• Journal of the Microelectronics and Packaging Society
• /
• v.13 no.1 s.38
• /
• pp.17-22
• /
• 2006

Ferroelectric PZT thin films were formed by 2-step sputtering and their dielectric properties and conduction mechanisms were investigated. Also. donor impurity doping was tried to compensate the carriers in PZT thin films. The leakage current density was able to reduce to $10^{-7}A/cm^2$ order by 2-step sputtering with thickness control of room temp.-layer. The conduction mechanism was confirmed as bulk-limited, and optimum donor impurities on PZT thin film were taken. Especially, leakage current characteristics was improved to $10^{-8}A/cm^2$ order in donor-doped PZT thin films formed by 2-step sputtering.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.5 no.1
• /
• pp.45-51
• /
• 2005

We have developed surface micromachined Infrared ray (IR) focal plane array (FPA), in which single $SiO_{2}$ layer works as an IR absorbing plate and $Pb(Zr_{0.3}Ti_{0.7})O_{2}$ thin film served as a thermally sensitive material. There are some advantages of applying $SiO_{2}$ layer as an IR absorbing layer. First of all, the $SiO_{2}$ has good IR absorbance within $8{\sim}12{\mu}m$ spectrum range. Measured value showed about 60% absorbance of incident IR spectrum in the range. $SiO_{2}$ layer has another important merit when applied to the top of Pt/PZT/Pt stack because it works also as a supporting membrane. Consequently, the IR absorbing layer forms one body with membrane structure, which simplifies the whole MEMS process and gives robustness Ito the structure.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.9 no.3
• /
• pp.576-581
• /
• 2005

In this paper. the a-Si:H TFT using ferroelectric of $SrTiO_3$ as a gate insulator is fabricated on glass. High k gate dielectric is required for on-current, threshold voltage and breakdown characteristics of TFT Dielectric characteristics of ferroelectric are superior to $SiO_2$ and $Si_3N_4$. Ferroelectric increases on-current and decreases threshold voltage of TFT and also ran improve breakdown characteristics.$SrTiO_4$ thin film is deposited by e-beam evaporation. Deposited films are annealed for 1 hour in N2 ambient at $150^{\circ}C\~600^{\circ}C$. Dielectric constant of ferroelectric is about 60-100 and breakdown field is about IMV/cm. In this paper, the TFT using ferroelectric consisted of double layer gate insulator to minimize the leakage current. a-SiN:H, a-Si:H (n-type a-Si:H) are deposited onto $SrTiO_3$ film to make MFNS(Metal/ferroelectric/a-SiN:H/a-Si:H) by PECVD. In this paper, TFR using ferroelectric has channel length of$8~20{\mu}m$ and channel width of $80~200{\mu}m$. And it shows that drain current is $3.4{\mu}A$at 20 gate voltage, $I_{on}/I_{off}$ is a ratio of $10^5\~10^8,\;and\;V_{th}$ is$4\~5\;volts$, respectively. In the case of TFT without having ferroelectric, it indicates that the drain current is $1.5{\mu}A$ at 20gate voltage and $V_{th}$ is $5\~6$ volts. If properties of the ferroelectric thin film are improved, the performance of TFT using this ferroelectric thin film can be advanced.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2004.05a
• /
• pp.53-56
• /
• 2004

The a-Si:H TFT using ferroelectric of SrTi $O_3$as a gate insulator is fabricated on glass. Dielectric characteristics of ferroelectric are superior to $SiO_2$and S $i_3$ $N_4$. Ferroelctric increases on-current, decreases thresh old voltage of TFT and also improves breakdown characteristics. The a-SiN:H has optical band gap of 2.61 eV, refractive index of 1.8~2.0 and resistivity of 10$^{13}$ - 10$^{15}$ $\Omega$cm, respectively. Insulating characteristics of ferroelectrics are excellent because dielectric constant of ferroelectric is about 60~100 and breakdown strength is over 1MV/cm. TFT using ferroelectric has channel length of 8~20${\mu}{\textrm}{m}$ and channel width of 80~200${\mu}{\textrm}{m}$. And it shows that drain current is 3.4$mutextrm{A}$ at 20 gate voltage, $I_{on}$ / $I_{off}$ is a ratio of 10$^{5}$ - 10$^{8}$ and $V_{th}$ is 4~5 volts, respectively. In the case of TFT without ferroelectric, it indicates that the drain current is 1.5 $mutextrm{A}$ at 20 gate voltage and $V_{th}$ is 5~6 volts. With the improvement of the ferroelectric thin film properties, the performance of TFT using this ferroelectric has advanced as a gate insulator fabrication technology is realized.zed.d.