• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.3
• /
• pp.125-132
• /
• 2014

Steel fiber is a effective composite for crack resistance and improve structural performance under tensile loading. This study presents an evaluation of crack resistance and structural performance in cement mortar with steel fiber and expansion agent through internal chemical prestressing. For this work, cement mortar samples with 10% replacement of cement binder with CSA (Calcium-Sulfo-Aluminate) expansion agent and 1% volume ratio of steel fiber are prepared. Including basic mechanical properties, initial cracking load and fracture energy are evaluated in cement mortar beam with notch. Initial cracking load and fracture energy in cement mortar with CSA and steel fiber increase by 1.75 and 1.41~1.53 times compared with those in cement mortar with steel fiber. With optimum mix design for steel fiber and CSA expansive agent, the composite with chemical prestressing can be applied to various members and effectively improve crack resistance to external loading.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.6 no.4
• /
• pp.81-85
• /
• 2007

A safety valve is used for protecting the pressure vessel and facilities by discharging the operating fluid into the valve from the accident when the pressure is over the designated value. The fluid is sulfurous acid and nitric acid. etc. in the semi-conductor assembly line. Thus the valve elements material must be acid resistance. Teflon, which is used generally as inner parts of a valve, tends to easily sticks to sliding surface by thermal expansion under high temperature. Some studies are performed to change teflon to another material and shape to have a better fluidity under the condition. The analysis of the thermal expansion is conducted by commercial FEM software to improve the problems. Boundary conditions were temperature and load in this study. From the analysis, the thermal expansion of stainless steel is verified to be lower than that of teflon under high temperature. Thus coupled teflon/stainless steel-made valve is applied to assembly line without danger due to thermal expansion.

• Korean Journal of Materials Research
• /
• v.33 no.10
• /
• pp.422-429
• /
• 2023

High-strength low-alloy steel is one of the widely used materials in onshore and offshore plant engineering. We investigated the alloying effect of solute atoms in α-Fe based alloy using ab initio calculations. Empirical equations were used to establish the effect of alloying on the Vicker's hardness, screw energy coefficient, and edge dislocation energy coefficient of the steel. Screw and edge energy coefficients were improved by the addition of V and Cr solute atoms. In addition, the addition of trace quantities of V, Cr, and Mn enhanced abrasion resistance. Solute atoms and contents with excellent mechanical properties were selected and their thermal conductivity and thermal expansion behavior were investigated. The addition of Cr atom is expected to form alloys with low thermal conductivity and thermal expansion coefficient. This study provides a better understanding of the state-of-the-art research in low-alloy steel and can be used to guide researchers to explore and develop α-Fe based alloys with improved properties, that can be fabricated in smart and cost-effective manners.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.275-278
• /
• 2000

In this paper, we carried out fundamental experiments to use steel manufacturing slag as a concrete aggregate. Generally, there are two types of slag, the blast-furnace slag and the steel manufacturing slag. The latter is classified by the difference of manufacturing method of steel into the convertor slag and the electric-furnace slag. The steel manufacturing slag mainly contains $SiO_2$ and CaO as the chemical composition. The reaction with water and a little of free CaO in the steel manufacturing slag made the expansion of volume change, Therefore, we primarily investigated physical properties, expansion mechanism, pH value, aging effect and aging methods in the steel manufacturing slag, Then compressive strength of concrete with steel slag aggregate is measured.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.233-236
• /
• 1999

In this paper, we carried out fundamental experiments to use the steel manufacturing slag as a concrete aggregate. Generally there are two types of slag, the blast-furnace slag and the steel manufacturing slag. The latter is classified by the difference of manufacturing method of steel into the convertor slag and the electric-furnace slag. The steel manufacturing slag mainly contains SiO2 and CaO as the chmical composition. The reaction with water and a little of free CaO in the steel manufacturing slag makes the expansion of volume change. Therefore, we primarily investigated physical properties, expansion mechanism, pH value, aging effects and aging methods in the steel manufacturing slag. Then compressive strength of concrete with steel slag aggregate is measured.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.49-54
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of brown waste glass content, and fibers(steel fiber, polypropylene fiber) and fiber content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum content can not be found. Also, when used the fibers with waste g1ass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass. Specially, adding 1.5 vol.% of steel fiber to 20% of waste glass the expansion ratio was reduced by 40% and flexural strength was developed by up to 110% comparing with only Waste glass ( $80^{\circ}C$ $H_{2}$ O curing).

• Korean Journal of Materials Research
• /
• v.30 no.6
• /
• pp.292-300
• /
• 2020

In this study, the effect of tempering on the stretch-flangeability is investigated in 980 MPa grade dual-phase steel consisting of ferrite and martensite phases. During tempering at 300 ℃, the strength of ferrite increases due to the pinning of dislocations by carbon atoms released from martensite, while martensite is softened as a consequence of a reduction in its carbon super-saturation. This strength variation results in a considerable increase in yield strength of the steel, without loss of tensile strength. The hole expansion test shows that steel tempered for 20 min (T20 steel) exhibits a higher hole expansion ratio than that of steel without tempering (T0 steel). In T0 steel, severe plastic localization in ferrite causes easy pore formation at the ferrite-martensite interface and subsequent brittle crack propagation through the highly deformed ferrite area during hole expansion testing; this propagation is mainly attributed to the large difference in hardness between ferrite and martensite. When the difference in hardness is not so large (T20 steel), on the other hand, tempered martensite can be considerably deformed together with ferrite, thereby delaying pore formation and hindering crack propagation by crack blunting. Eventually, these different deformation and fracture behaviors contribute to the superior stretch-flangeability of T20 steel.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.8 no.5
• /
• pp.7-13
• /
• 2008

This paper presents experimental and analysis studies about both the corroded steel expansion and the variation of poor bonding range between steel and concrete. A loss of overall bonding capacity at the concrete-steel interface is evaluated experimentally and crack patterns at the bottom of the concrete are presented here. Steel-concrete interface is covered by rubber due to present local loss of the concrete-steel interface bonding capacity. In case of crack analysis performed by commercial FEM programs. we investigated crack‘s pattern and location. Finally, it is concluded that overall flexural capacity of the reinforced concrete structure is increased by the corroded steel expansion and is dependent of the bonding range at the steel- concrete interface. These results give an important factor to decide a life of reinforced concrete structures.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.19 no.2
• /
• pp.249-263
• /
• 2017

The expansion behavior of inflatable steel pipe rockbolt shows geometric nonlinearity due to its ${\Omega}-shaped$ section. Previous studies on the anchoring behavior of inflatable steel pipe rockbolt were mainly performed using theoretical method. However, those studies oversimplified the actual behavior by assuming isotropic expansion of inflatable steel pipe rockbolt. In this study, the anchoring behavior of the inflatable steel pipe rockbolt were investigated by the numerical method considering the irregularity of pipe expansion and other influencing factors. The expansion of inflatable steel pipe rockbolt, the contact stress distribution and the change of the average contact stress and the contact area during installation were analyzed. The contact stresses were developed differently depending on the constitutive behavior of rocks. Small contact stresses occurred in steel pipes installed in elasto-plastic rock compared to steel pipes installed in elastic rock. Also, the anchoring behaviors of the inflatable steel pipe rockbolt were different according to the stiffness of the rock. The steel pipe was completely unfolded in the case of the stiffness smaller than 0.5 GPa, but it was not fully unfolded in the case of the stiffness larger than 0.5 GPa for the given analysis condition. When the steel pipe is completely unfolded, the contact stress increases as the rock stiffness increases. However, the contact stress decreases as the rock stiffness increases when the steel pipe is not fully expanded.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.228-229
• /
• 2007

As one way of weight saving of the vehicle, 1-piece typed lower control arm has been developed using high strength hot rolled steel sheet. In order to overcome the edge splitting problem during edge flanging or burring process, HER (hole expansion ratio) value of steel sheet was primarily considered. The strength grade of steel sheet and the shape were optimized utilizing Taguchi method.