• Corrosion Science and Technology
• /
• v.9 no.6
• /
• pp.259-264
• /
• 2010

In continuous hot dip galvanizing process, oxide formation on steel surface has an influence on Zn wetting. High strength automotive steel contains high amount of Si and Mn, where Si-Mn composite oxides such as $Mn_2SiO_4$ or $MnSiO_3$ covers the surface after annealing. Zn wetting depends on how the aluminothermia reaction can reduce the Mn-Si composite oxides and then form inhibition layer such as $Fe_2Al_5$ on the steel surface. The outward diffusion of metallic ions such as $Mn^{2+}$, $Si^{2+}$ in the steel matrix is very important factor for the formation of the surface oxides on the steel surface. The surface state and grain boundaries provide an important role for the diffusion and the surface oxide reactions. Some elements such as P, Sb, and B have a strong affinity for the interface precipitation, and it influence the diffusivity of metallic ions on grain boundaries. B oxide forms very rapildly on the steel surface during the annealing, and this promote complex oxides with $SiO_2$ or MnO. P has inter-reacted with other elements on the grain boundaries and influence the diffusion through on them. Small addition of Sb could suppress the decarburization from steel surface and retards the formation of internal and external selective oxides on the steel surface. Interface control by the trace elements such as Sb could be available to improve the Zn wettability during the hot dip galvanizing.

• Journal of Powder Materials
• /
• v.12 no.1
• /
• pp.43-50
• /
• 2005

Mechanical alloying using high-energy ball mill and subsequent spark plasma sintering (SPS) process was applied to Al-Fe-Cr and Al-Fe-Mo powder mixture to investigate effects of Cr and Mo addition on thermal stability of Al-Fe, and thereby to enhance its thermal stability up to $500^{\circC}$. Various analytical techniques including micro-Vickers hardness test, SEM, TEM, X-ray diffractometry and corrosion test were carried out. It was found that addition of Cr and Mo to Al-Fe system played a role of grain growth inhibitor of matrix Al and some precipitates such as $Al_3Fe$ during SPS and subsequent heat treatment. The inhibition of grain growth resulted in increased Vickers hardness and thermal stability up to $500^{\circC}$ comparing to those of Al-Fe alloy system.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.3
• /
• pp.135-138
• /
• 2015

A manganese dioxide (MnO₂) layer and zinc (Zn) layer are used as the cathode and the anode to develop filmtype manganese battery, in which a stack of a MnO₂ layer, gel electrolyte, and Zn layer are sandwiched between two plastic layers. This paper describes the chemical equation of swelling control upon the film-type manganese battery. We examined the reduction of hydrogen formation, by using calcium hydroxide Ca(OH)₂ as an additive in the electrolyte of film-type manganese battery. The phenomena or an effect of reduced hydrogen gas was proven by cyclic voltammogram, X-ray photoelectron spectra (XPS), and volume of hydrogen formation. The amount of H₂ gas generation in the presence of Ca²⁺ ion was reduced from 4.81 to 4.15 cc/g-zinc (14%), and the corrosion of zinc electrode in the electrolyte was strongly inhibited as time passed.

• Journal of Korean Society of Environmental Engineers
• /
• v.33 no.4
• /
• pp.258-266
• /
• 2011

Scale induced by hardness materials in water must be controled because of it can be result in remarkable damages of pipeline as well as water quality deterioration. Especially hot water system is one of scale management required facility as scale formation can be accelerated by temperature. The scale control performance of frequency driver (FD) was tested instead of existing methods such as chemical, physical and electromagnetic methods which needs chemicals and electric power. Three kinds of pipe coupons were submerged in test water with 500 mg/L of hardness for 33 days and XRD and SEM were analysed for comparing scale formation characteristics of these coupons. Calcite ($CaCO_3$) which came from hardness of water was formed on only cast iron pipe coupon and this coupon showed higher corrosion rate than copper and stainless steel pipe coupon. Hot water circulating system connected cast iron pipe with and without FD was operated with 300 mg/L of hardness water at $50^{\circ}C$ for monitoring of scale formation and water quality with and without FD. XRD showed that FD leaded to magnetite ($Fe_3O_4$) scale which is good scale for preventing corrosion than calcite and SEM image also indicated the scale control effect of FD. Scales of 16% on pipe joint, 14% on pipe length, and 42% on heat exchanger decreased with FD comparing scales of those parts without FD. From the results of water quality, FD reduced crystallization of hardness material without chemical reaction in water and it can indicate that FD is safe and proenvironmental technology for scale reduction.

• Journal of the Korea Institute of Building Construction
• /
• v.10 no.4
• /
• pp.41-47
• /
• 2010

It has been continuously noted that many sewage treatment concrete structures have deteriorated due to sulfur-oxidizing bacteria. There have been many reports on approaches to protecting concrete from this bacteria corrosion. The purpose of this study is to evaluate the inhibition of growth of a sulfur-oxidizing bacterium by a antifungal agent such as $NiSO_4{\cdot}6H_2O$, and the characteristics of polymer cement mortar using nickel type antifungal agent. First, we developed antifungal agents using metal nickel and $NiSO_4{\cdot}6H_2O$ to inhibit the growth of thiobacillus novellus, which is the sulfur-oxidizing bacteria in concrete. Then, ordinary cement mortar and polymer cement mortar using nickel type antifungal agent with various polymer-cement ratios, and antifungal agent content were prepared, and were tested for the antifungal adding effect, compressive and flexural strengths, expansion and leaching of nickel ion. From the test results, it was confirmed that the adding of an antifungal agent has an inhibition effect on the growth of sulfur-oxidizing bacteria at antifungal agent contents of 20 mM or more. In addition, the strengths and expansion of polymer cement mortars are not significantly changed by the addition of an antifungal agent. Therefore, the nickel-type antifungal agent developed in this study can be used to improve the durability of reinforced concrete hume pipe in the construction industry.

• Korean Journal of Metals and Materials
• /
• v.50 no.1
• /
• pp.34-38
• /
• 2012

Titanium has good deformability, high hardness, high biocompatibility, excellent corrosion resistance and low density. Due to these attractive properties, it has been used in many industrial applications. Dense nanostructured Ti was sintered from mechanically activated Ti and $TiH_2$ powders by high frequency induction heating under pressure of 80 MPa. The advantage of this process is that it allows very quick densification to near theoretical density and inhibition of grain growth. $TiH_2$ powder was decomposed to Ti during sintering. The hardness of Ti increased and the average grain size of Ti decreased with increasing milling time. The average grain sizes of Ti samples sintered from Ti and $TiH_2$ powder milled for 5 hrs were about 26 nm, 44 nm, respectively. The hardness of Ti sintered from Ti and $TiH_2$ powder milled for 5 h was $504kg/mm^2$ and $567kg/mm^2$, respectively.

• Clean Technology
• /
• v.19 no.3
• /
• pp.257-263
• /
• 2013

The zinc phosphate-coated mica (ZP/mica) pigments were prepared using phosphoric acid, zinc nitrate and mica as starting materials, and used as anticorrosive pigments. The scanning electron microscopy (SEM) and x-ray diffraction (XRD) techniques were used to observe the morphology and crystal structure of prepared pigments. The prepared pigments were incorporated into an epoxy binder to prepare coating and the corrosion inhibition performance of the pigments was evaluated using electrochemical impedance spectroscopy (EIS). It was found that the anticorrosive performance of the ZP/mica pigment prepared at $70^{\circ}C$ was the better than that prepared at $20^{\circ}C$. The formation of ZnO, in addition to $Zn_3(PO_4)_2{\cdot}2H_2O$, was observed on ZP/mica pigment prepared at $70^{\circ}C$. The excellent anticorrosive performance of ZP/mica pigment could be ascribed to the synergistic effect with electrochemical anticorrosive mechanism from zinc compounds on mica and barrier anticorrosive mechanism from lamellar mica.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.108-108
• /
• 1998

일반적으로 탄소강은 수용액 중에 노출될 경우 전면부식에 의한 손상을 받는다. 그러나 부식방지를 위하여 부식억제제를 적용할 경우, 탄소강의 부식거동은 현저한 변화를 겪게된다. 이러한 부식거동의 변화는 첨가되는 부식억제제의 종류에 따라 분 류할 수가 있는데, 양극부식억제제, 음극부식억제제 그리고 이들의 혼합부식억제제로 분류할 수가 있다. 현장에 적용된 부식억제제 시스템 중에는 자동차용 부동액과 가스히터용 열전달 매체액이 있다. 이러한 부식억제제가 적용된 시스댐은 정확한 부식억제능의 평가에 의한 그 교체 시기의 결정이 매우 중요하다. 교체 시기가 빠를 경우, 유지비용이 과다하게 소요되는 문제가 있으며, 교체시기가 늦을 경우 설비의 부식을 초래하는 문제 가 있다. 따라서 부식억제제의 정확한 성능 평가법은 매우 중요하며, 이에 대한 다양 한 연구가 진행 중이다. 부식억제제가 함유된 용액의 부식억제성능을 평가하는 방법에는 대표적으로 무게 감량법을 이용하고 있다. 이 방법은 다종의 금속이 적용된 자동차용 부동액을 실제 사용조건과 유사한 실험 조건에서 단기간, 가혹조건에서의 무게 감량에 의해 부식억 제능을 평가하는 방법이다. 그러나 이러한 방법은 특히 국부부식이 진행될 경우 부 식억제능을 정량화 하는데 어려움이 있다. 한편 전기화학적 측정방법으로는 분극곡선법을 이용한 $E_P$(공식개시전위), $E_R$(재부동태 화전위)의 측정법이 있다. 또한 부식억제피막의 안정성을 측정하기 위한 방법으로 인 위적인 양극전류 인가에 의한 피막의 파괴후에 피막이 복원가능 여부 및 그 속도 측 정에 의해 부식억제제의 건전성을 확인할 수가 었다. 본 연구에서는 가스히터의 주구성 재료인 A210 Gr Al의 탄소강을 사용하여, 사용기간이 5년 이상되어 부식억제 기능을 거의 상실한 것으로 여겨지는 열전달 매체액 과 신규 부식억제제가 적용된 시스템 등 객관적으로 확인된 부식억제제 시스랩에 대 하여 다양한 평가 방법을 동원 비교분석하고자 하였다. 실험은 KSM 2142에 의한 무게감량법, 분극곡선 측정에 의한 $E_P$(공식개시전위), $E_R$(재부동태화전위) 측정, 시간에 따른 자연전위 변화 측정 빛 이때의 부식속도(선형분극법), 인위적인 피막 파괴 전,후 의 전위 변화 및 부식속도 측정법에 의한 국부부식 발달 저지능 등을 평가하여 각 실험결과를 비교분석하여 보았다.