• The Journal of Korean Academy of Prosthodontics
• /
• v.55 no.3
• /
• pp.264-271
• /
• 2017

Purpose: The purpose of this study is to investigate the differences in bond strength of four different indirect composites to the gold alloy and Ni-Cr alloy according to type of metal surface treatment after water storage. Materials and methods: Type IV gold alloy and Ni-Cr alloy were used for casting alloy while four types of indirect composite resins (Gradia, Tescera Sinfony and in;joy) were used in this study. Metal specimens were produced by casting and total of 240 specimens (60 specimens per one indirect composite group) were prepared. After bonding indirect composite resin and undergoing 24 hours of polymerization, customized jig was attached to the metal specimen and shear bond strength were measured using universal testing machine. Also, differences in shear bond strength before and after water storage for 240 hours were also measured. Results: In the measurement of shear bond strength according to the metal surface treatments, bead group showed high strength followed by loop and flatting group (P<.05). After being stored in water bath for 240 hours, Gradia showed statistically significant high bond strength compared to other indirect composite resins in all groups (P<.05). Conclusion: Shearbond strength was found to be different according to type of metal surface treatment and type of metal used after storage in water. Further studies need to be developed for clinical practices as three are still problems of microleakage, stain or wear.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.36 no.1
• /
• pp.1-11
• /
• 2020

Purpose: The purpose was to compare shear bond strength (SBS) of three types of resin for temporary restoration to polyetherketoneketone (PEKK) depending on surface modification. Materials and Methods: Sixty disks made from PEKK were air-abraded with 110 ㎛ alumina particles (Cobra, Renfert GmbH, Hilzinge, Germany) and thirty specimens were divided into two groups each: PEKK without Visio.link (Bredent, Senden, Germany)(U) and with Visio.link (P). Resins for temporary restoration (polymethylmethacrylate; PMMA, polyethylmethacrylate; PEMA, bis-acryl composite resin) in the shape of a square with one side 3.2 mm were bonded to PEKK twenty respectively and classified into six groups (UM, UE, UC, PM, PE and PC). All specimens were stored in distilled water at 37℃ for 24 hours. SBS of each group was measured at a crosshead speed of 2 mm/min in universal testing machine. SBS was compared using one-way ANOVA and a Tukey HSD test (P = 0.05). Results: Group UM and group UE showed a significant difference in SBS with group UC (P < 0.05). Group PC showed a significant increase in SBS than group UC (P < 0.05). Conclusion: It is recommended to apply Visio.link to PEKK for adhering bis-acrylic composite resin, but not for PMMA and PEMA in clinical practice.

• Restorative Dentistry and Endodontics
• /
• v.33 no.2
• /
• pp.83-89
• /
• 2008

The purpose of this study was to evaluate the effect of the polymerization shrinkage and modulus of elasticity of composites on the cusp deflection of class V restoration in premolars. The sixteen extracted upper premolars were divided into 2 groups with similar size. The amounts of cuspal deflection were measured in Class V cavities restored with a flowable composite (Filtek flow) or a universal hybrid composite (Z-250). The bonded interfaces of the sectioned specimens were observed using a scanning electron microscopy (SEM). The polymerization shrinkage and modulus of elasticity of the composites were measured to find out the effect of physical properties of composite resins on the cuspal deflection. The results were as follows. 1. The amounts of cuspal deflection restored with Filtek flow or Z-250 were $2.18\;{\pm}\;0.92{\mu}m$ and $2.95\;{\pm}\;1.13\;{\mu}m$, respectively. Filtek flow showed less cuspal deflection but there was no statistically significant difference (p > 0.05). 2. The two specimens in each group showed gap at the inner portion of the cavity. 3. The polymerization shrinkages of Filtek flow and Z-250 were 4.41% and 2.23% respectively, and the flexural modulus of elasticity of cured Filtek flow (7.77 GPa) was much lower than that of Z-250 (17.43 GPa). 4. The cuspal deflection depends not only on the polymerization shrinkage but also on the modulus of elasticity of composites.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.32 no.3
• /
• pp.184-193
• /
• 2016

Purpose: To evaluate marginal leakage of bulk fill flowable composite resin filling with different curing time by using microcomputed tomography technology. Materials and Methods: 30 previously extracted human molars were randomly divided into 6 groups based upon restorative system and different curing time. Class II cavities (vertical slot cavities) were prepared. An individual metallic matrix was used to build up the proximal wall. The SonicFill or SureFil SDR flow was inserted into the preparation by using 1 bulk increment, followed by light polymerization for different curing times. The different exposure times were 20, 40, and 60 seconds. All specimens were submitted to 5,000 thermal cycles for artificial aging. Micro-CT scanning was performed by using SkyScan 1272. One evaluator assessed microleakage of silver nitrated solution at the resin-dentin interface. The 3D image of each leakage around the restoration was reconstructed with CT-Analyser V.1.14.4. The leakage was analyzed with the Mann-Whitney test. Results: Significant differences were observed between the light curing times, but no significant differences were found between the bulk fill composite resins. Increasing in the photoactivation time resulted in greater microleakage in all the experimental groups. Those subjected to 60 seconds of light curing showed higher microleakage means than those exposed for 20 seconds and 40 seconds. Conclusion: Increasing the photoactivation time is factor that may increase marginal microlekage of the bulk fill composite resins. Further, micro-CT can nondestructively detect leakage around the resin composite restoration in three dimensions.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.1
• /
• pp.1-9
• /
• 2006

Purpose: The purpose of this study was to evaluate the efficacy and substitute possibility of a newly developed flowable composite resins as a luting cement for translucent fiber post. Material & Method: Two kinds of 12 mm translucent fiber Post (D.T. Light-Post (Bisco, USA) and FRC Postec (Ivoclar vivadent, Liechtenstein) was inserted into the teflon mold (7 mm diameter, 9 mm long) and Filtek-Flow (3M ESPE. USA), a light activated flowable composite resin, was polymerized for 60 seconds through the post. Also, the post was cut from the tip to 9 mm, 6 mm, 3 mm, and Filtek-Flow was light cured according to each length. For comparison, 60 seconds light-cured and 24 hours self-cured two dual cured resin cement (Duo-cement (Bisco, USA) and 2 Panavia-F (Kuraray, Japan)) samples were prepared as control group. Also cavities (1 mm in width, 1 mm in depth and 12 mm in length) were prepared using acrylic plate and aluminum bar, and flowable composite resin was flied and light cured by the diffused light from the fiber post's side wall. The degree of polymerization was measured according to the distance from curing light using Vickers' hardness test. Result: Within the limitation of this study, the following conclusions were drawn: 1. Vickers' hardness of light cured dual cured resin cement and flowable composite resin decreased from Panavia-F, Filtek-Flow and Duo-cement accordingly (p<0.05). In the dual curing resin cement, light curing performed group showed higher surface hardness value than self cured only group (p<0.05). 2. Surface hardness ratio (light cured through fiber post /directly light cured) of D.T. Light-Post using Filtek-Flow showed about 70% in the 6 mm deep and about 50% in the 12 mm deep FRC Postec showed only 40% of surface hardness ratio. 3. Surface hardness ratio by diffused light from the post's side wall showed about 50% at 6 mm and 9 mm deep, and about 40% at 12 mm deep in D.T. Light-Post. However, FRC Postec showed about 40% at 6 mm deep, and almost no polymerization in 9 mm and 12 mm deep.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.24 no.1
• /
• pp.82-94
• /
• 1997

For the purpose of establishing the most appropriate method of bonding between glass ionomer liners and composite resin and comparing the materials for sandwich technique, an experiment was performed to measure the shear bond strengths between the two with the variables in the surface treatment of liners and elapsed time till composite buildup. Materials used were Vitrebond and Fuji II LC, each as the restorative and liner respectively, and each group was subdivided by surface treatment (acid etching and sandblasting) and time elapsed from GIC filling to composite buildup (immediately, 1 day, 7 days), consisting 12 groups as a whole. Each subgroup was composed of 10 specimens and the shear bond strength between GIC liners and composite resin was measured under UTM and analyzed. The result were as follows: 1. The shear bond strength between two materials was highest when initially filled Fuji II LC was sandblasted after 1 days and composite built-up (Group FS1). And the lowest value was found when GIC was acid-etched after 7 days and composite built-up (Group FE7). Significant difference was found between the two groups. (P<0.01) 2. In regard of surface treatment of GI liners, acid-etched group (VE) showed higher bond strength than sandblasted group (VS) for Vitrebond. But, the reverse was true for Fuji II LC. (P<0.05) 3. In regard to the time elapsed from GI filling to composite buildup, the group of 1 day elapse showed relatively higher strength for Vitrebond. On the contrary, immediate buildup group (FE0) was stronger for acid-etched group and 1 day elapse group(FS1) was higher for sand-blasted group in Fuji II LC. (P<0.05)

• Restorative Dentistry and Endodontics
• /
• v.39 no.1
• /
• pp.12-16
• /
• 2014

Objectives: Extensively destroyed teeth are commonly restored with composite resin before cavity preparation for indirect restorations. The longevity of the restoration can be related to the proper bonding of the resin cement to the composite. This study aimed to evaluate the microshear bond strength of two self-adhesive resin cements to composite resin. Material and Methods: Composite discs were subject to one of six different surface pretreatments: none (control), 35% phosphoric acid etching for 30 seconds (PA), application of silane (silane), PA + silane, PA + adhesive, or PA + silane + adhesive (n = 6). A silicone mold containing a cylindrical orifice ($1mm^2$ diameter) was placed over the composite resin. RelyX Unicem (3M ESPE) or BisCem (Bisco Inc.) self-adhesive resin cement was inserted into the orifices and light-cured. Self-adhesive cement cylinders were submitted to shear loading. Data were analyzed by two-way ANOVA and Tukey's test (p < 0.05). Results: Independent of the cement used, the PA + Silane + Adhesive group showed higher microshear bond strength than those of the PA and PA + Silane groups. There was no difference among the other treatments. Unicem presented higher bond strength than BisCem for all experimental conditions. Conclusions: Pretreatments of the composite resin surface might have an effect on the bond strength of self-adhesive resin cements to this substrate.

• Advanced Composite Materials
• /
• v.16 no.3
• /
• pp.207-221
• /
• 2007

The filling process of resin injection/compression molding (I/CM) can be divided into injection and compression phases. During the resin injection the mold is kept only partially closed and thus a gap is present between the reinforcements and the upper mold. The gap results in preferential flow path. After the gap is filled with the resin, the compression action initiates and forces the resin to penetrate into the fiber preform. In the present study, the resin flow in the gap is simplified by using the Stokes approximation, while Darcy's law is used to calculate the flow field in the fiber mats. Results show that most of the injected resins enter into the gap during the injection phase. The resin injection time is extremely short so the duration of the filling process is determined by the final closing action of the mold cavity. Compared with resin transfer molding (RTM), I/CM process can reduce the mold filling time or injection pressure significantly.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.88-91
• /
• 2004

In this study, a number of natural fiber henequen reinforced polymer matrix composites were successfully fabricated by means of a compression molding technique using chopped henequen fibers surface-treated with different electron beam irradiation (EBI) dosages, thermoplastic poly(butylene succinate), thermosetting unsaturated polyester and phenolic resins. Their interfacial and thermal characteristics were studied in terms of interfacial shear strength, fracture surface, dynamic mechanical properties, dimensional stability, and thermal stability using single fiber microbonding test, SEM, DMA, TMA, and TGA. The results show that their interfacial and thermal properties significantly depend on the intensity of EBl treatment on the natural fiber surface.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.172-176
• /
• 1999

에폭시 수지의 강인성 향상을 위하여 양말단에 아민 반응기를 가지는 PES-CTBN-PES triblock copolymer를 합성하여 이를 에폭시 수지의 강인화제로 사용하였으며 경화제로는 p-DDS(p-dichlorodiphenylsulfone)를 사용하였다. 또한 공중합체에 의한 물성 향상효과를 CTBN과 PES-NH$_2$의 블렌드에 의한 경우와 비교하였다. 강인화된 에폭시 수지의 물성은 강인성 및 굴곡특성을 측정하여 분석하였으며, 열특성은 DSC, TGA, 및 DMA에 의해 실시되었다. 그리고 강인화된 에폭시 수지의 강인성 향상 mechanism을 규명하기 위하여 파단면을 SEM으로 분석하여 상분리 거동을 고찰하였다. 높은 유리전이온도와 우수한 기계적 물성을 가지는 고성능 기능성 폴리설폰(PES-NH$_2$)과 상용 액상 고무 첨가제인 CTBN을 이용하여 합성된 공중합체를 강인화제로 사용함으로써 열안정성, 탄성률 및 내식성의 감소없이 에폭시 수지의 쳐대 단점인 강인성을 최적 수준으로 개선시킬 수 있었으며 공중합체의 에폭시 수지에 대한 우수한 용해도에 따른 가공성이 향상되었다.