• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.9
• /
• pp.423-429
• /
• 2002

RuOx thin films were fabricated by the method of liquid delivery MOCVD using Ru(C$_{8}$ $H_{13}$ $O_2$)$_3$ as the precursor and their thermal effects and conductivity were investigated. Ru films deposited at 25$0^{\circ}C$ were annealed at $650^{\circ}C$ for 1min with Ar, $N_2$ or N $H_3$ ambient. The changes of the micro-structure, the surface morphology and the electrical resistivity of the Ru films after annealing were studied. Ar gas was more effective than $N_2$ and N $H_3$ gases as an ambient gas for the post annealing of the Ru films, because of smaller resistivity and denser grains. The X-ray diffraction and X-ray photoelectron spectroscopy results indicate that the Ru $O_2$ phase and the silicidation are not observed regardless of the ambient gases. The minimum resistivity of the Ru film is found to have the value of 26.35 $\mu$Ω-cm in Ar ambient. Voids were formed at Ru/TiN interface of the Ru layer after annea1ing in $N_2$ ambient. The $N_2$ gas generated due to the oxidation of the TiN layer accumulated at the Ru/TiN interface, forming bubbles; consequently, the stacked film may peel off the Ru/TiN interface.e.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.4
• /
• pp.152-156
• /
• 2009

Electroless plating is influenced by kinds of parameters including concentrations of electrolyte, plating time, temperature and so on. In this study, the Pt thin films were prepared on GaAs substrate by a 2-step electroless plating depending method. The small Pt catalytic particles by using Pt I bath exhibited islands-morphology dispersed throughout the substrate surface at $65^{\circ}C$, as function as a sensitized thin film, and then a thicker Pt film grew upon the sensitized layer by the second Pt II bath. As the growth of Pt film is strongly influenced by the plating time and temperature, the plating time of Pt II bath varied from 5 min to 40 min at $60{\sim}80^{\circ}C$ after Pt I bath at $60{\sim}80^{\circ}C$ for 5 min. It is found that the film grows with the increasing plating time and temperature. The resistivity value of Pt deposited layer was characterized to study the growth mechanism of 2-step plating.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.12a
• /
• pp.68-70
• /
• 2006

$CuInS_2$ thin films were synthesized by sulpurization of Cu/In Stacked elemental layer deposited onto glass Substrates by vacuum furance annealing at temperature 200[$^{\circ}C$]. And structural and electrical properties were measured in order to certify optimum conditions for growth of the ternary compound semiconductor $CuInS_2$ thin films with non-stoichiometry composition. $CuInS_2$ thin film was well made at the heat treatment 200 [$^{\circ}C$] of SLG/Cu/In/S stacked elemental layer which was prepared by thermal evaporator, and chemical composition of the thin film was analyzed nearly as the proportion of 1:1:2. Physical properties of the thin film were investigated at various fabrication conditions substrate temperature, annealing and temperature, annealing time by XRD, FE-SEM and hall measurement system. At the same time, carrier concentration, hall mobility and resistivity of the thin films was $9.10568{\times}10^{17}[cm^{-3}]$, $312.502[cm^2/V{\cdot}s]$ and $2.36{\times}10^{-2}[{\Omega}{\cdot}cm]$, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.6
• /
• pp.348-352
• /
• 2016

In this paper, GaN film was grown on AlN/PSS by hydride vapor phase epitaxy compared with GaN on planar sapphire. Thin AlN layer for buffer layer was deposited on patterned sapphire substrate (PSS) by metal organic chemical vapor deposition. Surface roughness of GaN/AlN on PSS was remarkably decreased from 28.31 to 5.53 nm. Transmittance of GaN/AlN grown on PSS was lower than that of planar sapphire at entire range. XRD spectra of GaN/AlN grown on PSS corresponded the wurzite structure and c-axis oriented. The full width at half maximum (FWHM) values of ${\omega}$-scan X-ray rocking curve (XRC) for GaN/AlN grown on PSS were 196 and 208 arcsec for symmetric (0 0 2) and asymmetric (1 0 2), respectively. FWHM of GaN on AlN/PSS was improved more than 50% because of lateral overgrowth and AlN buffer effect.

• The Korean Journal of Quaternary Research
• /
• v.23 no.1
• /
• pp.1-24
• /
• 2009

Paleosol layers lying on top of the terrace in Jeongdongjin area appear to have been deposited under generally well-drained condition with periodic waterlogging. From a 4.5m-long profile observed, a total of 6 stratigraphic units were identified. Grain-size analysis indicates the dominance of silty and clay materials with some portions with high sand content. Major mineralogical elements are quartz, feldspar, mica and chlorite. Geo-chemical composition shows little change throughout the stratigraphy with some fluctuation in chemical weathering index. Marked increase in magnetic susceptibility is recognizable where stratigraphic unit changes. Soil- wedge layer is developed around 50cm below the surface with concentration of grains of AT tephra (c. 25,000 BP). An OSL date of c. 110,000 BP was obtained from a sand layer lying below the paleosol.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.380-381
• /
• 2007

This paper reports on the deposition conditions and properties of ITO films used as electrode layer in a organic light emitting diodes on a PET substrate. The deposition technique employed was specially designed roll-to-roll sputtering. The oxide was deposited at room temperature in an argon and oxygen plasma on a transparent conducting ITO layer on a PET film. The influence of deposition parameters such as DC power, working pressure and oxygen partial pressure has been investigated, in order to obtain the best compromise between a high deposition rate and adequate electro-optical properties. Electrical and optical properties of ITO films were analyzed by Hall measurement examinations with van der pauw geometry at room temperature and UV/Vis spectrometer analysis, respectively. In addition, the structural properties and surface smoothness were measured by x-ray diffraction and scaning electron microscopy, respectively. From optimized ITO films grown by roll-to-roll sputter system, good electrical$(6.44{\times}10^{-4}\;{\Omega}-cm)$ and optical(above 86 % at 550 nm) properties were obtained. Also, the ITO films exhibited amorphous structure and very flat surface beacause of low deposition temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.525-526
• /
• 2007

Over-polishing is required to completely remove the material of top surface across whole wafer, in spite of a local dishing problem. This paper introduces the two-step CMP process using protective layer and high selectivity slurry, to reduce dishing amount and variation. The 30nm thick protective oxide layer was deposited on the pattern, and then polished with low selectivity slurry to partially remove the projected area while suppressing the removal rate of the recessed area. After the first step CMP process, high selectivity slurry was used to minimize the dishing amount and variation in pattern structure. Experimental result shows that two-step CMP process can be successfully applicable to reduce the dishing defect generated in over-polishing.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.450-450
• /
• 2006

Organic light-emitting diodes (OLED) as pixels for flat panel displays are being actively pursued because of their relatively simple structure, high brightness, and self-emitting nature [1, 2]. The top-emitting diode structure is preferred because of their geometrical advantage allowing high pixel resolution [3]. To enhance the performance of TOLEDs, it is important to deposit transparent top cathode films, such as transparent conducting oxides (TCOs), which have high transparency as well as low resistance. In this work, we report on investigation of the characteristics of an indium tin oxide (ITO) cathode electrode, which was deposited on organic films by using a radio-frequency magnetron sputtering method, for use in top-emitting organic light emitting diodes (TOLED). The cathode electrode composed of a very thin layer of Mg-Ag and an overlaying ITO film. The Mg-Ag reduces the contact resistivity and plasma damage to the underlying organic layer during the ITO sputtering process. Transfer length method (TLM) patterns were defined by the standard shadow mask for measuring specific contact resistances. The spacing between the TLM pads varied from 30 to $75\;{\mu}m$. The electrical properties of ITO as a function of the deposition and annealing conditions were investigated. The surface roughness as a function of the plasma conditions was determined by Atomic Force Microscopes (AFM).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.7
• /
• pp.594-599
• /
• 2007

[ $CulnS_2$ ] thin films were synthesized by sulfurization of Cu/In Stacked elemental layer deposited onto glass Substrates by vacuum furnace annealing at temperature $200^{\circ}C$. And structural and electrical properties were measured in order to certify optimum conditions for growth of the ternary compound semiconductor $CuInS_2$ thin films with non-stoichiometry composition. $CuInS_2$ thin film was well made at the annealed $200^{\circ}C$ of SLG/Cu/In/S stacked elemental layer which was prepared by thermal evaporator, and chemical composition of the thin film was analyzed nearly as the proportion of 1 : 1 : 2. Physical properties of the thin film were investigated at various fabrication conditions substrate temperature, annealing and temperature, annealing time by XRD, FE-SEM and Hall measurement system. The compositional deviations from the ideal chemical formula for $200^{\circ}C$ material can be conveniently described by non-molecularity$({\Delta}x=[Cu/In]-1)$ and non-stoichiometry $({\Delta}y=[{2S/(Cu+3In)}-1])$. The variation of ${\Delta}x$ would lead to the formation of equal number of donor and accepters and the films would behave like a compensated material. The ${\Delta}y$ parameter is related to the electronic defects and would determine the type of the majority charge carriers. Films with ${\Delta}y>0$ would behave as p-type material while ${\Delta}y<0$ would show n-type conductivity. At the sane time, carrier concentration, hall mobility and resistivity of the thin films was $9.10568{\times}10^{17}cm^{-3},\;312.502cm^2/V{\cdot}s\;and\;2.36{\times}10^{-2}\;{\Omega}{\cdot}cm$, respectively.

• KSTLE International Journal
• /
• v.6 no.2
• /
• pp.39-44
• /
• 2005

Friction and wear properties of the Boron carbide ($B_{4}C$) coating 100 nm thickness were studied under various relative humidity (RH). The boron carbide film was deposited on silicon substrate by DC magnetron sputtering method using $B_{4}C$ target with a mixture of Ar and methane ($CH_4$) as precursor gas. Friction tests were performed using a reciprocation type friction tester at ambient environment. Steel balls of 3 mm in diameter were used as counter-specimen. The results indicated that relative humidity strongly affected the tribological properties of boron carbide coating. Friction coefficient decreased from 0.42 to 0.09 as the relative humidity increased from $5\%$ to $85\%$. Confocal microscopy was used to observe worn surfaces of the coating and wear scars on steel balls after the tests. It showed that both the coating surface and the ball were significantly worn-out even though boron carbide is much harder than the steel. Moreover, at low humidity ($5\%$) the boron carbide showed poor wear resistance which resulted in the complete removal of coating layer, whereas at the medium and high humidity conditions, it was not. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) analyses were performed to characterize the chemical composition of the worn surfaces. We suggest that tribochemical reactions occurred during sliding in moisture air to form boric acid on the worn surface of the coating. The boric acid and the tribochemcal layer that formed on steel ball resulted in low friction and wear of boron carbide coating.