• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.973-978
• /
• 2001

In clod weather regions, a strong seasonal wind brings sea salts to the land. In addition to it, recently, the spreading amount of de-icing salts has increased numerously for the purpose of removing snow and ice. Thus the salts environment around concrete structures becomes so severe that various damages of concrete due to applied salts will be brought up. It is briskly carried out study on effects of do-icing salts on concrete in America, Japan, European countries. However, there are not test method for the deterioration of concrete subjected to both freezing-thawing and chloride attack in Korea. In this study, we conduct on test for the compound deterioration subjected to both freezing-thawing and chloride attack, in order to investigate effects of de-icing salts on the deterioration of concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.04a
• /
• pp.77-82
• /
• 1996

The study was performed for the purpose of obtaining the fundamental data to improve the durability of concrete structures due to de-icing salts. To assume the degree of concrete deterioration, soluble chloride content in concrete, the depth of carbonation and compressive strength of core specimens were measured. The porgress of corrosion of concrete bridge was electrochemically monitored. The results show that the concrete structure was deteriorated and reinforced steel in concrete was corroded due to de-icing salts.

• Computers and Concrete
• /
• v.21 no.6
• /
• pp.649-659
• /
• 2018

Adaptive neuro-fuzzy inference systems (ANFIS) can be efficient in modelling non-linear, complex and ambiguous behavior of cement-based materials undergoing combined damage factors of different forms (physical and chemical). The current work investigates the use of ANFIS to model the behavior (time of failure (TF)) of a wide range of concrete mixtures made with different types of cement (ordinary and portland limestone cement (PLC)) without or with supplementary cementitious materials (SCMs: fly ash and nanosilica) under various exposure regimes with the most widely used chloride-based de-icing salts (individual and combined). The results show that predictions of the ANFIS model were rational and accurate, with marginal errors not exceeding 3%. In addition, sensitivity analyses of physical penetrability (magnitude of intruding chloride) of concrete, amount of aluminate and interground limestone in cement and content of portlandite in the binder showed that the predictive trends of the model had good agreement with experimental results. Thus, this model may be reliably used to project the deterioration of customized concrete mixtures exposed to such aggressive conditions.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.1
• /
• pp.1-9
• /
• 2022

De -icing salts have been used commonly in areas where snow or ice is a seasonal safety hazard for roadway, however, the salts is one of main causes on serious deterioration of road infrastructures in crowded urban city like Seoul. In order to establish maintenance strategy of road infrastructures under de-icing salts laden environment, it is necessary to examine environmental characteristics and its response to the existing facilities. The purpose of this study is to evaluate the deterioration environment of road infrastructures. Additional purpose is to develop a design model and details for durability design of infrastructures under de-icing salts laden environment, considering mainly a build-up rate of surface chlorides. Concentration of external chloride solution and surface chloride content were calculated at the level of average de-icing salts for 5 years, ratio of auxiliary road of 17.5 to 30%, and effective exposure area to snow 50 to 80%. The chloride build-up rate was 0.073 ~ 0.077% / year and the maximum surface chloride content was calculated to be 2.2 ~ 2.31% by concrete wt. This study is expected to be used for establishing integrated strategy of road infrastructures, such as predicting chloride profiles or degree of chemical corrosion to exposure concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.507-510
• /
• 2005

In winter, a large amount of de-icing salts such as $CaCl_2$, NaCl have been used on highways for road safety. They make concrete structures deteriorated. In this study, the chloride diffusion of concrete in presence of de-icing salt was investigated. The diffusion coefficient of chloride in presence of $CaCl_2$ solution was larger than in presence of NaCl solution. Therefore, it is necessary to assess chloride profile in presence of $CaCl_2$ by different way from the case in presence of NaCl solution or seawater.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.04a
• /
• pp.137-139
• /
• 2007

Recently, the research on durability of concrete proceed rapidly in the building industry. Deterioration due to do-icing salts occurs in practice in bridge structure, dike, barrier and similar structure. This paper reports the results of effect of chlorides on the freeze-thaw properties of concrete bridge deck in winter. The case fresh water condition where the concrete will receives a freez-thaw effect compared to decrease of durability quotient a lot occurs is a possibility of knowing from brine condition.

• Journal of the Korean Society of Safety
• /
• v.29 no.6
• /
• pp.87-93
• /
• 2014

In this study, the reinforced concrete rahmen bridge damaged by the chloride attack was investigated. According to the investigation, the degraded concretes on cantilever kerb and end part were intensively observed. Thus, the chloride content test and half-cell method were performed to evaluate the degraded parts. As a result, the contents of chloride on degraded parts were C and D grade. On the other hand, the half-cell potential values of rebar in degraded concrete were measured with the minor corrosion. This rebar corrosion is expected to progressing. Chloride content D grade is due to expansion pressure by corrosion of rebar and freeze-thaw by permeate water, could see progresses rapidly degradation. In order to prevent chloride attack to concrete deck caused by deicing salts, corresponding to the chloride critical concentration must maintain grade b or at least grade c. Chloride condition evaluation standard apply to evaluation of marine structure chloride attack with chloride attack by deicing salts.

• Advances in concrete construction
• /
• v.5 no.6
• /
• pp.671-683
• /
• 2017

Commonly used concrete in general, consists of cement, fine aggregate, coarse aggregate and water. Natural river sand is the most commonly used material as fine aggregate in concrete. One of the important requirements of concrete is that it should be durable under certain conditions of exposure. The durability of concrete is defined as its ability to resist weathering action, chemical attack or any other process of deterioration. Durable concrete will retain its original form, quality and serviceability when exposed to its environment. Deterioration can occur in various forms such as alkali aggregate expansion, freeze-thaw expansion, salt scaling by de-icing salts, shrinkage, attack on the reinforcement due to carbonation, sulphate attack on exposure to ground water, sea water attack and corrosion caused by salts. Addition of admixtures may control these effects. In this paper, an attempt has been made to replace part of fine aggregate by tailing material and part of cement by fly ash to improve the durability of concrete. The various durability tests performed were chemical attack tests such as sulphate attack, chloride attack and acid attack test and water absorption test. The concrete blend with 35% Tailing Material (TM) in place of river sand and 20% Fly Ash (FA) in place of OPC, has exhibited higher durability characteristics.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.681-686
• /
• 2003

One of the major degradation processes of reinforced concrete (RC) structure is corrosion of reinforced steel due to chloride attack. Severe environments, such as marine environment and exposure to de-icing salts, could accelerate the steel corrosion of RC structures through the chloride ion intrusion into concrete. In order to delay this degradation process, several kinds of admixtures have been used in concrete mix. In this study, effective diffusion coefficient of chloride ion ($D_{eff}$) and total passed charge of concrete with and without fly ash were measured using electrical method. It is found that fly ash concrete has much less chloride ion coefficient than ordinary concrete at later age. By analyzing the test results, $D_{eff}$ at 28 and 90 days was obtained as a function of water-binder ratio (W/B) and an equation for predicting $D_{eff}$ with age was proposed considering the decreasing rate of $D_{eff}$.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.3
• /
• pp.30-38
• /
• 2015

In cold-climate regions, deicing agents is used for smooth traffic on the road due to freezing and snowdrift in winter. The use of de-icing salts has resulted in the accelerated scaling damage of concrete with salt damage under freezing and thawing condition. Scaling is the deterioration of concrete where in the paste-mortar structure delaminates in flakes from the surface of the concrete. Due to such damage, concrete pavement causes various problems such as early deterioration according to the decrease in the thickness of cover concrete and user's stability issues. Accordingly, various tests and evaluation methods have been suggested in order to evaluate these phenomena in other countries. However, there have been no regulations for the evaluation method in South Korea, and related studies are also very rare. Therefore, in this study, the evaluation methods proposed by each institution and country were investigated and the experiments were performed according to each regulation, followed by the comparison and analysis of the results. Furthermore, this study aims to suggest the optimized experimental method adopted to domestic field through the discussion of such experimental methods and results.