• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.04a
• /
• pp.113-116
• /
• 2003

The investigation of delamination growth behavior in hybrid composite material such as FRMLs should be considered delamination growth rate, dA_D/da$ using the delamination shape factor, $f_S$ instead of traditional fracture mechanics parameters. The main objective of this study is to evaluate the relationship between delamination element (i. e. delamination width, b, delamination contour, c, delamination shape factor, $f_S$ and delamination growth rate, dA_D/da$) and delamination growth in FRMLs under cyclic bending moment. The delamination shape formed along the fatigue crack between aluminum layer and glass fiber/epoxy layer are measured by scanning method. The details of study are as follow : ⅰ) Relationship between crack length, a and delamination width, b. ⅱ) Variation of delamination growth rate, dA_D/da$ was attendant on delamination shape factors, $f_{S1}$, $f_{S2}$, $f_{S3}$. The test result indicated the delamination growth behavior depends in delamination element such as delamination width, b, delamination shape factors, $f_{S1}$, $f_{S2}$, $f_{S3}$.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.10
• /
• pp.154-160
• /
• 2001

For major structural components periodic inspections and integrity assessments are needed for the safety. However, many flaws are undetectable because sampling inspection is carried out during in-service inspection. Probabilistic integrity assessment is applied to take into consideration of uncertainty and variance of input parameters arise due to material properties and undetectable cracks. This paper describes a Probabilistic Fracture Mechanics(PFM) analysis based on the Monte Carlo(MC) algorithms. Taking a number of sampling data of probabilistic variables such as fracture toughness value, crack depth and aspect ratio of an initial surface crack, a MC simulation of failure judgement of samples is performed. for the verification of this analysis, a comparison study of the PFM analysis using a commercial code, mathematical method is carried out and a good agreement was observed between those results.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2003.04a
• /
• pp.398-404
• /
• 2003

Most previous researches for the hybrid composite materials such as FRMLs(Al/AFRP, Al/GFRP) have evaluated the fatigue delamination behavior using the traditional fracture mechanism. However, most previous researches have not generally been firmed yet. Because delamination growth behavior in hybrid composite should be consider delamination growth rate, $dA_D$/da using the delamination shape factors, fs instead of traditional fracture mechanic parameters. The major purpose of this study was to evaluate the relationship between delamination shape factor, fs and delamination growth rate, $dA_D$ . And a propose parameter on the delamination aspect ratio, b/a. The details of the study are as follow : 1) Relationship between crack length, a and delamination width,b. 2) Relationship between delamination aspect ration, b/a and delamination area rate,($(A_D)_{N}(A_D)_{ALL}$. 3) Variation of delamination growth rate, $dA_D/da$ was attendant on delamination shape factors, $fs_1$, $fs_2$, $fs_3$. The test results indicated the delamination growth rate depends on delamination shape factors.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.6
• /
• pp.59-66
• /
• 2020

Two octagonal RC bridge columns of small scale model were tested under cyclic lateral load with constant axial load. One in two specimens was solid cross section, the other was hollow cross section. The volumetric ratio of transverse spiral hoop of all specimens is 0.00206. The columns showed flexure-shear failure. Failure behavior and seismic performance were investigated. The test results showed that the structural performance of the hollow specimen such as initial crack pattern, initial stiffness, and energy dissipation performance was comparable to that of the solid specimen, but the lateral strength, ultimate displacement, energy dissipation performance of hollow specimen noticeably decreased after drift ratio of 3%.

• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.11-18
• /
• 2013

Cement concrete pavement offers long-term service life and excellent applicability for heavy traffic. It is easier to purchase and more durable and economical than the asphalt pavement. However, it is difficult to repair and rehabilitate compared to the asphalt pavement when it comes to the maintenance problem. Since the crack is the main reason of the damage of concrete pavement, it is necessary to control the early and long-term crack in the concrete pavement. In this experimental study, the basic performance tests have been carried out to investigate the effect of hybrid fibers which were composed of micro fibers with small diameter and high aspect ratio and macro fibers with large diameter and low aspect ratio on the concrete pavement, in which lower water ratio and larger aggregates were used compared to the general concrete mixture. The test results showed that the flexural strength and toughness of concrete pavement mixture have been increased with the use of hybrid fibers in the concrete pavement mixture, even though they were less effective compared to the normal concrete mixture. It was found that the hybrid fibers were effective to control the early shrinkage of the concrete pavement which is one of the main reasons of the damage in the concrete pavement.

• Nuclear Engineering and Technology
• /
• v.52 no.3
• /
• pp.614-620
• /
• 2020

In a previous study, delayed hydride cracking (DHC) assessment of pressurized water reactor (PWR) spent fuel during dry storage using the threshold stress intensity factor (K_IH) was performed. However, there were a few limitations in the analysis of the cladding properties, such as oxide thickness and mechanical properties. In this study, those models were modified to include test data for irradiated materials, and the cladding creep model was introduced to improve the reliability of the DHC assessment. In this study, DHC susceptibility of PWR spent fuel during dry storage depending on the axial elevation was evaluated with the improved assessment methodology. In addition, the sensitivity of affecting parameters such as fuel burnup, hydride thickness, and crack aspect ratio are presented.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.265-266
• /
• 2010

In this study, reduction of the crack in the lean concrete for pavements by combining different types of fibers is discussed to compare and verify its validities. Experimental result using NY fibers is depending on excellent aspect ratio and hydrophilic. Vebe time has shown good results. In addition, the addition of PP fiber had most favorable flexural strength.

• Transactions of Materials Processing
• /
• v.11 no.7
• /
• pp.608-613
• /
• 2002

An ultrasonic machining process is efficient and economical means for precision machining of glass and ceramic materials. However, the mechanism of the process with respect to the crack initiation and propagation and the stress development in the ceramic workpiece subsurface arc still not well understood. In this research, we have investigated the basic mechanism of ultrasonic machining of ultrasonic machining of glass by the experimental approach. For this purpose, we designed and fabricated the desktop micro ultrasonic machine. The feed is controlled precisely by using the constant load control system. During machining experiments, the effects of abrasive characteristics and machining conditions on the surface roughness and the material removal rate are measured and compared.

• Structural Engineering and Mechanics
• /
• v.72 no.1
• /
• pp.19-30
• /
• 2019

The mechanical behavior of Fiber Reinforced Cementitious Composites (FRCC) under direct shear is studied through experiment and analytical simulation. The cementitious composite considered contains 55% replacement of cement with fly ash and 2% (volume ratio) of short discontinuous synthetic fibers (in the form of mass reinforcement, comprising PVA - Polyvinyl Alcohol fibers). This class of cementitious materials exhibits ductility under tension with the formation of multiple fine cracks and significant delay of crack stabilization (i.e., localization of cracking at a single location). One of the behavioral parameters that concern structural design is the shear strength of this new type of fiber reinforced composites. This aspect was studied in the present work with the use of Push-off tests. The shear strength is then compared to the materials' tensile and splitting strength values.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.1
• /
• pp.1-8
• /
• 2017

Three small scale hollow circular reinforced concrete columns with aspect ratio 4.5 were tested under cyclic lateral load with constant axial load. Diameter of section is 400 mm, hollow diameter is 200 mm. The selected test variable is transverse steel ratio. Volumetric ratios of spirals of all the columns are 0.302~0.604% in the plastic hinge region. It corresponds to 45.9~91.8% of the minimum requirement of confining steel by Korean Bridge Design Specifications, which represent existing columns not designed by the current seismic design specifications or designed by seismic concept. The longitudinal steel ratio is 2.017%. The axial load ratio is 7%. This paper describes mainly crack behavior, load-displacement hysteresis loop, seismic performance such as equivalent damping ratio, residual displacement and effective stiffness and flexural over-strength of circular reinforced concrete bridge columns with respect to test variable. The regulation of flexural over-strength is adopted by Korea Bridge Design Specifications (Limited state design, 2012). The test results are compared with nominal strength, result of nonlinear moment-curvature analysis and the design specifications such as AASHTO LRFD and Korea Bridge Design Specifications(Limited state design).