 완만해지는 경향을 보였다(P<0.05). 2. 동일한 광조사 군내에서는 hybrid형인 Filtek $Z-250^{TM}$군보다는 flowable형인 $Filtek\;flow^{TM}$군이 더 적은 수축 응력을 보였다. 3. Filtek $Z-250^{TM}$군에서는 LED 단계별 조사군이 수축 응력 이 가장 적게 나타났다(P<0.05) 4. $Filtek\;flow^{TM}$군 역시 LED단계별 조사군이 수축 응력이 가장 작게 나타났으나(P<0.05) Filtek Z-250군에서와 같이 다른 조사군에 비해 많은 차이를 보여주지는 못했다. 5. 주사전자현미경으로 관찰한 복합레진과 와동벽과의 접합 상태는 긴밀한 상태를 보였으나 LED 조사군에서 일부 틈이 관찰되었다. 이상의 결과를 종합해 보면 hybrid형 복합레진의 경우 단계별 중합방식을 사용할 경우 단일광도의 중합방식에 비해 수축 응력을 감소시킬 수 있고 적절한 변연 적합상태를 유지시킴으로써 임상적으로 고광도 LED 광중합기의 경우 단계별 중합방식의 사용이 유리하다고 사료된다.

• 구강회복응용과학지
• /
• 제34권4호
• /
• pp.290-296
• /
• 2018

목적: 본 연구의 목적은 치아 스플린팅에 사용되는 레진계 재료들의 두께에 따른 중합 능력을 평가하는 것이다. 연구 재료 및 방법: 레진계 스플린팅 재료로 개발된 Light-Fix와 G-FIX, 수복용과 스플린트용으로 사용 가능한 고흐름성 복합레진인 G-aenial Universal Flo를 사용하여 직경 5 mm, 두께 2, 3, 4, 5 mm의 시편을 각각 10개씩(총 120개) 제작하였다. 비커스 경도 측정기를 이용하여 시편 상면과 하면의 미세경도값을 측정하였다. 각 두께에서 복합레진의 중합정도를 95% 유의수준에서 independent T-test를 이용하여 통계적으로 분석하였다. 결과: Light-Fix와 G-FIX는 두께에 상관없이 중합도의 차이를 보이지 않았다. G-aenial Universal Flo는 3 mm 두께부터 유의하게 낮은 중합도를 보였다. 결론: 스플린팅 전용 레진계 재료인 Light-Fix와 G-FIX는 5 mm 두께까지 적절한 광중합이 가능할 것으로 사료된다.

• Restorative Dentistry and Endodontics
• /
• 제44권4호
• /
• pp.37.1-37.10
• /
• 2019

Objectives: This study evaluated the bond strength of various fiberglass post cementation techniques using different resin-based composites. Materials and Methods: The roots from a total of 100 bovine incisors were randomly assigned to 5 treatment groups: G1, post + Scotchbond Multi-Purpose (SBMP) + RelyX ARC luting agent; G2, relined post (Filtek Z250) + SBMP + RelyX ARC; G3, individualized post (Filtek Z250) + SBMP; G4, individualized post (Filtek Bulk-Fill) + SBMP; G5, individualized post (Filtek Bulk-Fill Flow) + SBMP. The samples were subjected to the push-out (n = 10) and pull-out (n = 10) bond strength tests. Data from the push-out bond strength test were analyzed using 2-way analysis of variance (ANOVA) with the Bonferroni post hoc test, and data from the pull-out bond strength test were analyzed using 1-way ANOVA. Results: The data for push-out bond strength presented higher values for G2 and G5, mainly in the cervical and middle thirds, and the data from the apical third showed a lower mean push-out bond strength in all groups. No significant difference was noted for pull-out bond strength among all groups. The most frequent failure modes observed were adhesive failure between dentine and resin and mixed failure. Conclusions: Fiberglass post cementation using restorative and flowable bulk-fill composites with the individualization technique may be a promising alternative to existing methods of post cementation.

• 대한소아치과학회지
• /
• 제32권1호
• /
• pp.132-135
• /
• 2005

본 연구의 목적은 유전치 심미수복의 새로운 방법으로 glass fiber를 이용한 강화형 strip crown의 사용을 제시하고자 하는 것이다. Strip crown의 제작을 위하여 celluloid crown form(3M, USA)과 복합레진은 Z100(P shade, 3M, USA)을, 유동성 복합레진은 Aeliteflo(Bisco Inc., USA)를 사용하였다. 상아질 결합제는 Clearfil SE Bond(Kuraray Medical Inc., Japan)를 사용하였고 강화를 위하여 그물형 glass fiber(TESCERA Fiber Mesh, Bisco Inc, USA)를 사용하였다. 적절한 크기의 celluloid crown form을 성형하여 삭제된 치아에 시적한 후 레진 접착제와 유동성 복합레진으로 처리한 그물형 glass fiber를 설측 내면에 삽입하고 광중합하였다. 잔여 공간에 복합레진을 채우고 치아에 끼운 다음 광중합하였다. 복합레진의 심미성은 유지하면서 glass fiber로부터 기계적 장점을 얻을 수 있을 것으로 사료된다. 새로운 강화형 strip crown의 물성에 대한 후속연구가 필요하다.

• 치위생과학회지
• /
• 제12권5호
• /
• pp.477-485
• /
• 2012

본 연구는 레진 종류별 착색음식물별 착색시간별 착색정도와 연마, 과산화수소에 의한 미백 후의 색 변화를 관찰하여 착색과 미백이 레진의 CIELAB 색 표시계와 반사율에 미치는 영향을 알아보고자 한하였다. 시편은 동일 회사의 전구치부겸용 레진(A2), 유동형 레진(A2)을 가로, 세로 11 mm, 높이 3 mm의 직육면체모양으로 30초간 광중합한 시편 총 36개를 사용하였다. 착색원으로는 김치국물, 고추장, 카레, 블루베리즙, 홍차와 대조군으로 증류수를 사용하였으며 각 레진당 음식물별 3개의 시편을 사용하였고 측정은 윗면과 아랫면을 측정하여 각 6개면을 측정하였다. 착색기간은 총 8일, 35% 과산화 수소에 의한 미백은 1시간이 소요되었고, 음식물의 시간에 따른 착색 정도와, 미백 후의 반사율과 색값은 분광광도계를 이용하여 측정하였다. 그 결과, 1. 음식물별 시간에 따른 착색의 정도는 전구치부겸용 레진과 유동형 레진 모두에서 착색 1일차부터 L, a, b값과 반사율에서 모두 통계적으로 유의한 차이가 있었으며(p<0.05), 그 중 블루베리와 카레의 L, a, b값 변화가 크게 나타났다. 2. 음식물별 시간에 따른 착색후 반사율은 블루베리와 고추장이 대조군에 비해 유의하게 감소하였기 때문에(p<0.05) 같은 L, a, b값이더라도 블루베리, 고추장 착색 레진이 시각적으로 더 어둡게 보였다. 3. 전구치부겸용 레진은 과산화수소 미백과 연마를 한 경우가 단일 방법에 비해 ${\Delta}{E_{ab}}^2$의 값이 유의하게 변하였다(p=0.022). 그러나, 유동형 레진에서는 미백 방법에 따른 유의성은 없었다(p=0.385). 레진의 색 안정성을 위해서 착색이 심한 카레와 블루베리의 섭취빈도를 낮추도록 하거나 섭취 후 가급적 빠른 시간내에 입안을 헹구는 것이 레진수복물의 색 안정성을 유지시킬 것으로 사료되었다.

• 대한소아치과학회지
• /
• 제47권3호
• /
• pp.320-326
• /
• 2020

이 연구의 목적은 최근 소개된 alkasite 수복재료의 압축강도와 미세경도를 글라스아이오노머 시멘트와 유동성 복합레진과 비교하여 alkasite 수복재의 물성을 예측하는 것이었다. 압축강도와 비커스 미세경도 측정을 위해 각 재료당 20개의 시편을 제작하였다. 만능시험기를 사용하여 초 당 1 mm 횡단 속도 하에서 압축강도를 측정하였으며, 미세경도는 비커스 미세경도 측정기를 사용하여 보압 시간(dwelling time) 10초 조건 하에서 500 g의 힘을 가해 시편 제작 1시간, 1일, 7일, 14일, 21일, 35일 후에 측정하였다. 연구결과 압축강도는 복합레진이 가장 높았으며 alkasite, 글라스아이오노머 시멘트 순이었다. 미세경도 측정 결과 복합레진은 연구기간동안 미세경도의 변화가 없었으며 시편제작 1시간 후, 1일차, 7일차 측정까지 가장 높은 미세경도를 보였다. 글라스아이오노머 시멘트의 경우 7일차까지 미세경도가 증가하여 복합레진과 차이가 없어진 반면, alkasite는 14일차까지 서서히 미세경도가 증가하다가 이후 다시 감소하는 양상이 관찰되었다.

• 한국치위생학회지
• /
• 제12권3호
• /
• pp.533-541
• /
• 2012

Objectives : The purpose of this study was to evaluate the effects of tooth bleaching agent contained 35% hydrogen peroxide on the color, microhardness and surface roughness of tooth-colored restorative materials. Methods : Four types of tooth-colored restorative materials, including a composite resin(Filtek Z350 ; Z350), a flowable composite resin(Filtek P60 : P60), a compomer(Dyract$^{(R)}$ AP ; DY), and a glass-ionomer cement(KetacTM Molar Easymix ; KM) were used in the study. The specimens($8mm{\times}5mm$) were made by using a customized acrylic mold. Each material was divided into two groups equally(n=40) : experimental group(35% HP) and control group(distilled water). 35% HP group was treated 30 mim/5 days for 15 days. Each 30 minute treatment session consisted of two 15 minute cycles of gel application with 20 second light exposure. The authors measured the color, microhardness, and roughness of the specimens before and after bleaching. The data were analyzed with ANOVA and T-test. Results : 35% HP group showed an apparent color change(${\Delta}E^*$) than control group. In particular, DY and KM showed a noticeable color change and statistically significant differences(p<0.05). 35% HP group showed a reduction in microhardness. Z350 and P60 does not have a statistically significant difference(p>0.05), DY and KM showed a statistically significant difference(p<0.05). Percentage microhardness loss(PML) of control group was 0.6 to 5.5% in the group, 35% HP group was 6.6 to 34.6%. Roughness was increased in 35% HP group after bleaching. Especially DY and KM were significantly increased(p<0.05). Conclusions : Bleaching agents may affect the surface of existing restorations; therefore, they should not be used indiscriminately when tooth-colored restorations are present.