• Journal of the Korean institute of surface engineering
• /
• v.39 no.6
• /
• pp.245-249
• /
• 2006

In this study, ternary Ti-Mo-N and new quaternary Ti-Mo-Si-N coatings were synthesized on steel substrates(AISI D2) and Si wafers by a hybrid coating system of arc ion plating (AIP) using Ti target and d.c. magnetron sputtering technique using Mo and Si targets in $N_2/Ar$ gaseous mixture. Ternary Ti-Mo-N coatings were substitutional solid-solution of (Ti, Mo)N and showed maximum hardness of approximately 30 GPa at the Mo content of ${\sim}10$. %. The Ti-Mo-Si-N coating with the Si content of 8.8 at. % was a composite consisting of fine (Ti, Mo)N crystallites and amorphous $Si_3N_4$ phase. The hardness of the Ti-Mo-Si(8.8 at. %)-N coatings exhibited largely increased hardness value of ${\sim}48$ GPa due to the microstructural evolution to the fine composite microstructure and the refinement of (Ti, Mo)N crystallites. The average friction coefficient of the Ti-Mo-Si-N coatings largely decreased with increase of Si content. The microstructures of Ti-Mo-Si-N coatings were investigated with instrumental analyses of XRD, XPS, and HRTEM in this work.

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.1
• /
• pp.31-36
• /
• 2011

$TiO_2$ films were deposited on a glass substrate with RF magnetron sputtering and then surface of $TiO_2$ films were electron beam irradiated in a vacuum condition to investigate the effect of electron bombardment on the thin film crystallization, surface roughness and gas sensitivity for hydrogen. $TiO_2$ films that electron beam irradiated at 450eV were amorphous phase, while the films irradiated at 900 eV show the anatase (101) diffraction peak in XRD pattern. AFM measurements show that the roughness is depend on the electron irradiation energy. As increase the hydrogen gas concentration and operation temperature, the gas sensitivity of $TiO_2$ and $TiO_2$/ZnO films is increased proportionally and $TiO_2$ films that electron beam irradiated at 900 eV show the higher sensitivity than the films were irradiated at 450eV. From the XRD pattern and AFM observation, it is supposed that the crystallization and rough surface promote the hydrogen gas sensitivity of $TiO_2$ films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.5
• /
• pp.387-392
• /
• 2019

$Dy^{3+}$ and $Eu^{3+}$-co-doped $La_2MoO_6$ phosphor thin films were deposited on sapphire substrates by radio-frequency magnetron sputtering at various growth temperatures. The phosphor thin films were characterized using X-ray diffraction (XRD), scanning electron microscopy, ultraviolet-visible spectroscopy, and fluorescence spectrometry. The optical transmittance, absorbance, bandgap, and photoluminescence intensity of the $La_2MoO_6$ phosphor thin films were found to depend on the growth temperature. The XRD patterns demonstrated that all the phosphor thin films, irrespective of growth temperatures, had a tetragonal structure. The phosphor thin film deposited at a growth temperature of $100^{\circ}C$ indicated an average transmittance of 85.3% in the 400~1,100 nm wavelength range and a bandgap energy of 4.31 eV. As the growth temperature increased, the bandgap energy gradually decreased. The emission spectra under ultraviolet excitation at 268 nm exhibited an intense red emission line at 616 nm and a weak emission line at 699 nm due to the $^5D_0{\rightarrow}^7F_2$ and $^5D_0{\rightarrow}^7F_4$ transitions of the $Eu^{3+}$ ions, respectively, and also featured a yellow emission band at 573 nm, resulting from the $^4F_{9/2}{\rightarrow}^6H_{13/2}$ transition of the $Dy^{3+}$ ions. The results suggest that $La_2MoO_6$ phosphor thin films can be used as light-emitting layers for inorganic thin film electroluminescent devices.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.3
• /
• pp.269-276
• /
• 2009

Antimony doped tin oxide ($SnO_2:Sb$) films, which are used as the front contact and back reflector of thin film solar cells, have been deposited by d,c, magnetron sputtering. The dependence of electrical and optical properties of the films on the preparation conditions, such as $O_2$ gas ratio, substrate temperature, annealing temperature was investigated. The sputter gas composition was found to affect the properties of the films. With incorporating $O_2$ gas, the electrical and optical properties of films significantly were improved. The minimum resistivity and optical transmittance over 80 % in visible region were obtained at the oxygen concentration of 30 %, When the substrate temperature was higher, the resistivity of $SnO_2:Sb$ films was decreased, while the absorption edge shifted to shorter wavelength, indicating higher optical band gap. Heat treatment over $600^{\circ}C$ resulted in poorer electrical and optical properties due to SnO phase (102) plane.

• Journal of the Korean institute of surface engineering
• /
• v.28 no.6
• /
• pp.386-392
• /
• 1995

The RF planar magnetron sputtering technique was used to fabricate uniform ZnO/$SiO_2$/Si thin films at high growth rate. A detailed crystallographic character of these thin films has been carried oct using XRD, XRC, and SEM. These thin films have the configuration of c-axis orientation perpendicular to $SiO_2$/ Si substrate. The dependence of the thickness of ZnO/$SiO_2$/Si films on applied RF power parameters was also investigated. The crystallinity of films was improved as the substrate temperature was high, RF input power increased, and Ar/$O_2$ ratio decreased. Also, most of ZnO films fabricated on $SiO_2$/Si were suitable for SAW filter since a standard deviation of XRC (002) peak was less than $6^{\circ}$. The presence of the $SiO_2$ layer has a beneficial effect on the crystalline quality of the grown ZnO films.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.6
• /
• pp.316-326
• /
• 1993

Adhesion and hardeness are the most important properties of a hard coated layer which is applied to wear-resistant devices. Zr/ZrN layer was deposited on tool steel(SKH9) and stainless steel(SUS304) by a re-active D.C. magnetron sputtering technique and their microhardness and adhesion strength were measured for the films processed by changing the partial pressures of $N_2$ gas (4~10$\times$$10^{-4}$mbar) and the substrate bias voltage(0~250V). The adhesion strength was evaluated by acoustic signals through the scratch-test with the incremental applied load. As the partial pressure of $N_2$ gas and the substrate bias voltage were increased, the adhesion strength of tool steel was observed to be stronger than that of the stainless steel. The adhesion strength was generally, observed to decrease with the same tendency regardless of the kinds of substrates. The adhesion strength of tool steel was increased more and more strongly than that of stainless steel as heat-treated temperature was increased. The strength of tool steel was appeared to be high adhesion strength at $400^{\circ}C$. From the failure mode of the film during the scratch adhesion test, the cohesive failure was observed to be obvious and the adhesive failure in a minor portion in the Zr/ZrN doublelayer regardless of the kinds of substrates.

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.6
• /
• pp.307-310
• /
• 2011

We have investigated the structural, electrical and optical properties of $In_2O_3$ thin films deposited by RF magnetron sputtering and then annealed at $150^{\circ}C$ and $300^{\circ}C$ in vacuum. The structural and electrical properties are strongly related to annealing temperature. All the annealed $In_2O_3$ films are grown as a hexagonal wurtzite phase and the largest grain size is observed in the films annealed at $300^{\circ}C$. The sheet resistance decreases with a increase in annealing temperature and $In_2O_3$ film annealed at $300^{\circ}C$ shows the lowest sheet resistance of $174{\Omega}/{\Box}$. The optical transmittance of $In_2O_3$ films in a visible wavelength region also depends on the annealing temperature. The films annealed at $300^{\circ}C$ show higher transmittance of 76% than those of the films prepared in this study.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.235-235
• /
• 2009

This paper describes the influence of a polycrystalline (poly) 3C-SiC buffer layer on the surface acoustic wave (SAW) properties of poly aluminum nitride (AlN) thin films by comparing the center frequency, insertion loss, the electromechanical coupling coefficient ($k^2$), andthetemperaturecoefficientoffrequency(TCF) of an IDT/AlN/3C-SiC structure with those of an IDT/AlN/Si structure, The poly-AlN thin films with an (0002)-preferred orientation were deposited on a silicon (Si) substrate using a pulsed reactive magnetron sputtering system. Results show that the insertion loss (21.92 dB) and TCF (-18 ppm/$^{\circ}C$) of the IDT/AlN/3C-SiC structure were improved by a closely matched coefficient of thermal expansion (CTE) and small lattice mismatch (1 %) between the AlN and 3C-SiC. However, a drawback is that the $k^2(0.79%)$ and SAW velocity(5020m/s) of the AlN/3C-SiC SAW device were reduced by appearing in some non-(0002)AlN planes such as the (10 $\bar{1}$ 2) and (10 $\bar{1}$ 3) AlN planes in the AlN/SiC film. Although disadvantages were shown to exist, the use of the AlN/3C-SiC structure for SAW applications at high temperatures is possible. The characteristics of the AlN thin films were also evaluated using FT-IR spectra, XRD, and AFM images.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.346-346
• /
• 2012

We investigated electrical and optical properties and chemical states of amorphous In-Ga-Zn-O (a-IGZO) thin films deposited at different substrate temperatures (from room temperature to $300^{\circ}C$). a-IGZO thin films were fabricated by radio frequency magnetron sputtering using $In_2O_3$ : $Ga_2O_3$ : ZnO = 1 : 1 : 1 target, and their electrical and optical properties and chemical states were investigated by Hall-measurement, UV-visible spectroscopy and x-ray photoelectron spectroscopy (XPS), respectively. The data showed that as substrate temperature increased, carrier concentration increased, but mobility, conductivity, transmittance in the shorter wavelength region (>350 nm), and the Tauc-plot-estimated optical bandgap decreased. XPS data indicated that the intensity of In 3d peak compared to Ga 3d peak increased but the intensity of Zn 3d peak compared to Ga 3d decreased, and that, from the deconvoluted O 1s peak, defects or oxygen vacancies and non-quaternary contents increased as the temperature increased. The relative intensity changes of the In, Zn, and O 1s sub-component are suggested to explain the changes in electrical and optical properties.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.3
• /
• pp.39-45
• /
• 1998

SrBi$_{2}$Ta$_{2}$O$_{9}$ (SBT) ferroelectric thin films for nonvolatile memory were prepared on Pt/Ti/SiO$_{2}$/Si and RuO$_{2}$/SiO$_{2}$/Si substrates by RF magnetron sputtering. The dependences of crystalline and electrical properties on the lower electrode type(Pt and RuO$_{2}$) and the annealing temperatures were investigated. SBT films regardless of their electrode types showed typeical Bi layered peroviskite crystal structures. The crystalline quality of as-deposited SBT films was improved by the rapid thermal annealing at 650.deg. C for 30 sec. The remanetn polarization of 2Pr (Pr+-Pr-) of the annealed SBT films deposited on Pt/Ti/SiO$_{2}$/Si substrates were about 11 .mu.C/cm$^{2}$ and 3 .mu.C/cm$^{2}$, respectively. The leakage currents at 3 V bias voltage were about 0.8 .mu.A/cm$^{2}$ for SBT/ Pt/Ti/SiO$_{2}$/Si and about 1 .mu.A/cm$^{2}$ for SBT/RuO$_{2}$/SiO$_{2}$/Si sample. SBT films annealed at 650 .deg. C showed no degradation in Pr values after 10$^{11}$ polarization switching cycles, indicating good fatigue properties. In addition, for SBT samples deposited on Pt/Ti/SiO$_{2}$/Si, Pr values increased to more than that of initial state, suggesting the increament of leakage current caused by repeated polarization.