THE COMPARISON OF MICROLEAKAGE OF CLASS V COMPOSITE RESIN RESTORATIONS WITH VARIOUS DENTIN BONDING SYSTEMS

5급 와동에서 수종의 상아질 접착제에 따른 미세누출의 비교

The purpose of this study was to evaluate microleakage of six current dentin bonding systems. In this in vitro study, class V cavities were prepared on buccal and lingual surfaces of thirty extracted human molars. Each margin was on enamel and dentin/cementum. Experimental teeth were randomly divided into six groups of 5 each. Group 1 : Scotchbond Multi-Purpose; Group 2 : Single Bond; Group 3 : Prime&Bond NT ; Group 4 : Clearfil Liner Bond 2 ; Group 5 : MAC Bond II ; Group 6 : One-up Bond F. The bonding agent and composite resin were applied to class V cavities according to manufacturer's directions. After thermocycling, the specimens were immersed in 0.5% basic fuchsin dye solution for 6 hours and sectioned longitudinally through the center of the restoration with a low speed diamond saw. The degree of microleakage was measured as the extent of dye penetration under the stereomicroscope at $\times$20. The data were analyzed using one way ANOVA. When significant differences found. multiple comparisons were made using Duncan's Multiple Range Test. The results of this study were as follows: 1. In all groups, leakage value seen at the enamel margin was significantly lower than that seen at the dentin margin(P<0.001). 2. At the enamel margin, none of the dentin bonding systems used in this study showed statistically significant difference in leakage values(P<0.05). 3. At the cementum margin, group 3 showed the highest leakage value, and others were decreased as group 5, 6, 4 in that order, and group 1, 2 showed the lowest leakage value. There was statistically significant difference between group 3 and the other groups except for group 5(P<0.05).