• Asian-Australasian Journal of Animal Sciences
• /
• 제28권7호
• /
• pp.1053-1060
• /
• 2015

In this study, the optimal operation factors for struvite crystallization for removing and recovering nitrogen and phosphorus from anaerobic digestive fluid of swine manure containing highly concentrated nitrogen was determined. Every experiment for the struvite crystallization reaction was conducted by placing 1,000 mL of digestion fluid in a 2,000 mL Erlenmeyer flask at various temperatures, pH, and mixing speed. Except for special circumstances, the digestion fluid was centrifuged (10,000 rpm, 10 min) and then the supernatant was used for the experiment at room temperature and 100 rpm. The optimal mole ratio of $PO_4{^{3-}}:Mg^{2+}$ was 1:1.5, and the pH effect ranging from 9 to 11 was similar, when mixed for 1 hour. Under this condition, the removal efficiency of $NH_4{^+}-N$ and $PO_4{^{3-}}-P$ was 40% and 88.6%, respectively. X-shaped crystal was observed by light and scanning electron microscopy. In addition, struvite crystal structure was confirmed through X-ray diffraction analysis.

• Journal of Pharmaceutical Investigation
• /
• 제13권1호
• /
• pp.1-9
• /
• 1983

The effect of humidity on crystallization and polymorphic transformation of hydrous aluminum oxide under various humidity at $37^{\circ}$ was examined by means of X-ray diffraction, scanning electron micrograph, IR spectra and DTA. The humidity was an important factor influencing crystallization of hydrous aluminum oxide. The growth or crystal was strongly accelerated by humidity. The aging process is assumed that it is composed of two seperate steps, an increase of the diffraction around $36{\sim}42^{\circ}$, and an appearance and its development of the peak at $18{\sim}20^{\circ}$ of $2{\theta}$ value. The former is considered to be nucleation and the latter correspond to the growth period on crystallization. The crystalline form of aging products was various depending on the degree of humidity, directly it leads to the eventual formation of bayerite in more than 72%, $b{\"{o}}hmite$ in 50% and resembled to Nordstandite in 0% relative humidity, respectively but once formed, it was mostly stable in each surroundings and does not transform to the other more stable form in solid state even after aging for five years. The mechanism responsible for aging is further polymerization process of six-membered rings by deprotonation-dehydration reaction in which positively charged polynuclear hydroxy aluminum complexes formed in the presence of moisture are joined at their edges by double hydroxide bridges.

• 한국세라믹학회지
• /
• 제35권7호
• /
• pp.706-714
• /
• 1998

The MgO-{{{{ { {Al }_{2 }O }_{3 } }}-{{{{ { {SiO }_{2 } }_{ } }}system containing alumina powder was fabricated sintered at various temperature and analyzed in order to study the sintering mechanism and crystallization characteristics. The specimen composed of glass powder with average particle size of 8.27 $\mu\textrm{m}$ and 0-40 vol% alumina powder were sint-ered for 3 hrs at the temperature between 850$^{\circ}C$ and 1350$^{\circ}C$ The sintering mechanism consists of the redis-tribution of particles occuring at 750$^{\circ}C$ and the viscous flow at 850∼950$^{\circ}C$. The degree of crystallization and sintering temperatue were dependent upon the ratio of glass/alumina. The second phase from the reaction between glass and alumina was not observed which was confirmed by XRD and properties analysis. The density dielectric constant and specific resistivity of specimen were 2.30∼3.26g/cm2 5.8∼7.38 at 1 GHz density dielectric constant and specific resistivity of specimen were 2.30∼3.26g/cm3 5.8∼7.38 at 1GHz and 1.23∼4.70${\times}$107 $\Omega$$.$m respectively.

• 한국응용과학기술학회지
• /
• 제26권3호
• /
• pp.317-327
• /
• 2009

In this study DMT(Dimethylterephthalate), NDC(Dimethyl-2, 6-Naphthalene Dicarboxylate) were used to synthesize polyester polyol which shows enhanced storage stability, improved flame retardancy, and good compressive strength. If DMT and NDC react respectively with DEG(Diethylene Glycol) which is kind of linear diol, the obtained polyester polyols tend to crystallize easily after the reaction. In case of DMT, PA(Phthalic Anhydride) which has asymmetric structure was introduced to retard the crystallization. In case of NDC, DPG(Dipropylene Glycol) which has an methyl side chain was introduced to prevent the crystallization. It was found that to introduce DPG was much more effective method to prevent the crystallization than PA. NDC and DMT were reacted together with DPG for various compositions of NDC:DMT(8:2, 6:4, 4:6 mol ratio). The obtained NDC-DMT-DPG based polyester polyol showed improved flame retardancy, and good compressive strength with increasing the content of NDC.

• 한국세라믹학회지
• /
• 제33권6호
• /
• pp.693-699
• /
• 1996

YIG precursor powder was obtained by homogeneous precipitation in chloride salt solution by thermal decom-position of urea. It was found that ferric ions precipitated prior to yttrium ions. The precipitate was minute and spherical in shape. The precipitate formed consisted of the mixture of amorphous and ferric oxyhydroxide. Crystallization of YIG was proceeded by solid state reaction of intermediate YFeO3 and Fe2O3 in the temperature range of 85$0^{\circ}C$ to 140$0^{\circ}C$. Single phase of YIG was obtained by heat-treatment of the powder at 140$0^{\circ}C$ for 6 hrs in air. The powder calcined was molded into pellets and sintered in air. The maximum density of 4,92 g/cm3(95.1% of theoretical density) was obtainable for the pellet sintered at 145$0^{\circ}C$ using the powder calcined at 90$0^{\circ}C$.

• 한국세라믹학회지
• /
• 제39권4호
• /
• pp.420-426
• /
• 2002

가열가수분해반응에 의하여 제조된 구형의 $ZrO_2$ 겔을 수열결정화시켜 순수한 $ZrO_2$ 분말과 $Y2_O_3$, CaO 등 상안정화제가 도핑된 $ZrO_2$ 분말을 합성하였다. 합성된 $ZrO_2$ 결정분말들은 평균 10nm 크기의 일차 입자들로 구성된 이차입자들이었다. 이차입자의 평균 크기는 $0.4{\mu}m$였고, 수열결정화과정에서 겔의 구형 형상이 그대로 유지되었으며 일차 입자들 사이에는 약한 응집으로 존재하였다. 입자모양, 크기, 상분율, 도핑된 분율 등을 SEM, TEM, XRD, ICP로 연구하였고 구형 겔의 수열결정화기구를 논의하였다.

• 방사선산업학회지
• /
• 제4권4호
• /
• pp.313-317
• /
• 2010

The struvite crystallization was applied to remove $NH_4{^+}$ in livestock wastewater. The ammonium ions can be very toxic to the aquatic creatures. In this experiments, the livestock wastewater from Gongju livestock wastewater treatment plant was used. The behaviors of various parameters such as pH, mole ratio of $Mg^{2+}$ : $NH_4{^+}$ : $PO{_4}^{3-}$ and reaction temperature for struvite crystallization of livestock wastewater and the effect of gamma ray irradiation were evaluated. As results, for the pH variation, the $NH_4{^+}$ removal efficiency showed the highest, 88%, at pH 9~9.25. The removal efficiency of $NH_4{^+}$, $Mg^{2+}$ and $PO{_4}^{3-}$ was showed highest when same molar ratio of $Mg^{2+}$ and $PO{_4}^{3-}$ were applied. The $NH_4{^+}$ removal efficiency showed 82% at $7^{\circ}C$, and 90% at $30^{\circ}C$ with temperature. When the wastewater was irradiated with 20 kGy of gamma ray, $NH_4{^+}$ was removed as much as 83%.

• Korean Chemical Engineering Research
• /
• 제47권2호
• /
• pp.213-219
• /
• 2009

탄산칼슘의 Biomineralization 반응을 수행하기 위해 다양한 아미노산을 첨가하여 결정화 실험을 하였다. 탄산칼슘의 액체-액체 반응으로 염화칼슘과 탄산나트륨을 사용하였고, Silk fibroin, 아스파라긴, 아스파르트산, 글루탐산과 글리신과 같은 첨가제를 사용하여 실험을 수행하였다. 그리고 결정화 반응에서 반응 시간, pH, 용질의 농도를 변경하여 탄산칼슘 결정의 형태 변화를 조사하였다. 결정의 분석을 수행하기 위해 XRD, FE-SEM 그리고 FT-IR 장치를 사용하였다. XRD로 칼사이트와 베터라이트의 결정과 피크 강도를 계산하였다. FE-SEM으로 결정의 외형과 크기를 비교하였고, FT-IR 스펙트럼으로 결정을 확인하였다. 반응 시간에 따른 결정의 분포는 XRD의 피크 영역과 FT-IR의 데이터로 확인하였다.

• 공업화학
• /
• 제31권3호
• /
• pp.299-304
• /
• 2020

나노입자는 많은 화학합성에서 중요한 촉매역할을 한다. 촉매로 이용되는 나노입자를 합성할 때 colloidal synthesis를 많이 활용하고 있다. Colloidal synthesis를 이용해 나노입자를 합성할 경우 환원제, capping agent, shape directing agent 등이 촉매에 surface poisoning을 일으켜 촉매의 특성이 낮아질 수 있으며 합성 및 분리 과정 중 유해폐기물의 발생한다. Colloidal synthesis에서 사용되는 첨가제들의 양을 줄여 합성할 수 있는 새로운 나노입자를 합성법을 개발하여 은나노입자를 합성하였다. 결정화 기술을 이용하여 환원제, capping agent의 양을 줄일 수 있고 더욱이 합성된 나노입자 표면의 흡착되는 물질의 양을 줄여 surface poisoning을 낮출 수 있었다. 환원제로는 단당류와 이당류를 이용하여 surface poisoning이 거의 없는 은 나노입자는 resazurin의 산화환원 반응의 촉매로 이용할 수 있어 은 나노입자를 이용한 촉매 반응의 메커니즘을 분석하였다.

• 한국표면공학회지
• /
• 제29권6호
• /
• pp.683-690
• /
• 1996

In this study, the diffusion barrier properties of $1000 \AA$ thick molybdenum compounds (Mo, Mo-N, $MoSi_2$, Mo-Si-N) were investigated using sheet resistance measurements, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Scanning electron microscopy (SEM), and Rutherford backscattering spectrometry (RBS). Each barrier material was deposited by the dc magnetron sputtering, and annealed at 300-$800^{\circ}C$ for 30min in vacuum. Mo and $MoSi_2$ barrier were failed at low temperature due to Cu diffusion through grain bound-aries and defects of Mo thin film and the reaction of Cu with Si within $MoSi_2$ respectively. A failure temperature could be raised to $650^{\circ}C$-30min in the Mo barrier system and to $700^{\circ}C$-30min in the Mo-silicide system by replacing Mo and $MoSi_2$ with Mo-N and Mo-Si-N, respectively. The crystallization temperature in the Mo-silicide film was raised by the addition of $N_2$. It is considered that not only the N, stuffing effect but also the variation of crystallization temperature affects the reaction of Cu with Si within Mo-silicide. It was found that Mo-Si-N is more effective barrier than Mo, $MoSi_2$, or Mo-N to copper penetration preventing Cu reaction with the substrate for 30min at a temperature higher than $650^{\circ}C$.