• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2015년도 추계 학술논문 발표대회
• /
• pp.126-127
• /
• 2015

Because of the high-rise and bigger building structure, high strength concrete's demand was increased. However, chemicophysical property of concrete is changed by high temperature. Therefore, this study evaluated on spalling properties of 80MPa high strength concrete with fireproof coating. The result, when complex fireproof coating spread on concrete, it has good fire safety that was thinner than single fireproof coating spread on concrete.

• Structural Engineering and Mechanics
• /
• 제83권4호
• /
• pp.551-561
• /
• 2022

In this paper, the effect of fire conditions according to ISO 834 standard on the behavior of carbon fibre-reinforced plastic (CFRP) reinforced steel beams coated with gypsum-based mortar has been investigated numerically. To study the efficiency of these beams, 3D coupled temperature-displacement finite element analyzes have been conducted. Mechanical and thermal characteristics of three different parts of composite beams, i.e., steel, CFRP plate, and fireproof coating, were considered as a function of temperature. The interaction between steel and CFRP plate has been simulated employing the adhesion model. The effect of temperature, CFRP plate reinforcement, and the fireproof coating thickness on the deformation of the beams have been analyzed. The results showed that within the first 120 min of fire exposure, increasing the thickness of the fireproof coating from 1 mm to 10 mm reduced the maximum temperature of the outer surface of the steel beam from 380℃ to 270℃. This increase in the thickness of the fireproof layer decreased the rate of growth in the temperature of the steel beam by approximately 30%. Besides excellent thermal resistance and gypsum-based mortar, the studied fireproof coating method could provide better fire resistance for steel structures and thus can be applied to building materials.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 추계 학술논문 발표대회
• /
• pp.104-105
• /
• 2013

The buildings constructed with steel structure is coated with certified fire resistive material to resist from fire. Coating materials lose their initial performances as time passes, so they need some maintenance. Fireproof spray-application also loses its performance and this performance loss of thr fireproof spray-application is very important because fire resistance of buildings depends on fireproof spray-application. So this study is to develop Acceleration durability test method of Fireproof spray-application, and use the Certification of fire resistant coating system.

• 한국건축시공학회지
• /
• 제11권4호
• /
• pp.353-362
• /
• 2011

High Strength Concrete (HSC) has weakness that in a fire, it is spalled and brittles. The phenomenon of spalling is made by water vapor's being confined in watertight concrete. This study is aimed to evaluate explosive spalling properties of high strength concrete with ${\square}100{\times}100{\times}200$ mm specimen and ${\square}400{\times}400{\times}1500$ mm column. To prevent spalling of concrete, fireproof coating and PP fiber are used. As a result, ${\square}400{\times}400{\times}1500$ mm column was prevented spalling likes ${\times}100{\times}100{\times}200$ mm specimen. When concrete protected failure to explosive spalling, quantity heat ratio (which fireproof coating specimen to pp fiber mixed specimen) between ${\square}100{\times}100{\times}200$ mm and ${\square}400{\times}400{\times}1500$ mm was maximum value at 20 minute, but difference of quantity heat ratio decreased and quantity heat ratio of each specimen is almost same at 30 minute.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 춘계 학술논문 발표대회
• /
• pp.176-177
• /
• 2017

IN order to use it for high-temperature fire, Fireproof boards mainly composed of Ca and Mg used. Korea does not have a fireproof board for explosive high temperatuer fire in tunnel, and it is applying existing fireproof coating. However, when a high-temperature fire(1350℃)with explosion occurs, it can not sustain its strength and can not be destroyed to have fire resistance. Each year, more than 100,100tons of wastes are produced by using Ca as an oyster shell. In this study, we try to determine whether or not to reuse the heat-heated fireproof board.

• 공업화학
• /
• 제28권4호
• /
• pp.437-441
• /
• 2017

본 연구에서는 방화용 실란트의 첨가제로 사용되는 팽창흑연의 부피팽창률과 경도특성을 개선하기 위해 팽창흑연에 다양한 수지를 코팅한 후 그 특성을 고찰하였다. 수지의 코팅률을 나타내는 평균코팅두께는 수지의 건조속도와 점도의 영향으로 초산비닐계수지 > 아크릴수지 > 우레탄수지 > 수용성라텍스의 순으로 크게 나타났다. 또한 수지의 종류에 따라 코팅된 팽창흑연의 부피팽창률은 우레탄수지 > 수용성라텍스 > 아크릴수지 > 초산비닐계수지의 순으로 컸으며, 경도는 초산비닐계수지 > 아크릴수지 > 수용성라텍스 > 우레탄수지의 순으로 증가함을 알 수 있었다. 이는 코팅처리를 하지 않은 팽창흑연에 비해 부피팽창률은 감소하나 경도가 현저하게 증가되어 방화첨가제로 사용이 가능함을 알 수 있었다. 반응표면분석법에 의한 최적화실험 결과 아크릴수지의 최적코팅 조건은 수지의 첨가량 37.6 wt%과 코팅 교반속도 441.4 rpm이었다.

• 한국화재소방학회논문지
• /
• 제29권1호
• /
• pp.12-18
• /
• 2015

본 연구에서는 실내장식 및 가구류 등에 이용되고 있는 편백루바와 파티클보드를 이용하여 방염처리 방법에 따른 방염성능 및 연소특성을 비교하는 실험을 하였다. 편백루바의 방염성능검사 결과 진공가압처리를 이용하여 난연수지를 주입한 편백루바가 표면에 염화고무수지 성분의 방염도료처리를 한 편백루바 보다 탄화면적은 9.55%, 탄화길이에서는 22.91% 우수한 것으로 나타났으며, 파티클보드는 파티클보드에 방염필름을 부착한 시편이 비방염필름을 부착한 시편보다 탄화면적 40.10%, 탄화길이에서는 43.40% 우수한 것으로 파악 되었다. Cone calorimeter를 이용한 연소특성 결과 편백루바 표면에 방염도료 처리를 한 시편이 진공가압처리를 이용한 난연수지 주입방식의 편백루바 보다 착화가 빨리 발생하였고, 총방출열량에서는 진공가압처리를 이용한 난연수지 주입방식의 편백루바가 $68.2MJ/m^2$, 편백루바 표면에 방염도료 처리를 한 시편이 $111.52MJ/m^2$을 나타내었으며, 파티클보드의 경우 착화시간에서는 미소한 차이를 보인 반면 총 방출열량에서는 파티클보드에 방염필름을 부착한 시편이 $90.1MJ/m^2$, 비방염필름을 부착한 시편은 $107.6MJ/m^2$의 총열방출량을 나타내었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 가을 학술논문 발표대회
• /
• pp.33-34
• /
• 2022

The purpose of this study was to provide basic data for applying oyster shells and egg shells as fireproof cladding materials by substituting fine aggregates for oyster shell powder and egg shell powder, and comparing strength and fire resistance performance. The reason for the high strength was thought to be that the oyster shell had higher strength than the egg shell itself, and both ESP and OSP were measured at a backside temperature of less than 500℃, so it was judged that it could be used as a fireproof coating for steel structures.

• 한국화재소방학회논문지
• /
• 제25권1호
• /
• pp.63-71
• /
• 2011

비대칭 H형강을 활용한 슬림플로어의 경우, 상대적으로 열전달 속도가 낮은 콘크리트에 강재가 매립된 형상으로 설계되어 화재조건에서 강재의 강성저하를 최소화 할 수 있는 형상으로 설계되었다. 그러나 비대칭 H형강의 하부플렌지는 화재에 직접적으로 노출되므로, 이 부분에 대한 내화피복을 적용하여 슬림플로어 보의 내화성능을 최대한 확보할 수 있는 방안을 모색하고자 하였다. 실험계획은 재하 하중비 0.4와 0.3을 조정하여 하중조건에 따른 내화성능을 비교하고자 하였고 철근보강에 따른 내화성능 향상효율, 내화피복을 적용하였을 경우의 180분 내화성능 확보 유 무를 분석하고자 실험을 수행하였다. 하중비 변화에 따른 실험체를 비교한 결과, 0.1 의 하중비를 낮출 경우 내화성능은 12분 차이가 나며, 처짐격차는 39mm였다. 철근보강에 따른 영향은 12분정도의 내화성능 향상이 가능하며, 최대 102.4mm의 처짐이 제어된다.

• 한국화재소방학회논문지
• /
• 제24권4호
• /
• pp.41-46
• /
• 2010

고강도 콘크리트는 대형 사회기반 구조물로서 많이 활용되고 있다. 고강도 콘크리트는 우수한 재료적 성능과 내구성을 확보하고 있지만 반면에 화재에 대한 급작스러운 폭렬현상으로 인하여 구조적인 문제를 야기시키기도 한다. 따라서 본 연구에서는 콘크리트 피복두께에 추가하여 내화피복재를 사용함으로써 내화피복두께에 따른 콘크리트의 내화성능을 평가하고 최적의 내화피복두께를 산정하는 실험적 연구를 수행하였다. 내화피복재를 10mm 간격으로 증가시키면서 실험을 수행한 결과 콘크리트의 내화성능이 크게 향상됨을 볼 수 있었으며, 최적의 내화피복두께는 약 1~3mm로 산정되었다. 또한 폭렬에 의하여 급작스러운 콘크리트 내부의 온도상승 이후 기화열에 의한 열손실로 완만하게 온도가 상승되는 현상이 실험적으로 관측되었다. PP 섬유는 약 $200^{\circ}C$ 부근에서 용해되어 고온에서는 빈 채널만 남게 되므로 내부 증기압을 저감시켜주는 역할도 관측되었다.