• 한국안전학회지
• /
• 제9권4호
• /
• pp.29-41
• /
• 1994

High temperature tensiles tests, steady state creep tests, internal stress tests and creep rupture tests using Al 7075 alloy were performed over the temperature range of 9$0^{\circ}C$~50$0^{\circ}C$ and stress range of 0.64~17.2(kgf/$\textrm{mm}^2$) in order to investigate the creep behavior and predict creep rupture life From the apparent activation energy Qc and the applied stress exponent n measured, at the temperature range of 9$0^{\circ}C$~l2$0^{\circ}C$, the creep deformation seemed to be controlled by cross slip. On the other hand at the temperature of 20$0^{\circ}C$~23$0^{\circ}C$ the creep deformation seemed to be controlled by dislocation climb but at 47$0^{\circ}C$~50$0^{\circ}C$, by diffusion creep. And the rupture life(t$_{f}$) might be represented by anthermal process attributed to the difference of the applied stress dependence of Internal stress and the ratio of the Internal stress to the applied stress, the thermal activated process attributied to the temperature dependence of the internal stress. Also the ratio between stress dependence of primary creep rate and that of minimum creep rate was measured 0.46, the minimum creep rate is expected to be appromately obtained from master creep curve including the relationship primary creep rate and minumum creep rate. Finally the relationship new rupture parameter and logarithmic stress was represented with including the ratio between the dependence of primary creep rate and that of minimum creep rate, using the new rupture parameter the rupture life predition is exactly expected.d.

• 한국재료학회지
• /
• 제23권7호
• /
• pp.385-391
• /
• 2013

The influence of Cu and Ni on the ductile-brittle transition behavior of metastable austenitic Fe-18Cr-10Mn-N alloys with N contents below 0.5 wt.% was investigated in terms of austenite stability and microstructure. All the metastable austenitic Fe-18Cr-10Mn-N alloys exhibited a ductile-brittle transition behavior by unusual low-temperature brittle fracture, irrespective of Cu and/or Ni addition, and deformation-induced martensitic transformation occasionally occurred during Charpy impact testing at lower temperatures due to reduced austenite stability resulting from insufficient N content. The formation of deformation-induced martensite substantially increased the ductile-brittle transition temperature(DBTT) by deteriorating low-temperature toughness because the martensite was more brittle than the parent austenite phase beyond the energy absorbed during transformation, and its volume fraction was too small. On the other hand, the Cu addition to the metastable austenitic Fe-18Cr-10Mn-N alloy increased DBTT because the presence of ${\delta}$-ferrite had a negative effect on low-temperature toughness. However, the combined addition of Cu and Ni to the metastable austenitic Fe-18Cr-10Mn-N alloy decreased DBTT, compared to the sole addtion of Ni or Cu. This could be explained by the fact that the combined addition of Cu and Ni largely enhanced austenite stability, and suppressed the formation of deformation-induced martensite and ${\delta}$-ferrite in conjunction with the beneficial effect of Cu which may increase stacking fault energy, so that it allows cross-slip to occur and thus reduces the planarity of the deformation mechanism.

• 한국전산구조공학회논문집
• /
• 제30권5호
• /
• pp.381-387
• /
• 2017

섬유강화 복합재료는 열팽창 계수의 방향성을 갖고 있을 뿐만 아니라 제작과정 온도와 실제 사용온도 사이의 차이 때문에 필연적으로 열응력 효과를 받게 된다. 이러한 열응력에 의한 파손현상은 실제 항공우주산업에서의 응용이 증대되고 있는 두꺼운 복합 적층판의 경우에 더욱 현저한 현상으로 적층판의 역학적 기능 및 파단강도에 큰 영향을 미치게 된다. 본 연구에서는 복잡한 재질로 구성되고 높은 세장비를 가진 블레이드 날개 구조의 차원축소 및 열 응력 복원 이론을 소개하고 3차원 유한요소모델과 비교결과를 통해 효율성과 정확성을 입증한다. 또한 차원을 축소한 모델링을 구성하고 복원이론를 이용하여 열적 환경에 적용된 복합재 보 단면의 열응력을 차원 복원하고 시각적으로 형상화하는 효율적인 복원해석 과정을 소개하고자 한다.

• 한국주조공학회지
• /
• 제27권5호
• /
• pp.203-208
• /
• 2007

The high temperature properties of vanadium and molybdenum added high silicon ductile iron, so called V-Mo-Si ductile iron, were investigated. The (V,Mo) complex carbides and Mo carbides precipitated at the cellular boundaries of the as-cast specimens. The microhardness of the (V,Mo) carbides were in the range of 553-619, while that of the Mo carbides in the range of 341-390. The thermo-mechanical tests were carried out with a Gleeble system at 700 and $800^{\circ}C$ under vacuum condition. The tensile strengths of the specimen tested at $700^{\circ}C$ with the dynamic deformation rate of 50 mm/sec and those with the static deformation rate of 0.15 mm/sec were 235.7 and 115.3 MPa, while the reduction in area were 23.7 and 22.4%, respectively. At the high dynamic deformation rates, the tensile strength was steeply increased due to promoting the brittle fracture of pearlite in the matrix of the specimens. But the changes of the reduction in area with the deformation rates on the same specimens were negligible. The weight gain of the V-Mo-Si specimens oxidized in the air atmosphere for 6 hours at 800 and $900^{\circ}C$ were 1.1 and 4.1.%, respectively. The cross-sectional microstructure of oxidized specimens consisted of the porous external scale layer grown outside from the original surface, the dense internal scale layer grown into the original surface, the decarburized ferrite layer between the internal scale and the matrix of base metal. The (V,Mo) carbides and Mo carbides formed in the matrix of as-cast specimen did not decompose during oxidation at 900 for 24 hours in air atmosphere.

• The Journal of Advanced Prosthodontics
• /
• 제2권1호
• /
• pp.14-17
• /
• 2010

PURPOSE. The purpose of this study was to investigate the diametral tensile strength of polymer-based temporary crown and fixed partial denture (FPD) materials, and the change of the diametral tensile strength with time. MATERIAL AND METHODS. One monomethacrylate-based temporary crown and FPD material (Trim) and three dimethacrylate-based ones (Protemp 3 Garant, Temphase, Luxtemp) were investigated. 20 specimens (${\phi}\;4\;mm\;{\times}\;6\;mm$) were fabricated and randomly divided into two groups (Group I: Immediately, Group II: 1 hour) according to the measurement time after completion of mixing. Universal Testing Machine was used to load the specimens at a cross-head speed of 0.5 mm/min. The data were analyzed using one-way ANOVA, the multiple comparison Scheff$\acute{e}$ test and independent sample t test ($\alpha\;=\;0.05$). RESULTS. Trim showed severe permanent deformation without an obvious fracture during loading at both times. There were statistically significant differences among the dimethacrylate-based materials. The dimethacrylate-based materials presented an increase in strength from 5 minutes to 1 hour and were as follows: Protemp 3 Garant (23.16 - 37.6 MPa), Temphase (22.27 - 28.08 MPa), Luxatemp (14.46 - 20.59 MPa). Protemp 3 Garant showed the highest value. CONCLUSION. The dimethacrylate-based temporary materials tested were stronger in diametral tensile strength than the monomethacrylate-based one. The diametral tensile strength of the materials investigated increased with time.

• Structural Engineering and Mechanics
• /
• 제35권5호
• /
• pp.571-592
• /
• 2010

An energy-based fatigue life prediction framework was previously developed by the authors for prediction of axial, bending and shear fatigue life at various stress ratios. The framework for the prediction of fatigue life via energy analysis was based on a new constitutive law, which states the following: the amount of energy required to fracture a material is constant. In the first part of this study, energy expressions that construct the constitutive law are equated in the form of total strain energy and the distortion energy dissipated in a fatigue cycle. The resulting equation is further evaluated to acquire the equivalent stress per cycle using energy based methodologies. The equivalent stress expressions are developed both for biaxial and multiaxial fatigue loads and are used to predict the number of cycles to failure based on previously developed prediction criterion. The equivalent stress expressions developed in this study are further used in a new finite element procedure to predict the fatigue life for two and three dimensional structures. In the second part of this study, a new Quadrilateral fatigue finite element is developed through integration of constitutive law into minimum potential energy formulation. This new QUAD-4 element is capable of simulating biaxial fatigue problems. The final output of this finite element analysis both using equivalent stress approach and using the new QUAD-4 fatigue element, is in the form of number of cycles to failure for each element on a scale in ascending or descending order. Therefore, the new finite element framework can provide the number of cycles to failure at each location in gas turbine engine structural components. In order to obtain experimental data for comparison, an Al6061-T6 plate is tested using a previously developed vibration based testing framework. The finite element analysis is performed for Al6061-T6 aluminum and the results are compared with experimental results.

• 한국구조물진단유지관리공학회 논문집
• /
• 제17권5호
• /
• pp.136-145
• /
• 2013

최근 발생한 대규모 지진으로 구조물의 내진보강에 대한 사회적 관심도가 높아지고 있다. 특히 내진 설계가 반영되지 않은 기둥은 취성적인 파괴로 구조물 전체붕괴를 유발하기 때문에 내진보강이 적용 되어야한다. 과거에는 단면증설법, 강판보강법등이 주로 적용되었고 최근에는 복합재료의 장점을 이용한 섬유보강법이 선호되고 있다. 그러나 이러한 보강법들은 구조물의 물리적 손상을 유발하며, 작업공간과 시간소비가 크다는 단점이 있다. 본 연구에서는 기존 보강법의 단점을 보강하여 복합재료 (Fiber reinforced polymer)와 Aluminum 체결부 이용한 FRP 내진보강재를 개발하였다. 비선형 유한요소 해석프로그램을 통해 개발된 FRP 내진보강재의 최적 보강량을 결정하였다.

• Restorative Dentistry and Endodontics
• /
• 제26권1호
• /
• pp.23-31
• /
• 2001

The purpose of this study was to search the optimal silane concentrations for filler- silanization of seven experimental composites. Silica filer was a 25micron crushed type. 0.0%, 0.5%, 1.0%, 1.5%, 2.0%, 2.5%, and 3.0% silane($\gamma$-methacrylooxypropyltrimethoxysilane)were added into silica-filler with weight percentage (wt%). Mixtures(silica filler/silane)were reacted at 6$0^{\circ}C$ for 72hours, and crushed into fine particles those were used as fillers for 7 experimental composites. Monomer was a 3 : 1 mixture of Bis-GMA and TEGDMA containing 0.2% tertiary amine and 0.4% camphoroquinone for light curability. A ratio for mixing the monomer and filler was 75% and 25% respectively. Seven experimental composites was classified with the concentration of silane treated, and the specimen number for each test was 10. Specimens with 6mm diameter and 3mm height dimension for measuring the diametral tensile strength were destroyed with 1mm/min cross-head speed on Instron universal testing machine (No. 4467, USA). Shear bond strength was measured on the specimens bonded to bovine enamel etched with 37% phosphoric acid solution for 1 minute Fractured surfaces were observed by SEM (Hitachi S-3200, Japan) among that of the highest values measured from each groups. Following results were obtained: 1. Experimental composites containing silanized filter showed the significantly higher diametral tensile strength and shear bond strength than the composites containing un-silanized fillers(Group1) (p<0.05). 2. In silanized filler composite resins(Group 2~7), Diametral tensile strength of Group 3 showed the significantly higher than that of Group 2 and Group 6(p<0.05). 3. Shear bond strength was higher in Group 3 than that of Group 7 (p＜0.05)in silanized fillers composite resins. 4. Fracture surface was formed in resin matrixes on the specimens from composites containing the fillers treated with 0.5% 1.0%, and 1.5% silane. These results mean that the optimal silane concentrations are exist for each fillet with its size and surface area, and that 1.0% is a optimal value for concentration to coat the 25$\mu\textrm{m}$ filler with silane.

• 한국지하수토양환경학회지:지하수토양환경
• /
• 제7권1호
• /
• pp.3-14
• /
• 2002

강원도 원주지역 암반대수층과 경기도 의왕지역 천층대수층에서 측정한 연속지하수위자료에 대해 시계열분석을 하였다. 연구에 사용한 시계열특성함수는 자기상관함수, 스펙트럼밀도함수, 그리고 상호상관함수이다. 분석결과 강원도 원주지역의 천층대수층의 지하수위는 자기상관성이 상대적으로 작고 상부토양층을 통한 강우의 직접적 침투에 민감하고 단열암반대수층의 지하수위는 상대적으로 외부자극(강우)에 안정적인데 이는 먼 곳으로부터 단열망을 통한 자극의 전파에 기인하거나 혹은 중간에 투수성이 낮은 비풍화편마암대의 영향으로 보인다. 의왕지역의 지하수위의 시계열적 특성은 원주지역의 단열암반대수층의 그것과 유사하다. 이는 지하수위측정 지역의 지하수함양이 직접적 강우침투보다는 광역적 함양과 그 스트레스의 전파에 기인하는 것으로 판단된다. 본 연구에서는 강우와 지하수위와의 시계열 분석이 지하수 함양기작 이해에 어떻게 이용되는지를 보여주었다.

• 근관절건강학회지
• /
• 제14권2호
• /
• pp.181-187
• /
• 2007

Purpose: The purpose of the study was to identify the relationship between obesity and bone mineral density in middle aged women. Methods: A cross-sectional survey design was utilized with a check list and physiological measurements. A total of 827 convenient samples were recruited from women who lived in the community. Bone mineral density was measured by T-score using the pixi method of Lumar on the left heel. Descriptive statistics and pearson correlation coefficient were utilized for data analysis. Results: Most were assessed as having normal weight(37.9%) or obese (57.4%) by BMI. Only 32% was assessed as having normal bone mineral density, while 40.3% had osteopenia, and 27.7% as osteoporosis. The BMI scores were significantly related to age, and episodes of fractures. Those with lower bone mineral density reported significantly more episodes of fractures and chronic disease. The T scores of Bone mineral density were significantly correlated with the scores of BMI (r= .126, p< .001). Conclusion: There is a strong need to develop intervention programs for this age group to manage bone mineral density loss to prevent occurrences of osteoporosis, and episodes of fracture.