• Journal of the Korean Chemical Society
• /
• v.11 no.1
• /
• pp.33-37
• /
• 1967

The influence of impurities contained in Marmatite ores on leaching of zinc was investigated. The zinc sulfide having the same crystal structure of natural Sphalerite was prepared by heating the zinc sulfide chemically precipitated, at $650^{\circ}C$ in nitrogen atmosphere. The activation energy of the sample was 25.8 kcal per mole in the leach test when oxygen partial pressure was 5 atm. and the value was exceedingly high compared to that obtained in Marmatite ores. Synthetic zinc sulfides added with small amount of each impurities were treated in same procedure. As a result, it was found that the leaching velocity was accelerated sharply when about 1 percent of $Cu^{++}$ was blended to the sample. Larger amount of iron has also same effect but the effect was minor compared to the copper. The other impurities indicated no appreciable catalytic action.

• Resources Recycling
• /
• v.25 no.1
• /
• pp.3-9
• /
• 2016

The leaching behavior of gold from waste CPU chip using Iodide/Iodine solution was studied. The direct leaching of gold with Iodide/Iodine solution for CPU chip under the size of 150 mesh showed leaching ratio of 20%. It was assumed that the copper film was produced on the gold particle during grinding process and the copper film prevents lodine/Iodide solution from contacting with leachable gold. Meanwhile, the extraction of gold was improved to 90% by pretreatment process with $HNO_3$ solution. In order to explain the result, EDS and ICP analysis for the leaching residue were conducted. It was found that the copper coated on the surface of the gold particle was removed about 80% by $HNO_3$, resulting in the increment of gold leaching rate.

• Resources Recycling
• /
• v.31 no.1
• /
• pp.21-28
• /
• 2022

The smelting reduction of spent lithium-ion batteries results in metallic alloys of cobalt, nickel, and copper. To develop a process to separate the metallic alloys, leaching of the metallic mixtures of these three metals with H₂SO₄ solution containing 3% H₂O₂ dissolved all the cobalt and nickel, together with 9.6% of the copper. Cyanex 301 selectively extracted Cu(II) from the leaching solution, and copper ions were completely stripped with 30% aqua regia. Selective extraction of Co(II) from a Cu(II)-free raffinate was possible using the ionic liquid ALi-SCN. Three-stage cross-current stripping of the loaded ALi-SCN by a 15% NH₃ solution resulted in the complete stripping of Co(II). A process was proposed to separate the three metal ions from the sulfuric acid leaching solutions of metallic mixtures by employing solvent extraction.

• Proceedings of the IEEK Conference
• /
• 2001.10a
• /
• pp.193-197
• /
• 2001

This study was carried out to recover gold, silver and other valuable metals from the printed circuit boards (PCB) of waste computers. PCB samples were crushed to under 1mm by a shredder and initially separated into 30% conducting and 70% non-conducting materials by an electrostatic separator. The conducting materials, which contained the valuable metals, were then used as the feed material for magnetic separation where it was found that 42% was magnetic and 58% non- magnetic. The non-magnetic materials contained 0.227mg/g Au and 0.697mg/g Ag. Further leaching of the non-magnetic component using 2.0M sulfuric acid and 0.2M hydrogen peroxide at 85$^{\circ}C$ extracted more than 95% copper, iron, zinc, nickel and aluminium. Au and Ag were not extracted in this solution, however, more than 95% of Au and 100% of Ag were selectively leached with a mixed solvent (0.2M ammonium thiosulfate, 0.02M copper sulfate, 0.4M ammonium hydroxide). Finally, the residues were reacted with a NaCl solution to leach out Pb while sulfuric acid was used to leach out Sn. Recoveries reached 95% and 98% in solution, respectively.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.10
• /
• pp.1777-1780
• /
• 2007

The synthesis of well-defined dendrons based on aliphatic polyether dendritic cores and glassy polystyrene peripheries is described. The synthetic route involves a combination of living anionic polymerization and a stepwise convergent method consisting of iterative Williamson etherification and hydroboration/oxidation reactions. On the basis of molecular weight, as characterized by gel permeation chromatography (GPC), the first generation dendron (Generation-1) shows a random coil conformation like a linear polystyrene, while higher generations (Generation-2 and 3) reveal globular forms in solution.

• Journal of environmental and Sanitary engineering
• /
• v.14 no.3
• /
• pp.71-79
• /
• 1999

The Hg, Cd, Cu, Mn, and Zn in bottom sediments of han river and their tributaries were analyzed to evaluate the seasonal variations of heavy metals. Leaching tests were also performed for estimation of availability of heavy metal retention in sediments. Sediments of Anyang stream showed the highest concentration of heavy metal in the sediment samples. Heavy metal concentration was heavily depended upon the heavy metal source of tributaries of han river and particle distribution. Clay and silt had higher concentration of heavy metals than very fine san and fine sand due to difference of retention capability of heavy metal. The highest concentration of heavy metal was observed in bottom sediments irrespective of sites investigated. Heavy metals and ignition loss showed positive relations, and higher relationships with p-value <0.01 were observed between copper and lead. copper and zinc, and depended on the pH condition of leaching test, and leachated fraction increased with decrease of the pH.

• Resources Recycling
• /
• v.22 no.5
• /
• pp.13-19
• /
• 2013

The effect of pH on the citrate leaching behavior of heavy metal ion was investigated to develop an eco-friendly process for removing heavy metals from soil contaminated with copper, zinc, and lead. The leaching tests were performed using citrate solution with pH adjusted by mixing citric acid and sodium citrate under the following leaching conditions: particle size, under $75{\mu}m$; temperature, $50^{\circ}C$; citrate concentration, $1kmol/m^3$; pulp density, 5%; shaking speed, 100 rpm; leaching time, 1 hour. The difference of pH before and after the leaching test was not observed, and this result indicates the direct effect of hydrogen ion concentration on the leaching of metals was insignificant. The removal ratios of copper, zinc, and lead from the contaminated soil decreased with increasing pH. The thermodynamic calculation suggests that the leaching behaviors of metal ions were determined by two reactions; one is the reaction to form complex ions between heavy metal ions and citrate ion species, and the other is the reaction to form metal hydroxide between heavy metal ions and hydroxide ion.

• Proceedings of the IEEK Conference
• /
• 2001.10a
• /
• pp.448-452
• /
• 2001

An Experimental study was carried out to develop a simple method of processing copper waste sludge which is produced by PBC manufacturing. The procedure is based on leaching of wet sludge in 2N H$_2$SO$_4$, and the solid / liquid ratio is controlled approximately at 1/10. The recovery of copper is 85.4%, and pH of the leachate is 3.20. Adding ammonia solution into leachate forms ammine, and hydroxide compounds derived from other impurities in leachate at pH 10. The hydroxide compound can be treated by ferrite process, and the product is a stable oxide compound. Then the ammine solution is heated to evaporate ammonia, and the copper hydroxide is formed. Heating at 8$0^{\circ}C$by aeration, copper hydroxide is transformed into copper oxide with a purity of 98.4%. This process can recover most copper from sludge and the residue can be stabilized by the formation of a stable oxide compound which is not hazardous to environment.

• Analytical Science and Technology
• /
• v.21 no.1
• /
• pp.1-8
• /
• 2008

This study was conducted to investigate the characteristics of the leaching of metal components from CCA-treated wood during outdoor exposure. CCA-treated wood specimens were placed horizontally or buried vertically into the soil, and then exposed to the natural environment for a year. Wood samples were collected from the side of the horizontal wood specimens using a drill and saw dust samples were collected at the end of the exposure. Soil samples were also obtained around the wood specimens and at different depths of the posts. Wood and soil samples were analyzed for metals using an atomic absorption spectrometer. Monthly metal concentrations varied greatly and more metals were released when wood specimens were exposed vertically than horizontally. Arsenic was released from the wood by 80 % of the intial content. In addition, more leaching was observed from the zone below the ground than above the ground, and soil around the posts was contaminated with metals released from CCA-treated wood.

• Resources Recycling
• /
• v.15 no.6 s.74
• /
• pp.41-47
• /
• 2006

A study for recovering of copper and lead from electronic scraps has been carried out using a combination of bioleaching and solvent extraction. It was found that the citric acid generated by Aspergillus niger could be an imporant leaching agent acting in the solubilization of copper, iron, lead and tin from the electronic scrap. Copper could be selectively extracted by 10% LIX84 from the leaching solution and it recoved 99.9% of metallic copper by electrowinning process. Tin and iron were extracted from the remaining solution by 10% Alamine336 and stripped by NaCl solution. Finally, tin could be recovered as a metallic precipitates from the mixed solution of tin and iron by cementation with iron powder.