• Computers and Concrete
• /
• 제11권4호
• /
• pp.305-316
• /
• 2013

This paper aims to study the effect of measurement methods and cracking on chloride transport of concrete materials. Three kinds of measurement methods were carried out, including immersion test, rapid migration test and steady-state migration test. All of these measurements of chloride transport show that chloride ion diffusion coefficient decreased with the reduction of water to cement ratio. Results of the immersion test were less than that of rapid migration test and steady-state migration test. For the specimen of lower water to cement ratio, the external electrical field has little effect on chloride binding relatively. Compared with the results obtained by these different measurement methods, the lower water to cement ratio may cause smaller differences among these different methods. The external voltage can reduce chloride binding of concrete, and the higher electrical field made a strong impact on the chloride binding. Considering the effect of high voltage on the specimen, results indicate that results based on the steady-state migration test should be more reasonable. For cracked concrete, cracking can accelerate the chloride ion diffusion.

• Computers and Concrete
• /
• 제31권6호
• /
• pp.485-499
• /
• 2023

Both damage and unsaturated conditions accelerate the transport of erosive media inside concrete. However, their combined effects have not been fully investigated. A multiscale mortar model using representative volume elements is developed, capturing the number and distribution in each phase. Afterwards, mortar damage microstructure evolution is simulated in the tensile process. Finally, the unsaturated mortar transport is predicted and analysed. The results indicate that damage significantly affects the diffusion process in the early stage, while the transport performance is weakened due to the obstruction of the nontransport phase in the later stage. The higher the saturation and the more connected pores, the faster the diffusion rate of chloride ions. Chloride ions spread around the cracks in a tree-like manner along. The model can very well predict the chloride ion transport performance of unsaturated and damaged mortar.

• Advances in concrete construction
• /
• 제4권4호
• /
• pp.305-317
• /
• 2016

Porous materials such as concrete could be subjected to aggressive ions transport. Durability of cement paste is extremely depended on water and ions penetration into its interior sections. These ions transport could lead different damages depending on reactivity of ions, their concentrations and diffusion coefficients. In this paper, chloride diffusion process in cement hydrates is simulated at atomistic scale using molecular dynamics. Most important phase of cement hydrates is calcium silicate hydrate (C-S-H). Tobermorite, one of the most famous crystal analogues of C-S-H, is used as substrate in the simulation model. To conduct simulation, a nanopore is considered in the middle of simulation cell to place water molecules and aggressive ions. Different chloride salts are considered in models to find out which one is better for calculation of the transport properties. Diffusion coefficients of water molecules and chloride ions are calculated and validated with existing analytical and experimental works. There are relatively good agreements among simulation outputs and experimental results.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1997년도 봄 학술발표회 논문집
• /
• pp.254-260
• /
• 1997

Chloride-induced corrosion of reinforcement is one of the main factors which cause the deterioration of concrete structures. Durability and service lives of the concrete sturctures should be predicted in order to minimize the risk of corrosion of reinforcement. The objective of this study is to suggest the basis of analytical methods of predicting the corrosion threhold time of concrete structures. Based on the chemistry and physics of chloride ion transport and corrosion process, chloride intrusion with various exposure conditions, variability of diffusivity and transport of pore water in concrete are taken into consideration in applying finite element formulation to the predicion of corrosion threhold time. The effects of main factors on the prediction of chloride intrusion and corrosion threhold time are examined. In addition, after chloride diffusivities of several mixture proportions with different parameters are measured by chloride diffusion test, the exemplary anayses of corrosion threhold time of those mixture proportions are carried out.

• Computers and Concrete
• /
• 제23권2호
• /
• pp.145-153
• /
• 2019

Adaptive schemes are constructed in this paper for modeling the effective chloride diffusion coefficient of cement-based materials (paste and concrete). Based on the polarization approximations for the effective conductivity of isotropic multicomponent materials, we develop some fitting procedures to include more information about the materials, to improve the accuracy of the scheme. The variable reference parameter of the approximation involves a few free scalars, which are determined through the available numerical or experimental values of the macroscopic chloride diffusion coefficient of cement paste or concrete at some volume proportions of the component materials. The various factors that affect the chloride diffusivity of cement-based material (porous material structure, uncertainty of value of the chloride diffusion coefficient in water-saturated pore spaces, etc.) may be accounted to make the predictions more accurate. Illustrations of applications are provided in a number of examples to show the usefulness of the approach.

• Computers and Concrete
• /
• 제15권2호
• /
• pp.183-198
• /
• 2015

Chloride ingress implies a complex interaction between physical and chemical process, in which heat, moisture and chloride ions transport through concrete cover. Meanwhile, reinforced concrete structure itself undergoes evolution due to variation in temperature, relative humidity and creep effects, which can potentially change the deformation and trigger some micro-cracks in concrete. In addition, all of these process show time-dependent performance with complex interaction between structures and environments. In the present work, a time-dependent behavior of chloride transport in reinforced concrete beam subjected to flexural load is proposed based on the well-known section fiber model. The strain state varies because of stress redistribution caused by the interaction between environment and structure, mainly dominated by thermal stresses and shrinkage stress and creep. Finally, in order to clear the influence of strain state on the chloride diffusivity, experiment test were carried out and a power function used to describe this influence is proposed.

• 한국결정성장학회지
• /
• 제19권3호
• /
• pp.116-124
• /
• 2009

Our computational studies for the physical vapor transport crystal growth of $Hg_2Cl_2-Cl_2$ system evidence suggests that the PVT growth process exhibits the diffusion-dominated behaviors for aspect ratios more than and equal to 10, which would provide purely diffusive transport conditions adequate to microgravity environments less than $10^{-3}g_0$. Also, the regimes of high temperature difference based on the fixed source temperature of $380^{\circ}C$, where ${\Delta}T$ is relatively large enough for the crystal growth of mercurous chloride, the transport rates do not keep increasing with ${\Delta}T$ but tend to some constant value of $2.12\;mole\;cm^{-2}s^{-1}$. For the aspect ratios of 5, 10, and 20, the transport rate is directly proportional to the total pressure of the system under consideration. For Ar = 5, the rate is increased by a factor of 2.3 with increasing the total pressure from 403 Torr to 935 Torr, i.e., by a factor of 2.3. For both Ar = 10 and 20, the rate is increased by a factor of 1.25 with increasing the total pressure from 403 Torr to 935 Torr.

• Corrosion Science and Technology
• /
• 제22권2호
• /
• pp.115-122
• /
• 2023

This study aimed to elucidate causes of corrosion of heat transport pipes and air vents installed under a manhole of heat transport facilities and suggest effective anticorrosive measures by applying paints or adhesive tapes. It was found that air vent corrosion was attributed to corrosion under insulation caused by the inflow of water and the enrichment of chloride ions. The infiltrated water caused a hydrolysis of polyurethane foam (PUF) insulation by concentrating chloride ions at the interface between a pipe and the PUF. As insulator deteriorated, more chloride ions were eluted as confirmed by ion chromatograph (IC) analysis. As an effective method to prevent air vent corrosion, different types of paints and adhesive tapes with higher corrosion resistance on chloride ions were applied and environmental resistance tests were performed with those samples. Based on environmental test results of samples exposed to 10% HCl solution, it was revealed that a wax tape was the most adequate from a viewpoint of stability at operating condition, environmental resistance, surface treatment, and field applicability.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.635-640
• /
• 2001

In this study, a mathematical model is established for prediction of chloride penetration in unsaturated cracked early-age concrete. The model is combined with models for thermo-hygro dynamic coupling of cement hydration, moisture transport and micro-structure development. Chloride permeability and water permeability at cracked early-age concrete specimens are evaluated using a rapid chloride permeability test and a low-pressure water permeability test, respectively. Then, a homogenization technique is introduced into the model to determine equivalent diffusion coefficient and equivalent Permeation coefficient. Increased chloride transport due to cracks at the specimen could be predicted fairly well by characterizing the cracks using proposed model. Proposed model is verified by comparing diffusion analysis results with test results.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2010년도 춘계 학술대회 제22권1호
• /
• pp.477-478
• /
• 2010

Concretes with binary blends of Portland cement, silica fume, fly ash and ground granulated blast furnace slag were produce to investigate their effects on compressive strength and chloride transport in rapid chloride permeability. Ten different mix of concrete with 0.45 water/binder were produced. Portland cement was replacedby: (i) 10%, 20%, 30% Fly ash (ii) 3%, 5%, 10% Silica Fume (iii) 20%, 40%, 60% GGBS. Compressive strength of concrete with the pozzolans is higher compared to that of the Portland cement concrete. The test results indicate the fly ash, silica fume, and ground granulated furnace slag greatly reduce the rapid chloride permeability of concrete. It was concluded that pozzolans are more effective to reduce chloride permeability of concrete.