• Architectural research
• /
• v.20 no.1
• /
• pp.27-34
• /
• 2018

To improve the chloride ingress resistance of concrete, slag is widely used as a mineral admixture in concrete industry. And currently, most of experimental investigations about non steady state diffusion tests of chloride penetration are started after four weeks standard curing of concrete. For slag blended concrete, during submerged chloride penetration tests periods, binder reaction proceeds continuously, and chloride diffusivity decreases. However, so far the dependence of chloride ingress on curing ages are not detailed considered. To address this disadvantage, this paper shows a numerical procedure to analyze simultaneously binder hydration reactions and chloride ion penetration process. First, using a slag blended cement hydration model, degree of reactions of binders, combined water, and capillary porosity of hardening blended concrete are determined. Second, the dependences of chloride diffusivity on capillary porosity of slag blended concrete are clarified. Third, by considering time dependent chloride diffusivity and surface chloride content, chloride penetration profiles in hardening concrete are calculated. The proposed prediction model is verified through chloride immersion penetration test results of concrete with different water to binder ratios and slag contents.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2005.05a
• /
• pp.21-24
• /
• 2005

In this paper, field application of mass concrete using setting time difference of super retarding agent is reported to reduce hydration heat of concrete placed at newly constructed apartment house in Daejeon. Horizontal placing lift is applied. According to test results,: slump and air content meets the requirement of target values. For compressive strength, it exceeds the nominal strength ordered by the costumer. For temperature history, maximum temperature of center at top section shows $25.6^{\circ}C$, and at bottom section, $35.4^{\circ}C$. According to naked eye's investigation, no hydration heat crack is observed at the surface of concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.315-316
• /
• 2009

In this study, latent heat material was used to reduce hydration heating velocity of high-strength mass concrete. And the properties of hydration heat and autogenous shrinkage, and the relationship between hydration heat and autogenous shrinkage of high-strength mass concrete were numerically investigated.

• Computers and Concrete
• /
• v.6 no.1
• /
• pp.19-40
• /
• 2009

This paper describes the development of modified heat of hydration and maturity-strength models for concrete containing fly ash and slag. The modified models are developed based on laboratory and literature test results, which include different types of cement, fly ash, and slag. The new models consider cement type, water-to-cementitious material ratio (w/cm), mineral admixture, air content, and curing conditions. The results show that the modified models well predict heat evolution and compressive strength development of concrete made with different cementitious materials. Using the newly developed models, the sensitivity analysis was also performed to study the effect of each parameter on the hydration and strength development. The results illustrate that comparing with other parameters studied, w/cm, air content, fly ash, and slag replacement level have more significantly influence on concrete strength at both early and later age.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.229-230
• /
• 2023

In this study, the hydration heat differential method was applied to mass concrete structures, and the hydration heat analysis was compared and analyzed with on-site measurement results. The results showed that the temperature history measurements of mass concrete were managed at a difference of 8.4 ℃, and although there was some deviation in thermal stress, a similar trend was observed. Consequently, it was determined that the thermal stress on the surface of mass concrete is less than its tensile strength, which would prevent the occurrence of thermal cracks.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.425-428
• /
• 2006

The bigger of concrete strctures by a construct technique improvement, and the increase of the cement quantity which is caused by with use of the high-strength concrete for the load-carrying-capacity and a durability cause temperature cracks by a heat of hydration. The temperature crack due to the heat of hydration classified a nonstructural crack. but it has a bad effect on durability of concrete structures. especially, in case of a subway concrete box structure, when a water-proof facilities is beaked on an outer-wall, the water leakage occurs through a penetration crack generated from a wall of the concrete structure too. This paper, for the subway concrete box strucuture, the use of blended cement, the temperature of air and concrete, control joint, was considered and analysed by a three dimensional finite element method.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.707-710
• /
• 2004

This paper reported the results of mock-up test on mass concrete for transfer girder using setting time difference of super retarding agent(SRA). According to test results, two mock-up structures were made. Plain concrete without placing layer reached maximum temperature after 24hours since placement and caused surface hydration cracks at top section. However, concrete with placing layer reached maximum temperature after 72hours and surface temperature was higher than center temperature, which did not cause surface crack. After form removing, no crack was observed at side surface of plain concrete, while concrete using SRA at mid section had surface scaling and settling crack. According to coring results, concrete with placing layer had a penetration crack from top section to bottom section. Therefore, the setting time difference method to reduce hydration heat will have difficulty in applying the mass concrete for transfer girder.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.705-708
• /
• 2006

The bigger of concrete structures by a construct technique improvement, and the increase of the cement quantity which is caused by with use of the high-strength concrete for the load-carrying-capacity and a durability cause temperature cracks by a heat of hydration. The temperature crack due to the heat of hydration classified a nonstructural crack. but it has a bad effect on durability of concrete structures. especially, in case of a subway concrete box structure, when a water-proof facilities is beaked on an outer-wall, the water leakage occurs through a penetration crack generated from a wall of the concrete structure too. This paper, for the subway concrete box structure, which is located in chloride attack region, the use of blended cement, the temperature of air and concrete, was considered and analysed by a three dimensional finite element method.

• Journal of the Korea Concrete Institute
• /
• v.21 no.4
• /
• pp.481-488
• /
• 2009

It has been reported that the magnitude and the development rate of autogenous shrinkage of cement paste, mortar and concrete were affected by history and magnitude of inner temperature at an early age. But it was not enough to explain the relation between hydration heat and autogenous shrinkage at an early age, because there was no certain analysis on histories of hydration heat and autogenous shrinkage in previous studies. In our prior study, to understand the relationship between hydration heat and autogenous shrinkage of concrete at an early age, the analysis method for histories of hydration heat and autogenous shrinkage was suggested. Based on this method, early age properties of hydration heat and autogenous shrinkage of high strength concrete with different sizes and hydration retardation were investigated in this study. As a result of the study, properties of hydration temperature and autogenous shrinkage were different according to specimen size and hydration retardation. However, there was a close relationship between hydration temperature and autogenous shrinkage at an early age, especially between HHV and ASV as linear slopes of the sections where hydration temperature and autogenous shrinkage increase rapidly; the higher HHV, the higher ASV and the greater ultimate autogenous shrinkage. And it was found that, among the setting time, bend point and temperature increasing point, they were close relationship each other on cement hydration process.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.723-730
• /
• 2001

Mass concrete of reaction structure was investigated to minimize cracks generated by the heat of hydration. Suggestions are noted in this paper through the experiences of planning, technical study, computational analysis and field instrumentation.