• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.1
• /
• pp.18-25
• /
• 1998

G $d_{0.2}$C $e_{0.8}$ $O_{1.9}$(CGO) for electrolyte and L $a_{0.5}$S $r_{0.5}$Mn $O_3$(LSM50) for cathode in Solid Oxide Fuel Cells(SOFC) were synthesized by citrate process. Specimens were prepared with sintering temperatures at 110$0^{\circ}C$, 120$0^{\circ}C$ and 130$0^{\circ}C$, which were fabricated by slurry coating with citric acid contents. Interfacial resistance was measured between cathode and electrolyte using AC-impedance analyzer. With various citric acid content, the degree of agglomeration for the initial particles changed. Also sintering temperature changed the particle size and the degree of densification of cathode. Factors affecting the interfacial resistance were adherent degree of the electrolyte and cathode, distribution of TPB(three phase boundaries, TPB i.e., electrolyte/electrode/gas phase area) and porosity of cathode. By increasing the sintering temperature, particle size and densification of the cathode were increased. And then, TPB area which occurs catalytic reaction was reduced and so interfacial resistance was increased.sed.sed.d.

• Korean Journal of Metals and Materials
• /
• v.50 no.9
• /
• pp.685-690
• /
• 2012

Decalcomania is a new method for SOFCs (solid oxide fuel cells) unit cell fabrication. A tight and dense $5{\mu}m$ Yttria-stabilized zirconia (8YSZ) electrolyte layer on anode substrate was fabricated by the decalcomania method. After 8YSZ as the electrolyte starting material was calcined at $1200^{\circ}C$, the particle size was controlled by the attrition mill. The median particle size (D50) of each 8YSZ was $39.6{\mu}m$, $9.30{\mu}m$, $6.35{\mu}m$, and $3.16{\mu}m$, respectively. The anode substrate was coated with decalcomania papers which were made by using 8YSZ with different median particle sizes. In order to investigate the effect of median particle sizes and sintering conditions on the electrolyte density, each sample was sintered for 2, 5 and 10 h, respectively. 8YSZ with a median particle size of $3.16{\mu}m$ which was sintered at $1400^{\circ}C$ for 10 had the highest density. With this 8YSZ, a SOFCs unit cell was manufactured with a $5{\mu}m$ layer by the decalcomania method. Then the unit cell was run at $800^{\circ}C$. The Open Circuit Voltage (OCV) and Maximum power density (MPD) was 1.12 V and $650mW/cm^2$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.45 no.12
• /
• pp.760-765
• /
• 2008

In this study, the effects of small amounts (${\leq}3\;mol%$) of Li doping on the sintering characteristics and electrochemical performance of $(ZrO_2)_{0.89}(ScO_{1.5})_{0.1}(CeO_2)_{0.01}$ (ScSZ) were investigated. By adding 3 mol% lithium, the densification temperature of ScSZ was reduced from the conventional temperature of $1400^{\circ}C$ to $1200^{\circ}C$. It was found that Li doping also led to changes in the Zr:Sc ratio at the grain boundaries. Correspondingly, the dispersion of lithium zirconia at the grain boundaries accelerated the growth of ScSZ grains and increased the grain boundary resistance at temperatures below $450^{\circ}C$. At elevated temperatures of $450{\sim}750^{\circ}C$, the electrical conductivity of the ScSZ after doping remained almost unchanged under air and reducing atmospheres. These results suggest that the addition of lithium is promising for use in low temperature co-firing of ScSZ-based components for intermediate temperature solid oxide fuel cells.

• Journal of the Korean Ceramic Society
• /
• v.45 no.12
• /
• pp.782-787
• /
• 2008

Ni-ceria cermets have been extensively investigated as candidates for the anode in intermediate-temperature solid oxide fuel cells. We have used the citric method to synthesize nanocomposite powders consisting of NiO (Ni metal content: $40{\sim}60%$ by volume) highly dispersed in $Ce_{0.9}Gd_{0.1}O_{1.95}$ (CGO). The microstructure characteristics and sintering behaviors of the nanocomposites were investigated. No impurity phases were observed and the shrinkage of these substrates matched well with that of a CGO electrolyte with a specific surface area of $11\;m^2/g$. Densification of the CGO electrolyte layer to $<5\;{\mu}m$ thickness was achieved by co-firing the laminated electrolyte with the porous NiO-CGO substrate at $1400^{\circ}C$ for 6 h.

• Journal of the Korean Ceramic Society
• /
• v.56 no.1
• /
• pp.91-97
• /
• 2019

The effect of different Ni-containing additives on the sintering behavior and electric conductivity of the proton conducting electrolyte $BaCe_{0.35}Zr_{0.5}Y_{0.15}O_{3-{\delta}}$ (BCZY5) was investigated. Ni-doped, NiO-added, and $BaY_2NiO_5$(BYN)-added (all 4 mol%) BCZY5 samples were prepared by the solid state synthesis method and sintered at $1400^{\circ}C$ for 6 h. Among the three samples, the onset of densification was observed at the lowest temperature for NiO-added BCZY5, which is attributed to the formation of an intermediate phase at a low melting temperature. The BYN-added sample, where no consumption of the constitutional elements of the electrolyte was expected during sintering, exhibited the highest electrical conductivity whereas the doped sample had the lowest conductivity. The electrical conductivities at $500^{\circ}C$ under humid argon atmosphere were measured to be 2.0, 4.8, and $6.2mS{\cdot}cm^{-1}$ for Ni-doped and NiO- and BYN-added samples, respectively.

• Journal of Powder Materials
• /
• v.25 no.2
• /
• pp.151-157
• /
• 2018

In this study, the compound $Li_3BO_3$ (LBO) is intended to be prepared by a polymeric complex method as a sintering aid for the densification of $Li_7La_3Zr_2O_{12}$ (LLZ) solid electrolyte. A polymeric precursor containing Li and B is heat-treated in an air atmosphere at a temperature range between $600^{\circ}C$ and $800^{\circ}C$. Instead of LBO, the compound $Li_{2+x}C_{1-x}B_xO_3$ (LCBO) is unexpectedly synthesized after a heat-treatment of $700^{\circ}C$. The effect of LCBO addition on sintering behavior and ion conductivity of LLZ is studied. It is found that the LCBO compound could lead to significant improvements in the densification and ionic conductivity of LLZ compared to pure LLZ. After sintering at $1100^{\circ}C$, the density of the LLZ-12wt%LBO composite is $3.72g/cm^3$, with a high Li-ion conductivity of $1.18{\times}10^{-4}Scm^{-1}$ at $28^{\circ}C$, while the pure LLZ specimen had a densify of $2.98g/cm^3$ and Li-ion conductivity of $5.98{\times}10^{-6}Scm^{-1}$.

• Journal of the Korean Ceramic Society
• /
• v.55 no.6
• /
• pp.576-580
• /
• 2018

In this study, a small amount of CoO was added to commercial Gd-doped $CeO_2$ (GDC) powder. The CoO addition greatly enhanced sinterability at low temperatures, i.e., more than 98% of relative density was achieved at $1,000^{\circ}C$. When GDC/8YSZ (8 mol% yttrium stabilized zirconia) bilayers were sintered, Co-doped GDC showed excellent adhesion to the YSZ electrolyte. Transmission electron microscope (TEM) analysis showed that there were no traces of liquid films at the grain boundaries of GDC, whereas liquid films were observed in the Co-doped GDC sample. Because liquid films facilitate particle rearrangement and migration during sintering, mechanical stresses at the interface of a bilayer, which are developed based on different densification rates between the layers, might be reduced. In spite of $Co^{2+}$ doping in GDC, the electrical conductivity was not significantly changed, relative to GDC.

• Journal of the Korean Ceramic Society
• /
• v.53 no.6
• /
• pp.712-718
• /
• 2016

In this study, we investigate the effect of the$Li_3BO_3$ additive on the densification and ionic conductivity of garnet-type $Li_7La_3Zr_2O_{12}$ solid electrolytes for all-solid-state lithium batteries. We analyze their densification behavior with the addition of $Li_3BO_3$ in the range of 2-10 wt.% by dilatometer measurements and isothermal sintering. Dilatometry analysis reveals that the sintering of $Li_7La_3Zr_2O_{12}-Li_3BO_3$ composites is characterized by two stages, resulting in two peaks, which show a significant dependence on the $Li_3BO_3$ additive content, in the shrinkage rate curves. Sintered density and total ion conductivity of the system increases with increasing $Li_3BO_3$ content. After sintering at $1100^{\circ}C$ for 8 h, the $Li_7La_3Zr_2O_{12}-8$ wt.% $Li_3BO_3$ composite shows a total ionic conductivity of $1.61{\times}10^{-5}Scm^{-1}$, while that of the pure $Li_7La_3Zr_2O_{12}$ is only $5.98{\times}10^{-6}Scm^{-1}$.

• Journal of the Korean Ceramic Society
• /
• v.42 no.12 s.283
• /
• pp.821-826
• /
• 2005

Gadolinia-doped ceria nanopowder was prepared by glycine-nitrate combustion method with different glycine/nitrate mixing ratio. The characteristics of the synthesized powder were investigated by X-ray diffraction method, transmission electron microscopy, thermal gravity, differential thermal analysis and thermo-mechanical analysis. The smallest powder was obtained with glycine/nitrate ratio 1.00 and the lowest organic and water vapor contained powder was made with glycine/nitrate ratio 1.75. According to dilatometry, fast densification was occurred around $1000^{\circ}C$ and shows full density over $1300^{\circ}C$. Finally near-fully dense ceria electrolyte was fabricated with conventional sintering technique. Glycine-nitrate process yields fine nanopowders which enable low temperature sintering and fabrication of fully dense and nanostructured oxide electrolyte.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.521-526
• /
• 2015

$Ce_{0.8}Gd_{0.2}O_{1.9}$(GDC20) powder was prepared from a mixture of submicron-sized $CeO_2$ powder and Gd precipitates using ammonium carbonate $((NH_4)_2CO_3)$ as a precipitant. The mixture was calcined at $700^{\circ}C$ for 4 h followed by ball-milling that resulted in the GDC powder with an average particle size of $0.46{\mu}m$. The powder had a very uniform particle size distribution with particle sizes ranging from $0.3{\mu}m$ to $1{\mu}m$. Sintering of undoped GDC samples did not show a relative density of 99.2% until the temperature was increased to $1500^{\circ}C$, whereas GDC samples doped with 5 mol% CoO exhibited a significant densification at lower temperature reaching a relative density of 97.6% at $1100^{\circ}C$ and of 98.8% at $1200^{\circ}C$.