• Restorative Dentistry and Endodontics
• /
• v.26 no.2
• /
• pp.153-161
• /
• 2001

The purpose of this study was to evaluate microleakage of six current dentin bonding systems. In this in vitro study, class V cavities were prepared on buccal and lingual surfaces of thirty extracted human molars. Each margin was on enamel and dentin/cementum. Experimental teeth were randomly divided into six groups of 5 each. Group 1 : Scotchbond Multi-Purpose; Group 2 : Single Bond; Group 3 : Prime&Bond NT ; Group 4 : Clearfil Liner Bond 2 ; Group 5 : MAC Bond II ; Group 6 : One-up Bond F. The bonding agent and composite resin were applied to class V cavities according to manufacturer's directions. After thermocycling, the specimens were immersed in 0.5% basic fuchsin dye solution for 6 hours and sectioned longitudinally through the center of the restoration with a low speed diamond saw. The degree of microleakage was measured as the extent of dye penetration under the stereomicroscope at $\times$20. The data were analyzed using one way ANOVA. When significant differences found. multiple comparisons were made using Duncan's Multiple Range Test. The results of this study were as follows: 1. In all groups, leakage value seen at the enamel margin was significantly lower than that seen at the dentin margin(P<0.001). 2. At the enamel margin, none of the dentin bonding systems used in this study showed statistically significant difference in leakage values(P<0.05). 3. At the cementum margin, group 3 showed the highest leakage value, and others were decreased as group 5, 6, 4 in that order, and group 1, 2 showed the lowest leakage value. There was statistically significant difference between group 3 and the other groups except for group 5(P<0.05).

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.304-315
• /
• 1998

The purpose of this study was to evaluate the microleakage of light cured glass ionomer restorative materials in class 5 cavities. In this in vitro study, class 5 cavities were prepared on buccal and lingual surfaces of forty extracted human premolars and molars on cementum margin. These specimen were randomly divided into four groups of 10 each : Group 1 was Fugi II (control), Group 2 was Fugi II LC, Group 3 was Vitremer, and Group 4 was Dyract. Group 2 was also divided once more into 2 groups of 5 each : Group 2-1 was pretreated with dentin conditioner and Group 2-2 was not. All teeth were restored according to the manufacturer's instructions. After 500 thermocycling between $5^{\circ}C$ and $55^{\circ}C$, the 40 teeth were placed in 2 % Methylene blue dye for 24hr, then rinsed with tab water. The specimen were embedded in clear resin, then sectioned buccolingually through the center of restoration with a low speed diamond saw. The dye penetration on each of the specimen were then observed with a stereomicroscope at 20. The results of the study were statistically analyzed using the Student-Newman-Keuls Methods and the Mann-Whitney Rank Sum Test. Tooth restorative interfaces were evaluated using SEM analysis. Results were as follows, 1. Compared to conventional glass ionomer restoratioqs, all light cured glass ionomer restorations were fairly resistant to microleakage (P<0.05). 2. Groups 3 (Vitremer) and Group 4 (Dyract) were found to be the most resistant, Group 2 (Fugi II LC) fairly resistant, and Group 1 (Fugi II) least resistant to microleakage(P<0.05). 3. No significant differences were found between Group 2-1 and Group 2-2 (P>0.08). 4. With the backscattered SEM analysis, the degrees to which tight bonding occurred were also observed in all the groups except for Group 1. Group 4 showed the highest degree of tight bonding than any other materials used in this study.

• Restorative Dentistry and Endodontics
• /
• v.33 no.1
• /
• pp.28-38
• /
• 2008

This study was to investigate the influence of composite resins with different elastic modulus, cavity modification and occlusal loading condition on the stress distribution of restored notch-shaped noncarious cervical lesion using 3-dimensional (3D) finite element (FE) analysis. The extracted maxillary second premolar was scanned serially with Micro-CT. The 3D images were processed by 3D-DOCTOR. ANSYS was used to mesh and analyze 3D FE model. A notch-shaped cavity and a modified cavity with a rounded apex were modeled. Unmodified and modified cavities were filled with hybrid or flowable resin. After restoration, a static load of 500N was applied in a point-load condition at buccal cusp and palatal cusp. The stress data were analyzed using analysis of principal stress. The results were as follows: 1. In the unrestored cavity, the stresses were highly concentrated at mesial CEJ and lesion apex and the peak stress was observed at the mesial point angle under both loading conditions. 2. After restoration of the cavity, stresses were significantly reduced at the lesion apex, however cervical cavosurface margin, stresses were more increased than before restoration under both loading conditions. 3. When restoring the notch-shaped lesion, material with high elastic modulus worked well at the lesion apex and material with low elastic modulus worked well at the cervical cavosurface margin. 4. Cavity modification the rounding apex did not reduce compressive stress, but tensile stress was reduced.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.269-277
• /
• 1998

This in vitro study compared the microleakage of 4 lining conditions when used with Gallium alloy GF II and Valiant PhD. Class V cavity was prepared on both buccal and lingual surface of 80 extracted human premolar & molar teeth with one margin in enamel and another in dentin. Before restoration, prepared cavities were applied to no-liner, cavity varnish, Scotchbond multipurpose, and Superbond D-liner II plus according to manufacture's instructions. The restored teeth were stored in saline for 1 week, then thermocycled for 100 times, stained with 0.5% basic fuchsin dye for 1 day, sectioned, and observed using a light microscope. Following results were obtained. 1. The leakage value of Superbond-lined group showed significantly lower than that of nolined group on both margins of Valiant PhD(p<0.05). 2; There was no significant difference between the 4 lining conditions in Gallium alloy GF II (p>0.05). 3. When We make a comparison between Gallium alloy GF II and Valiant PhD under same lining conditions, the microleakage value of Gallium alloy GF II showed lower than that of Valiant PhD on occlusal & gingival margin(p<0.05) except for Superbond-lined group(p>0.05).

• Restorative Dentistry and Endodontics
• /
• v.13 no.1
• /
• pp.139-150
• /
• 1988

The purpose of this study was to evaluate the marginal adaptation of Class V resin restorations by the filling techniques. The cavities were filled with Heliosit$^{(R)}$ light curing composite resin system in accordance with the following three filling techniques - bulk-pack placement technique, apical to occlusal layering placement technique, and buccolingual layering placement technique. And the interface between the restoration and the tooth structure was observed with scanning electron microscope. The following results were obtained. 1. Marginal adaptation of enamel showed excellent irrespective of the filling techniques. 2. Marginal leakage of dentin was observed irrespective of the filling techniques. 3. No difference of marginal adaptation according to the filling techniques was observed in light curing composite resin.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.558.2-558
• /
• 2001

The aims of this study are (1) to investigate the relation of irradiation mode, polymerization shrinkage and degree of cure of composite resin and(2) it effect on micorleakage of class V restorations. VIP(BISCO Dental Products, Schaumburg, IL, USA) and Optilux 501 (Demetron/Kerr, Danbury, CT, USA) curing lights were used for curing Z-250 composite resin following irradiation mode: VIP 200㎽d, VIP 400㎽, VIP 600㎽, pulse-delay(200㎽ 3sec, 5min wait, 600㎽ 30sec), Optilux R mode.(omitted)

• Restorative Dentistry and Endodontics
• /
• v.30 no.2
• /
• pp.112-120
• /
• 2005

This study was done to evaluate whether there were any differences in microleakage of class V composite restorations according to restoration site and cavity size. Total sixty-four restorations were made in molar teeth using Esthet-X. Small ($2\;{\times}\;2\;{\times}\;1.5\;mm$) and large ($4{\times}2{\times}1.5\;mm$) restorations were made at the buccal/lingual surface and the proximal surface each. After 1,000 times of thermocycling ($5^{\circ}\;-\;55^{\circ}C$), resin replica was made and the percentage of marginal gap to the whole periphery of the restoration was estimated from SEM evaluation. Thermocycled tooth was dye penetrated with $50\%$ silver nitrate solution. After imbedding in an auto-curing resin, it was serially ground with a thickness of 0.25 mm. Volumetric microleakage was estimated after reconstructing three dimensionally. Two-way ANOVA and independent T-test for dye volume, Mann-Whitney U test for the percentage of marginal gap, Spearman's rho test for the relationship between two techniques were used, The results were as follows : 1. The site and size of the restoration affected on the microleakage of restoration. Namely, much more leakage was seen in the proximal and the large restorations rather than the buccal/lingual and the small restorations. 2. Close relationship was found between two techniques (Correlation coefficient = 0.614/ P = 0.000). Within the limits of this study, it was noted that proximal and the large restorations leaked more than buccal/lingual and the small restorations. Therefore, it should be strictly recommended large exposure of margins should be avoided by reducing unnecessary tooth reduction.

• Journal of the Korean Society of Environmental Restoration Technology
• /
• v.9 no.4
• /
• pp.24-35
• /
• 2006

The vascular plants of the studied area was listed 384 taxa of 90 families, 234 genera, 331 species, 1 subspecies, 45 varieties and 7 forms. The flora of each reservoir, 285 taxa of 83 families, 190 genera, 247 species, 1 subspecies, 30 varieties, 7 forms in Osongjae, 117 taxa of 39 families, 87 genera, 100 species, 17 varieties in Ogongjae, 83 taxa of 30 families, 67 genera, 73 species, 8 varieties, 2 forms in Shinyongjae and 86 taxa of 33families, 70 genera, 75 species, 1 subspecies, 10 varieties in Eodujae. Based on the list of the rare plants by the Forest Research Institute, 3 taxa were recorded in the studied areas; Magnolia kobus (Preservation priority order : No. 187), Penthorum chinense (No. 144), Prunus yedoensis (No. 110) and based on the list of Korean endemic plants, 4 taxa were recorded; Populus tomentiglandulosa, Clematis trichotoma, Prunus yedoensis, Paulownia coreana. Specific plant species by floral region were total 15 taxa; Prunus yedoensis in class V, 2 taxa (Carex idzuroei, Magnolia kobus) in class IV, 2 taxa (Monochoria korsakowi, Poncirus trifoliata ) in class III, 10 taxa (Sagittaria aginashi, Salix glandulosa, Clematis brachyura, Nymphoides peltata, etc.) in class I. The naturalized plants in this site were 13 families, 29 genera, 43 species, 1 varieties, 44 taxa and naturalization rate was 11.5% and based on the list of an ecosystem disturbance plants, 3 taxa were recorded in the studied areas : Paspalum distichum, Solanum carolinense, Ambrosia artemisiifolia var. elatior. The hydrophytes was listed 31 taxa of 15 families, 20 genera, 29 species, 2 varieties and Eleocharis mamillata var. cyclocarpa, Penthorum chinense, Soirodela polyrhiza were recorded in Osongjae, Sagittaria aginashi, Eleocharis kuroguwai, Scirpus juncoides, Scirpus triqueter, Monochoria korsakowi, Monochoria vaginalis var. plantaginea were recorded in Ogongjae. Besides, Scirpus fluviatilis, Trapa pseudoincisa were recorded in Shinyongjae and Scirpus triangulatus, Nymphoides peltata, Myriophyllum verticillatum were recorded in Eodujae. This site is located in the urban area and ecosystem-disturbing wild animal and plant has been imported here, therefore ecosystem has been disturbed more and more. The wetland here rapidly has changed into upland, so it needs conservation measures through long-term monitoring.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.182-190
• /
• 2009

Statement of problem: Microleakage at the occlusal and gingival margin of Class V cavities restored with composite resin has traditionally been considered an obstacle to successful restoration. Purpose: The aim of this study was to assess the effectiveness of three different surface sealants(Fortify, Permaseal and Biscover LV) on the marginal sealing of Class V light-activated composite resin restorations(Z250). Material and methods: Forty noncarious human premolars and molars extracted within a three-month period were selected. Class V cavities with the occlusal margin in enamel and gingival margin in cementum were prepared in both buccal and lingual surfaces. The teeth, randomly assigned in four groups with twenty cavities in each group, were restored with composite resin after applying an adhesive system(Clearfil SE bond). After the finishing and polishing procedures, the restorations were covered with a specific surface sealants, except for the control samples, which were not sealed. After placing restorations, the specimens were thermocycled, and immersed in a 2% methylene blue solution for twenty four hours and sectioned longitudinally. The marginal microleakage was evaluated at the occlusal and gingival interfaces using a microscope and compared among the four groups using ANOVA test and Wilcoxon Rank-Sum test($\alpha$=0.05). Results: Statistical analysis showed that there was significantly less leakage when the surface sealants were used than there was in control group(P<.05). There were no significant differences of microleakage at occlusal and gingival margins among groups. There were no significant differences between microleakage of occlusal and gingival margins in each group. Fortify was not statistically different from control group at the gingival margin(P>.05). Conclusion: Application of surface sealants was an effective method of surface coating in reducing microleakage at occlusal and gingival margins of Class V composite resin restorations. However, it is certain that some microleakage still occurred despite the application of surface sealants, especially gingival margins.

• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.377-384
• /
• 2007

Present tooth bonding system can be categorized into total etching bonding system (TE) and self-etching boding system (SE) based on their way of smear layer treatment. The purposes of this study were to compare the effectiveness between these two systems and to evaluate the effect of number of themocycling on microleakage of class V composite resin restorations. Total forty class V cavities were prepared on the single-rooted bovine teeth and were randomly divided into four experimental groups: two kinds of bonding system and another two kinds of thermocycling groups. Half of the cavities were filed with Z250 following the use of TE system, Single Bond and another twenty cavities were filled with Metafil and AQ Bond, SE system. All composite restoratives were cured using light curing unit (XL2500, 3M ESPE, St. Paul, MN, USA) for 40 seconds with a light intensity of $600mW/cm^2$. Teeth were stored in distilled water for one day at room temperature and were finished and polished with Sof-Lex system. Half of teeth were thermocycled 500 times and the other half were thermocycled 5,000 times between $5^{\circ}C$ and $55^{\circ}C$ for 30 second at each temperature. Teeth were isolated with two layers of nail varnish except the restoration surface and 1 mm surrounding margins. Electrical conductivity (${\mu}A$) was recorded in distilled water by electrochemical method. Microleakage scores were compared and analyzed using two-way ANOVA at 95% level. From this study, following results were obtained: There was no interaction between variables of bonding system and number of thermocycling (p = 0.485). Microleakage was not affected by the number of thermocycling either (p = 0.814). However, Composite restoration of Metafil and AQ Bond, SE bond system showed less microleakage than composite restoration of Z250 and Single Bond, TE bond system (p = 0.005).