The characteristics of the stress corrosion cracking of SUS 304 stainless steel were studied with the specimens of the constant displacement type under the environment of various MgCl sub(2) aqueous solutions. Main results obtained are as follows; 1) Latent time of crack initiations is delayed in the SCC under low condition of initial stress intensity K sub(Ii) value. 2) SCC occurs owing to the passive film-rupture by both load and Cl ion under MgCl sub(2) boiled aqueous solution. 3) The susceptibility of SCC can be largely improved by reducing the temperature in case of the high concentration of MgCl sub(2) aqueous solution.

• Nuclear Engineering and Technology
• /
• v.30 no.3
• /
• pp.262-272
• /
• 1998

The experiences and causes of pressure tube cracking accidents in the CANDU reactors and the development of the fuel channel at AECL(Atomic Energy Canada Limited) have been described. Most of the accidents were caused by Delayed Hydride Cracking(DHC). In the cases of the Pickering units 3&4 and the Bruce unit 2, excessive residual stresses induced by an improper rolled joint process played a role in DHC. In the Pickering unit 2, cracks formed by contact between the pressure and calandria tubes due to the movement of the garter spring were the direct cause of the failure. To extend the life of a fuel channel, several R&D programs examining each component of the fuel channel have been carried out in Canada. For a pressure tube, the main concern is focused on changing the fabrication processes, e.g., increasing cold working rate, conducting intermediate annealing and adding a third element like Fe, V, and Cr to the tube material. In addition to them, chromium plating on the end fitting and increasing wall thickness at both ends of the calandria tube are considered. There has also been much interest in the improvement of fuel channel performance in our country and several development programs are currently under way.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.155-160
• /
• 2001

This paper describes a probabilistic fracture mechanics (PFM) analysis based on Monte Carlo (MC) simulation. In the analysis of CANDU pressure tube, it is necessary to perform the PFM analyses based on statistical consideration of flaw generation time. A depth and an aspect ratio of initial semi-elliptical surface crack, a fracture toughness value, delayed hydride cracking (DHC) velocity, and flaw generation time are assumed to be probabilistic variables. In all the analyses, degradation of fracture toughness due to neutron irradiation is considered. Also, the failure criteria considered are plastic collapse, unstable fracture and crack penetration. For the crack growth by DHC, the failure probability was evaluated in due consideration of flaw generation time.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.93-98
• /
• 1998

CANDU 압력관의 집합조직을 원주 방향 집합조직에서 반경 방향 집합조직으로 변화시켜 $K_{IH}$ 를 평가하였다. 집합조직은 평면 변형에 의한 25% 확관 방법으로 번화시켰고 (0002) direct pole figure와 basal pole component (기저면 성분, Kearns number)로 분석하였다. 반경 방향집합조직의 압력관의 $K_{IH}$ 는 2$50^{\circ}C$에서 17MPa√m 이상으로 나타났으며, 이것은 상용 압력관의 $K_{IH}$ =8-10 MPa√m보다 70% 이상 높은 값이다. 반경 방향 집합조직의 압력관에서 나타나는 $K_{IH}$ 거동을 균열 진전면에서의 기저면 성분과 연계하여 분석하였으며, 평면 면형에 따른 집합조직의 변화는 슬립과 쌍정 기구의 작용으로 설명하였다. 본 연구의 결과는 CANDU 압책관의 delayed hydride cracking (DHC) 저항성 관점에서 반경 방향으로 집합조직을 제어하면 매우 효율적이라는 것을 보여 준다.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1192-1197
• /
• 2003

The aim of this study is to investigate the hydride embrittlement when the LBB evaluation is carried out for the integrity of PHWR Pressure Tubes. The transverse tensile and CCT tests were performed at three hydrogen concentrations while the test temperatures were changed (RT to $300^{\circ}C$). The specimens were directly machined from the pressure tube retaining original curvature. Both the transverse tensile and the fracture toughness tests showed the hydrogen embrittlement clearly at RT but this phenomenon was disappeared while the test temperature arrived over $250^{\circ}C$. Using the DHC test results, the CCL and LBB time were calculated and compared. The hydride embrittlement behavior at the LBB evaluation was definitely showed.

• Journal of Pharmaceutical Investigation
• /
• v.12 no.4
• /
• pp.112-125
• /
• 1982

Sulfamethoxazole particles were microencapsulated using the gelatin-acacia complex coacervation method. Micromeritic properties and dissolution characteristics of the microcapsules were studied. The particle size distribution followed log-normal form. As the hardening time increased, the particle size and wall thickness increased ($45.3-52.0\;{\mu}m$, $2.02-5.12\;{\mu}m$, respectively). This is considered to be due to the cross-linked wall structure of formalized microcapsules which prevents shrinking of gelatin during the dehydration and drying processes. An increase of hardening time clearly delayed the release rate. The in vitro 50% dissolution time $(t_{50})$ for unencapsulated sulfamethoxazole powder was less than 3 min.; for microcapsules hardened for 30 min, the $t_{50}$ was 20.1 min.; for those hardened for 60 min. the $t_{50}$ was 25.0 min.; for those hardened for 120 min., the $t_{50}$ was 35.8 min. The surface of the unhardened microcapsules was smooth and had no cracking or pore penetration. However, the surface of the hardened microcapsules was folded and invaginated.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.5
• /
• pp.610-616
• /
• 2004

The aim of this study was to investigate the hydride embrittlement when the LBB evaluation was carried out for the integrity of PHWR Pressure Tubes. The transverse tensile and CCT toughness tests were performed at three hydrogen concentrations while the test temperatures were changed (RT to 30$0^{\circ}C$). Both the transverse tensile and the fracture toughness tests showed the hydrogen embitterment clearly at RT but this phenomenon was disappeared while the test temperature arrived at 25$0^{\circ}C$. Using the DHC test results, the CCL and LBB time were calculated and compared. The hydride embrittlement at the LBB evaluation made the LBB time short definedly. If the operating temperature, DHCV and LBB deterministic parameters such as A and m were known, LBB time could be estimated without the calculation of CCL.

• Nuclear Engineering and Technology
• /
• v.56 no.2
• /
• pp.728-744
• /
• 2024

The presence of hydrogen absorbed by zirconium-based cladding materials during reactor operation can trigger degradation mechanisms and endanger the rod integrity. Ensuring the durability of the rods in extended time-frames like dry storage requires anticipating hydrogen behavior using numerical modeling. In this context, the present paper describes a hydrogen post-processing tool for Falcon - HYPE, a PSI's in-house tool able to calculate hydrogen uptake, transport, thermochemistry, reorientation of hydrides and hydrogen-related failure criteria. The tool extracts all necessary data from a Falcon output file; therefore, it can be considered loosely coupled to Falcon. HYPE has been successfully validated against experimental data and applied to reactor operation and interim storage scenarios to present its capabilities.

• Nuclear Engineering and Technology
• /
• v.46 no.6
• /
• pp.869-874
• /
• 2014

It was discovered in a Korean PWR that an extensive number of very short and shallow cracks in the SG tubes were undetectable by eddy current in-service-inspection because of the masking effect of sludge deposits. Axial stress corrosion cracks at the outside diameter of the steam generator tubes near the line contacts with the tube support plates are the major concern among the six identical Korean nuclear power plants having CE-type steam generators with Alloy 600 high temperature mill annealed tubes, HU3&4 and HB3~6. The tubes in HB3&4 have a less susceptible microstructure so that the onset of ODSCC was substantially delayed compared to HU3&4 whose tubes are most susceptible to ODSCC among the six units. The numbers of cracks detected by the eddy current inspection jumped drastically after the steam generators of HB4 were chemically cleaned. The purpose of the chemical cleaning was to mitigate stress corrosion cracking by removing the heavy sludge deposit, since a corrosive environment is formed in the occluded region under the sludge deposit. SGCC also enhances the detection capability of the eddy current inspection at the same time. Measurement of the size of each crack using the motorized rotating pancake coil probe indicated that the cracks in HB4 were shorter and substantially shallower than the cracks in HU3&4. It is believed that the cracks were shorter and shallower because the microstructure of the tubes in HB4 is less susceptible to ODSCC. It was readily understood from the size distribution of the cracks and the quantitative information available on the probability of detection that most cracks in HB4 had been undetected until the steam generators were chemically cleaned.

• Journal of the Korea Concrete Institute
• /
• v.12 no.2
• /
• pp.63-69
• /
• 2000

This study investigates a new method of using a concrete disk to calculate stress intensity factor (SIF) for mixed mode cases. The results indicate that the disk method is more accurate than three point bending test (TPB) in obtaining correct SIF values for mixed mode fracture propagation. Stress intensity factors $K_{I}$ and $K_{II}$ are calculated using a center notched disk subjected to splitting load. The notch angle is calculated by finite element (FEM). Fracture toughness $K_\textsc{k}$ of the concrete is obtained from the load intensities at the initiation of crack propagation. According to the finite element analysis(FEA) and disk test, the results show that mode I and mixed mode cracks propagate toward the directions of crack face and loading point, respectively. The results from FEA with maximum stress theory compare well with the experimental date. Unlike TPB method where an accurate fracture toughness value is difficult to obtain due to the irregular shape of load deflection curve and delayed final crack propagation (following slow stable cracking). fracture toughness value is easily measured in the disk test from the crack initial load. Therefore, it is safe to conclude that disk method is more advantageous than TPB method in analyzing combined mode fracture problems.