• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2009년도 9th International Meeting on Information Display
• /
• pp.614-615
• /
• 2009

For the high reflectance under the ambient light condition, a highly efficient diffractive reflector has been proposed, based on a micro grating structure.[1] This reflector was designed to show highly concentrated distribution of the reflected light to the normal direction of the reflector under specific incident conditions of the light. In order to apply a diffractive reflector to a reflective liquid crystal display, the coupling between the viewing angle characteristics of a liquid crystal (LC) cell and the reflective distribution of the reflector should be considered. Under the optimum configuration confirmed through the analysis of the coupling between a LC cell and a reflector, a reflective vertical alignment (VA) cell with a diffractive reflector shows contrast ratio and brightness much higher than that with a conventional bumpy reflector.

• 한국전기전자재료학회논문지
• /
• 제16권4호
• /
• pp.336-342
• /
• 2003

(Sm/Y)$_{1.8}$B $a_{2.4}$C $u_{3.4}$$O_{7-x}$ [(Sm/Y)1.8] high $T_{c}$ superconductors were directionally grown by Rod-type Seed Melt Growth(RSMG) process in air atmosphere. The sintered polycrystalline N $d_{1.8}$B $a_{2.4}$C $u_{3.4}$$O_{7-x}$(Nd1.8) of rod-type seed crystal grown by extrusion mold process were used for achieving the ab-plane alignment haying large grains perpendicular to the center of (Sm/Y)1.8 samples. The observations using TEM micrographs of the melt-textured (Sm/Y)1.8 samples revealed that the nonsuperconducting (Sm/Y)211 inclusions are uniformly distributed in the superconducting (Sm/Y)123 matrix. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The RSMG (Sm/Y)1.8 samples showed an onset $T_{c}$ $\geq$ 90 K and sharp superconducting transition.nsition.ion.nsition.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 춘계학술대회 논문집 디스플레이 광소자 분야
• /
• pp.185-188
• /
• 2005

We synthesized the two types of photoalignment material of high thermal resistance with hydroxyl aromatic polyimide, and studied the liquid crystal (LC) aligning capabilities on the photopolymer layers. Also, electro-optical (EO) performances for the twisted-nematic (TN)-liquid crystal display (LCD) photoaligned with linearly polarized UV exposure were investigated. A good LC alignment with UV exposure on the two types of photopolymer surface can be obtained. The Voltage-transmittance (V-T) curve in the photoaligned TN cell with UV exposure was different from two type. The response time of photoaligned TN cell was measured about 21 ms in two alkyl chain and about 15ms in four alkyl chain.

• Transactions on Electrical and Electronic Materials
• /
• 제9권5호
• /
• pp.202-205
• /
• 2008

We have studied the liquid crystal (LC) orientation behavior on the organic hybrid overcoat layer with ion beam irradiation. Excellent LC alignments of the nematic liquid crystal (NLC) on the ion beam irradiated organic hybrid overcoat layers were observed in various intensities above 600 eV. Pretilt angles of the NLC on the organic hybrid overcoat layers for all ion beam energy intensities were observed from 0.2 to 0.5 degrees. Also, we used the atomic force microscopy (AFM) images for measuring the roughness of the organic hybrid overcoat layers with ion beam irradiation before and after. The surface of organic hybrid overcoat layers was leveled off by the ion beam irradiation. Finally, a good LC alignment thermal stability on the organic hybrid overcoat layer with ion beam irradiation can be achieved.

• 폴리머
• /
• 제35권3호
• /
• pp.272-276
• /
• 2011

선택 반사를 보여주는 콜레스테릭 액정의(cholesteric liquid crystal; CLC) planar 배열이 유도되는 메카니즘을 CLC 셀의 선택 반사율과 FTIR $C{\equiv}N$ 피크 세기를 측정하여 조사하였다. 배향막을 사용한 경우보다는 planar 배열 유도가 완전하지는 않았지만 shear force를 이용하거나 또는 고분자 기판을 연신하여 배향막을 사용하지 않은 상태에서 planar 배열을 유도하였다. CLC의 planar 배열이 유도되는 메카니즘은 기판 표면에 접촉하는 액정분자들이 한 방향으로 늘어서면, 그 액정분자 위에 CLC의 나선 구조들이 기판에 수직으로 형성되며 planar 배열이 유도되는 것이다.

• 열처리공학회지
• /
• 제7권1호
• /
• pp.61-71
• /
• 1994

This study is to investigate the stress distributions, crystal orientations and magnetic properties during die-upsetting according to working temperature of Nd-Fe-B-Cu alloys. The stress distributions in the specimens during compressing process were calculated by a finite element method program(SPID). The calculated stresses were effective stress (${\sigma}_{eff}$), compression stress(${\sigma}_z$), radial direction stress(${\sigma}_r$) rotational direction stress(${\sigma}_e$) and shear stress(${\tau}_{rz}$). The stress distributions of ${\sigma}_z$, obtained by a computer simulation showed that the stress components causing the magnetic alignment during die-upsetting of the cast magnets were very high at the center-part of a specimen, and decreased toward the periphery-part of a specimen. In view of the above results the magnetic properties should be better at the center-part of a specimen than any other parts. But the measured magnetic properties were better at the mid-part. These results should be due to the fact that the specimens were casted. Normally the magnetic properties are affected by the casting process as well as by the stress levels. ${\sigma}_r$, ${\sigma}_e$ are thought to affect the liquid phase flowing and domain patterns, respectively. The influence of ${\tau}_{rz}$ was trivial, ${\sigma}_{eff}$ distributed similar throughout the specimen. The Nd-rich phase appeared at the peripheral of the specimen where the stress level of ${\sigma}_r$, ${\sigma}_z$, was low or the stress level of ${\sigma}_e$ was high. The Nd-rich phase was squeezed out during die-upsetting. This phase had an effect on the crystal orientation and grain growth. The stress distributions of alloy were irregular at the parts of the specimen where the die contacted with specimen.

• Journal of the Optical Society of Korea
• /
• 제13권4호
• /
• pp.428-433
• /
• 2009

A photonic crystal fiber with two large air holes outside the holey cladding region is fabricated to induce an effective long periodic grating (LPG) in the core by an electric arc discharge. We believe that the two large air holes lead to the asymmetric perturbation in the core under the electric arc discharge, thereby introducing the coupling to the first higher-order mode. The transmission characteristics of the PCF with the LPG for the external perturbation such as strain, curvature, and temperature are also investigated. It was found that the shift of resonance peak in the transmission spectrum depends on the bending direction. The curvature of 8.55 $m^{-1}$ results in the center wavelength shifts of 1.8, 4.3, and 11 nm for a vertical, diagonal, and horizontal direction of the curvature to the large air-hole alignment, respectively.

• 공업화학
• /
• 제22권1호
• /
• pp.81-86
• /
• 2011

자기 조립성 염료인 Sunset Yellow-FCF 수용액은 상온에서 농도 25 wt%부터 schlieren 구조의 액정상을 보이기 시작하여, 28 wt% 이상이면 완전한 네마틱 액정상으로 관찰되었다. 전단배향에 의한 코팅으로 광학적 이방성 필름을 제조하기 위해서는 30 wt% 이상의 농도가 필요하였다. 액정 색소의 농도, 코팅속도, 건조 온도, 상대습도 등 코팅 변수가 최종 박막필름의 두께, 투과도에 미치는 영향 분석에 의하면, 최종 필름의 두께에는 용액의 농도가 가장 큰 영향을 주었으며, 평행방향의 투과도에는 건조 온도와 농도의 영향이 가장 컸다. 특히 Sunset Yellow-FCF의 농도 증가로 전단코팅에 의한 배향성이 개선되고 높은 편광도를 갖는 필름제조가 가능하였다. 본 실험에서는 33 wt%의 Sunset Yellow-FCF 수용액을 사용하면, 89.7~98.7%의 편광도를 갖는 광학적 이방성 필름이 제조되었다.

• 폴리머
• /
• 제34권1호
• /
• pp.32-37
• /
• 2010

액정표시소자의 광배향막으로 적용하기 위하여 올리고머 신나메이트와 폴리(비닐 신나메이트) (PVCi)의 블렌드를 이용하여 그루브 패턴을 형성하고 광배향 특성을 관찰하였다. UV-vis 스펙트럼 분광계를 이용하여 자외선 조사 시간에 따른 광반응 속도를 평가한 결과 올리고머 신나메이트는 폴리(비닐 신나메이트)에 비해 빠른 반응속도를 나타내었다. 폴리(비닐 신나메이트)를 주성분으로 하여 올리고머 신나메이트를 블렌드한 경우 반응속도가 약간 향상되는 특성을 확인하였다. 올리고머 신나메이트는 높은 결정성으로 인해 표면 그루브 패턴을 단독으로 형성할 수 없었지만 폴리(비닐 신나메이트)와의 블렌드를 통하여 그루브 패턴을 형성할 수 있었으며 그루브 패턴에서도 polar plot에 의해 분자 배향성을 나타냄을 확인하였다. 올리고머 신나메이트와 고분자계 신나메이트의 블렌드를 통하여 반응속도의 향상과 박막 구조의 패턴을 형성하기에 적합함의 확인을 통해 새로운 광배향막 재료로 적용 가능함을 알 수 있었다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 하계학술대회 논문집 D
• /
• pp.1815-1817
• /
• 1999

In this paper, the generation of high pretilt angle in nematic liquid crystal (NLC) by dipping effect on three kinds of the rubbed polyimide (PI) surface was investigated. The generated pretilt angle of NLC increases due to dipping effect before rubbing treatment on two kinds of the rubbed PI surface with side chain. The generated pretit angle in NLC by using dipping effect after rubbing treatment on PI surface with short side chain is high compared to the PI surface with long side chain. The generated pretit angle of the positive type NLC $(\Delta{\varepsilon}>0)$ is higher as than that of the negative type NLC $({\Delta}{\varepsilon}<0)$ by using dipping effect before rubbing treatment on homeotropic layer. The generated pretilt angle of NLC is attributed to perpendicular component of permittivity ${\varepsilon}_{\perp}$ of NLC on rubbed PI surface.