• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.697-700
• /
• 2000

Fatigue damage to reinforced concrete bridge decks have been found in many bridges. Failure mode of most reinforced concrete decks is caused by local punching shear rather than flexural moment due to cumulated damage. In this study, mechanical degradation of unstrengthened and strengthened bridge deck specimens is experimentally investigated. The unstrengthened deck specimens were damaged under the pulsating loading condition. After the test, deteriorated deck specimens were strengthened with Carbon Fiber Sheet, then loaded to observe the improvement of the fatigue behavior. It is shown that fatigue damaged specimens are similar to real bridge rather than static damaged specimens.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.303-306
• /
• 2005

For checking influence of load-position and system of stress-transmission in precast concrete bridge deck system, the test composite bridge was made a experiment by the wheel load machine. The result of experiment was the loop joint system of the precast decks has a difference which was the transmission system of longitudinal stress, comparing with general RC bridge deck system. The loop joint system has a behavior independently.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.21-22
• /
• 2010

Recently, many concrete cable-stayed bridges are under construction for economic benefits. This study deals with analyzing construction cost of the Second-Dolsan Bridge and the Sepung Bridge as examples of concrete cable-stayed bridges.

• Proceedings of the KSR Conference
• /
• 2007.11a
• /
• pp.1050-1057
• /
• 2007

The objective is to compare with economic evaluation and to analysis the LCC for prestressed concrete used on rail bridge. A new style concrete bridge is difficult to estimate a history for maintenance cost reliably. For the reason, we introduce a analogical interpretation by similar bridge style in order to estimate a appropriate maintenance profile. The proposed method is usefully supplied to estimating the LCC for bridge which is difficult to determine the maintenance cost.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05a
• /
• pp.103-106
• /
• 2005

Bridge deck is the element presenting the largest damage potentiality among the major bridge structural members. In the previous study, a new-type of FRP-concrete composite bridge deck system was proposed and its static performance was experimentally verified, This study aim at investigation of fatigue behavior such as failure mechanism through rolling fatigue test.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.59-64
• /
• 2001

The concrete bridge decks are in need of replacement and rehabilitation due to decreasing load carrying capacity. In this study, to extend life cycle of the concrete bridge decks which are reinforced with the glass fiber sheets, the concrete bridge decks are examined on the strengthen effect and the fatigue behavior. The behavior of strengthened slabs is represented by load-displacement relationship, variation of compliance and total released energy. Owing to result of that, the strengthened slabs is modified the elasticity, the compliance and represents to control the crack elongation, to elevate the total released energy, to modify the fatigue life. When the concrete bridge deck is strengthened, the crack propagation nay be controled efficiently.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05a
• /
• pp.34-37
• /
• 2006

Accoarding as a specimen for reinforced concrete bridge deck was designed by each researcher's opinions, its size and shape was variable. Therefore, it makes difficult to comparison with other experiments. In the result of researching papers for design method of reinforced concrete bridge deck specimens, there is hardly found. The target of this study is introduction of the design method of a reinforced concrete bridge deck specimen. The most important point for the specimen design is materialization of the curvature of the real bridge deck. The result of this study appears that the specimens thickness effects highly to fit for the real reinforced concrete bridge deck's curvature.

• Steel and Composite Structures
• /
• v.21 no.3
• /
• pp.661-677
• /
• 2016

The quasi static test of the steel reinforced concrete (SRC) bridge piers and rigid frame arch bridge structure with SRC piers was conducted in the laboratory, and the seismic performance of SRC piers was compared with that of reinforced concrete (RC) bridge piers. In the test, the failure process, the failure mechanism, hysteretic curves, skeleton curves, ductility coefficient, stiffness degradation curves and the energy dissipation curves were analyzed. According to the $M-{\Phi}$ relationship of fiber section, the three-wire type theoretical skeleton curve of the lateral force and the pier top displacement was proposed, and the theoretical skeleton curves are well consistent with the experimental curves. Based on the theoretical model, the effects of the concrete strength, axial compression ratio, slenderness ratio, reinforcement ratio, and the stiffness ratio of arch to pier on the skeleton curve were analyzed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.457-462
• /
• 2003

It studies the non-structural crack factors that are produced in Steel Box Girder Bridge concrete floor plate using analytical method. It mainly studies humidity and design standard of concrete strength. It used MIDAS CIVIL Ver 5.4.0, a general structure analysis program that applies drying shrinkage rate of domestic road bridge design standard and standard value of creep coefficient, CEF-FIP standard equation and ACI standard equation from the aspect of creep, drying shrinkage and hydration heat to see the effect of the two factors on concrete crack and found the following result. The analytical results of this study showed that the initial stress, which was obtained by ACI standard, exceeds the allowable tensile stress between 5 to 18 days. This result means that even if a bridge is designed and constructed according to design standard, the bridge can have cracks due to various variables such as drying shrinkage, hydration heat and creep that produce stress in slab.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10b
• /
• pp.1063-1068
• /
• 2000

Latex modified concrete (LMC) has grown to be accepted as a standard material of construction overlaying bridge decks in America due to its superior physical and chemical properties. The properties of latex, combined with the low water-cement ratio, produce a concrete that has improved flexural, tensile, and bond strength, lower modulus of elasticity, increased freeze-thaw resistance, and reduced permeability compared to conventional concrete of similar mix design. LMC overlays have been service in excellence for 30 years on thousands of bridge in U.S.A. This may, also, prolong the life cycle of bridge deck once it is adopted in Korea. The self-contained, mobile, continuous mixer is most appropriate particularly for concrete quality assurance. Assuring quality on a bridge deck overlay project should begin in the design phase and continue after the construction is completed. Quality should be the concern of everyone involved-owner, designer, and contractor.