• Magazine of the Korea Concrete Institute
• /
• v.7 no.6
• /
• pp.209-215
• /
• 1995

Corrosion of steel reinforcment is the most significant factor of deterioration in reinforced concrete structures. Chloride ion is considered one of the most common culprits in the corrosion of steel in concrete. It breaks down the passive film and allows the steel to corrode actively at a high rate. The main objective of this study is to determine the critical chloride ion concentrations in the pore solutions and chloride binding effect of cement pastes made with and without fly ash. Cement pastes with water-binder ratio of 0.5, allowed to hydrate in sealed containers for 28 days and to express pore solution. The expressed pore fluids were analyzed for chloride and hydroxyl ion concentrations. Evaporable water on paralled specimens was determined a.s the loss of weight per 100g of unhydreded cement when the specimens were heated to constant weight at 105'C. It was found that the replaced cement with fly ash has negligible influnce on the chloride binding and chloride binding capacity and rises the $Cl^-$ /$OH^-$ ratio in pore solution.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.186-190
• /
• 1997

Corrosion of steel reinforcement is the most significant factor of deterioration in reinforced concrete structures. It breaks down the passive film and allows the steel to be corroded severely at a high rate. The main object of this study is to determine the critical chloride ion concentrations in the pore solutions and chloride binding effect of cement pastes. It is found that binding chloride ion ratio of cement is between 0.04% and 0.3% and Cl/OH in pore solution under 0.3.

• Corrosion Science and Technology
• /
• v.3 no.1
• /
• pp.34-38
• /
• 2004

The corrosion of reinforcement is a very important factor on the serviceability and safety of reinforced concrete structures. The corrosion rate influences directly the cover failure time of reinforced concrete structures because the corrosion rate is used to estimate the amount of corrosion and thus expansive pressure due to corrosion. In this study, several series of experiments are performed considering the chloride concentration in artificial pore solution. The potentials are measured according to the applied current density and then corrosion current densities are obtained from the Tafel plot for various chloride concentrations. The measured corrosion rates show good correlation with those of other researchers.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.32-33
• /
• 2021

The corrosion of the embedded steel rebars and the consequent deterioration of the reinforced concrete structure has become a challenging concern to the construction industries for the fiscal deficit. However, corrosion inhibitors are potential and being widely used for corrosion mitigation to solve such problems. This study has been focused on the mixed type of corrosion inhibitor where one component of the corrosion inhibitor is organic and another one is inorganic material. 0.1 (M) triethanolamine (TEA) and 0.01 (M) sodium hexametaphosphate (SHMP) have been mixed in distilled water to produce the mixed inhibitor. Studies of the steel rebar corrosion in chloride contaminated (3.5 wt.% NaCl) concrete pore (CCCP) solution has been conducted using different concentrations of corrosion inhibitor. Electrochemical impedance spectroscopy (EIS) method is involved to understand the corrosion behaviour of the steel rebars at different exposure durations.

• Computers and Concrete
• /
• v.19 no.3
• /
• pp.257-262
• /
• 2017

The aim of this study is to investigate the pH threshold value for the corrosion of steel reinforcement in concrete. A method was designed to attain the pH value of the pore solution on the location of the steel in concrete. Then the pH values of the pore solution on the location of steel in concrete were changed by exposing the samples to the environment (CO25%, RH 40%) to accelerate carbonation with different periods. Based on this, the pH threshold value for the corrosion of steel reinforcement had been examined by the methods of half-cell potential and electrochemical impedance spectra (EIS). The results have indicated that the pH threshold value for the initial corrosion of steel reinforcement in concrete was 11.21. However, in the carbonated concrete, agreement among whether steel corrosion was initiatory determined by the detection methods mentioned above could be found.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.537-540
• /
• 2006

Over the past few decades, a considerable number of studies on the durability of concrete have been carried out extensively. A lot of improvements have been achieved especially in modeling of ionic flows. However, the majority of these researches have not dealt with the chloride binding isotherm based on the mechanism, although chloride binding capacity can significantly impact on the total service life of concrete under marine environment. The purpose of this study is to develop the model of chloride binding isotherm based on the individual mechanism. It is well known that chlorides ions in concrete can be present; free chlorides dissolved in the pore solution, chemical bound chlorides reacted with the hydration compounds of cement, and physical bound attracted to the surface of C-S-H grains. First, sub-model for water soluble chloride content is suggested as a function of pore solution and degree of saturation. Second, chemical model is suggested separately to estimate the response of binding capacity due to C-S-H and Friedel's salt. Finally, physical bound chloride content is estimated to consider a surface area of C-S-H nano-grains and the distance limited by the Van der Waals force. The new model of chloride binding isotherm suggested in this study is based on their intrinsic binding mechanisms and hydration reaction of concrete. Accordingly, it is possible to characterize chloride binding isotherm at the arbitrary stage of hydration time and arbitrary location from the surface of concrete. Comparative study with experimental data of published literature is accomplished to validity this model.

• Journal of the Korea Concrete Institute
• /
• v.11 no.3
• /
• pp.193-203
• /
• 1999

The corrosion of steel reinforcements in concrete is of great concern in recent years. This study is focused on the corrosion behavior of steel bars induced by internal chlorides in concrete at early ages. The main objective of this study is to determine the chloride thresholds causing depassivation and active corrosion of steel reinforcement in concrete. To examine the threshold concentration of chloride ion, the half-cell potential, chemical composition of expressed pore solutions of concrete and the rate of corosion area of the specimens were measured. Major variables include the added amount of chlorides in concrete, types of binders, and water-to-binder ration. From the present comprehensive experimental results, the factors influencing chloride-induced corrosion are investigated, and the chloride thresholds causing active corrosion of steel bars are proposed. The present study will enable to specify the realistic chloride limit in concrete which can be used in the future technical specification.

• Journal of the Korea Concrete Institute
• /
• v.14 no.5
• /
• pp.789-795
• /
• 2002

To evaluate the bind rate and behavior of two types chloride ion-one is the chloride ion added in mixture when un-washed sea sand is used as fine aggregate, one is the chloride ion admitted in the new version of concrete standard specification, pore solution extracted in cement paste were analyzed. The results are follow. 1 As passing the time, the chloride concentration in the pore solution decreases with the Increase in the chloride content absorbed by the hydrate products. As compared with chloride contents in mixing water, the bound ratio of chloride at 49 days is 64∼90％. 2. The bound ratio of chloride in cement paste considering evaporable water as pore solution is obtained. In case of Pl∼P3(added chloride content wt of cement 0.046∼0.16 ％), the bound ratio of chloride is 91.8∼93.5 ％. P4(added chloride wt of cement 0.3％) is 89.1％, but P5(added chloride wt of cement 0.617％) bound is only 77％. 3. The bound ratio of chloride to wt of cement is 0.015∼0.475％ with adding chloride. In case chloride added over 0.091 ％ wt of cement, the bound chloride content increases 1.7∼1.8 times in spite of added chloride increase twice. The bound ratio of chloride to wt of cement decreased with the increase in the chloride content. 4. The more increase added chloride content, the more increase the bound ration of chloride. But the absolute value of chloride content in pore solution increased.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.11a
• /
• pp.119-120
• /
• 2023

Corrosion of the steel rebar in coastal environment caused huge economical loss of the globe. Therefore, coating on the steel rebar being used to mitigate the corrosion. In the present study, we have applied epoxy coating on arc thermal sprayed Al coating (a dual metal/polymeric coating) vis-à-vis compared with as coated one (Al coating). The corrosion studies were performed in simulated concrete pore solution with 3.5 wt. % NaCl solution. The morphology of the dual epoxy/Al coating is smooth while Al coating shows rankle and defects. Due to defects, Al coating is susceptible to corrosion while dual epoxy/Al coating has performed excellent compared to as coated one at extended period of immersion.

• Corrosion Science and Technology
• /
• v.16 no.4
• /
• pp.175-182
• /
• 2017

Galvanic current measurement, polarization curves, electrochemical impedance spectroscopy and weight loss test were used to study the corrosion behavior of carbon steel before and after carbon fibers coupling to the carbon steel in simulated concrete pore solutions, and the film composition on the steel surface was analyzed using XPS method. The results indicate that passive film on steel surface had excellent protective property in pore solutions with different pH values (13.3, 12.5 and 11.6). After coupling with carbon fibers (the area ratio of carbon steel to carbon fiber was 12.31), charge transfer resistance $R_{ct}$ of the steel surface decreased and the $Fe^{3+}/Fe^{2+}$ value in passive film decreased. As a result, stability of the film decreased and the corrosion rate of steel increased. Decreasing of the area ratio of steel to carbon fiber from 12.3 to 6.15 resulted in the decrease in $R_{ct}$ and the increase in corrosion rate. Especially in the pore solution with pH 11.6, the coupling leads the carbon steel to corrode easily.