• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 1997년도 추계학술대회 논문집
• /
• pp.140-145
• /
• 1997

In case of spot-welded joints, the fatigue cracks generally originate from the weld interfaces of the neighborhood nugget tips, and propagate toward the outer surfaces of the sheets. Generally, because fatigue crack was observed in nugget around, strain gage was attached at nugget zone. Accordingly, it was very difficult to detect the generation time of fatigue crack in spot-welded joints and to measure the propagation speed of fatigue crack. We developed the non-destructive method, according to which th fatigue crack propagation rate can be quantitatively estimated by utilizing information obtained from strain gages bonded on the electrode indentations of spot welds. The results measured by real crack were compared with the data which was measured by strain gauge method in fatigue testing. And so fatigue strength was evaluated by stress intensity factor. In this study behavior of fatigue crack propagation under repeated load were considered.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2005년도 춘계학술대회 논문집
• /
• pp.239-245
• /
• 2005

Through the fatigue test of plastic gears using polyacetal polymer, this research aims at providing basic data for not only specifying operation conditions of plastic gears, but also designing dimensions of plastic gears with giving fatigue life and the estimated equation of fatigue life of plastic gears. That is, from the fatigue life curves, the estimated equation of fatigue life of plastic gears is taken out. For the estimated equation of fatigue life of plastic gears, this research provides two test methods; one is preserving non-limited temperature of tooth flank, the other is preserving limited temperature of tooth flank. As results, how the temperature of tooth flank affects the fatigue life is shown. In addition, based on the endurance limit, the essential factors of the unit load and K-factor are determined, which are needed in the design of gear by bending strength and surface durability.

• 한국강구조학회 논문집
• /
• 제12권5호통권48호
• /
• pp.617-628
• /
• 2000

이 연구에서는 하중비전달형 필렛용접부를 대상으로 순수휨상태에서 TIG 처리에 따른 피로강도 향상정도 및 피로특성을 정량적으로 평가하기 위해서 4점 휨실험을 실시하였다. 피로실험결과 용접후처리를 실시하지 않은 시험체는 국내 외에서 규정하는 피로강도등급을 만족하고 있고 TIG 처리한 시험체는 용접후처리를 실시하지 않은 시험체보다 $2{\times}106$회 피로강도가 상회하는 것을 알 수 있었다. 또한 비치마크실험결과 피로균열은 용접지단부의 비드접선각도 및 곡률반경이 최소로 되는 점에서 다발적으로 발생하며, 반타원형 균열로 성장, 합체되어 파단에 이르는 것을 확인할 수 있었다. 한편 유한요소해석결과 용접지단부의 응력집중계수는 용접지단부의 비드접선각도 및 곡률반경과 밀접한 관계가 있으며, 이 중에서 곡률반경이 용접지단부의 응력집중계수에 보다 큰 영향을 미치는 것을 알 수 있었다. 한편 파괴역학적 해석결과 a/t가 0.4 이하인 경우에 기하학적형상보정계수가 균열보정계수에 가장 지배적인 영향을 미치는 인자임을 알 수 있었다. 또한 유한요소해석결과로부터 산정한 응력확대계수범위와 피로균열성장속도의 관계식으로부터 피로수명을 비교적 정확하게 산정할 수 있었다.

• 한국자동차공학회논문집
• /
• 제10권1호
• /
• pp.187-194
• /
• 2002

It has been reported that cracks in mechanical joints is generally under mixed-mode and there is critical inclined angle at which mode I stress intensity factor becomes maximum. The crack propagates in arbitrary direction and thus the prediction of crack growth path is needed to provide against crack propagation or examine safety. In order to evaluate the fatigue life of cracks in mechanical joints, horizontal crack normal to the applied load and located on minimum cross section is major concern but critical inclined crack must also be considered. In this paper mixed-mode fatigue crack growth test is performed far horizontal crack and critical inclined crack in mechanical joints. Fatigue crack growth path is predicted by maximum tangential stress criterion using stress intensity factor obtained from weight function method, and fatigue crack growth rates of horizontal and inclined crack are compared.

• Journal of Welding and Joining
• /
• 제16권4호
• /
• pp.73-82
• /
• 1998

This paper is especially concerned with the weldment between support beam and square bar that plays important roles in control box of Expansion Joint as a brdige structure. Fatigue strength ({TEX}$$\sigma$_{ult}${/TEX}) of the weldment is dependent on notch factor ({TEX}$K_{f}${/TEX}) become important factors to predict fatigue life. The fatigue notch sensitivity (η) for metals can be divided into two types ; high and low notch sensitivity. In this work, the Expansion Joint weldment was found to have low notch sensitivity. The maximum strain distribution during static loading is similar to the FEM analysis. Fatigue test of real structure was performed up to {TEX}$10^{6}${/TEX} cycles to be compared with predicted endurance limit.

• Nuclear Engineering and Technology
• /
• 제44권6호
• /
• pp.683-688
• /
• 2012

The structural integrity of mechanical components during several transients should be assured in the design stage. This requires a fatigue analysis including thermal and stress analyses. As an example, this study performs a fatigue analysis of the reactor pressure vessel of SMART during arbitrary transients. Using heat transfer coefficients determined based on the operating environments, a transient thermal analysis is performed and the results are applied to a finite element model along with the pressure to calculate the stresses. The total stress intensity range and cumulative fatigue usage factor are investigated to determine the adequacy of the design.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2004년도 춘계학술대회 논문집
• /
• pp.136-142
• /
• 2004

Effects of Nb(Niobium) contents and solution annealing on the strength and fatigue lift of 18%Ni maraging steel commonly using in aircraft, space field, nuclear energy, and vehicle etc. were investigated. Also the fatigue life stress intensity factor were compared experiment result and FEA(finite element analysis) result. The more Nb content, the higher or the lower fatigue lift on base metal specimens or solution annealed specimens showing that the fatigue life was almost the same. The maximum stresses of X, Y, and Z axis direction showed about 2.12${\times}$10$^2$MPa, 4.40${\times}$10$^2$MPa and 1.32${\times}$10$^2$MPa respectively. The Y direction stress showed the highest because of the same direction as the loading direction. The fatigue lives showed about 7% lower FEA result than experiment result showing almost invariable error every analyzed cycle. Stress intensity factor of the FEA result was lower about 3.5∼10% than that of the experiment result showing that the longer fatigue crack length, the higher error. It considered that the cause for the difference was the modeled crack tip having always the same shape and condition regardless of the crack growth.

• 한국해양공학회지
• /
• 제1권1호
• /
• pp.104-110
• /
• 1987

Fatigue tests by axial loading (R = 0.05) were carried out to investigate fatigue crack growth characteristics of small surface cracks in 2 1/4 Cr-1 Mo steel at room temperature by using flat specimens with a small artificial pit. All the data of the fatigue crack growth rate obtained in the present test are determined as a function of the stress intensity factor range about a semi-elliptical crack, so that the application of linear fracture mechanics to the surface fatigue crack growth and to the fatigue crack growth into depth, and all the data obtained from tests were discussed in comparison with the data of Type 304 stainless steel and two type of mild steel under the same test conditions. The obtained results are as follows: 1)When the cycle ratios are same, surface fatigue crack length and its depth are almost same and fall within a narrow scatter band in spite of different stress levels. 2)Relations of the surface fatigue crack growth rate (da/dN) and fatigue crack growth rate into depth (db/dN) to its stress intensity factor range ($\Delta K_{Ia}, \Delta K_{Ib}$) can be plotted as a straight line at log-log diagram without dependence of stress level and coincide with the data of part-through crack in various steels.

• Asian Pacific Journal of Cancer Prevention
• /
• 제15권22호
• /
• pp.9891-9898
• /
• 2014

Background: This study was planned in an attempt to develop scales for the assessment of fatigue in pediatric oncology patients aged 13-18 and also for their parents. Materials and Methods: In collecting the study data, we used the Child and Parent Information Form, Visual Fatigue Scale, Scale for the Assessment of Fatigue in Pediatric Oncology Patients Aged 13-18 and the Scale for the Assessment of Fatigue in Pediatric Oncology Patients Aged 13-18 for Parents. We also used Pearson correlation analysis, Cronbach alpha coefficient, factor analysis and ROC analysis for the study data. Results: In this study, the total Cronbach alpha value of the parent form was 0.99, the total factor load was 0.72-0.94 with 95% the total variance being explained. The cutoff point of the parent form is 73 points. The total Cronbach alpha value of the child form was 0.99, the total factor load was 0.82-0.95, with 89.4% of the total variance being explained. The cutoff point of the child form was 75.5 points. Conclusions: This study suggests that the Scale for the Assessment of Fatigue in Pediatric Oncology Patients Aged 13-18 and the Scale for the Assessment of Fatigue in Pediatric Oncology Patients Aged 13-18 for Parents are valid and reliable instruments in assessing the fatigue symptoms of children in Turkey.

• 한국안전학회지
• /
• 제6권4호
• /
• pp.81-87
• /
• 1991

We propose the crack growth rate equation which will model fatigue crack growth rate behavior such that constant stress amplitude fatigue crack growth behavior can be predicted. Constant stress amplitude fatigue tests are conducted for four materials under three stress ratios of R＝0.2, R＝0.4 and R＝0.6. Materials which have different mechanical properties i.e. stainless steel, low carbon steel, medium carbon steel and aluminum alloy are used. Through constant stress amplitude fatigue test by using unloading elastic compliance method, it is confirmed that crack closure is a close relationship with fatigue crack propagation. We describe simply fatigue crack propagation behavior as a function of the effective stress intensity factor range ($\Delta$ $K_{eff}$＝U .$\Delta$K) for all three regions (threshold region, stable region). The fatigue crack growth rate equation is given by da / dN＝A($\Delta$ $K_{eff}$­$\Delta$ $K_{o}$ )$^{m}$ / ($\Delta$ $K_{eff}$­$\Delta$K) Where, A and m are material constants, and $\Delta$ $K_{o}$ is stress intensity factor range at low $\Delta$K region. $K_{cf}$ is critical fatigue stress intensity factor.actor.