• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.1
• /
• pp.1-6
• /
• 2022

In this research, a ring-shaped silicon carbide (SiC) single crystal manufactured using the PVT (Physical Vapor Transport) method was proposed to be applied to a SiC focus ring in semiconductor etching equipment. A cylindrical graphite structure was placed inside the graphite crucible to grow a ring-shaped SiC single crystal by the PVT method. SiC single crystal ring without crack was successfully obtained in case of using SiC single crystal wafer as a seed. A plasma etching process was performed to compare plasma resistance between the CVD-SiC focus ring and the PVT-SiC focus ring. The etch rate of ring materials in PVT-single crystal SiC focus ring was definitely lower than that of CVD-SiC focus ring, indicating better plasma resistance of PVT-SiC focus ring.

• Korean Chemical Engineering Research
• /
• v.53 no.5
• /
• pp.557-564
• /
• 2015

The previous etching, rinsing and drying processes of wafers for MEMS (microelectromechanical system) using SC-$CO_2$ (supercritical-$CO_2$) consists of two steps. Firstly, MEMS-wafers are etched by organic solvent in a separate etching equipment from the high pressure dryer and then moved to the high pressure dryer to rinse and dry them using SC-$CO_2$. We found that the previous two step process could be applied to etch and dry wafers for MEMS but could not confirm the reproducibility through several experiments. We thought the cause of that was the stiction of structures occurring due to vaporization of the etching solvent during moving MEMS wafer to high pressure dryer after etching it outside. In order to improve the structure stiction problem, we designed a continuous process for etching, rinsing and drying MEMS-wafers using SC-$CO_2$ without moving them. And we also wanted to know relations of states of carbon dioxide (gas, liquid, supercritical fluid) to the structure stiction problem. In the case of using gas carbon dioxide (3 MPa, $25^{\circ}C$) as an etching solvent, we could obtain well-treated MEMS-wafers without stiction and confirm the reproducibility of experimental results. The quantity of rinsing solvent used could be also reduced compared with the previous technology. In the case of using liquid carbon dioxide (3 MPa, $5^{\circ}C$, we could not obtain well-treated MEMS-wafers without stiction due to the phase separation of between liquid carbon dioxide and etching co-solvent(acetone). In the case of using SC-$CO_2$ (7.5 Mpa, $40^{\circ}C$), we had as good results as those of the case using gas-$CO_2$. Besides the processing time was shortened compared with that of the case of using gas-$CO_2$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.1
• /
• pp.5-10
• /
• 2012

In general, the fabrications of the LEDs with mesa structure are performed grown by MOCVD method. In order to etch and separate each chips, the LEDs are passed the RIE and scribing processes. The RIE process using plasma dry etching occur some problems such as defects, dislocations and the formation of dangling bond in surface result in decline of device characteristic. The SAG method has attracted considerable interest for the growth of high quality GaN epi layer on the sapphire substrate. In this paper, the SAG method was introduced for simplification and fabrication of the high quality epi layer. And we report that the size of selective area do not affect the characteristics of original LED. The diameter of SAG circle patterns were choose as 2500, 1000, 350, and 200 ${\mu}m$. The SAG-LEDs were measured to obtain the device characteristics using by SEM, EL and I-V. The main emission peaks of 2500, 1000, 350, and 200 ${\mu}m$ were 485, 480, 450, and 445 nm respectively. The chips of 350, 200 ${\mu}m$ diameter were observed non-uniform surface and resistance was higher than original LED, however, the chips of 2500, 1000 ${\mu}m$ diameter had uniform surface and current-voltage characteristics were better than small sizes. Therefore, we suggest that the suitable diameter which do not affect the characteristic of original LED is more than 1000 ${\mu}m$.