• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.305-309
• /
• 2002

We have successfully fabricated a Metal-Ferroelectric-Insulator-Semiconductor (MFIS) structure using Bi$\sub$4-x/La$\sub$x/Ti$_3$O$\sub$12/ (BLT) ferroelectric thin film and SiO$_2$/Nitride/SiO$_2$ (ONO) stacked buffer layers for single transistor type ferroelectric nonvolatile memory applications. BLT films were deposited on 15 nm-thick ONO buffer layer by sol-gel spin-coating. The dielectric constant and the leakage current density of prepared ONO film were measured to be 5.6 and 1.0 x 10$\^$-8/ A/$\textrm{cm}^2$ at 2MV/cm, respectively, It was interesting to note that the crystallographic orientations of BLT thin films were strongly effected by pre-bake temperatures. X-ray diffraction patterns showed that (117) crystallites were mainly detected in the BLT film if pre-baked below 400$^{\circ}C$. Whereas, for the films pre-baked above 500$^{\circ}C$, the crystallites with preferred c-axis orientation were mainly detected. From the C-V measurement of the MFIS capacitor with c-axis oriented BLT films, the memory window of 0.6 V was obtained at a voltage sweep of ${\pm}$8 V, which evidently reflects the ferroelectric memory effect of a BLT/ONO/Si structure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.235-238
• /
• 1998

Ferroelectric $LiNbO_3$ thin films were grown directly on Si(100) substrates by 13.55MHz RF magnetron sputtering system using a ceramic target ($Nb_2O_5/Li_2C0_3$ = 51.4/48.6). Because high temperature process have to avoided to prevent degradation of the interface (insulator/Si), $LiNbO_3$ thin films were deposited below $300^{\circ}C$. After as-deposited films were performed RTA treatments in an oxygen ambient at $600^{\circ}C$ for 60s, electrical measurements performed films before and after anneal treatment. In high field region, the leakage current density of the films after annealing was deceased about 4order and the resistivity of these was increased to about 5\times 10^{11} \Omega \cdot cm$ at 500kV/cm. In accumulation region of C-V curve, we calculated dielectric constant of thin film $LiNbO_3$ as 27.9 which is close to that of bulk value.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.224-227
• /
• 1999

Ferroelectric Pb(Zr$\sub$0.52/Ti$\sub$0.48/)O$_3$ thin films were fabricated by pulsed laser deposition, mainly varying process conditions such as substrate temperature, oxygen pressure, and laser energy, PZT films annealed at more than 600$^{\circ}C$ were crystallized into pure perovskite phases regardless of deposition temperatures. Lower deposition temperature of 400$^{\circ}C$ accompanied with post-annealing at 650$^{\circ}C$ resulted in denser microstructures with extremely small grains compated to those of thin films annealed at higher deposition temperatures. Hysteresis curves of thin film with small grains exhibitied good squareness and low leakage characteristics.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.719-722
• /
• 2003

Ferroelectric $Pb(Zr_{1-x}Ti_x)O_3$ (PZT) films were deposited on (001) MgO single crystals using sol-gel method. Structural properties and surface morphologies of PZT films were investigated using an X-ray diffractometer and a scanning electron microscopy, respectively. The dielectric properties of PZT films were investigated with the dc bias field using interdigitated capacitors (IDC) which were fabricated on PZT films using a thick metal layer by photolithography and dry etching process. The small signal dielectric properties of PZT films were calculated by a modified conformal mapping method with low and high frequency data, such as capacitance measured by an impedance gain/phase analyzer at 100 kHz and reflection coefficient (S-parameter) measured by a HP 8510C vector network analyzer at 1 -20 GHz. The IDC on PZT films exhibited about 67% of capacitance change with an electric field of 135 kV/cm at 10 GHz. These PZT thin films can be applied to tunable microwave devices such as phase shifters, tunable resonators and tunable filters.

• Korean Journal of Materials Research
• /
• v.14 no.10
• /
• pp.701-706
• /
• 2004

Bismuth layered structure ferroelectric thin films, La-substituted $Bi_{4}Ti_{3}O_{12}$ ($Bi_{1-x}La_{x}Ti_{3}O_{12}$, x=0.75, BLT) were prepared on the $Pt(111)/Ti/SiO_2/Si(100)$ substrates by a sol-gel spin coating process. The thin films were annealed in various conditions, i.e., oxygen, nitrogen and vacuum atmospheres for various annealing time. We investigated the annealing condition effects on the grain orientation and ferroelectric properties. The measured XRD patterns revealed that the BLT thin films showed only $Bi_{4}Ti_{3}O_{12}$-type phase with random orientation. $La^{3+}$ ion substitution for $Bi^{3+}$ ion in perovskite layers of $Bi_{4}Ti_{3}O_{12}$ decreased the degree of c-axis orientation and increased the remanent polarization ($2P_{r}$). The remanent polarization ($2P_{r}$) and the coercive field ($2E_{c}$) of the BLT thin film annealed at $650^{\circ}C$ for 5 min in oxygen atmosphere were $87{\mu}C/cm^2$ and 182 kV/cm, respectively, at an applied electric field of 240 kV/cm. For all of the BLT thin films annealed in various conditions, the fatigue resistance was shown. The improvement of ferroelectric properties with La substitution in $Bi_{4}Ti_{3}O_{12}$ could be attributed to the changes in space charge densities and grain orientation in the thin film.

• Electrical & Electronic Materials
• /
• v.7 no.5
• /
• pp.369-375
• /
• 1994

In this study, ferroelectric thin films of PZT with different Zr/Ti ratio were prepared by sol-get processing and annealed by rapid thermal annealing at >$500^{\circ}C$>$-700^{\circ}C$ for 10 sec. -1 min. Structures of the annealed films were examined by X-ray diffraction and SEM. Thin films of PZT with perovskite structure have been obtained by annealing at >$600^{\circ}C$ or above and for 20 seconds or longer. Maximum remnant polarization of 10.24.mu.C/cm$^{2}$ and minimum coercive field of 20.06 kV/cm were obtained from the 56/44 and 65/35 Zr/Ti composition films, respectively. Dielectric constant, .epsilon.$_{r}$ of 500-1300 and dielectric loss, tan .delta., of 0.01-0.035 were obtained from the films.s.

• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.138-142
• /
• 2000

Thin film $LiNbO_3$MFS (metal-ferroelectric-semiconductor) capacitor showed improved characteristics such as low interface trap density, low interaction with Si substrate, and large remanent polarization. This paper reports ferroelectric $LiNbO_3$thin films grown directly on p-type Si (100) substrates by 13.56 MHz RF magnetron sputtering system for FRAM (ferroelectric random access memory) applications. RTA (rapid thermal anneal) treatment was performed for as-deposited films in an oxygen atmosphere at $600^{\circ}C$ for 60sec. We learned from X-ray diffraction that the RTA treated films were changed from amorphous to poly-crystalline $LiNbO_3$which exhibited (012), (015), (022), and (023) plane. Low temperature film growth and post RTA treatments improved the leakage current of $LiNbO_3$films while keeping other properties almost as same as high substrate temperature grown samples. The leakage current density of $LiNbO_3$films decreased from $10^{-5}$ to $10^{-7}$A/$\textrm{cm}^2$ after RTA treatment. Breakdown electric field of the films exhibited higher than 500 kV/cm. C-V curves showed the clockwise hysteresis which represents ferroelectric switching characteristics. Calculated dielectric constant of thin film $LiNbO_3$illustrated as high as 27.9. From ferroelectric measurement, the remanent polarization and coercive field were achieved as 1.37 $\muC/\textrm{cm}^2$ and 170 kV/cm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.377-380
• /
• 2001

The BST thin films to composite (Ba$\sub$x/Sr$\sub$l-x/)TiO$_3$ using sol-gel method were fabricated on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric materials was investigated by structural and electrical properties. BST solution was composited by moi ratio, and then spin-coated (from 3 times to 5 times coating on Pt/SiO$_2$/Si substrate. Thickness of BST ceramics thin films are about 2600∼2800[${\AA}$] in 3 times deposition. The property of leakage current was stable when the applied voltage was 3[V]. Leakage current of 3 times coated BST thin film was 10$\^$-9/∼10$\^$-11/[A] at 0∼3[V].

• Proceedings of the KIEE Conference
• /
• 2003.07c
• /
• pp.1562-1564
• /
• 2003

In this study, PZT thin films were fabricated using sol-gel processing onto Si/$SiO_2$/Ti/Pt substrates. PZT sol with different Zr/Ti ratio(20/80, 30/70, 40/60, 52/48) were prepared, respectively. The films were fabricated by using the spin-coating method on substrates. The films were heat treated at $450^{\circ}C,\;650^{\circ}C$ by rapid thermal annealing(RTA). The preferred orientation of the PZT thin films were observed by X-ray diffraction(XRD), and Scanning electron microscopy(SEM). All of the resulting PZT thin films were crystallized with perovskite phase. The fine crystallinity of the films were fabricated. Also, we found that the ferroelectric properties from the dielectric constant of the PZT thin films were over 600 degrees, P-E hysteresis constant. And the leakage current densities of films were lower than $10^{-8}A/cm^2$. It is concluded that the PZT thin films by sol-gel process to be convinced of application for ferroelectric memory device.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.290-291
• /
• 2006

The effect of praseodymium substitution on the ferroelectric properties of $Bi_4Ti_3O_{12}$ thin films have been investigated. Ferroelectric Pr-substituted $Bi_4Ti_3O_{12}$ thin films were fabricated by chemical solution deposition onto Pt/Ti/$SiO_2$/Si substrates. The structure and morphology of the films were analyzed using Xray diffraction, and scanning electron microscopy, respectively. About 200-nm-thick BPT films grown at $720^{\circ}C$ exhibited a polycrystalline structure and showed excellent ferroelectric properties with a remanent polarization ($2P_r$) of $28.21\;{\mu}C/cm^2$ at an applied voltage of 5 V. The films a1so demonstrate fatigue-free behavior up to $10^{11}$ read/write switching cycles with 1 MHz bipolar pulses at an electric field of ${\pm}5\;V$.