• 한국가구학회지
• /
• 제11권1호
• /
• pp.61-68
• /
• 2000

This study was carried out to investigate the effect of grain and veneer thickness on drying rate, required energy consumption, and drying defects such as checking, end waving, and burning during a far-infrared radiation drying process of decorative veneers of hard maple and beech. Most of the veneer could be dried from green to in-use moisture content within 30 to 360 seconds. The drying rates were significantly affected by veneer thickness, but there was little difference between edge-and flat-sliced veneers. The formation of checking during drying test was none or very slight. The percentages of the veneers defected by checks were higher in the flat-sliced veneers than in the edge-sliced veneers. The maximum end wavinesses in the flat-sliced veneers were almost 1.6 to 3 times larger than that in the edge-sliced veneers. All veneers were fee from burned marks during drying test.

• Journal of the Korean Wood Science and Technology
• /
• 제42권4호
• /
• pp.407-419
• /
• 2014

잣나무, 리기다소나무, 낙엽송, 백합나무 등 수종과 두께가 다른 평단판 및 단판롤(롤 형태의 단판)을 고정형 마이크로파로 가열하여 가열 전후 형상, 표면 함수율, 함수중량 변화와 표면 열분포를 분석한 결과는 다음과 같다. 평단판의 경우 마이크로파 가열에 따른 품질상태는 비교적 양호한 것으로 나타났지만, 약간의 뒤틀림이 발생하였으며, 이는 비균일 건조응력에 따른 변형과 고정형 마이크로파 장비의 특성상 단판 형태로 가열 시 국부적인 조사가 이루어진 영향이 컸기 때문으로 판단된다. 단판롤 형태의 마이크로파 가열 특성은 가열 후 품질 모두 양호하였으며, 특히 평단판에서 나타난 뒤틀림 등의 결함은 없는 것으로 나타났다. 또한 열분포 및 확산 등이 매우 안정적으로 이루어진 것으로 판단되며, 이러한 열분포는 표면 함수율 분포 및 함수중량 감소에 많은 영향을 미치는 것으로 나타났다. 따라서 단판롤 형태는 수종 및 두께에 따라 출력과 조사시간 등 충분한 시험이 실시된다면, 고정형 장비에서도 충분한 건조효율을 나타낼 수 있을 것으로 판단된다.

• 한국가구학회지
• /
• 제10권2호
• /
• pp.29-36
• /
• 1999

During a radio-frequency/vacuum plus press drying process of some hardwood veneers for decoration we investigated the effect of a grain and thickness of a veneer sheet on drying rates, variations of final moisture content within a bundle of veneer sheets, and formation of checking, end waving, and burning mark. About thirty three hundreds sheet of veneer could be dried in sixty five hours from green to in0-use moisture content, and a final moisture content was significantly effected by initial moisture content of veneer. There were nearly variations in a final moisture content among the veneer sheets in the same bundle. A checking was never found in a edge-sliced veneer, and very slight in a flat-sliced veneer of ash and red oak. There were no end waving and no burning mark in all veneer sheets.

• 대한치과보철학회지
• /
• 제49권4호
• /
• pp.308-315
• /
• 2011

연구 목적: IPS Empress Esthetic$^{(R)}$ system의 ingot은 다양한 반투명도를 가지고 있지만, 실제 다양한 색조의 자연치를 배경으로 각각의 ingot을 laminate veneer로 제작했을 때 어느 정도의 차폐능력을 나타내는지 알 수 없다. 본 연구의 목적은 반투명도가 서로 다른 ingot으로 제작한 IPS Empress Esthetic$^{(R)}$ laminate veneer 수복 시 다른 색상의 지대치상에서 최종 색조의 차이(color difference, ${\Delta}E$)를측정, 분석해서 그 차폐효과를 평가하고, 최종 색조에 미치는 영향을 알아보고자 하였다. 연구 재료 및 방법: Laminate veneer 수복을 위해 삭제된 6가지 다른 색조(A1, A3, A4, B2, B3, C3)의 자연치아 위에 반투명도가 서로 다른 6가지 IPS Empress Esthetic$^{(R)}$ ingot (E 01, E 03, E OC1, E TC1, E TC2, E TC3)으로 제작된 총 두께 0.6 mm의 도재 시편들을 translucent shade의 시적용 합착제로 시적한 뒤 각 시편 조합의 색조를 색채계(colorimeter)를 이용하여 측정하였다. 서로 다른 색조의 지대치아 위에서 측정된 도재시편들의 색차를 비교, 분석하였다. 결과: 지대치 색조 및 coping의 반투명도에 따라서 laminate veneer 수복물의 최종 색조가 다르게 나타났다(P<.05). 모든 도재 시편에서 A3, B3, 그리고 C3 shade를 가진 지대치들 사이의 평균 색차값(${\Delta}E$)이 2.7 이하로 나타났고, 지대치들 간의 색조가 A3 와 A4, B3 와 A4, 그리고 C3 와 A4 인 경우 평균 색차값은 몇 가지 도재 시편에서 2.7 이하를 나타내어 laminate veneer 수복물에 의한 지대치 색조의 차폐효과를 보여 주었다. 반면, A1 과 B2 shade의 지대치는 다른 지대치들과 비교하여 높은 색조 차이를 보였으며, 특히A4와 B2, A3 와 B2, 그리고 A1 과 A4 색조의 지대치들 사이에는 그 색조 차이가 컸다. 결론: IPS Empress Esthetic$^{(R)}$ coping으로 제작된 laminate veneer의 최종 색조는 지대치 색조 및 coping의 반투명도에 의해 영향을 받았다. 서로 다른 $a^*$와 $b^*$ 값을 나타내는 지대치들의 색상 차이는 어느 정도 차폐 되는 효과를 보여주고 있으나, 명도($L^*$)의 차이가 많이 나타나는 지대치 색조들을 차폐하는 것은 한계가 있었다.

• The Journal of Advanced Prosthodontics
• /
• 제15권5호
• /
• pp.238-247
• /
• 2023

PURPOSE. The purpose of this study was to assess the effect of resin cement shade on the color of different novel ultratranslucent monolithic zirconia and lithium disilicate veneer materials. MATERIALS AND METHODS. For a total of 40 specimens, flat cylindrical discs with a 9-mm diameter and 0.5-mm thickness were created using CAD/CAM technology. The specimens were divided into five groups according to their material (n = 8) (e.max, Prettau, Aidite, Shofu and Dima) using A1 shade. Resin discs with the same diameter and shade as the specimens served as tooth-colored substructures. Three shades (neutral, light and warm) of resin cement try-in pastes (Variolink Esthetic LC) were used as the luting cement material. The color of each material group was measured before and after cementation using the three cement shades, and the CIE L^*a^*b^* coordinates were obtained with a spectrophotometer. Values for the translucency parameter (TP) and color change delta E (E) before (baseline) and after cementation of each specimen were determined. To compare differences among the material groups within each shade of cement and among various shades of cement within each material, the data were analyzed using one-way ANOVA and post hoc testing. RESULTS. Color coordinates L^*, a^* and b^* significantly changed after the application of try-in pastes relative to baseline values, with a noticeable decrease in lightness (L^*) (P < .05). A significant color change (ΔE) was observed in all tested materials after cementation, with ΔE values exceeding 3.3 (P < .05). Although TP changed after cementation for most materials tested, these changes were not statistically significant (P > .05). Shofu and Dima ceramics showed the lowest TP values, while Aidite and Prettau showed the highest TP values. For e.max, translucency decreased after cementation with neutral and warm shades, and it significantly increased after cementation with a light shade. CONCLUSION. The shade of cement significantly altered the final color of the ceramic veneer material to a level above the threshold at which the clinical perception of color change occurred (> 3.3). The TP was not influenced by the cement shade. The translucency levels of the novel ultratranslucent multilayer monolithic zirconia ceramics Aidite and Prettau were higher than that of the lithium disilicate e.max material.

• Restorative Dentistry and Endodontics
• /
• 제19권1호
• /
• pp.159-168
• /
• 1994

The purpose of this study was to evaluate the shear bond strength of the porcelain laminate specimens according to the surface roughness of the cut enamel of human anterior teeth. Flat enamel surfaces were prepared in 30 extracted human anterior teeth with diamond disc which were divided into two groups. Group 1 Coarse enamel surface group prepared with LVS-3 bur. Group 2 Fine enamel surface group prepared with superfine diamond bur. 30 teeth specimens of two group were stored in normal saline during 24 hours. 30 disk - type porcelain laminate specimens with diameter 4mm and thickness 1mm were made and sand - blasted on internal surface which were to cemented on enamel surface. Porcelain laminate specimens were cemented on enamel surface with Choice Veneer System (Bisco Dental, U.S.A) according to manufacture's instructions. All teeth specimens of two groups were manipulated with same method and stored In normal saline before testing. An Universal Testing machine (Model No.UTM-4206,Instron, U.S.A) was used to apply shear loads in the vertical directed, and the force required for separation was recorded with a cross head speed of 3mm/min and 500kg in full scale. The results were as follow ; 1. The mean shear bond strength of coarse surface group was 36.30kg and that of fine surface group was 44.39 kg, but there was no significant difference in breaking strength of two groups(p>0.05).

• Journal of the Korean Wood Science and Technology
• /
• 제50권2호
• /
• pp.134-147
• /
• 2022

The objective of this study is to determine the effect of fiber direction arrangement and layer composition of hybrid bamboo laminate boards on the physical and mechanical properties. The raw material used was tali bamboo (Gigantochloa apus (J.A. & J.H. Schultes) Kurs) rope in the form of flat sheets (zephyr) and falcata veneer (Paraserianthes falcataria (L) Nielsen). Zephyr bamboo was arranged in three layers using water-based isocyanate polymer (WBPI) with a glue spread rate of 300 g/m². There were variations in the substitution of the core layer with falcata veneers (hybrid) as much as two layers and using a glue spread rate of 170 g/m². The laminated bamboo board was cold-pressed at a pressure of 22.2 kgf/cm² for 1 h, and the physical and mechanical properties were evaluated. The results showed that the arrangement of the fiber direction significantly affected the dimensional stability, modulus of rupture, modulus of elasticity, shear strength, and screw withdrawal strength. However, the composition of the layers had no significant effect on the physical and mechanical properties. The bonding quality of bamboo laminate boards with WBPI was considered to be quite good, as shown by the absence of delamination in all test samples. The bamboo hybrid laminate board can be an alternative based on the physical and mechanical properties that can meet laminated board standards.

• 한국지형학회지
• /
• 제23권1호
• /
• pp.17-33
• /
• 2016

Samples from newly exposed outcrop of sedimentary layers forming Jeongdongjin coastal terrace in Gangreung area are collected and analyzed to find the sedimentary environment. The site are located at the gentle hillslope of the terrace surface area. The height of the outcrop is about 8m and the altitude of it's highest part is 68~73m MSL. The lowest part of this out crop is the partly consolidated sand layer with gravel veneer within it. It is found that this part is not in-situ weathered sand stone through the OSL method. This sand layer is overlain by the gravel layer with sand matrix. The shapes of the gravels from this part are mainly 'platy', 'elongated', and 'bladed' by the index of Sneed and Folk(1958). In addition, mean roundness is not so high. It is sceptical to regard this part as marine sediments which are continuously exposed to erosional processes. The boundary between the lowest sand layer and gravel layer showing the abrupt change in forming material without any mixture or transitional zone, so gravels are seemed to deposited after some degree of consolidation of the lowest sand layer. In addition, the hight of the boundary between layers are changed by the place, so the surface of the partly consolidated sand layer is not flat and has irregularity on topography when it buried by gravels. Main part of this out crop is the poorly sorted coarse gravel(22.4mm) with sand matrix($1.36{\phi}$) layer with at least 2m thick covering the relatively fine gravels discussed above. Over 20% of particles have 'very platy', 'very elongated' and 'very bladed' shape and only less than 5% of particles have 'compact' shape, So this particles are also very hard to be regard as marine gravels which are abraded by marine processes. It can be concluded that this gravel layer formed by fluvial processes rather than coastal processes base on the form of the clast and sedimentary structure. The gravel layer is covered by fine($3{\sim}4{\phi}$) material layers of psudo-gleization which showing inter-bedding of red and white layers. Chemical composition of matrix and other fine materials should be analyzed in further studies. It is attempted to fine the burial ages of the sediment using OSL method, but failed by the saturation. So it can be assumed that these sediments have be buried over 120ka.