• Journal of the Korean Wood Science and Technology
• /
• v.33 no.3 s.131
• /
• pp.45-52
• /
• 2005

This research was performed to evaluate adsorption behavior of woody charcoals obtained from wood powder, fiber and bark of spruce (Abies sibirica Ledeb). The wood materials were carbonized at various temperatures for 1 hour using experimental rotary kiln without any inert gas. The adsorption capacity of iodine and toluene, specific surface area and removal efficiency of acetic acid and ammonia gas of those charcoals were measured. The higher was the temperature for carbonization, the lower yields of charcoals were. Ash content of bark charcoal was higher than that of wood powder charcoal or fiber charcoal. Elemental analysis of woody charcoal revealed that the content of carbon was gradually lincreased as carbonization temperature was higher. When carbonization temperature was higher, adsorption capacity of woody charcoals for iodine was much improved. Wood powder charcoal and fiber charcoal were more effective for iodine adsorption rather than bark charcoal. Capacity of toluene adsorption was the highest in the charcoal of $600^{\circ}C$. Charcoals produced at high temperature efficiently removed acetic acid gas, while charcoals carbonized at low temperature such as $400^{\circ}C$ were proper to remove ammonia gas. This difference may be explained that the acidity of charcoals depends on the carbonization temperature: charcoals of low temperature indicate acidic property, while those of high temperature turned to alkaline.

• Korean Chemical Engineering Research
• /
• v.60 no.2
• /
• pp.208-216
• /
• 2022

Surface morphology and adsorption characteristics of black and white charcoals prepared from Korean traditional kiln were quantitatively analyzed. TGA and elemental analysis of charcoals were different from produced kiln, and thermal degradation temperature and carbon content of white charcoals were apparently higher than those of black charcoals. Surface morphology shows the activation progressed through the longitudinal direction of woods and new micropores were developed to radial direction on the surface of macropores as the furthermore activation resulting in the pore connection. BET adsorption isotherms show that there are low-pressure hysteresis due to the no desorption of adsorbates, which resulted in unique Type of charcoals overlapping Type I and Type IV. Such a low-pressure hysteresis is occurred from expansion of adsorbates, which were embedded in the micropore entrances and did not get out during the desorption run. The characteristics of charcoals such as specific surface area and pore size distribution did not show correct values depending on not only produced company but also sampling sites of one piece of charcoal. Therefore, it is not easy to suggest the quantitative characteristics of charcoals prepared from Korean traditional kiln. On the other hand, preparation the quality standard of charcoal is necessary for their special uses such as adsorbent.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.3
• /
• pp.181-186
• /
• 2013

In this work, charcoal making characteristics of Quercus phyllyaeoides (which has been known as one of best raw materials for charcoals) was investigated. Charcoal from Quercus phyllyaeoides had more than 85% of fixed carbon, which is 5~25% higher fixed carbon content than other charcoals. Also specific gravity of this charcoal was more than 1.0, which is quite higher than other black charcoals (average of commercial products: 0.52) or white charcoals (average of commercial products: 0.73). Methylene blue adsorption, pH, and adsorption of water vapour was lower than other commercial charcoals. Carolic value of this charcoal was similar to other commercial products. Far infrared ray's emission from this charcoal was higher than others. Application of charcoal from Quercus phyllyaeoides should be consider the characteristics of this product.

• Resources Recycling
• /
• v.17 no.5
• /
• pp.66-75
• /
• 2008

Using a pinus koraiensis and pinus rigida which are normally being discarded in South Korea, the optimal condition of producing charcoals has been studied to develop activated carbons which can be recycled as a higher value-added product. A study on manufacture of activated carbons from a discarded timber consists of two processes, the production process of charcoals from a discarded timber by low temperature pyrolysis process and the production process of activated carbons from the charcoals by chemical activation reaction. This study deals with the production process of charcoals from a discarded timber by low temperature pyrolysis process. As a results of experiment, it was investigated that charcoals produced through drying at $150^{\circ}C$ for 6hr and pyrolysis process at $500^{\circ}C$ for 1hr had the highest values in physical properties such as iodine number and BET surface area. Furthermore, through observing SEM images, the maximum development of porosity had been founded in this condition. It was confirmed that values of physical properties on using a pinus koraiensis are superior to the ones when using a pinus rigida. When charcoals were produced from a pinus koraiensis in this condition, BET surface area was approx. $640m^2/g$.

• Journal of Conservation Science
• /
• v.24
• /
• pp.13-22
• /
• 2008

The identification of species, hygroscopic property, and ability of ethylene gas absorption of 23 ancient charcoals excavated from wooden coffin burials and roof-tile kilns of Chudong-ri cultural site were investigated. All of the 12 charcoals excavated from wooden coffin burials were broad-leaved trees. Among the total 12 samples, 9 samples were Lepidobalanus and others were Celtis spp.. On the other hand, other 11 charcoals from roof-tile kilns were needle-leaved tree, Pinus spp.(hard pine). The broad-leaved tree charcoals from wooden coffin burials showed a higher moisture absorption capacity than needle-leaved tree charcoals from roof-tile kilns. The ethylene gas absorption was greater in the Lepidobalanus charcoal than that of Celtis spp. and Pinus spp. (hard pine) charcoal. The broad-leaved tree charcoal having high absorption ability of substances was due to a large microporous and specific surface area. Therefore, it was estimated that broad-leaved tree charcoals were filled in order to make favorable condition in tomb. The wood quality of pine is soft and easy to burn because of low specific gravity, as well as high calorific value by resin in wood. We could assume that the pine wood was used as fuel for roof-tile kilns because of easy control of heating and thermal power.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.29 no.2
• /
• pp.279-285
• /
• 2005

In order to activate the characteristics of charcoals in fiber systems, this study was carried out to experiment with the particle size from two micrometers to ten micrometers of charcoal powders on silk fabrics. The results obtained were as follows; The silk fabrics were dyed with gray color by charcoals effectively. The K/S value, that is indicative of the dye affinity, became higher as the increase of dyeing temperature, dyeing time, and dyeing concentration. Te dyeing effects were the highest with 50%(o.w.f.) of charcoals at $100^{\circ}C$ for 120 minutes in this experiments, It was observed the surfaces of silk fibers were mainly adcorbed with charcoal powders of the particle size from two micrometers to four micrometers by scanning electron microscope. Dyed silk fabrics showed comparatively low fastness to the fade of launding, the stain of the treatment of perspirations, and the strain of water fastness test, but good fastness to the stran of laundering, te drycleaning, the fade of treatment of perspirations, and the fade of water fastness test. In connection with the functional properties of dyed fabrics, the deodorizations were drastically improved, and the far-infrared emissions improved highly, and also the antibacterials were comparatively good.

• Journal of the Korean Wood Science and Technology
• /
• v.30 no.1
• /
• pp.34-39
• /
• 2002

This study examined the effect of carbonized wastewoods on purification of waste water. The purification ability of charcoals(lump-shaped, approximately 3×3×3 cm) maded by wood-based material for waste water from a kitchen and septic tank was superior to those of thinned wood. For lump-shaped charcoal, gaps between particles in particleboard, and gaps between fibers in MDF were much more effective than micropore in purification of waste water. After purification test, color of waste water from wood-based material charcoals were much more lighter than thinned wood charcoals. In addition, odors of waste water from both charcoals tended to be decreased.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.1
• /
• pp.40-51
• /
• 2006

The objective of this research is to analyze a possibility for the utilization of carbonized bark and develop the technique for carbonization of bark for using as the adsorbent, the soil improvement agent, the carrier for microbial activity, health products, and so on. The properties of bark charcoals such as methylenehlue adsorption (MBA), equilibrium moisture content (EMC), far infra rad emissivity, pH, water retention and caloric value were analyzed. The MBA values of bark charcoals carbonized for 8 hr of carbonization time at $800^{\circ}C$ of carbonization temperature for Larix leptolepis, Pinus koraiensis, Pinus rigida were greater than 110 mg/g. The bark charcoals pH values of all three species that were carbonized for 4 hr of carbonization time at $400^{\circ}C$ of carbonization temperature was 6.6 and carbonized for 4 hr at 600 and $800^{\circ}C$ was about 9. Therefore the bark charcoals of those species could be used as charcoals if the carbonization temperature and time were controlled.

• Journal of the Korean Wood Science and Technology
• /
• v.30 no.4
• /
• pp.33-40
• /
• 2002

This research was to investigate the adsorption characteristics of charcoals of major Korean wood species (thinned trees) and wood-based materials. As carbonization time and temperature increased, methylene-blue adsorption (MBA) of charcoals of thinned trees and wood-based materials increased. Pinus koraiensis charcoal showed the highest MBA. MBA of softwoods was higher than that of hardwoods. There was a negative correlation between air-dried specific gravity before carbonization and MBA of carbonized thinned trees. The MBA of wood-based materials showed similar value, but wood-based materials in MBA was lower than thinned woods. Surface area and total pore volume of thinned trees and wood-based materials increased as carbonization temperature increased. The species showing highest MBA appeared to have the highest surface area at the carbonization temperature of 600℃ as well. There was a positive correlation between surface area, total pore volume and MBA of charcoals. The charcoal of wood-based materials generally exhibited micro pores.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.6
• /
• pp.69-76
• /
• 2008

To estimate removal ability of harmful gas by charcoal, we carbonized Red oak (Quercus mongolica Fischer) wood and Larch (Larix leptoepis) bark at $300^{\circ}C$, $600^{\circ}C$ and $900^{\circ}C$ for 1 hour. Gas removal ratios was increased with carbonization temperature but there is no difference between wood and bark charcoal. In the case of bad smell and VOC gas, woody charcoal including bark charcoal carbonized at $300^{\circ}C$ showed low removal ratio, less than 50%, whereas woody charcoals which was carbonized at more than $600^{\circ}C$ reached almost 100% removal ratio to bad smell gas such as trimethylamine, methymercaptan, hydrogen sulfide, and to VOC such as benzene, toluene, xylene in $5{\ell}$ tedler bag with each gas of 100 ppm. It was thought that because charcoals carbonized at high temperature, for example, $600^{\circ}C$ or $900^{\circ}C$ have enough specific surface area to adsorb gas of 100 ppm. Moreover these charcoals rapidly removed almost gas in 10 minutes. However, acetylene, $SO_2$ and $NO_2$, charcoals which was carbonized more than $600^{\circ}C$ and which showed high removal ratio had low gas removal ratio of 40% at even 4 hours adsorption. It was concluded that adsorptive ability of woody charcoal was mainly influenced with carbonizing temperature, so that different charcoals carbonized at different temperature brings different gas removal ratio because these charcoals have not only different physical factor such as specific surface area but different chemical characteristic such as functional group, expected.