• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.263-266
• /
• 2000

Effects of excess Pb(50 mole ％) on the crystallization properties of amorphous PZT thin films on the glass substrates by post-annealing in oxygen ambient were investigated to lower the crystallization temperature of the PZT thin films with a single perovskite phase. The PZT thin films(350nm) were prepared on Pt/Ti/corning glass(1737) substrates. The PZT thin films and bottom electrode were deposited by RF magnetron sputtering. Crystallization properties of PZT thin films were strongly dependent on RTA(Rapid Thermal Annealing) temperature. We were able to obtain a perovskite structure of PZT at 600$^{\circ}C$ for 10min. After thermal treatments were done, electrical properties such as I-V, P-E, and fatigue were measured.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.80-83
• /
• 2000

The post-annealing treatments on rf magnetron sputtered PZT($Pb_{1.05}(Zr_{0.52},\;Ti_{0.48})O_3$) thin films($4000{\AA}$) have been investigated for a structure of PZT/Pt/Ti/Coming glass(1737). Crystallization properties of PZT films were strongly dependent on RTA(Rapid Thermal Annealing) annealing temperature and time. We were able to obtain a perovskite structure of PZT at $650^{\circ}C$ and 10min. P-E curves of Pd/PZT/Pt capacitor demonstrate typical hysteresis loops. The measured values of $P_r$, $E_c$ were $8.1[{\mu}C/cm^2]$, 95[kV/cm] respectively. Polarization value decrease about 25% after $10^9$ cycles.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.1
• /
• pp.24-29
• /
• 2001

PZT thin films(4000A) have prepared onto 1737 corning glass and ITO coated glass substrates with a RF magnetron sputtering system using Pb_{1.05}(Zr_{0.52},Ti_{0.48})O_3$ceramic target, Electrical properties of PZT thin film deposited after ITO coated glass were P${\gamma}$ was decreased by 25% after 109cycles, respectively. With the RTA treatment duration and temperature increased, the crystallization of PZT thin films were enhanced, however, the leakage current density became higher. The leakage current mechanism was found to be space charge conduction by the defects and oxygen vacancies existing in PZT and PZT/bottom electrode interfaces.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1818-1820
• /
• 1999

This paper presents direct ${\mu}c$-Si:H thin film growth on the glass substrates using RPCVD system (remote plasma chemical vapor deposition) in low temperature. Hydrogenated micro-crystalline silicon deposited by RPCVD system in low temperature is very useful material for photovoltaic devices, sensor applications, and TFTs (thin film transistors). Varying the deposition conditions such as substrate temperature, gas flow rate, reactive gas ratio $(SiH_4/H_2)$, total chamber pressure, and rf power, we deposited ${\mu}c$-Si:H thin films on the glass substrates (Corning glass 1737). And then we measured the structural and electrical properties of the films.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.497-502
• /
• 2005

This study investigated the effects of the substrate and powder content on the fabrication of SiO$_{2}$ photonic crystals by evaporation method. Photonic crystals were self-assembled on quartz, Corning 1737 glass, slide glass, and ITa glass to verify the effects of the wetting angle and surface morphology. The powder contents of the solution were varied from 0.2 to 2.0 wt$\%$. The number of photonic crystal layers increased according to the decrease of wetting angle and surface roughness. The resultant photonic crystals showed the best optical characteristics when the number of photonic crystal layers was within 40 and 50. In addition, the intensity peak of Fabry¡?Perot fringes increased when the wetting angle was large and the particle size was small. Photonic crystals coated on ITO glass showed the highest reflectance peak of 63$\%$ relative intensity.

• Korean Journal of Materials Research
• /
• v.11 no.3
• /
• pp.178-184
• /
• 2001

Transparent and highly oriented KLN thin films have been grown by an rf- magnetron sputtering deposition method. A homogeneous and stable KLN target was prepared by calcine and sintering process. For KLN target, stoichiometry and composition excess with K of 30% and 60%, and Li of 15% and 30% respectively, was prepared. The targets were sintered at low temperature to prevent vaporization of K and Li. KLN thin films were fabricated by rf-magnetron sputtering method using those targets. In this experiment, using the target of composition excessed with K of 60% and Li of 30%, single phase KLN thin film was produced. KLN thin film has excellent crystallinity and highly c-axis oriented on Corning 1737 substrate. Transmittance of thin film in visible range was 90%, absorption edge is 333 nm and refractive index at 632.8 nm was 1.93.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.5
• /
• pp.370-375
• /
• 2001

PZT thin films (3500${\AA}$) ahve been prepared onto Pt/Ti/corning glass (1737) substrates with a RF magnetron sputtering system using Pb$\sub$1.50/(Zr$\sub$0.52/,Ti$\sub$0.48)O$_3$ ceramic target. We used two-step annealing techniques, PZT thin films were grown at a 300$^{\circ}C$ substrate temperature and then subjected to an RTA treatment. In case of 500$^{\circ}C$ RTA temperature show pyrochlore phase. The formation of Perovskite phase started above 600$^{\circ}C$ and PZT thin films generated (101) preferred orientation. As the RTA time and temperature increased, crystallization of PZT films were enhanced. The PZT capacitors fabricated at 650$^{\circ}C$ for 10 minutes RTA treatment showed remanent polarization 30 ${\mu}$C/$\textrm{cm}^2$, saturation polarization 42${\mu}$C/$\textrm{cm}^2$, coercive field 110kV/cm, leakage current density 2.83x10$\^$-7/A/$\textrm{cm}^2$, remanent polarization were decreased by 30% after 10$\^$9/ cycles.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.06a
• /
• pp.154-159
• /
• 2005

Low RF power density was used for preparing transparent conducting AI-doped ZnO (AZO) thin films by RF Magnetron Sputtering on Corning 1737 glass. The dependence of films' structural, optical and electrical properties on sputtering gas, film's thickness and substrate temperature were investigated. Low percent of incorporated H2 in Ar sputtering gas has proven to reduce film's resistivity and sheet resistance as low as $4.1\times10^{-3}{\Omega}.cm$. It also formed new preferred peaks orientation of (101) and (100) which indicated that the c-axis of AZO films was parallel to the substrate. From UN-VIS-NIR Spectrophotometer analysis, it further showed high optical transmittance at about $\~ 90\%$ at visible light spectra (400-700nm).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.1
• /
• pp.34-42
• /
• 2001

The influences of substrate temperature were studied when fabricating KLN thin film on amorphous substrate using an rf-magnetron sputtering method. Investigating the vaporization temperature of the each element, the excess ratio of target and the optimum deposition conditions were effectively selected when thin filmizing a material which have elements with large difference fo vaporization temperature. In order to compensate K and Li which have lower vaporization temperatures than Nb, KLN target of composition excess with K of 60% and Li of 30% was used. KLN thin film fabricated on Corning 1737 glass substrate had single KLN phase above 58$0^{\circ}C$ of substrate temperature and crystallized to c-axis direction. The optimum conditions were rf power of 100W, process pressure of 150mTorr, and substrate temperature of $600^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.91-92
• /
• 2006

Aluminum-doped zinc oxide (AZO) films are attractive materials as transparent conductive electrode because they are inexpensive, nontoxic and abundant element compared with indium tin oxide (ITO). AZO films have been deposited on glass (corning 1737) substrates by RF magnetron sputtering system. The electrical resistivity of AZO films was $1.81{\times}10^{-2}{\Omega}cm$ and the average transmittance in the visible range 400-800 nm was more than 76% Organic light-emitting diodes (OLEDs) with AZO/TPD/$Alq_3$/Al configuration were fabricated. The current density-voltage properties of devices were studied and compared with ITO devices fabricated under the same conditions.